Objectives. The surface of pure titanium (Ti) shows decreased histocompatibility over time; this phenomenon is known as biological ageing. UV irradiation enables the reversal of biological ageing through photofunctionalisation, a physicochemical alteration of the titanium surface. Ti implants are sterilised by UV irradiation in dental surgery. However, orthopaedic biomaterials are usually composed of the alloy Ti6Al4V, for which the antibacterial effects of UV irradiation are unconfirmed. Here we evaluated the bactericidal and antimicrobial effects of treating Ti and Ti6Al4V with UV irradiation of a lower and briefer dose than previously reported, for applications in implant surgery. Materials and Methods. Ti and Ti6Al4V disks were prepared. To evaluate the bactericidal effect of UV irradiation, Staphylococcus aureus 834 suspension was seeded onto the disks, which were then exposed to UV light for 15 minutes at a dose of 9 J/cm. 2. To evaluate the antimicrobial activity of UV irradiation, bacterial suspensions were seeded onto the disks 0, 0.5, one, six, 24 and 48 hours, and three and seven days after UV irradiation as described above. In both experiments, the bacteria were then harvested, cultured, and the number of colonies were counted. Results. No colonies were observed when UV irradiation was performed after the bacteria were added to the disks. When the bacteria were seeded after UV irradiation, the amount of surviving bacteria on the Ti and Ti6Al4V disks decreased at 0 hours and then gradually increased. However, the antimicrobial activity was maintained for seven days after UV irradiation. Conclusion. Antimicrobial activity was induced for seven days after UV irradiation on both types of disk. Irradiated Ti6Al4V and Ti had similar antimicrobial properties. Cite this article: T. Itabashi, K. Narita, A. Ono, K. Wada, T. Tanaka, G. Kumagai, R. Yamauchi, A. Nakane, Y. Ishibashi. Bactericidal and antimicrobial effects of pure titanium and titanium alloy treated with short-term, low-energy UV irradiation. Bone Joint Res 2017;6:108–112. DOI: 10.1302/2046-3758.62.2000619

The Thompson hemiarthroplasty is a common treatment option for acute neck of femur fractures in the elderly population. Our department noted a significant number of patients returning with thigh pain, radiographic loosening and femoral osteolysis following cemented implantation of the titanium alloy version of the Thompson hemiarthroplasty. We are not aware of any previous reports documenting complications specific to the titanium Thompson implant and a retrospective cohort study was therefore initiated following clinical governance approval. 366 titanium alloy Thompson prostheses were implanted for hip fracture treatment between 2017 and 2020. As of February 2023, 6 of these have been revised at our hospital. 5 were revised for symptomatic femoral osteolysis and 1 presented with an acute periprosthetic fracture. All revised cases were determined to be aseptic. 32 living patients were excluded from recall on compassionate grounds due to permanent nursing home residence. 47 living patients were identified of which 33 attended for xray. 28 deceased and/or nursing home resident patients who had pelvis x-rays in the previous 12 months were also included in the analysis. Including the 6 index hips already revised, a total of 61 hip xrays were analysed, of which 19 hips (31.1%) showed radiographic evidence of femoral osteolysis or loosening. We conclude that there is a concerning incidence of femoral osteolysis and implant loosening associated with the titanium Thompson implant. We have discontinued use of the implant and reported our experience to the MHRA. We encourage other Scottish Health-Boards who use this implant to consider enhanced follow-up

Objectives. Laser-engineered net shaping (LENS) of coated surfaces can overcome the limitations of conventional coating technologies. We compared the in vitro biological response with a titanium plasma spray (TPS)-coated titanium alloy (Ti6Al4V) surface with that of a Ti6Al4V surface coated with titanium using direct metal fabrication (DMF) with 3D printing technologies. Methods. The in vitro ability of human osteoblasts to adhere to TPS-coated Ti6Al4V was compared with DMF-coating. Scanning electron microscopy (SEM) was used to assess the structure and morphology of the surfaces. Biological and morphological responses to human osteoblast cell lines were then examined by measuring cell proliferation, alkaline phosphatase activity, actin filaments, and RUNX2 gene expression. Results. Morphological assessment of the cells after six hours of incubation using SEM showed that the TPS- and DMF-coated surfaces were largely covered with lamellipodia from the osteoblasts. Cell adhesion appeared similar in both groups. The differences in the rates of cell proliferation and alkaline phosphatase activities were not statistically significant. Conclusions. The DMF coating applied using metal 3D printing is similar to the TPS coating, which is the most common coating process used for bone ingrowth. The DMF method provided an acceptable surface structure and a viable biological surface. Moreover, this method is automatable and less complex than plasma spraying. Cite this article: T. Shin, D. Lim, Y. S. Kim, S. C. Kim, W. L. Jo, Y. W. Lim. The biological response to laser-aided direct metal-coated Titanium alloy (Ti6Al4V). Bone Joint Res 2018;7:357–361. DOI: 10.1302/2046-3758.75.BJR-2017-0222.R1

Introduction. Hydroxyapatite and poly-L-lactide (HA/PLLA) composites are osteoconductive and biodegradable. They have already been used clinically to treat fractured bones by inducing osteosynthesis and serving as the bone filling material. During revision of total hip arthroplasty, we have grafted bone onto the bone defect and covered it with an HA/PLLA mesh instead of using a metal mesh on the non-load bearing portion of the cup (Figure 1). However, whether the interface between the HA/PLLA and the titanium alloy cup was stable remains unclear. Objectives. The purpose of this study was to determine and compare the histological osteoconductivity and osteoinductivity of HA/PLLA and titanium alloy. Methods. Semicylindrical samples (diameter: 3 mm; height: 5 mm) were fabricated from a composite unsintered-HA/PLLA containing 40% fine HA particles and from titanium alloy (Ti-6AL-4V). These two samples were combined to form one cylinder (Figure 2). Defects 3 mm in diameter were drilled into both femoral condyles of nine Japanese white rabbits, and the samples were implanted by press fitting. The rabbits were euthanized at 2, 4, 8, and 25 weeks after implantation, and undecalcified ground samples were prepared. New bone formation was examined histologically using Toluidine blue and Villanueva Goldner stains. Results. New bone formation was observed around the sample at 4 weeks, and the amount increased by 8 weeks. In addition, partial remodeling of the trabecular bones and absorption of the HA/PLLA were found at 25 weeks. Small amounts of new bone formation were found at 4 weeks between the HA/PLLA and titanium alloy materials (Figure 3: Toluidine blue stain), and the amount increased at 8 and 25 weeks. The HA/PLLA had been slightly absorbed and new bone was formed in the gap, which was close to the border between the materials, at 25 weeks. However, the amount of absorption was limited, and no new bone was found in samples where the materials were firmly in contact. Conclusions. HA/PLLA was only slight absorbed at 25 weeks, suggesting that it was stable in vivo and has good osteoconductive and osteoinductive properties. No new bone was found in the regions where the sample was stable and had no gaps between the HA/PLLA and titanium alloy, probably because there was no space for new bone to form in those regions. In contrast, new bone formation was found in gaps of more than 20 μm. Clinically, many gaps likely exist, allowing new bone formation to occur even in a stable implant. This may stabilize the HA/PLLA and titanium alloy materials for longer times. As expected, the HA/PLLA and titanium alloy were mostly stablein vivo

Aims. The Intraosseous Transcutaneous Amputation Prosthesis (ITAP) may improve quality of life for amputees by avoiding soft-tissue complications associated with socket prostheses and by improving sensory feedback and function. It relies on the formation of a seal between the soft tissues and the implant and currently has a flange with drilled holes to promote dermal attachment. Despite this, infection remains a significant risk. This study explored alternative strategies to enhance soft-tissue integration. Materials and Methods. The effect of ITAP pins with a fully porous titanium alloy flange with interconnected pores on soft-tissue integration was investigated. The flanges were coated with fibronectin-functionalised hydroxyapatite and silver coatings, which have been shown to have an antibacterial effect, while also promoting viable fibroblast growth in vitro. The ITAP pins were implanted along the length of ovine tibias, and histological assessment was undertaken four weeks post-operatively. Results. The porous titanium alloy flange reduced epithelial downgrowth and increased soft-tissue integration compared with the current drilled flange. The addition of coatings did not enhance these effects. Conclusion. These results indicate that a fully porous titanium alloy flange has the potential to increase the soft-tissue seal around ITAP and reduce susceptibility to infection compared with the current design. Cite this article: Bone Joint J 2017;99-B:393–400

Introduction. We have investigated the long-term (minimum follow-up period; 10 years) clinical results of the total hip arthroplasty (THA) using K-MAX HS-3 tapered stem. Materials and Methods. In K-MAX HS-3 THA (Kyocera Medical, Kyoto, Japan), cemented titanium alloy stem and all polyethylene cemented socket are used. This stem has the double tapered symmetrical stem design, allowing the rotational stability and uniform stress distribution. The features of this stem are; 1. Vanadium-free high-strength titanium alloy (Ti-15Mo-5Zr-3Al), 2. Double-tapered design, 3. Smooth surface (Ra 0.4µm), 4. Broad proximal profile, 5. Small collar. Previous type stem, which was made of the same smooth-surface titanium alloy, has the design with cylindrical stem tip, allowing the maximum filling of the femoral canal. Osteolysis at the distal end of the stem had been reported in a few cases in previous type with cylindrical stem tip, probably due to the local stress concentration. Therefore the tapered stem was designed, expecting better clinical results. 157 THAs using HS-3 taper type stem were performed at Kitano Hospital between March 2004 and March 2008. And 101 THAs, followed for more than 10 years, were investigated (follow-up rate; 64.3%). The average age of the patients followed at the operation was 61.7 years and the average follow-up period was 10.9 years. The all-polyethylene socket was fixed by bone cement, and the femoral head material was CoCr (22mm; 5 hips, 26 mm; 96 hips). Results. Two hips were revised, one was due to late infection, and the other due to breakage of the implant in trauma. Japanese orthopaedic association (JOA) score improved from 40 to 86 points. Postoperative complication was three periprosthetic fractures (one femoral shaft fracture and two greater trochanteric fractures) and femoral shaft fracture case was operated. Dislocation was not observed. Socket loosening (Hodgkinson, Type 3, 4) and stem loosening (Harris, definite and probable) were not observed radiographically. Cortical hypertrophy was observed in 7.9%. The survival rate of HS-3 tapered stem was 98% for revision due to any reason and 100% for revision due to aseptic loosening. Discussion. The long-term clinical results of K-MAX HS-3 tapered stem were excellent. The osteolysis at the stem tip was not observed in this type, which was observed in a few cases in previous type. From the X-ray finding, it was suggested that this taperd stem had more uniform stress distribution to the femoral bone than previous type. Moreover, the problems associated with titanium alloy usage were not observed. From the present investigation, good farther long-term results of the tapered titanium stem were expected

Introduction. We have compared the middle-term (average follow-up period; 10 years) clinical results of the K-MAX HS-3 tapered stem with those of the previous type having cylindrical tip. Materials and Methods. In K-MAX HS-3 THA (Kyocera Medical, Kyoto, Japan), cemented titanium alloy stem and all polyethylene cemented socket are used. This stem has the double tapered symmetrical stem design, allowing the rotational stability and uniform stress distribution (Type T) (Fig. 1). The features of this stem are; 1. Vanadium-free high-strength titanium alloy (Ti-15Mo-5Zr-3Al), 2. Double-tapered design, 3. Smooth surface (Ra 0.4μm), 4. Broad proximal profile, 5. Small collar. In contrast, previous type stem, which was made of the same smooth-surface titanium alloy, has the design with cylindrical stem tip, allowing the maximum filling of the femoral canal (Type C) (Fig. 2). Osteolysis at the distal end of the stem had been reported in a few cases in Type C, probably due to the local stress concentration. Therefore the tapered stem was designed, expecting better clinical results. All surgery was performed at Kitano Hospital between September 2003 and June 2006. 72 THA were performed (Type T; 52 hips, Type C; 20 hips). The average age of the patients at the operation was 61 and 69 years and the average follow-up period was 10.1 and 10.4 years for the Type T and C, respectively. The all-polyethylene socket was fixed by bone cement, and the femoral head material was alumina or CoCr (22 or 26 mm). Results. One hip was revised in Type C. Japanese orthopaedic association (JOA) score improved from 39/37 to 84/77 points (Type T/C). Postoperative complication was dislocation in one case (Type C; 1). Socket loosening was not observed radiographically. Stem loosening was observed in one hip in Type C, demonstrating osteolysis at the distal end of the stem. In this case, revision THA was performed 3.5 years postoperatively. Bone resorption was more frequently observed in Type C than Type T. Cortical hypertrophy was observed in 7.7% in Type T and 25% in Type C. Discussion. The middle-term clinical results of K-MAX HS-3 taper stem (Type T) was excellent. The osteolysis at the stem tip was not observed in this type, which was observed in a few cases in previous Type C. From the X-ray finding, it was suggested that Type T had more uniform stress distribution to the femoral bone than Type C. Moreover, the problems associated with titanium alloy usage were not observed. From the present investigation, good long-term results of the tapered titanium stem (Type T) was expected. For any figures or tables, please contact authors directly (see Info & Metrics tab above).

Introduction. Following amputation, residual stumps used to attach the external prostheses can be associated with sores, infection and skin necrosis. These problems could be overcome by off loading the soft tissues. Intraosseous transcutaneous amputation prostheses (ITAP) attach external implants directly to residual bone reducing these complications. However, a tight seal at the skin implant interface is crucial in preventing epithelial down-growth and infection. Fibronectin (Fn) and laminin 332 (Ln), enhance early cell growth and adhesion of keratinocytes. Silanization to titanium alloy (Ti) allows these proteins to bond to the metal directly. We hypothesize that silanized dual coatings of fibronectin and laminin (SiFnLn) will be more durable than absorbed proteins and that keratinocyte adhesion will be increased compared with Ti controls and single silanized proteins. Methods. 10 mm diameter Ti alloy discs were polished, sterilized and silanized. The kinetics of silanized single and dual protein coating attachment onto titanium alloy was quantified using radio-labelled Fn(125I-Fn) and Ln(125I-Ln). Coating durability was assessed when soaked in fetal calf serum (FCS) for 0, 1, 24, 48, 72hrs. Data was compared to un-silanized Ti discs with the same amount of adsorbed proteins. In order to study cell attachment 20 × 103 keratinocytes were seeded on the discs (n = 6): silanized (Si), silanized fibronectin (SiFn), silanized laminin (SiLn), silanized dual coating (SiFnLn) for 1, 4 and 24hrs. Adhesion of cells was assessed using mouse vinculin antibody for 2hrs and alexafluor for 1hr which stains focal adhesions responsible for attaching cells to surfaces. Axiovision Image Analysis software was used to measure cell area, vinculin markers per cell unit and per unit cell area on 15 cells per disc. Data was analysed in SPSS and significance was assumed at the 0.05 level. Results. Silanized dual coatings bonded to Ti alloy in significantly larger quantities compared with adsorbed coatings (all p values < 0.05). When proteins were combined on silanized discs the same amount of each protein was attached as when used as a single coating (i.e. non competitive binding). Keratinocytes cultured on silanized dual coatings were significantly larger, produced more vinculin markers per unit cell and per cell area compared with single coatings at all time points. Conclusion. This study has demonstrated that silanized using dual proteins on Ti alloy enhances early keratinocyte growth and attachment in vitro. It also shows that there is non-competitive binding of laminin to Ti alloys in presence of fibronectin. This may lead to improved epidermal attachment to ITAP creating a tight seal at the implant interface, which will prevent migration of the epithelium and subsequent infection in vivo

Introduction. Intraosseous transcutaneous amputation prostheses (ITAP) provide an alternative means of attaching artificial limbs for amputees. Conventional stump-socket devices are associated with soft tissue complications including; pressure sores and tissue necrosis. ITAP resolves these problems by attaching the exo-prosthesis transcutaneously to the skeleton. The aim of this study is to increase the attachment of dermal fibroblasts to titanium alloy in vitro. Fibronectin (Fn) and laminin 332 (Ln) enhance early cell growth and adhesion. We hypothesize that silanized dual coatings of fibronectin and laminin (SiFnLn) will be more durable when compared with adsorbed dual coating (AdFnLn), and will enhance early fibroblast growth and adhesion compared to single coatings. Methods. The kinetics of dual single and dual protein coating attachment onto titanium alloy was quantified on silanized 10mm diameter discs using radiolabelled Fn (125I-Fn) and Ln (125I-Ln). Sixty discs were polished, sterilized and silanized. Coating durability was assessed when soaked in fetal calf serum (FCS) for 0, 1, 24, 48 and 72hrs. Data was compared to un-silanized Ti discs with the same coatings. Five thousand human dermal fibroblasts were seeded on discs (n = 6) of Ti polished alone (Pol), Ti with adsorbed fibronectin (AdFn), Ti with adsorbed laminin (AdLn), Ti adsorbed dual coating (AdFnLn), Ti silanized (Si), Ti silanized with fibronectin (SiFn), Ti silanized with laminin (SiLn), Ti silanized with a dual coating (SiFnLn) for 24hrs. In order to measure cell adhesion fibroblasts were fixed, vinculin stained using mouse vinculin antibody and alexa fluor. Axiovision Image Analysis software was used to measure cell area, vinculin focal adhesion markers per cell and per unit cell area. Data was analysed in SPSS and significance was assumed at the 0.05 level. Results. Silanized dual coatings bonded to Ti alloy in significantly larger quantities compared with adsorbed coatings at all time points (all p values < 0.05). Fibroblasts cultured on dual coatings were significantly larger, produced more vinculin markers per cell, and per unit cell area compared with single coatings. Cells on SiFnLn were larger with more numerous vinculin markers per cell, and per unit cell area compared with AdFnLn (p<0.05). Conclusion. This study has demonstrated that covalently bonding both fibronectin and laminin to Ti alloy provides a durable, dual coating that enhances early fibroblast growth and attachment compared with either protein coating alone in vitro. Our study showed that there is non-competitive binding of laminin on Ti surfaces in the presence of fibronectin. Dual coatings may be applied to the skin-penetrating region of transcutaneous devices to improve the skin seal and this may have positive implications for the development of ITAP

An experimental study is reported of fracture healing in the femora of 36 Beagle dogs, comparing the results of using stainless steel plates with those of using less rigid titanium alloy plates. The alloy plates led to the appearance of a small amount of periosteal callus without any histological evidence of fracture instability, thus allowing the radiological assessment of fracture union. This also produced less bone loss during the remodelling phase. Radiological measurements 24 weeks after osteotomy showed cortical thickness to be reduced by six per cent under titanium alloy and by 19 per cent under stainless steel, while histological measurements showed a total bone loss of 3.7 per cent under titanium alloy and of 11 per cent under stainless steel plates. Removal of the titanium alloy plates after eight weeks followed by a recovery period of 16 weeks produced an increase of cortical thickness of 69 per cent and a gain in total bone mass of 30 per cent. Titanium alloy plates also produced less soft-tissue reaction than stainless steel plates. It is concluded that this alloy is a promising material for internal fixation devices

Introduction: Cell adhesion to titanium alloy implants is important in osseointegration [1,2] and attachment of the soft tissues to skin penetrating implants e.g. external fixator pins and Intraosseous Transcutaneous Amputation Prostheses [3,4]. Cell adhesion can be assessed using cell area data and immunolocalisation of focal contact proteins e.g. vinculin; however no method of assessing biophysical attachment is performed routinely. Cell adhesion can be enhanced with adhesion proteins including fibronectin (Fn)[5]. We have previously shown that covalently binding Fn to titanium also increases cell adhesion, and produces a more robust protein coating [6]. However the strength of adhesion of cells to this coating has not been measured. Our hypothesis was that biophysical cell adhesion measured using novel radial flow apparatus would correlate with cell area and focal contact data and that covalently bound fibronectin substrates would increase cell adhesion compared with adsorbed and uncoated controls. Method: Dermal fibroblasts were cultured for 1, 4, and 24 hours on 30mm and 10mm diameter polished titanium alloy discs (n = 6). Cells on 30mm discs were calcein stained and subjected to shear stress in a submerged, media filled, custom-made radial flow apparatus at 37¬C at 1.66ml/s for 15s. Cells were fixed in 10% formal saline and photographs were taken using a tangential light source. Fluorescent microscopy was performed at 2mm intervals along two perpendicular diameters. Using image analysis, the central cell free zone was measured and radial distance and shear stress calculated. Cells on 10mm discs were fixed, permeablised and vinculin stained (mouse vinculin antibody (1:200) 2hrs; FITC mouse antibody (1:100)1hr). Images were analyzed with a Zeiss microscope linked to image analysis software and the number of focal contacts were counted per cell area. The medians of the radial flow data were compared with data for cell area and focal contact production at the same time points using Spearman¡s regression correlation. This method was subsequently used to compare cell adhesion at one hour with adsorbed and covalently bound Fn substrates (10¥ìg/disc). Results/Discussion: The shear strength of cells increased between 4 and 24hrs (p=0.002) on polished untreated control substrates. Attachment values (dynes/cm2) were 84.90 (73.98–97.19), 96.30 (91.66–100.89), and 136.69 (134.68–140.30) for 1, 4 and 24 hours respectively. At 1hr, covalently bound Fn (509.90 dynes/cm2 (490.55–528.49) significantly increased cell adhesion compared with adsorbed Fn(434.45 dynes/cm2(385.25–465.62)) and control substrates(p=0.002). There was significant correlation between shear stress and focal contacts/cell (1.00(p< 0.01)) and focal contacts/cell area (0.900(p=0.037)), but not cell area (0.600(p=0.285)). Conclusion: Radial flow measurement is a useful direct method to quantify cell adhesion to orthopaedic implants and correlates well with other methods of measurement. Covalently bound Fn significantly increases biophysical cell attachment compared with adsorbed and uncoated controls

Introduction. During revision surgery, the active electrode of an electrocautery device may get close to the implant, potentially provoking a flashover. Incidents have been reported, where in situ retained hip stems failed after isolated cup revision. Different sizes of discoloured areas, probably induced by electrocautery contact, were found at the starting point of the fracture. The effect of the flashover on the implant material is yet not fully understood. The aim of this study was to investigate the fatigue strength reduction of Ti-6Al-4V titanium alloy after electrocautery contact. Material and Methods. 16 titanium rods (Ti-6Al-4V, extra low interstitial elements, according to DIN 17851, ⊘ 5 mm, 120 mm length) were stress-relief annealed (normal atmosphere, holding temperature 622 °C, holding time 2 h) and cooled in air. An implant specific surface roughness was achieved by chemical and electrolytic polishing (Ra = 0.307, Rz = 1.910). Dry (n = 6) and wet (n = 6, 5 µl phosphate buffered saline) flashovers were applied with a hand-held electrode of a high-frequency generator (Aesculap AG, GN 640, monopolar cut mode, output power 300 W, modelled patient resistance 500 Ω). The size of the generated discoloured area on the rod's surface - representative for the heat affected zone (HAZ) - was determined using laser microscopy (VK-150x, Keyence, Japan). Rods without flashover (n = 4) served as control. The fatigue strength of the rods was determined under dynamic (10 Hz, load ratio R = 0.1), force-controlled four-point bending (FGB Steinbach GmbH, Germany) with swelling load (numerical bending stress 852 MPa with a bending moment of 17.8 Nm) until failure of the rods. The applied bending stress was estimated using a finite-element-model of a hip stem during stumbling. Metallurgical cuts were made to analyse the microstructure. Results. The control rods failed at the pushers of the setup (median: 94,550, range: 194,000 cycles). The rods with flashover failed directly at the HAZ significantly earlier than the control rods (p = 0.018). The analysis of the microstructure showed a transformation of the equiaxed α+β microstructure to a bimodal state. The size of the HAZs were equal for the dry (median: 1.51 mm. 2. , range: 5.68 mm. 2. ) and wet flashovers (median: 0.92 mm. 2. , range: 2.50 mm. 2. , p = 0.792). The cycles to failure were smaller for the dry flashover (median: 22,650 cycles, range: 5,700) than the wet flashover but not reaching statistical significance (median: 32,200, range: 57,900; p = 0.052). No correlation between the dimension of the HAZs and the cycles to failure was found (dry: r. 2. = 0.019, p = 0.8; wet: r. 2. = 0.015, p = 0.721). Discussion. Flashovers induced by an electrocautery device reduce the fatigue strength of Ti-6Al-4V. Since no correlation between the size of the HAZs and the cycles to failure was found, every contact between electrocautery devices and metal implants should be avoided. For any figures or tables, please contact authors directly

Aim. To control the growth and function of osteoblasts on Titanium alloy surfaces produced by electrochemical patterning. Methods. Samples of Ti6Al4V were prepared with three different finishes; no surface preparation following machining, polishing on a grinding wheel with sequential grit papers up to 4000 to achieve a mirror finish and treatment in a flat electrochemical cell with a 3M sulphuric acid in methanol using 9V supplied over 60 seconds to produce a surface with defined nano/microscale roughness. Glass coverslips were used as control surfaces. Surfaces were seeded with primary rat calvarial osteoblasts and incubated in Dulbecco's Modified Eagle Medium with 10% (v/v) sera for 24 hours before fixing and performing immunofluorescence staining with anti-vinculin antibody. Photomicrographs of the surfaces were analysed with Image J and analySIS FIVE programs. Results for cell number, cell area, focal adhesion area and polarity (lack of roundness) were analysed (using the Mann Whitney test) for ANOVA using SPSS. Results. Cells adhered to all surfaces with the most cells on the polished surface and the fewest on the glass and 9V60s surfaces. There were significant differences in cell number only between the polished surface and the glass control (p=0.026) and the 9V60s surface (p=0.006). Cells grown on the glass control surfaces exhibited the largest areas (mean = 840micron2) whilst those on the machined surface were the smallest (mean = 601micron2). A significant difference in cell area was seen between the machined and polished surfaces (p=0.025). The area of the focal adhesions was significantly different between the cells on 9V60s surface and the glass control (p=0.004), machined (p=0.003) and polished surfaces (p=0.006). Significant differences in polarity were seen between the cells on machined surface and the glass control (p=0.004), polished (p=0.004) and 9V60s surfaces (p=0.004). Discussion. Differences in cell numbers on glass and two of the Ti surfaces may be explained by the smooth nature of the glass coverslips in comparison to the nanoscale topography on the polished and 9V60s treated surfaces. Cell area was noted to be different between the machined and smoother polished surface. This may be explained by the grooves present on the machined surfaces preventing normal cell spreading by the process of contact guidance. There was a marked difference in polarity between the most polarised cells on the machined surface and the more rounded cells on the smoother surfaces, again consistent with the behaviour of contact guidance, with cells growing in the direction of the surface grooves. Focal adhesions present on the 9V60s treated surface were very small in comparison to those on other surfaces. Several features of implant surfaces may affect osteoblast growth, including surface roughness, chemical composition, surface charge and surface energy. These features influence the adsorption of proteins onto the surfaces, in turn influencing the growth and behaviour of the adherent cell population. Conclusion. Mechanical and electrochemical treatment of titanium alloy can significantly affect the growth and behaviour of osteoblasts grown on the surface. This has potential applications in arthroplasty and fracture fixation

The success of long-term transcutaneous implants depends on dermal attachment to prevent downgrowth of the epithelium and infection. Hydroxyapatite (HA) coatings and fibronectin (Fn) have independently been shown to regulate fibroblast activity and improve attachment. In an attempt to enhance this phenomenon we adsorbed Fn onto HA-coated substrates. Our study was designed to test the hypothesis that adsorption of Fn onto HA produces a surface that will increase the attachment of dermal fibroblasts better than HA alone or titanium alloy controls. . Iodinated Fn was used to investigate the durability of the protein coating and a bioassay using human dermal fibroblasts was performed to assess the effects of the coating on cell attachment. Cell attachment data were compared with those for HA alone and titanium alloy controls at one, four and 24 hours. Protein attachment peaked within one hour of incubation and the maximum binding efficiency was achieved with an initial droplet of 1000 ng. We showed that after 24 hours one-fifth of the initial Fn coating remained on the substrates, and this resulted in a significant, three-, four-, and sevenfold increase in dermal fibroblast attachment strength compared to uncoated controls at one, four and 24 hours, respectively

Introduction. Periprosthetic joint infection (PJI) remains the main cause of failure in primary and revision total knee arthroplasties (TKAs). Local delivery of antibiotics, mainly antibiotic-loaded bone cement (ALBC), is commonly employed to prevent PJI. Over the past decade, tantalum and porous titanium have been successfully utilized as metaphyseal fixation devices to address bone loss and improve biologic fixation during revision TKA. However, no study has examined the antimicrobial properties compared to bone cement. The purpose of this study was to compare the ability of tantalum, 3D porous titanium, antibiotic-loaded bone cement (ALBC) and smooth titanium alloy (STA) to inhibit Staphylococci bacterial agents in an in vitro medium environment, based on the evaluation of the zone of inhibition (ZOI) and the antibacterial activity duration. Our study hypothesis was that we will found no significant difference between groups to inhibit Methicillin-Sensitive or Methicillin-Resistant Staphylococcus aureus (MSSA/MRSA) agents. Methods. Thirty beads made of 3 different materials (tantalum/ 3D porous titanium/ STA) were bathed during 1hour inside of a solution made of 1g vancomycin with 20-mL of sterile water for injection (bath concentration: 50 mg/mL). Ten 1cm. 3. cylinders were also created mixing standard surgical cement with 1g of Vancomycin in standardized sterile molds (ALBC beads). Finally, thirty beads made of tantalum/ 3D porous titanium/ STA were bathed in phosphate buffered saline solution to act as a control group. Cylinders were then placed on agar plates inoculated with MSSA and MRSA. Inhibition zone diameters were measured each day and cylinders were transferred onto a new inoculated plate. Inhibition zones were measured with a manual Vernier caliper and with automated software. The mean inhibition zones between groups were compared using the Wilcoxon Test. Results. The inter-class coefficient correlation values indicated an optimal intra-observer and inter-observer reproducibility for ZOI measurement (ICC 0.96 and ICC 0.98). For MSSA and MRSA, no inhibitory effect was found in the control group and antibiotic-loaded STA beads exhibited a short inhibitory effect until day 2. For MSSA, both tantalum and 3D porous titanium beads exhibited larger inhibition zones than cement beads (all p<0.01) each day until day 7 for tantalum and until day 3 for 3D porous titanium. After 6 days, ALBC presented larger inhibition zone than the 3D porous titanium, but no difference was found with tantalum. For MRSA, both tantalum and 3D porous titanium beads had significantly larger inhibition zones than ALBC each day until day 6 for tantalum (all p<0.01) and until day 3 for 3D porous titanium (all p<0.04). ALBC presented larger inhibition zone than tantalum and 3D porous titanium from day 7 to 9 (all p<0.04). Conclusion. Our results demonstrate that porous metal implants can deliver local antibiotics over slightly varying time frames based on our in vitro analysis. Antibiotic-impregnated tantalum and 3D porous titanium constructs exhibited superior antimicrobial properties when compared to STA. Future goals include impregnating porous metals with antibiotics for intraoperative use during revision TKA. For figures, tables, or references, please contact authors directly

Our aim was to determine whether in vitro studies would detect differences in the cellular response to wear particles of two titanium alloys commonly used in the manufacture of joint replacement prostheses. Particles were of the order of 1 μm in diameter representative of those found adjacent to failed prostheses. Exposure of human monocytes to titanium 6-aluminium 4- vanadium (TiAlV) at concentrations of 4 x 10. 7. particles/ml produced a mean prostaglandin E. 2. release of 2627.6 pM; this was significantly higher than the 317.4 pM induced by titanium 6-aluminium 7-niobium alloy (TiAlNb) particles (p = 0.006). Commercially-pure titanium particles induced a release of 347.8 pM. In addition, TiAlV stimulated significantly more release of the other cell mediators, interleukin-1, tumour necrosis factor and interleukin-6. At lower concentrations of particles there was less mediator release and less obvious differences between materials. None of the materials caused significant toxicity. The levels of inflammatory mediators released by phagocytic cells in response to wear particles may influence the amount of periprosthetic bone loss. Our findings have shown that in vitro studies can detect differences in cellular response induced by particles of similar titanium alloys in common clinical use, although in vivo studies have shown little difference. While in vitro studies should not be used as the only form of assessment, they must be considered when assessing the relative biocompatibility of different implant materials

Objectives: The purpose of this biomechanical study was to compare the mechanical properties of locked nails and screws made from either stainless steel or titanium alloy. Methods: The specially designed locked nails and screws with the same structures were made from either stainless steel or titanium alloy. The structural factors investigated included inner diameter and root radius for locking screws and outer diameter and nail hole size for locked nails. The mechanical properties investigated included bending stiffness, strength, and fatigue life. Finite element models were used to simulate the mechanical tests and compute the stress concentration factors. Results: Increasing the root radius and the inner diameter could effectively increase the fatigue strength of the locking screws. Fatigue strength increased more in titanium than in stainless steel screws, especially when the inner diameter was increased. In contrast, the titanium locked nails were much weaker than their stainless steel counterparts. Finite element models could closely predict the results of the biomechanical tests with a correlation coefficient that ranged from −0.58 to −0.84 for screws and was −0.98 for nails. The stress concentration factors ranged from 1 to 1.81 for screws and from 3.06 to 4.17 for nails. Conclusions: With larger root radius and inner diameter, titanium locking screws could provide much stronger fatigue strength than stainless steel counterparts. However, titanium locked nails might lose their advantages of superior mechanical strength because of high notch sensitivity and this limitation should be a critical concern clinically. Finite element analyses could be reliably used in research and development of locked nails and locking screws

INTRODUCTION. Biomaterial-related infections are an important complication in orthopaedic surgery [1], and Staphylococcus sp. accounts for more than half of the prosthetic joint infection cases [2]. Adhesion of bacteria to biomaterial surfaces is a key step in pathogenesis of such infections [3]. Titanium alloys are widely used in orthopaedic implants because their biocompatibility [4]. Surface incorporation of ions with antimicrobial properties, like fluorine, is one strategy previously studied with good results [5]. MATERIAL AND METHODS. A 18mm diameter rod of Ti–6Al–4V alloy ELI grade according to the standard ASTMF136-02 supplied by SURGIVAL was cut into 2 mm thick disk specimens, ground through successive grades of SiC paper to 1200 grade, degreased with a conventional detergent and rinsed in tap water followed by deionised water. The specimens were then chemically polished (CP). The disks were anodized only on one side by using a two electrode cell in a suitable electrolyte. TiO. 2. barrier layers, without fluoride (BL), were produced by anodizing in 1 M H. 2. SO. 4. at 15 mA cm-2 to 90 V, reaching 200 nm of thickness. Fluoride barrier layers (FBL) were produced in an electrolyte containing 1 M NH. 4. H. 2. PO. 4. and 0.15 M NH. 4. F, at constant voltage controlled at 20 V for 120 min at 20°C; the thickness of the layer is 140 nm. Laboratory biofilm-forming strains of Staphylococcus aureus 15981 [6] and Staphylococcus epidermidis ATCC 35984 were used in adherence studies, which were performed using the protocol by Kinnari et al [7]. Photographs obtained were studied by ImageJ software. Statistical analysis was performed by EPI-INFO software. The experiments were performed in triplicates. RESULTS. Lower adherence was detected when compared FBL with unmodified controls (CP and BL). A statistical significant difference (p<0.01) was detected in the adhesion to modified material between both species, being the adherence of S. aureus lower than that of S. epidermidis (Figure 1). DISCUSSION & CONCLUSIONS. There is currently a discussion about the actual antibacterial properties of fluorine when incorporated in biomaterial surfaces. In this study we have demonstrated that both S. aureus and S. epidermidis strains showed a decrease of bacterial adhesion to modified surfaces with fluorine, a decrease that cannot be due to other surface modifications. Further studies, including adhesion studies with clinical strains [8], must be performed to confirm these results, which can lead to the development of new materials with a potential use in orthopaedic surgery

Introduction: Transcutaneous Amputation Prosthesis (ITAP) is an alternative for transfemoral amputees to conventional stump-socket prostheses which have many problems. These include: poor fit, stump pressure sores, pain, infections and unnatural gait. ITAP aims to overcome these by being osseointegrated into the femoral medulla with a pin protruding through the skin to which the external prosthesis attaches. Thus, the forces normally encountered by the stump soft tissues are now transferred directly to the skeleton. However, the transcutaneous pin produces a route for infection from the external to internal environment. Therefore, a key feature to the success of the ITAP is to produce a biological seal at the transcutaneous interface. Epithelial cells have been shown to attach to dental transcutaneous titanium devices via hemidesmosomes (HD).2 Focal contacts (FC) are also important in cell adhesion and to the underlying substratum.3 We grew human keratinocytes on different titanium surfaces to assess their morphology, ability to proliferate and produce HD and FC. Hypothesis: Surface topography influences keratinocytes morphology and proliferative capacity and expression of HD and FC. Materials and Methods: 4 titanium alloy (Ti6Al4V) surface topographies were used (10mm x 4mm discs): polished, machine finished, sandblasted and hydrofluoric acid etched (HF) and a control – plastic thermanox. Surface roughness profiling of titanium discs were measured (Mitutoyo Surftest SV-400). HaCaT keratinocytes were grown on disc surfaces in wells of culture medium at +37oC, 5% CO2 and analysed at 1, 2, 3 and 4 days. Cells were processed to visualise HD with fluorescence microscopy using antibodies to the 6-integrin and plec-tin. Anti-vinculin antibodies were used to visualise FC. Fluorescein isothiocyanate (FITC) secondary antibodies enabled counting of structures (all product: Sigma-Aldrich, UK). Alamar blue (Serotec, UK) measured cell proliferation and SEM (surface morphology, cell area) and TEM were also performed. Cells grown on polished, machined and thermanox discs supported a regular, confluent layer with many cytoplasmic processes and dividing cells. HF and sandblasted discs grew an irregularly layer with fewer cytoplasmic processes and fewer dividing cells (not quantified). Day 3 TEM revealed HD, FC and desmosomes; cells on polished and thermanox were more closely packed and in layers. Conclusion: Keratinocytes are significantly influenced by titanium surface topography. Smooth polished titanium alloy may be the ideal surface for a transcutaneous pin in the ITAP. Further experiments into isolating favourable biological components needed to encourage keratinocytes to attach onto titanium should be carried out. Results: No significant difference shown in cell proliferation between titanium discs but cells on thermanox grew significantly more (p< 0.05). FC and HD numbers increased on all surfaces (days 1–3); a negative correlation between surface roughness and HD and FC numbers observed (lower Ra values = more HD and FC expressed)

Introduction. In THA, fretting corrosion at the head-stem taper junction has emerged as a clinical concern that may result in adverse local tissue reactions, even in patients with a metal-on-polyethylene bearing [1]. Taper junctions that employ a ceramic head have demonstrated reduced corrosion at the interface [2]. However, during revision surgery with a well-fixed stem, a titanium sleeve is used in conjunction with a ceramic head to ensure proper fit of the head onto the stem and better stress distribution. In vitro testing has suggested that corrosion is not a concern in sleeved ceramic heads [3]; however, little is known about the in vivo fretting corrosion of the sleeves. The purpose of this study was to investigate fretting corrosion in sleeved ceramic heads. Materials and Methods. Between 2001 and 2014, 35 sleeved ceramic heads were collected during revision surgery as part of a multi-center retrieval program. The sleeves were all fabricated from titanium alloy and manufactured by 4 companies (CeramTec (n=14), Smith & Nephew (Richards, n=11), Stryker (n=5), and Zimmer (n=5)). The femoral heads were made from 3 ceramics (Alumina (n=7), Zirconia (n=11), and Zirconia-toughened Alumina (n=17)). Sleeve dimensions (length and thickness) were measured using calibrated calipers. Fretting corrosion of the sleeves and available associated stems was scored using a 4-point, semi-quantitative scoring system [4], with 1 being little-to-no damage, and 4 corresponded to severe fretting corrosion. Five sleeves could not be extracted; thus the external surface was not scored. Results. Moderate-to-severe fretting corrosion scores (Score ≥ 2) were observed in 97% (34/35) of internal tapers (sleeve-femoral stem contact), 57% (17/30) of external tapers (sleeve-femoral head contact), and 65% (11/17) of the stems. The internal sleeve had higher fretting corrosion scores than the external taper (Mean Score Difference [MSD] = 1.1; p = 0.001) and stem (MSD = 0.7; p = 0.016). Fretting corrosion scores were correlated with implantation time at all surfaces (Rho ≥ 0.53; p ≤ 0.015). Scores were not correlated with sleeve dimensions (p > 0.05). Fretting corrosion scores of the external sleeve correlated directly with activity level (p = 0.005) and inversely with patient age (p = 0.03). Discussion. The retrieval data shows that fretting corrosion can occur in these components, particularly on the internal surface of the sleeve. The corrosion scores were similar to levels observed in prior studies of tapers in CoCr heads [2]. Implantation time was the main predictor of increased fretting corrosion. The impact of ceramic material and sleeve design currently remain unclear as the analyses were confounded with implantation time. Thus, more detailed and quantitative analyses are required to fully determine the factors that influence fretting corrosion of sleeved ceramic heads in THA