In metal-on-polyethylene (MoP) total hip arthroplasty (THA), large metal femoral heads have been used to increase stability and reduce the risk of dislocation. The increased size of the femoral head can, however, lead to increased taper corrosion, with the release of metal ions and adverse reactions. The aim of this study was to investigate the relationship between the size of the femoral head and the levels of metal ions in the blood in these patients. A total of 96 patients were enrolled at two centres and randomized to undergo MoP THA using either a 32 mm metal head or a femoral head of between 36 mm and 44 mm in size, being the largest possible to fit the thinnest available polyethylene insert. The levels of metal ions and patient-reported outcome measures (Oxford Hip Score, University of California, Los Angeles Activity Scale) were recorded at two and five years postoperatively.Aims
Methods
The risk of mechanical failure of modular revision hip stems is frequently mentioned in the literature, but little is currently known about the actual clinical failure rates of this type of prosthesis. The current retrospective long-term analysis examines the distal and modular failure patterns of the Prevision hip stem from 18 years of clinical use. A design improvement of the modular taper was introduced in 2008, and the data could also be used to compare the original and the current design of the modular connection. We performed an analysis of the Prevision modular hip stem using the manufacturer’s vigilance database and investigated different mechanical failure patterns of the hip stem from January 2004 to December 2022.Aims
Methods
Taper corrosion has been widely reported to be problematic for modular total hip arthroplasty implants. A simple and systematic method to evaluate taper damage with sufficient resolution is needed. We introduce a semiquantitative grading system for modular femoral tapers to characterize taper corrosion damage. After examining a unique collection of retrieved cobalt-chromium (CoCr) taper sleeves (n = 465) using the widely-used Goldberg system, we developed an expanded six-point visual grading system intended to characterize the severity, visible material loss, and absence of direct component contact due to corrosion. Female taper sleeve damage was evaluated by three blinded observers using the Goldberg scoring system and the expanded system. A subset (n = 85) was then re-evaluated following destructive cleaning, using both scoring systems. Material loss for this subset was quantified using metrology and correlated with both scoring systems.Aims
Methods
The aim of this study was to evaluate the incidence of liner malseating in two commonly used dual-mobility (DM) designs. Secondary aims included determining the risk of dislocation, survival, and clinical outcomes. We retrospectively identified 256 primary total hip arthroplasties (THAs) that included a DM component (144 Stryker MDM and 112 Zimmer-Biomet G7) in 233 patients, performed between January 2012 and December 2019. Postoperative radiographs were reviewed independently for malseating of the liner by five reviewers. The mean age of the patients at the time of THA was 66 years (18 to 93), 166 (65%) were female, and the mean BMI was 30 kg/m2 (17 to 57). The mean follow-up was 3.5 years (2.0 to 9.2).Aims
Methods
A recent report from France suggested an association between the use of cobalt-chrome (CoCr) femoral heads in total hip arthroplasties (THAs) and an increased risk of dilated cardiomyopathy and heart failure. CoCr is a commonly used material in orthopaedic implants. If the reported association is causal, the consequences would be significant given the millions of joint arthroplasties and other orthopaedic procedures in which CoCr is used annually. We examined whether CoCr-containing THAs were associated with an increased risk of all-cause mortality, heart outcomes, cancer, and neurodegenerative disorders in a large national database. Data from the National Joint Registry was linked to NHS English hospital inpatient episodes for 374,359 primary THAs with up to 14.5 years' follow-up. We excluded any patients with bilateral THAs, knee arthroplasties, indications other than osteoarthritis, aged under 55 years, and diagnosis of one or more outcome of interest before THA. Implants were grouped as either containing CoCr or not containing CoCr. The association between implant construct and the risk of all-cause mortality and incident heart failure, cancer, and neurodegenerative disorders was examined.Aims
Methods
This study investigates head-neck taper corrosion with varying head size in a novel hip simulator instrumented to measure corrosion related electrical activity under torsional loads. In all, six 28 mm and six 36 mm titanium stem-cobalt chrome head pairs with polyethylene sockets were tested in a novel instrumented hip simulator. Samples were tested using simulated gait data with incremental increasing loads to determine corrosion onset load and electrochemical activity. Half of each head size group were then cycled with simulated gait and the other half with gait compression only. Damage was measured by area and maximum linear wear depth.Aims
Methods
Prior studies have identified that malseating of a modular dual mobility liner can occur, with previous reported incidences between 5.8% and 16.4%. The aim of this study was to determine the incidence of malseating in dual mobility implants at our institution, assess for risk factors for liner malseating, and investigate whether liner malseating has any impact on clinical outcomes after surgery. We retrospectively reviewed the radiographs of 239 primary and revision total hip arthroplasties with a modular dual mobility liner. Two independent reviewers assessed radiographs for each patient twice for evidence of malseating, with a third observer acting as a tiebreaker. Univariate analysis was conducted to determine risk factors for malseating with Youden’s index used to identify cut-off points. Cohen’s kappa test was used to measure interobserver and intraobserver reliability.Aims
Methods
The aim of this study was to present the first retrieval analysis findings of PRECICE STRYDE intermedullary nails removed from patients, providing useful information in the post-market surveillance of these recently introduced devices. We collected ten nails removed from six patients, together with patient clinical data and plain radiograph imaging. We performed macro- and microscopic analysis of all surfaces and graded the presence of corrosion using validated semiquantitative scoring methods. We determined the elemental composition of surface debris using energy dispersive x-ray spectroscopy (EDS) and used metrology analysis to characterize the surface adjacent to the extendable junctions.Aims
Methods
This study aims to enhance understanding of clinical and radiological consequences and involved mechanisms that led to corrosion of the Precice Stryde (Stryde) intramedullary lengthening nail in the post market surveillance era of the device. Between 2018 and 2021 more than 2,000 Stryde nails have been implanted worldwide. However, the outcome of treatment with the Stryde system is insufficiently reported. This is a retrospective single-centre study analyzing outcome of 57 consecutive lengthening procedures performed with the Stryde nail at the authors’ institution from February 2019 until November 2020. Macro- and microscopic metallographic analysis of four retrieved nails was conducted. To investigate observed corrosion at telescoping junction, scanning electron microscopy (SEM) and energy dispersive x-ray spectroscopy (EDX) were performed.Aims
Methods
Aims. Dual mobility implants in total hip arthroplasty are designed to increase the functional head size, thus decreasing the potential for dislocation. Modular dual mobility (MDM) implants incorporate a metal liner (e.g. cobalt-chromium alloy) in a metal shell (e.g. titanium alloy), raising concern for mechanically assisted crevice corrosion at the modular liner-shell connection. We sought to examine
Modular dual mobility (MDM) acetabular components are often used with the aim of reducing the risk of dislocation in revision total hip arthroplasty (THA). There is, however, little information in the literature about its use in this context. The aim of this study, therefore, was to evaluate the outcomes in a cohort of patients in whom MDM components were used at revision THA, with a mean follow-up of more than five years. Using the database of
a single academic centre, 126 revision THAs in 117 patients using a single
design of an MDM acetabular component were retrospectively reviewed. A total of 94 revision THAs in 88 patients with a mean follow-up of 5.5 years were included in the study. Survivorship was analyzed with the endpoints of dislocation, reoperation for dislocation, acetabular revision for aseptic loosening, and acetabular revision for any reason. The secondary endpoints were surgical complications and the radiological outcome.Aims
Methods
The Exeter V40 cemented femoral stem was first introduced in 2000. The largest single-centre analysis of this implant to date was published in 2018 by Westerman et al. Excellent results were reported at a minimum of ten years for the first 540 cases performed at the designer centre in the Exeter NHS Trust, with stem survivorship of 96.8%. The aim of this current study is to report long-term outcomes and survivorship for the Exeter V40 stem in a non-designer centre. All patients undergoing primary total hip arthroplasty using the Exeter V40 femoral stem between 1 January 2005 and 31 January 2010 were eligible for inclusion. Data were collected prospectively, with routine follow-up at six to 12 months, two years, five years, and ten years. Functional outcomes were assessed using Western Ontario and McMaster Universities Osteoarthritis Index (WOMAC) scores. Outcome measures included data on all components in situ beyond ten years, death occurring within ten years with components in situ, and all-cause revision surgery.Aims
Methods
Dual mobility (DM) bearings are an attractive treatment option to obtain hip stability during challenging primary and revision total hip arthroplasty (THA) cases. The purpose of this study was to analyze data submitted to the American Joint Replacement Registry (AJRR) to characterize utilization trends of DM bearings in the USA. All primary and revision THA procedures reported to AJRR from 2012 to 2018 were analyzed. Patients of all ages were included and subdivided into DM and traditional bearing surface cohorts. Patient demographics, geographical region, hospital size, and teaching affiliation were assessed. Associations were determined by chi-squared analysis and logistic regression was performed to assess outcome variables.Aims
Methods
The aim of this study was to develop a novel computational model for estimating head/stem taper mechanics during different simulated assembly conditions. Finite element models of generic cobalt-chromium (CoCr) heads on a titanium stem taper were developed and driven using dynamic assembly loads collected from clinicians. To verify contact mechanics at the taper interface, comparisons of deformed microgroove characteristics (height and width of microgrooves) were made between model estimates with those measured from five retrieved implants. Additionally, these models were used to assess the role of assembly technique—one-hit versus three-hits—on the taper interlock mechanical behaviour.Aims
Methods
We have previously demonstrated raised cobalt and chromium levels in patients with larger diameter femoral heads, following metal-on-polyethylene uncemented total hip arthroplasty. Further data have been collected, to see whether these associations have altered with time and to determine the long-term implications for these patients and our practice. Patients from our previous study who underwent Trident-Accolade primary total hip arthroplasties using a metal-on-polyethylene bearing in 2009 were reviewed. Patients were invited to have their cobalt and chromium levels retested, and were provided an Oxford Hip Score. Serum ion levels were then compared between groups (28 mm, 36 mm, and 40 mm heads) and over time.Aims
Methods
Aims. This combined clinical and in vitro study aimed to determine the incidence of liner malseating in modular dual mobility (MDM) constructs in primary total hip arthroplasties (THAs) from a large volume arthroplasty centre, and determine whether malseating increases the potential for
We evaluated a large database with mechanical failure of a single uncemented modular femoral component, used in revision hip arthroplasty, as the end point and compared them to a control group treated with the same implant. Patient- and implant-specific risk factors for implant failure were analyzed. All cases of a fractured uncemented modular revision femoral component from one manufacturer until April 2017 were identified and the total number of implants sold until April 2017 was used to calculate the fracture rate. The manufacturer provided data on patient demographics, time to failure, and implant details for all notified fractured devices. Patient- and implant-specific risk factors were evaluated using a logistic regression model with multiple imputations and compared to data from a previously published reference group, where no fractures had been observed. The results of a retrieval analysis of the fractured implants, performed by the manufacturer, were available for evaluation.Aims
Methods
The aim of this study was to evaluate blood metal ion levels, leucocyte profiles, and serum cytokines in patients with a total hip arthroplasty (THA) involving modular dual-mobility components. A total of 39 patients were recruited, with clinical follow-up of up to two years. Outcome was assessed using the Harris Hip Score (HHS, the 12-Item Short-Form Health Survey (SF-12), the Western Ontario and McMaster Universities Osteoarthritis Index (WOMAC), and a visual analogue scale (VAS) for pain. Blood concentrations of cobalt (Co), chromium (Cr), and serum cytokines were measured. Subpopulations of leucocytes were analyzed by flow cytometry.Aims
Patients and Methods
Modular dual-mobility constructs reduce the risk of dislocation after revision total hip arthroplasty (THA). However, questions about metal ions from the cobalt-chromium (CoCr) liner persist, and are particularly germane to patients being revised for adverse local tissue reactions (ALTR) to metal. We determined the early- to mid-term serum Co and Cr levels after modular dual-mobility components were used in revision and complex primary THAs, and specifically included patients revised for ALTR. Serum Co and Cr levels were measured prospectively in 24 patients with a modular dual-mobility construct and a ceramic femoral head. Patients with CoCr heads or contralateral THAs with CoCr heads were excluded. The mean age was 63 years (35 to 83), with 13 patients (54%) being female. The mean follow-up was four years (2 to 7). Indications for modular dual-mobility were prosthetic joint infection treated with two-stage exchange and subsequent reimplantation (n = 8), ALTR revision (n = 7), complex primary THA (n = 7), recurrent instability (n = 1), and periprosthetic femoral fracture (n = 1). The mean preoperative Co and Cr in patients revised for an ALTR were 29.7 μg/l (2 to 146) and 21.5 μg/l (1 to 113), respectively.Aims
Patients and Methods
Aims. The aim of this study was to evaluate
Modular dual mobility (DM) prostheses in which a cobalt-chromium liner is inserted into a titanium acetabular shell ( This was a prospective study of patients between 18 and 65 years of age, with a body mass index (BMI) < 35 kg/m2 and University of California at Los Angeles (UCLA) activity score > 6, who received a modular cobalt-chromium acetabular liner, highly crosslinked polyethylene mobile bearing, and cementless titanium femoral stem for their primary THA. Patients with a history of renal disease and metal hardware elsewhere in the body were excluded. A total of 43 patients (30 male, 13 female; mean age 52.6 years (Aims
Patients and Methods
Opening wedge high tibial osteotomy (HTO) is an established surgical procedure for the treatment of early-stage knee arthritis. Other than infection, the majority of complications are related to mechanical factors – in particular, stimulation of healing at the osteotomy site. This study used finite element (FE) analysis to investigate the effect of plate design and bridging span on interfragmentary movement (IFM) and the influence of fracture healing on plate stress and potential failure. A 10° opening wedge HTO was created in a composite tibia. Imaging and strain gauge data were used to create and validate FE models. Models of an intact tibia and a tibia implanted with a custom HTO plate using two different bridging spans were validated against experimental data. Physiological muscle forces and different stages of osteotomy gap healing simulating up to six weeks postoperatively were then incorporated. Predictions of plate stress and IFM for the custom plate were compared against predictions for an industry standard plate (TomoFix).Objectives
Materials and Methods
Objectives. The Precice nail is the latest intramedullary lengthening nail with excellent early outcomes. Implant complications have led to modification of the nail design. The aim of this study was to perform a retrieval study of Precice nails following lower-limb lengthening and to assess macroscopical and microscopical changes to the implants and evaluate differences following design modification, with the aim of identifying potential surgical, implant, and patient risk factors. Methods. A total of 15 nails were retrieved from 13 patients following lower-limb lengthening. Macroscopical and microscopical surface damage to the nails were identified. Further analysis included radiology and micro-CT prior to sectioning. The internal mechanism was then analyzed with scanning electron microscopy and energy dispersive x-ray spectroscopy to identify corrosion. Results. Seven male and three female patients underwent 12 femoral lengthenings. Three female patients underwent tibial lengthening. All patients obtained the desired length with no implant failure. Surface degradation was noted on the telescopic part of every nail design, less on the latest implants. Microscopical analysis confirmed
The aim of this study was to determine whether there is a difference
in the rate of wear between acetabular components positioned within
and outside the ‘safe zones’ of anteversion and inclination angle. We reviewed 100 hips in 94 patients who had undergone primary
total hip arthroplasty (THA) at least ten years previously. Patients
all had the same type of acetabular component with a bearing couple
which consisted of a 28 mm cobalt-chromium head on a highly crosslinked
polyethylene (HXLPE) liner. A supine radiostereometric analysis
(RSA) examination was carried out which acquired anteroposterior
(AP) and lateral paired images. Acetabular component anteversion
and inclination angles were measured as well as total femoral head
penetration, which was divided by the length of implantation to
determine the rate of polyethylene wear.Aims
Patients and Methods
Fretting and corrosion at the modular head/neck junction, known
as trunnionosis, in total hip arthroplasty (THA) is a cause of adverse
reaction to metal debris (ARMD). We describe the outcome of revision
of metal-on-polyethylene (MoP) THA for ARMD due to trunnionosis
with emphasis on the risk of major complications. A total of 36 patients with a MoP THA who underwent revision
for ARMD due to trunnionosis were identified. Three were excluded
as their revision had been to another metal head. The remaining
33 were revised to a ceramic head with a titanium sleeve. We describe
the presentation, revision findings, and risk of complications in
these patients.Aims
Patients and Methods
Taper junctions between modular hip arthroplasty femoral heads and stems fail by wear or corrosion which can be caused by relative motion at their interface. Increasing the assembly force can reduce relative motion and corrosion but may also damage surrounding tissues. The purpose of this study was to determine the effects of increasing the impaction energy and the stiffness of the impactor tool on the stability of the taper junction and on the forces transmitted through the patient’s surrounding tissues. A commercially available impaction tool was modified to assemble components in the laboratory using impactor tips with varying stiffness at different applied energy levels. Springs were mounted below the modular components to represent the patient. The pull-off force of the head from the stem was measured to assess stability, and the displacement of the springs was measured to assess the force transmitted to the patient’s tissues.Objectives
Methods
To present a surgically relevant update of trunnionosis. Systematic review performed April 2017.Aims
Materials and Methods
We sought to determine whether cobalt-chromium alloy (CoCr) femoral
stem tapers (trunnions) wear more than titanium (Ti) alloy stem
tapers (trunnions) when used in a large diameter (LD) metal-on-metal
(MoM) hip arthroplasty system. We performed explant analysis using validated methodology to
determine the volumetric material loss at the taper surfaces of
explanted LD CoCr MoM hip arthroplasties used with either a Ti alloy
(n = 28) or CoCr femoral stem (n = 21). Only 12/14 taper constructs
with a rough male taper surface and a nominal included angle close
to 5.666° were included. Multiple regression modelling was undertaken
using taper angle, taper roughness, bearing diameter (horizontal
lever arm) as independent variables. Material loss was mapped using
a coordinate measuring machine, profilometry and scanning electron
microscopy.Aims
Patients and Methods
Femoral stems with exchangeable (modular) necks were introduced
to offer surgeons an increased choice when determining the version,
offset and length of the femoral neck during total hip arthroplasty
(THA). It was hoped that this would improve outcomes and reduce
complications, particularly dislocation. In 2010, the Australian Orthopaedic
Association National Joint Replacement Registry (AOANJRR) first
reported an increased rate of revision after primary THA using femoral
stems with an exchangeable neck. The aim of this study was to provide
a more comprehensive up-to-date analysis of primary THA using femoral
stems with exchangeable and fixed necks. The data included all primary THA procedures performed for osteoarthritis
(OA), reported to the AOANJRR between 01 September 1999 and 31 December
2014. There were 9289 femoral stems with an exchangeable neck and
253 165 femoral stems with a fixed neck. The characteristics of
the patients and prostheses including the bearing surface and stem/neck
metal combinations were examined using Cox proportional hazard ratios
(HRs) and Kaplan-Meier estimates of survivorship. Aims
Materials and Methods
It may not be possible to undertake revision total hip arthroplasty
(THA) in the presence of massive loss of acetabular bone stock using
standard cementless hemispherical acetabular components and metal
augments, as satisfactory stability cannot always be achieved. We
aimed to study the outcome using a reconstruction cage and a porous
metal augment in these patients. A total of 22 acetabular revisions in 19 patients were performed
using a combination of a reconstruction cage and porous metal augments.
The augments were used in place of structural allografts. The mean
age of the patients at the time of surgery was 70 years (27 to 85)
and the mean follow-up was 39 months (27 to 58). The mean number
of previous THAs was 1.9 (1 to 3). All patients had segmental defects
involving more than 50% of the acetabulum and seven hips had an
associated pelvic discontinuity. Aims
Patients and Methods
Objectives. The use of ceramic femoral heads in total hip arthroplasty (THA) has increased due to their proven low bearing wear characteristics. Ceramic femoral heads are also thought to reduce wear and corrosion at the head-stem junction with titanium (Ti) stems when compared with metal heads. We sought to evaluate taper damage of ceramic compared with metal heads when paired with cobalt chromium (CoCr) alloy stems in a single stem design. Methods. This retrieval study involved 48 total hip arthroplasties (THAs) with CoCr V40 trunnions paired with either CoCr (n = 21) or ceramic (n = 27) heads. The taper junction of all hips was evaluated for
Modular or custom-made femoral components have been preferred
for total hip arthroplasty (THA) in patients with a history of Perthes’
disease because of the distortion in the anatomy of the proximal
femur. However, it has not been established whether a monobloc cementless
stem will fit the distorted proximal femur or whether the results
of the procedure are satisfactory in this group of patients. We reviewed 68 consecutive patients who had undergone THA for
childhood Perthes’ disease between June 2003 and December 2008.
There were 35 men and 33 women with a mean age of 48 years (16 to
73) at the time of index arthroplasty. Their mean body mass index
was 24.4 (18.3 to 32.9). Of the 68 hips, 32 were classified as Stulberg
class III and 36 as class IV. The mean pre-operative shortening
of the affected leg was 17.2 mm (5 to 34). The minimum follow-up
was five years (mean 8.5 years; 5.2 to 10).Aims
Patients and Methods
This study aimed to characterise and qualitatively grade the severity of the corrosion particles released into the hip joint following taper corrosion. The 26 cases examined were CoC/ABG Modular (n = 13) and ASR/SROM (n = 13). Blood serum metal ion levels were collected before and after revision surgery. The haematoxylin and eosin tissue sections were graded on the presence of fibrin exudates, necrosis, inflammatory cells and corrosion products. The corrosion products were identified based on visible observation and graded on abundance. Two independent observers blinded to the clinical patient findings scored all cases. Elemental analysis was performed on corrosion products within tissue sections. X-Ray diffraction was used to identify crystalline structures present in taper debris.Objectives
Methods
Modular junctions are ubiquitous in contemporary hip arthroplasty. The head-trunnion junction is implicated in the failure of large diameter metal-on-metal (MoM) hips which are the currently the topic of one the largest legal actions in the history of orthopaedics (estimated costs are stated to exceed $4 billion). Several factors are known to influence the strength of these press-fit modular connections. However, the influence of different head sizes has not previously been investigated. The aim of the study was to establish whether the choice of head size influences the initial strength of the trunnion-head connection. Ti-6Al-4V trunnions (n = 60) and two different sizes of cobalt-chromium (Co-Cr) heads (28 mm and 36 mm; 30 of each size) were used in the study. Three different levels of assembly force were considered: 4 kN; 5 kN; and 6 kN (n = 10 each). The strength of the press-fit connection was subsequently evaluated by measuring the pull-off force required to break the connection. The statistical differences in pull-off force were examined using a Kruskal–Wallis test and two-sample Mann–Whitney U test. Finite element and analytical models were developed to understand the reasons for the experimentally observed differences.Objectives
Materials and Methods
There is increasing global awareness of adverse
reactions to metal debris and elevated serum metal ion concentrations
following the use of second generation metal-on-metal total hip
arthroplasties. The high incidence of these complications can be
largely attributed to corrosion at the head-neck interface. Severe
corrosion of the taper is identified most commonly in association
with larger diameter femoral heads. However, there is emerging evidence
of varying levels of corrosion observed in retrieved components
with smaller diameter femoral heads. This same mechanism of galvanic
and mechanically-assisted crevice corrosion has been observed in
metal-on-polyethylene and ceramic components, suggesting an inherent
biomechanical problem with current designs of the head-neck interface. We provide a review of the fundamental questions and answers
clinicians and researchers must understand regarding corrosion of
the taper, and its relevance to current orthopaedic practice. Cite this article:
Recently, the use of metal-on-metal articulations
in total hip arthroplasty (THA) has led to an increase in adverse
events owing to local soft-tissue reactions from metal ions and
wear debris. While the majority of these implants perform well,
it has been increasingly recognised that a small proportion of patients
may develop complications secondary to systemic cobalt toxicity
when these implants fail. However, distinguishing true toxicity
from benign elevations in cobalt ion levels can be challenging. The purpose of this two part series is to review the use of cobalt
alloys in THA and to highlight the following related topics of interest:
mechanisms of cobalt ion release and their measurement, definitions
of pathological cobalt ion levels, and the pathophysiology, risk factors
and treatment of cobalt toxicity. Historically, these metal-on-metal
arthroplasties are composed of a chromium-cobalt articulation. The release of cobalt is due to the mechanical and oxidative
stresses placed on the prosthetic joint. It exerts its pathological
effects through direct cellular toxicity. This manuscript will highlight the pathophysiology of cobalt
toxicity in patients with metal-on-metal hip arthroplasties. Take home message: Patients with new or evolving hip symptoms
with a prior history of THA warrant orthopaedic surgical evaluation.
Increased awareness of the range of systemic symptoms associated
with cobalt toxicity, coupled with prompt orthopaedic intervention, may
forestall the development of further complications. Cite this article:
An uncemented hemispherical acetabular component
is the mainstay of acetabular revision and gives excellent long-term
results. Occasionally, the degree of acetabular bone loss means that a
hemispherical component will be unstable when sited in the correct
anatomical location or there is minimal bleeding host bone left
for biological fixation. On these occasions an alternative method
of reconstruction has to be used. A major column structural allograft has been shown to restore
the deficient bone stock to some degree, but it needs to be off-loaded
with a reconstruction cage to prevent collapse of the graft. The
use of porous metal augments is a promising method of overcoming
some of the problems associated with structural allograft. If the defect
is large, the augment needs to be protected by a cage to allow ingrowth
to occur. Cup-cage reconstruction is an effective method of treating
chronic pelvic discontinuity and large contained or uncontained
bone defects. This paper presents the indications, surgical techniques and
outcomes of various methods which use acetabular reconstruction
cages for revision total hip arthroplasty. Cite this article:
Tapered fluted titanium stems are increasingly
used for femoral revision arthroplasty. They are available in modular and
non-modular forms. Modularity has advantages when the bone loss
is severe, the proximal femur is mis shapen or the surgeon is unfamiliar
with the implant, but it introduces the risk of fracture of the
stem at the junction between it and the proximal body segment. For
that reason, and while awaiting intermediate-term results of more recently
introduced designs of this junction, non-modularity has attracted
attention, at least for straightforward revision cases. We review the risks and causes of fracture of tapered titanium
modular revision stems and present an argument in favour of the
more selective use of modular designs. Cite this article:
We compared the incidence of pseudotumours after
large head metal-on-metal (MoM) total hip arthroplasty (THA) with
that after conventional metal-on-polyethylene (MoP) THA and assessed
the predisposing factors to pseudotumour formation. From a previous randomised controlled trial which compared large
head (38 mm to 60 mm) cementless MoM THA with conventional head
(28 mm) cementless MoP THA, 93 patients (96 THAs: 41 MoM (21 males,
20 females, mean age of 64 years, standard deviation ( The incidence of pseudotumours, measured using a standardised
CT protocol was 22 (53.7%) after MoM THA and 12 (21.8%) after MoP
THA. Women with a MoM THA were more likely to develop a pseudotumour
than those with a MoP THA (15 Contrary to popular belief, pseudotumours occur frequently around
MoP THAs. Women with a MoM THA and an elevated cobalt level are
at greatest risk. In this study, pseudotumours had no effect on
the functional outcome after either large head MoM or conventional
MoP THA. Cite this article:
The October 2015 Hip &
Pelvis Roundup360 looks at: Smoking and complications in arthroplasty; Smoking cessation beneficial in arthroplasty; Intermediate care and arthroplasty; Do we still need cell salvage?; Femoroacetabular impingement in the Japanese population; Trunnionosis or taperosis and geometry; Decontamination for staphylococcus aureus works!; Policeman or opportunity? Quality improvement with registries; Death rates higher in readmission to other hospitals
Periprosthetic femoral fracture (PFF) is a potentially
devastating complication after total hip arthroplasty, with historically
high rates of complication and failure because of the technical
challenges of surgery, as well as the prevalence of advanced age
and comorbidity in the patients at risk. This study describes the short-term outcome after revision arthroplasty
using a modular, titanium, tapered, conical stem for PFF in a series
of 38 fractures in 37 patients. The mean age of the cohort was 77 years (47 to 96). A total of
27 patients had an American Society of Anesthesiologists grade of
at least 3. At a mean follow-up of 35 months (4 to 66) the mean
Oxford Hip Score (OHS) was 35 (15 to 48) and comorbidity was significantly
associated with a poorer OHS. All fractures united and no stem needed
to be revised. Three hips in three patients required further surgery
for infection, recurrent PFF and recurrent dislocation and three
other patients required closed manipulation for a single dislocation.
One stem subsided more than 5 mm but then stabilised and required
no further intervention. In this series, a modular, tapered, conical stem provided a versatile
reconstruction solution with a low rate of complications. Cite this article:
Adverse reaction to wear and corrosion debris
is a cause for concern in total hip arthroplasty (THA). Modular junctions
are a potential source of such wear products and are associated
with secondary pseudotumour formation. We present a consecutive series of 17 patients treated at our
unit for this complication following metal-on-highly cross-linked
polyethylene (MoP) THA. We emphasise the risk of misdiagnosis as
infection, and present the aggregate laboratory results and pathological
findings in this series. The clinical presentation was pain, swelling or instability.
Solid, cystic and mixed soft-tissue lesions were noted on imaging
and confirmed intra-operatively. Corrosion at the head–neck junction
was noted in all cases. No bacteria were isolated on multiple pre-
and intra-operative samples yet the mean erythrocyte sedimentation
rate was 49 (9 to 100) and C-reactive protein 32 (0.6 to 106) and
stromal polymorphonuclear cell counts were noted in nine cases. Adverse soft–tissue reactions can occur in MoP THA owing to corrosion
products released from the head–neck junction. The diagnosis should
be carefully considered when investigating pain after THA. This
may avoid the misdiagnosis of periprosthetic infection with an unidentified
organism and mitigate the unnecessary management of these cases
with complete single- or two-stage exchange. Cite this article:
Tribocorrosion at the head–neck taper interface
– so-called ‘taperosis’ – may be a source of metal ions and particulate
debris in metal-on-polyethylene total hip arthroplasty (THA). We examined the effect of femoral head length on
The aim of this study was to assess the effect
of frictional torque and bending moment on