Aims

Radiostereometric analysis (RSA) is the most accurate radiological method to measure in vivo wear of highly cross-linked polyethylene (XLPE) acetabular components. We have previously reported very low wear rates for a sequentially irradiated and annealed X3 XLPE liner (Stryker Orthopaedics, USA) when used in conjunction with a 32 mm femoral heads at ten-year follow-up. Only two studies have reported the long-term wear rate of X3 liners used in conjunction with larger heads using plain radiographs which have poor sensitivity. The aim of this study was to measure the ten-year wear of thin X3 XLPE liners against larger 36 or 40 mm articulations with RSA.

Aims

This study investigates head-neck taper corrosion with varying head size in a novel hip simulator instrumented to measure corrosion related electrical activity under torsional loads.

Aims

The optimum clearance between the bearing surfaces of hip arthroplasties is unknown. Theoretically, to minimize wear, it is understood that clearances must be low enough to maintain optimal contact pressure and fluid film lubrication, while being large enough to allow lubricant recovery and reduce contact patch size. This study aimed to identify the relationship between diametrical clearance and volumetric wear, through the analysis of retrieved components.

Introduction. The process of wear and corrosion at the head-neck junction of a total hip replacement is initiated when the femoral head and stem are joined together during surgery. To date, the effects of the surface topography of the femoral head and metal stem on the contact mechanics during assembly and thus on tribology and fretting corrosion during service life of the implant are not well understood. Therefore, the objective of this study was to investigate the influence of the surface topography of the metal stem taper on contact mechanics and wear during assembly of the head-neck junction using Finite Element models. Materials and Methods. 2D axisymmetric Finite Element models were developed consisting of a simplified head-neck junction incorporating the surface topography of a threaded stem taper to investigate axial assembly with 1 kN. Subsequently, a base model and three modifications of the base model in terms of profile peak height and plateau width of the stem taper topography and femoral head taper angle were calculated. To account for the wear process during assembly a law based on the Archard equation was implemented. Femoral head was modeled as ceramic (linear-elastic), taper material was either modeled as titanium, stainless steel or cobalt-chromium (all elastic-plastic). Wear volume, contact area, taper subsidence, equivalent plastic strain, von Mises stress, engagement length and crevice width was analyzed. Results. Titanium tapers showed largest wear volume throughout all simulations, followed by stainless steel and cobalt-chromium. A larger head taper angle resulted in an increase of the wear volume for all taper materials while the increase of the plateau width resulted in a decrease of the wear volume. Taper subsidence, von Mises stress and equivalent plastic strain followed the same trends. Contact area was largest for the models with a large plateau width for all taper materials. Other taper parameters had little effect on contact area. A pure increase of the angular mismatch (AM) resulted in the strongest decrease of the engagement length, while a combined increase of the AM and plateau width showed only a moderate decrease. The smallest effect concerning the engagement length was found when a combined increase of the profile peak height and AM was simulated. Crevice width was largest for a pure increase of the AM and for a combined increase of the AM and profile peak height for all taper materials. Discussion. This study showed that depending on the surface topography and material of the stem taper, wear and taper mechanics during assembly could be affected. For the examined surface topographies wear is distinctively elevated by increasing the AM and the profile peak height due to the resulting higher mechanical loading. More parameter studies under in vivo loading and the study of other taper surface parameters like the peak-to-peak distance have to be conducted to get a deeper insight into taper mechanics and wear effects. However, this study demonstrates the importance of good manufacturing practice of components for hip replacement systems to guarantee reproducible taper mechanics. For any figures or tables, please contact authors directly

Introduction. Hip stem taper wear and corrosion is a multifactorial process involving mechanical, chemical and biological damage modes. For the most cases it seems likely that the mechanically driven fretting wear is accompanied by other damage modes like pitting corrosion, galvanic corrosion or metal transfer. Recent retrieval studies have reported that the taper surface topography may affect taper damage resulting from fretting and corrosion [1]. Therefore, the current study aimed to examine effects of different taper topography parameters and material combinations on taper mechanics and results regarding wear and corrosion have been investigated. Materials and Methods. Combined experimental and numerical studies were conducted using titanium, cobalt-chromium and stainless steel generic tapers (Figure1). Uniaxial tensile tests were performed to determine the mechanical properties of the materials examined. For the taper studies macro-geometry of ceramic ball heads (BIOLOX. ®. delta) and tapers were characterized using a coordinate measuring machine, and assembly experiments according to ISO7206-10 were conducted up to 4kN. Before and after loading, taper subsidence was quantified by assembly height measurements. Taper micro-geometry, taper surface deformation, and contact area were determined by profilometry. Initial numerical studies determined coefficients of friction for the three material combinations. Macro- and micro-geometries of the tapers were modelled, and taper subsidence and assembly load served as boundary conditions. Further studies used simplified models to examine effects of varying profile depths and angular gaps on surface deformation, taper subsidence, contact area, engagement length and pull-off force. Results. Largest coefficient of friction and pull-off forces were calculated for steel (µ=0.32), cobalt-chromium revealed the lowest with µ=0.18. Titanium showed largest deformations and taper subsidence throughout all calculations (Figure2, Figure3). Taper subsidence, engagement length and deformations increased with increasing profile depth while contact area decreased. Pull-off forces were almost constant for different profile depths while they increased for increasing angular gaps. Taper subsidence and deformations also increased with increasing angular gap while engagement length decreased and contact area almost remained constant. Discussion. In order to decrease wear and corrosion micromotions should be minimized. Therefore, smaller angular gaps and smaller profile depths seems to be beneficial since deformation and taper subsidence are reduced. Literature data confirmed the results for different angular gaps showing that a larger angular gap is associated with larger amounts of micromotion and wear [2, 3]. Additionally, larger angular gaps and larger profile depths result in larger plastic deformation facilitating subsurface crack initiation and propagation. A large angular gap may also facilitate particle release [4]. Larger pull-off forces can indicate larger resistance against micromotion. Therefore, steel may tend to later develop fretting-corrosion in situ. However, among the metals examined steel also showed the largest equivalent plastic strain. This study is limited to pairings involving ceramic heads. These can help mitigating fretting corrosion resulting from micromotion between ball head and cobalt-chromium or titanium alloy tapers [5]. However, future studies will include other ball head materials. In conclusion, this study showed that taper surface topography affects taper mechanics and is important in terms of wear and corrosion

Introduction. Fretting corrosion at the taper interface of modular connections can be studied using Finite Element (FE) analyses. However, the loading conditions in FE studies are often simplified, or based on generic activity patterns. Using musculoskeletal modeling, subject-specific muscle and joint forces can be calculated, which can then be applied to a FE model for wear predictions. The objective of the current study was to investigate the effect of incorporating more detailed activity patterns on fretting simulations of modular connections. Methods. Using a six-camera motion capture system, synchronized force plates, and 45 optical markers placed on 6 different subjects, data was recorded for three different activities: walking at a comfortable speed, chair rise, and stair climbing. Musculoskeletal models, using the Twente Lower Extremity Model 2.0 implemented in the AnyBody modeling System™ (AnyBody Technology A/S, Aalborg, Denmark; figure1), were used to determine the hip joint forces. Hip forces for the subject with the lowest and highest peak force, as well as averaged hip forces were then applied to an FE model of a modular taper connection (Biomet Type-1 taper with a Ti6Al4V Magnum +9 mm adaptor; Figure 2). During the FE simulations, the taper geometry was updated iteratively to account for material removal due to wear. The wear depth was calculated based on Archard's Law, using contact pressures, micromotions, and a wear factor, which was determined from accelerated fretting experiments. Results. The forces for the comfortable walking speed had the highest peak forces for the maximum peak subject, with a maximum peak force of 3644 N, followed by walking up stairs, with a similar maximum peak force of 3626 N. The chair rise had a lower maximum peak force of 2240 N (−38.5%). The simulated volumetric wear followed the trends seen in the peaks of the predicted hip joint forces, with the largest wear volumes predicted for a comfortable walking speed, followed by the stairs up activity and the chair rise (Figure 3). The subjects with the highest peak forces produced the most volumetric wear in all cases. However, the lowest peak subject had a higher volumetric wear for the stairs up case than the average subject. Discussion. This study explored the effect of subject-specific variations in hip joint loads on taper fretting. The results indicate that taper wear was predominantly affected by the magnitudes of the peak forces, rather than by the orientation of the force. A more comprehensive study, capturing the full spectrum of patient variability, can help identifying parameters that accelerate fretting corrosion. Such a study should also incorporate other sources of variability, including surgical factors such as implant orientation, sizing, and offset. These factors also affect hip joint forces, and can be evaluated in musculoskeletal models such as presented here

Aims

The present study investigated the five-year interval changes in pseudotumours and measured serum metal ions at long-term follow-up of a previous report of 28 mm diameter metal-on-metal (MoM) total hip arthroplasty (THA).

Objectives

We investigated the reliability of the cobalt-chromium (CoCr) synovial joint fluid ratio (JFR) in identifying the presence of a severe aseptic lymphocyte-dominated vasculitis-associated lesion (ALVAL) response and/or suboptimal taper performance (SOTP) following metal-on-metal (MoM) hip arthroplasty. We then examined the possibility that the CoCr JFR may influence the serum partitioning of Co and Cr.

Objectives

Previous studies have suggested that metal-on-metal (MoM) Pinnacle (DePuy Synthes, Warsaw, Indiana) hip arthroplasties implanted after 2006 exhibit higher failure rates. This was attributed to the production of implants with reduced diametrical clearances between their bearing surfaces, which, it was speculated, were outside manufacturing tolerances. This study aimed to better understand the performance of Pinnacle Systems manufactured before and after this event.

Aims

This study presents the long-term survivorship, risk factors for prosthesis survival, and an assessment of the long-term effects of changes in surgical technique in a large series of patients treated by metal-on-metal (MoM) hip resurfacing arthroplasty (HRA).

Aims. There are limited published data detailing the volumetric material loss from tapers of conventional metal-on-polyethylene (MoP) total hip arthroplasties (THAs). Our aim was to address this by comparing the taper wear rates measured in an explanted cohort of the widely used Exeter THA with those measured in a group of metal-on-metal (MoM) THAs. Patients and Methods. We examined an existing retrieval database to identify all Exeter V40 and Universal MoP THAs. Volumetric wear analysis of the taper surfaces was conducted using previously validated methodology. These values were compared with those obtained from a series of MoM THAs using non-parametric statistical methodology. A number of patient and device variables were accounted for using multiple regression modelling. Results. A total of 95 Exeter MoP and 249 MoM THAs were examined. The median volumetric loss from the MoM cohort was over four times larger than that from the MoP cohort (1.01 mm. 3. vs 0.23 mm. 3. , p < 0.001), despite a significantly shorter median period in vivo for the MoM group (48 months vs 90 months, p < 0.001). Multiple regression modelling indicated that the dominant variables leading to greater female taper material loss were bearing diameter (p < 0.001), larger female taper angles (p < 0.001), and male titanium stem tapers (p < 0.001). Conclusion. Consistent with the long-term clinical success of the device, the volumetric material loss from Exeter femoral head tapers was, in general, small compared with that from larger-diameter MoM head tapers. Cite this article: Bone Joint J 2018;100-B:1310–9

Aims. We sought to determine whether cobalt-chromium alloy (CoCr) femoral stem tapers (trunnions) wear more than titanium (Ti) alloy stem tapers (trunnions) when used in a large diameter (LD) metal-on-metal (MoM) hip arthroplasty system. Patients and Methods. We performed explant analysis using validated methodology to determine the volumetric material loss at the taper surfaces of explanted LD CoCr MoM hip arthroplasties used with either a Ti alloy (n = 28) or CoCr femoral stem (n = 21). Only 12/14 taper constructs with a rough male taper surface and a nominal included angle close to 5.666° were included. Multiple regression modelling was undertaken using taper angle, taper roughness, bearing diameter (horizontal lever arm) as independent variables. Material loss was mapped using a coordinate measuring machine, profilometry and scanning electron microscopy. Results. After adjustment for other factors, CoCr stem tapers were found to have significantly greater volumetric material loss than the equivalent Ti stem tapers. Conclusion. When taper junction damage is identified during revision of a LD MoM hip, it should be suspected that a male taper composed of a standard CoCr alloy has sustained significant changes to the taper cone geometry which are likely to be more extensive than those affecting a Ti alloy stem. Cite this article: Bone Joint J 2017;99-B:1304–12

A modular hemiarthroplasty has a Metal-on-Metal (MoM) taper-trunnion junction, which may lead to increased wear and Adverse-Reaction-to-Metal-Debris (ARMD). To-date no wear related issues have been described in the elderly and less active that receives a hemiarthroplasty. This study aims to determine in vivo wear (i.e. serum metal ion levels) in hip hemiarthroplasty, and identify factors associated with increased wear. This is a prospective, IRB approved, single-centre, cohort study of patients that received an uncemented, modular hemiarthroplasty of proven design for the treatment of hip fracture between 2013–2015. All, alive, patients at 12-months post-implantation with AMTS≥6 were invited to participate. Of the 125 eligible patients, 50 accepted the invitation and were reviewed, including clinical/radiological assessment, metal-ion ([Chromium (Cr) and Cobalt (Co)]) measurement and Oxford Hip Score (OHS). Acetabular erosion was graded (0–3: normal-protrusio). Metal ion levels were considered high if ≥7ppb. The mean OHS was 37 (SD: 10). No acetabular erosion was detected in 21, whilst the remaining had either grade-1 (n=21) or grade-2 (n=8). The median Cr and Co levels were 2.9 (SD:9) and 2.2 (SD:4) respectively. There were 8 cases (16%) with high ion levels. To-date only 2 of them has an ARMD lesion, and none have been revised. Patients with metal ion levels had similar pre-fall mobility, taper- and head- size and OHS to those with low metal ion levels (p=0.2–0.7) However, all hips with high metal ion levels had evidence of acetabular erosion (≥1). Modular Hip hemiarthroplasties and their taper-trunnion junction are not immune to high wear and ARMD despite being implanted in a less active cohort. Acetabular erosion should alert clinicians, as it is associated with 20× increased-risk of taper wear, presumably due to the increased transmitted torque. Whether the use of modular hemiarthroplasties should remain is debatable

Objectives. The high revision rates of the DePuy Articular Surface Replacement (ASR) and the DePuy ASR XL (the total hip arthroplasty (THA) version) have led to questions over the viability of metal-on-metal (MoM) hip joints. Some designs of MoM hip joint do, however, have reasonable mid-term performance when implanted in appropriate patients. Investigations into the reasons for implant failure are important to offer help with the choice of implants and direction for future implant designs. One way to assess the performance of explanted hip prostheses is to measure the wear (in terms of material loss) on the joint surfaces. Methods. In this study, a coordinate measuring machine (CMM) was used to measure the wear on five failed cementless Biomet Magnum/ReCap/ Taperloc large head MoM THAs, along with one Biomet ReCap resurfacing joint. Surface roughness measurements were also taken. The reason for revision of these implants was pain and/or adverse reaction to metal debris (ARMD) and/or elevated blood metal ion levels. Results. The mean wear rate of the articulating surfaces of the heads and acetabular components of all six joints tested was found to be 6.1 mm. 3. /year (4.1 to 7.6). The mean wear rate of the femoral head tapers of the five THAs was 0.054 mm. 3. /year (0.021 to 0.128) with a mean maximum wear depth of 5.7 µm (4.3 to 8.5). Conclusion. Although the taper wear was relatively low, the wear from the articulating surfaces was sufficient to provide concern and was potentially large enough to have been the cause of failure of these joints. The authors believe that patients implanted with the ReCap system, whether the resurfacing prosthesis or the THA, should be closely monitored. Cite this article: S. C. Scholes, B. J. Hunt, V. M. Richardson, D. J. Langton, E. Smith, T. J. Joyce. Explant analysis of the Biomet Magnum/ReCap metal-on-metal hip joint. Bone Joint Res 2017;6:113–122. DOI: 10.1302/2046-3758.62.BJR-2016-0130.R2

Introduction. Fretting corrosion of the modular taper junction in total hip arthroplasty has been studied in several finite element (FE) investigations. In FE analyses, different parameters can be varied to study micromotions and contact pressures at the taper interface. However, to truly study taper wear, the simulation of micromotions and contact pressures in non-adaptive FE models is insufficient, as over time these can change due to interfacial changes caused by the wear process. In this study we developed an FE approach in which material removal during the wear process was simulated by adaptations to the taper geometry. The removal of material was validated against experiments simulating the clinical fretting wear process. Method. Experimental test: An accelerated fretting screening test was developed that consistently reproduced fretting wear features observed in retrievals. Biomet Type-1 (4°) tapers and +9 mm offset adaptors were assembled with a 4 kN force (N=3). A custom head fixture was used to create an increased offset and torque. The stems were potted in accordance with ISO 7206–6:2013. The set-up was submerged in a 37°C PBS solution with a pH adjusted to 3 using HCL and NaCl concentration of 90gl. −1. The components were cyclically loaded between 0.4 – 4 kN for 10 million cycles. After completion, the volumetric and linear wear was measured using a Talyrond-585 roundness measurement machine. FE model: This was created to match the experimental set up (Figure 1). Taper geometry and experimental material data were obtained from the manufacturer (Zimmer Biomet). The coefficient of friction of the studied combination of components was based on previous experiments (Bitter, 2016). After each change in load the geometry was updated by moving nodes inwards perpendicular to the taper surface. Archard's Law (Archard, 1953) was used to calculate the wear with the following equation: H=k*p*S. Where H is the linear wear depth in mm, k is a wear factor (mm³/Nmm), p is the contact pressure (MPa) and S is the sliding distance (mm). The 10 million experimental cycles were simulated using a range of 5 to 200 computational cycles. For this purpose, the wear factor (k) was scaled for each simulation to match the volumetric wear found in the experiments. Results. The accelerated fretting experiments resulted in an average volumetric wear of 0.79 mm³ after 10 million cycles. A thumbprint shaped wear patch was observed on the inferior-distal and superior-proximal side of the taper (Figure 2). Optimal results were found using 100 simulated cycles, and a wear factor of 1.25*10. −6. (mm. 3. /N*mm), balancing accurate results with computational time. The maximum wear depth found in the experiments was found to be 15 µm whereas the simulations predicted a maximum linear wear of 9.5 µm(Figure 3). Discussion and Conclusion. In this study we have shown that we can accurately model wear at the taper junction. The model was validated with experiments using the measured volumetric and linear wear. With this model we will look at the effect of several patient, implant, and surgical parameters on the volumetric wear

Objectives

Modular junctions are ubiquitous in contemporary hip arthroplasty. The head-trunnion junction is implicated in the failure of large diameter metal-on-metal (MoM) hips which are the currently the topic of one the largest legal actions in the history of orthopaedics (estimated costs are stated to exceed $4 billion). Several factors are known to influence the strength of these press-fit modular connections. However, the influence of different head sizes has not previously been investigated. The aim of the study was to establish whether the choice of head size influences the initial strength of the trunnion-head connection.

Aims

We wished to investigate the influence of metal debris exposure on the subsequent immune response and resulting soft-tissue injury following metal-on-metal (MoM) hip arthroplasty. Some reports have suggested that debris generated from the head-neck taper junction is more destructive than equivalent doses from metal bearing surfaces.

Aims

Surgeons have commonly used modular femoral heads and stems from different manufacturers, although this is not recommended by orthopaedic companies due to the different manufacturing processes.

We compared the rate of corrosion and rate of wear at the trunnion/head taper junction in two groups of retrieved hips; those with mixed manufacturers (MM) and those from the same manufacturer (SM).

Introduction. Historical studies have reported incidences of taper corrosion in retrieved MoP hips of 20–50%. These studies relied on visual assessments, rather than using modern analytical techniques. Patients/Materials and Methods. The Northern Retrieval Registry was initiated to routinely analyse all retrieved hips. The volumetric wear rates of retrieved Exeter head tapers were measured using a coordinate measuring machine using validated methods and compared to the available results obtained from an ongoing study of failed MoM prostheses. Power analysis suggested that we would need at least fifty Exeter head tapers to provide significant results. Non-parametric tests were used to assess differences. We have previously identified head diameter/offset/taper angle and taper surface roughness as variables associated with taper wear. The effect of bearing material combination remains unquantified. These design variables were entered into a multiple regression model following log normalisation of taper wear. Results. 56 consecutively retrieved Exeter head tapers underwent assessment. 36 were of size 28mm. Primary causes for revision were acetabular loosening/periprosthetic fractures. Mean duration in vivo was 87 (1 – 252) months. Median total volumetric wear was 0.29mm. 3. with a wear rate of 0.07mm. 3. /year. There were 353 MoMs. Median taper wear rates for 28mm MoM was 0.07, for 36mm was 0.11, for 38–44mm was 0.31, for 45 – 48mm was 0.52, for 49–52 was 0.55mm and for >52mm was 1.36mm. 3. /year. While Exeter taper wear was significantly lower than the MoM group as a whole (p<0.001), regression modelling indicated that bearing diameter had the greatest influence on taper wear. Discussion. Contrary to previous literature reports, significant material loss at the taper junction of conventional arthroplasties is not commonly observed. Exeter hips appear to be protected to some extent by the smaller head size and lower taper roughness when compared to contemporary MoM devices. The effect of the bearing combination remains under investigation

Introduction. Modular hip replacement systems use Morse tapers as an interlocking mechanism to connect ball heads to femoral stems. Even though this interlocking mechanism generally performs successfully for decades, failures due to disassociation of the ball head from the stem are reported in the literature. Therefore, this failure mechanism of a possible loosening is usually evaluated in the course of the development of femoral stems. The disassembly force is a possible parameter to characterize the strength of the interlocking mechanism. Thus, the aim of the current study was to examine the impact of different taper parameters on the disassembly force of ceramic ball heads from titanium stem tapers by finite element studies. Materials and Methods. A 2D axisymmetric finite element model was developed to simulate the disassembly procedure. First ball head and taper were assembled with a force of 4 kN. Afterwards the system was unloaded to simulate the settlement. Disassembly was simulated displacement controlled until no more adhesion between ball head and taper occurred. Isotropic elastic material behavior was modelled for the ceramic ball head while elastic-plastic material behavior was modelled for the titanium taper. Different angular gaps (0.2°, 0.15°, 0.1°, 0.05°, 0°, −0.05°, −0.1°) and different taper topography parameters regarding groove depth (12, 15 µm), groove distance (210, 310 µm) and plateau width (1, 5, 10, 20 µm) were examined. Frictional contact between ball head and taper was modelled. Results. The topography of the taper (groove depth, distance and plateau width) within the investigated range had only a small impact on the disassembly force (Fig. 1) while the varying angular gaps had a large effect (Fig. 2). Decreasing disassembly forces were found for decreasing angular gaps. For the negative angular gaps (i.e. male taper angle > female taper angle) the forces increased. The same trends were found for the sliding distance (sliding along the tangential direction in the taper region), deformation of the grooves and contact stresses. Reciprocal behavior was found for the contacting area. Discussion. Surface topography seems to have only minor influence, while macro-geometry seems to have major impact on the disassembly force. Higher disassembly forces are associated with smaller contacting areas, higher contact stresses, larger deformations of the grooves and larger sliding distances. For a negative angular gap the maximum stresses of the ceramic component were found at the taper mouth. This could be disadvantageous since the wall thickness in this region of the ball heads decreases and critical hoop stresses could increase the risk of a fracture. The decrease in contacting areas due to the extreme angular gaps could promote corrosive effects since a larger taper area is exposed to fluid. Furthermore, the higher contact stresses and groove deformations could increase taper wear. Therefore, a general examination of possible influencing factors and cross effects on the in vivo performance have to be conducted during the development of femoral stems. Future studies will include a wear model and include 3D calculations to examine more realistic loading scenarios. To view tables/figures, please contact authors directly