INTRODUCTION

The introduction of hard-on-hard bearings and the consequences of increased wear due to edge-loading have renewed interest in the importance of acetabular component orientation for implant survival and functional outcome following hip arthroplasty. Some studies have shown increased dislocation risk when the cup is mal-oriented which has led to the identification of a safe-zone1. The aims of this prospective, multi-centered study of primary total hip arthroplasty (THA) were to: 1. Identify factors that influence cup orientation and 2. Describe the effect of cup orientation on clinical outcome.

Plasma levels of cobalt and chromium ions and Metal Artefact Reduction Sequence (MARS)-MRI scans were performed on patients with 209 consecutive, unilateral, symptomatic metal-on-metal (MoM) hip arthroplasties. There was wide variation in plasma cobalt and chromium levels, and MARS-MRI scans were positive for adverse reaction to metal debris (ARMD) in 84 hips (40%). There was a significant difference in the median plasma cobalt and chromium levels between those with positive and negative MARS-MRI scans (p < 0.001). Compared with MARS-MRI as the potential reference standard for the diagnosis of ARMD, the sensitivity of metal ion analysis for cobalt or chromium with a cut-off of > 7 µg/l was 57%. The specificity was 65%, positive predictive value was 52% and the negative predictive value was 69% in symptomatic patients. A lowered threshold of > 3.5 µg/l for cobalt and chromium ion levels improved the sensitivity and negative predictive value to 86% and 74% but at the expense of specificity (27%) and positive predictive value (44%).

Metal ion analysis is not recommended as a sole indirect screening test in the surveillance of symptomatic patients with a MoM arthroplasty. The investigating clinicians should have a low threshold for obtaining cross-sectional imaging in these patients, even in the presence of low plasma metal ion levels.

Patients with hip fracture are at high risk of venous thromboembolism (VTE). Chemical thromboprophylaxis with low molecular weight heparin (LMWH) is associated with a risk of major bleeding in certain patient groups, such as those with renal failure. In these patients, unfractionated heparin should be used. Our aim was to determine the practice of VTE risk assessment in patients admitted with hip fracture against the national guidance, which states that all should have VTE risk assessment on admission. We also assessed the impact of introducing the VTE risk assessment form on prescribing practice of chemical thromboprophylaxis in patients with renal failure.

Prospective audit of patients of 50 patients admitted with hip fracture from 4/8/10 with re-audit of 50 patients admitted from 17/2/2011 after introducing the VTE risk assessment form into the hip fracture admissions proforma. Retrospective analysis was undertaken to determine chemical thromboprophylaxis prescribing in patients with eGFR <30ml/min/1.73m².

Patient demographics were comparable in both audit loops, with the mean age being equal (84 years) and an equal majority of female patients (76%). There were similar numbers of patients with eGFR <30ml/min/1.73m² in both audit loops with 8% (n=4) in the initial audit, and 10% (n=5) in the re-audit. Frequency of VTE risk assessment significantly increased from 16% to 86% after including the VTE risk assessment form in the hip fracture proforma (p<0.0001). Despite this, there was no significant reduction in prescribing of LMWH in patients with renal failure with eGFR <30ml/min/1.73m², (P=0.52).

Documentation of VTE risk assessment in patients admitted with hip fracture can be improved by simple measures such as inclusion of the VTE risk assessment form in the admissions proforma. However, this did not result in a reduction of LMWH prescribed in patients with significant renal failure and risk of major bleeding.

Cognitive impairment is common in patients with hip fracture both on admission and may develop later on. Reduced cognitive function is a risk factor for development of delirium, correlates with poor rehabilitation, and is an independent predictor of increased mortality. Despite its commonplace and potential for serious morbidity, cognitive dysfunction is often poorly assessed & diagnosed.

Our aims were to 1) assess the practice of cognitive assessment on admission for hip fracture patients according to local guidelines and 2) ascertain whether it can be improved by the formal introduction of Abbreviated Mental Test Score (AMTS) & Clock Drawing Test (CDT) in the hip fracture admission proforma.

A prospective audit was undertaken of cognitive assessment by either AMTS or CDT for 50 consecutive patients admitted with hip fracture from 4/8/2010. Subsequently, the hip fracture admission proforma was amended to include both the AMTS & CDT. A re-audit was performed on 50 consecutive patients admitted from 17/2/2011 to determine the change in practice.

Patient demographics were comparable in both audit loops, with the mean age being equal (84 years) and an equal majority of female patients (76%). Cognitive assessment by either AMTS or CDT significant increased from 28% (n=14) to 86% (n=43) in the re-audit (p<0.0001). All AMTS were completed in accordance with instructions, whereas almost half of CDTs were incompletely or incorrectly filled out (45%).

The assessment of cognitive function can be greatly improved by inclusion of both the AMTS & CDT to the hip fracture admission proforma, allowing the most appropriate multi-disciplinary care to be planned for the patient. Whilst both CDT and AMTS are good screening tools for cognitive impairment, many are unfamiliar with CDT & more training is needed.

Stem geometry is known to influence the outcome in THA; however it is unknown whether the material properties, stiffness in particular can influence the stem stability and outcome. The aim of this study was to measure the influence of stem material properties on micromotion and migration using Roentgen Stereophotogrammetric Analysis (RSA) system.

41 patients were implanted with a collarless polished tapered (CPT) femoral stem (Zimmer, Warsaw, Indiana), which was made of either cobalt-chromium (CoCr) (n=21) or stainless steel (n=20). RSA was used to measure dynamically inducible micromotion (DIMM: difference in stem position in going from double-leg stance (DLS) to single leg stance (SLS)), prosthesis bending (difference in the head-tip distance when going from DLS to SLS), and mean migration of the head, tip and the cement restrictor. DIMM and bending were measured at 3 months, migration at 6, 12 and 24 months. All analyses were carried out using SPSS for windows (v.15.0.0, Chicago. IL, USA). Results were reported as mean ± 95% confidence interval (CI) and regarded as significant when p < 0.05.

Preliminary analysis showed that total head DIMM was significantly (p = 0.02) greater for CoCr (0.97mm ± 0.6mm) than stainless steel (0.27mm ± 0.6mm). The mean stem bending for CoCr was 0.08mm (± 0.06mm) and for stainless steel 0.15mm (± 0.06mm) (p =0.77). Both implants heads migrated posteriorly, medially and distally. The mean subsidence for the cobalt-chromium and stainless steel stems was 1.02mm (± 0.19mm) (p < 0.001) and 1.12mm (± 0.34mm) (p=0.001) (p= 0.07) at 24 months.

It was interesting to note that the dynamically induced micromotion was greater for the stiffer stem, however there were no differences in terms of overall migration, indicating that survival (in terms of loosening) should be the similar for both steel and CoCr versions of this implant.

INTRODUCTION

The risk of dislocation in large diameter metal on metal hip replacement is significantly lower than in standard THR. This is due to the increased primary arc, increased jump distance and possibly a suction effect. Our unit has performed over 1500 of these cases with an overall revision rate of <1%. We report a case series of dislocations in 5 large diameter metal on metal hips undertaken at our unit.

Femoral stem varus has been associated with poorer results. We report the incidence of varus/valgus malalignment of the Exeter polished, double taper design in a multicentre prospective study. The surgical outcomes at a minimum of five year and complication rates are also reported.

A multicentre prospective study of 987 total hip replacements was undertaken to investigate whether there is an association between surgical outcome and femoral stem malalignment. The primary outcome measure was the change in the Oxford hip score (OHS) at five years. Secondary outcomes included the rate of dislocation and revision.

The incidence of varus and valgus malignment were 7.1% and 2.6% respectively. There was no significant difference in OHS between neutral and malaligned femoral stems at 5 years (neutral, mean = 40.2; varus, mean 39.3, p = 0.465; valgus, mean = 40.9, p = 0.605). There was no significant difference in dislocation rate between the groups (p = 0.66). There was also no significant difference in revision rate (p = 0.34).

This study provides evidence that the Exeter stem is extremely tolerant of varus and valgus malalignment, both in terms of outcome and complication rate.

Aim

To determine the outcome, the need for revision surgery, quality of life (QOL) of patients and the financial implications of instability following successful closed reduction of dislocation after primary total hip arthroplasty (THA).

We obtained pre-operative and six-month post-operative Oxford hip (OHS) and knee scores (OKS) for 1523 patients who underwent total hip replacement and 1784 patients who underwent total knee replacement. They all also completed a six-month satisfaction question.

Scatter plots showed no relationship between pre-operative Oxford scores and six-month satisfaction scores. Spearman’s rank correlation coefficients were -0.04 (95% confidence interval (CI) -0.09 to 0.01) between OHS and satisfaction and 0.04 (95% CI -0.01 to 0.08) between OKS and satisfaction. A receiver operating characteristic (ROC) curve analysis was used to identify a cut-off point for the pre-operative OHS/OKS that identifies whether or not a patient is satisfied with surgery. We obtained an area under the ROC curve of 0.51 (95% CI 0.45 to 0.56) for hip replacement and 0.56 (95% CI 0.51 to 0.60) for knee replacement, indicating that pre-operative Oxford scores have no predictive accuracy in distinguishing satisfied from dissatisfied patients.

In the NHS widespread attempts are being made to use patient-reported outcome measures (PROMs) data for the purpose of prioritising patients for surgery. Oxford hip and knee scores have no predictive accuracy in relation to post-operative patient satisfaction. This evidence does not support their current use in prioritising access to care.

Introduction: Metal-on-metal-hip-resurfacing-arthroplasty (MoMHRA) has been associated with the development of inflammatory pseudotumours(IP), especially in females. IPs have been linked to wear debris, which can be related to metal-ion blood levels. Acetabular component position has been shown to influence wear. We have identified an optimum component orientation minimising IP risk around an inclination/anteversion of 40°/20°±10°. Our aim was to see if this optimal position results in lower metal ions and to identify the boundary of an optimal placement zone for low wear.

Methods: A cohort of 104 patients(60M:44F) with unilateral MoMHRA was studied. Blood tests were obtained at a mean follow up of 3.9 years and serum Co/Cr levels were measured(ICPMS). High metal ion concentrations were defined as Co> 4.1ppb and Cr> 5.2ppb. Radiographic cup inclination/anteversion were measured using EBRA. The differences in ion levels between different orientation zones were investigated. Three orientation zones were defined centered on 40°/20°: Z1-within ±5°, Z2-outside ±5°/within ±10° and Z3-within ±10°.

Results: There was a wide range of cup placements. Females had significantly (p< 0.001) smaller components(mean:51, 44–60) than males(mean: 56, 52–64). Cr levels, but not Co, were higher in females(p=0.002) and those with small femoral components(< 50mm, p =0.03). Patients with cups within Z1 (n=13) had significantly lower Co(p=0.005) and Cr(p=0.001). Males with cups within Z3(n=27) had lower ion levels in comparison to those outside, which were significantly lower for Co(p=0.049) but not Cr(p=0.084). Females had similar ion levels within and out of Z3(Cr/Co: p=0.83/0.84). Co levels were significantly lower in Z1(n=13) in comparison to Z2(n=33)(p=0.048) but Cr levels were not different (p=0.06).

Discussion: MoMHRA cups placed within ±5° of the optimum(40°/20°) had significantly lower metal ions indicating lower wear within this narrow zone. This safe zone, could extend to ±10° for males only. The narrower safe zone coupled with smaller components implanted are possible factors contributing to the increased IP incidence seen in females.

Introduction: Metal on metal hip resurfacing arthroplasty-induced pseudotumours are a serious complication, which occur in 1.8% of patients who undergo this procedure in our institution. The aim of this study was to measure the 3D in vivo wear on the surface of resurfacing components revised for pseudotumour, compared to a control group.

Method: Thirty-six hip resurfacing implants were divided into two groups; 18 patients with a clinical and histopathological diagnosis of pseudotumour and 18 controls (revised for femoral neck fracture and infection). Three dimensional contactless metrology (Redlux^™ Ltd) was used to scan the surface of the femoral and acetabular components, to a resolution of 20 nanometers. The location, depth and area of the wear scar were determined for each component. A separate blinded analysis to determine the presence of absence of impingement was performed by one of the authors.

Results: The volumetric wear rate for femoral component of the pseudotumour group was 3.29 mm3/yr (SD5.7) and 0.79 mm3/yr (SD1.2) for the control group (p=0.005). In the pseudotumour group, the volumetric wear rate of the acetabular component was 2.5 mm3/yr (SD6.9) compared to 0.36 mm3/yr (SD0.80) for the control group (p=0.008). Edge-wear was detected in 89% of acetabular components in the pseudotumour group and 21% of those in the control group (p=0.01). Anterior or posterior edge-wear, consistent with impingement was present on the femoral components of 73% of patients in the pseudotumour group and 22% in the control group (p=0.01).

Discussion: This work demonstrates that implants revised for pseudotumour have significantly higher volumetric wear rates than controls. They also have a significantly higher incidence of edge-wear than controls. We suggest that a significant proportion of pseudotumours are associated with high concentrations of metal wear debris; however a minority may result from a hypersensitivity reaction to metal ions.

Introduction: The use of highly cross-linked polyethylene (HXLPE) is now commonplace for total hip arthroplasty, however there is no long-term data to support its use. Hip simulator studies suggest that the wear rate of some types of HXLPE is ten times less than conventional polyethylene (UHMWPE). The outcomes of hip simulator studies are not always reproduced in vivo and there is some evidence that HXLPE wear may increase between 5 and 7 years.

Method: A prospective double blind randomised control trial was conducted using Radiostereometric Analysis (RSA). Fifty-four subjects were randomised to receive hip replacements with either UHMWPE liners or HXLPE liners. All subjects received a cemented CPT stem and uncemented Trilogy acetabular component (Zimmer, Warsaw, IN, USA). The 3D penetration of the head into the socket was determined to a minimum of 7 years.

Results: The total liner penetration was significantly different at 7 years (p=0.005) with values of 0.33 mm (SE 0.05 mm) for the HXLPE group and 0.55 mm (SE 0.05 mm) for the UHMWPE group. The steady state wear rate from 1 year onwards was significantly lower for HXLPE (0.005 mm/yr, SE 0.007 mm/yr) than for UHMWPE (0.037 mm/yr, SE 0.009 mm/yr) (p=0.007). The direction of wear was supero-lateral.

Discussion: We have previously demonstrated that the penetration in the first year is creep-dominated, from one year onwards the majority of penetration is probably due to wear. This study confirms the predictions from hip simulator studies which suggest that the wear rate of this HXLPE approaches that of metal-on-metal and ceramic-on-ceramic articulations. HXLPE may have the potential to reduce the need of revision surgery, due to wear debris induced osteolysis. It may also enable surgeons to use larger couples, thus reducing the risk of impingement and dislocation.

Introduction: Metal on metal hip resurfacing arthroplasty(MoMHRA) is an alternative option to THR in the treatment of young adults with OA. A recognised MoMHRA complication is the development of an inflammatory pseudotumour(IP). Diagnosis is made with the aid of US and/or MRI. To-date, no radiographic indication of the presence of IP has been identified. Neck thinning is a recognised phenomenon in MoMHRA hips not associated with any adverse clinical events. Its pathogenesis is considered multi-factorial. Our aim was to establish whether excessive neck narrowing is associated with the presence of a pseudotumour.

Methods: Twenty-seven hips (26 patients) with IP confirmed clinically, radiologically, intra-operatively and histologically were matched for sex, age, pre-operative diagnosis, component size and follow-up with an asymptomatic MoMHRA cohort (Control n=60). For all patients, prosthesis-neck-ratio(PNR) was measured on plain AP pelvic radiographs post-operatively and at follow-up as previously described and validated.

Results: All IP patients (4M:23F) and all (12M:48F) but two controls had a posterior approach at the time of MoMHRA. Post-operatively, there was no difference in the PNR between the two groups (p=0.19). At an average follow up of 3.5 years (range:0.7–8.3), IP patients(mean 1.26, 1.10–1.79) had a significantly higher (p< 0.0001) PNR in comparison to their controls(mean 1.14, 1.03–1.35). Greater neck narrowing occurred in both genders. IP necks had narrowed by an average of 8% (range:3–23). The degree of neck narrowing was correlated with length of survival of implant (p=0.001).

Discussion: This study shows a strong association between IP and neck narrowing. Processes such as impingement and increased wear are considered to be involved in the pathogenesis of both IP and neck narrowing. Furthermore, the presence of an IP, could lead to altered vascularity via a mass effect and further contribute to neck narrowing. Neck narrowing in symptomatic MOMHRA patients should alert surgeons of the possible presence of IP.

Introduction: The assessment of quality in the provision of healthcare is one of the core features of the National Health Service in the 21st Century. From April 2009 Patient Reported Outcome Measure (PROM) data are being collected for the Department of Health for elective hip and knee arthroplasty using generic and disease specific measures of health status. The perceived uses of these data may be for research, assessment of procedural outcome, measures of health inequalities and to aid commissioning groups in selecting their secondary care providers. Foot and ankle surgery covers a wide spectrum of operative procedures with patient responses less predictable than with major joint arthroplasty. We report the use of a sixteen point satisfaction-based questionnaire in order to investigate the nature of patient outcome after the processes of foot and ankle surgery.

Methods: A prospective series of 100 two-part Visual Analogue Scale (VAS) questionnaires was distributed to patients undergoing elective foot and ankle surgery at the Northern General Hospital under the care of four foot and ankle surgeons over a three-month period. The questionnaires were numbered to allow patient anonymity. The first part of nine questions enquired about pre-operative preparation and information and was distributed before surgery. The second part of seven questions, distributed at the first post-operative clinic sought to investigate their hospital and operative experience. Free text comments were requested in addition to the VAS responses, which were expressed as percentages.

Results: 97% of part one and 85% of part two questionnaires were returned completed. 82% had both parts completed and matched. The day case to inpatient ratio was 55: 45. For part one, all clinically related questions scored more than 90% satisfaction, with only two scores for administration-based questions falling below this level. For part two, satisfaction for clinical questions again scored more than 90% and overall, all scored more than 80% satisfaction. Only 23% of pre-operative and 28% of post-operative questionnaires were returned with free-text comments.

Conclusions: A simple patient satisfaction-based questionnaire may be as useful as existing non-validated generic scoring systems used in foot and ankle surgery when assessing quality in the health service, particularly where regional demographics or referral patterns may be important factors influencing patient outcomes. Active dialogue with the surgical colleges and Department of Health should be pursued to avoid inappropriate outcome measures being imposed in foot and ankle surgery.

Metal on metal hip resurfacing (MMHR) is a popular procedure for the treatment of osteoarthritis in young patients. Several centres have observed masses, arising from around these devices, we call these inflammatory pseudotumours. They are locally invasive and may cause massive soft tissue destruction. The aim of this study was to determine the incidence and risk factors for pseudotumours that are serious enough to require revision surgery.

In out unit, 1,419 MMHRs were performed between June 1999 and November 2008. All revisions were identified, including all cases revised for pseudotumour. Pseudotumour diagnosis was made by histological examination of samples from revision. A Kaplan-Meier survival analysis was performed, Cox regression analysis was used to estimate the independent effects of different factors.

The revision rate for pseudotumour increased with time and was 4% (95% CI: 2.2% to 5.8%) at eight years. Female gender was a strong risk factor: at eight years the revision rate for pseudotumours in men was 0.5% (95% CI 0% to 1.1%), in women over 40 it was 6% (95% CI 2.3% to 10.1%) and in women under 40 it was 25% (95% CI 7.3% to 42.9%) (p< 0.001). Other factors associated with an increase in revision rate were, small components (p=0.003) and dysplasia (p=0.019), whereas implant type was not (p=0.156).

We recommend that resurfacings are undertaken with caution in women, especially those younger than 40 years of age, but they remain a good option in men. Further work is required to understand the patho-aetiology of pseudotumours so that this severe complication can be avoided.

Introduction: Pseudotumours (soft-tissue masses relating to the hip joint) following metal-on-metal hip resurfacing arthroplasty (MoMHRA) have been associated with elevated serum and hip aspirate metal ion levels, suggesting that pseudotumours occur when there is increased wear. This study aimed to quantify in vivo wear of implants revised for pseudotumours and a control group of implants revised for other reasons of failure.

Methods: A total of 30 contemporary MoMHRA implants in two groups were investigated in this Institutional Review Board approved study:

8 MoMHRA implants revised due to pseudotumour;

The linear wear of retrieved implants was measured using a Taylor-Hobson Roundness machine. The average linear wear rate was defined as the maximum linear wear depth divided by the duration of the implant in vivo.

Results: In comparison with the non-pseudotumour implant group, the pseudotumour implant group was associated with:

significantly higher median linear wear rate of the femoral component: 8.1um/year (range 2.75–25.4um/year) vs. 1.79um/year (range 0.82–4.15um/year), p=0.002; and

Similarly, differences were also measured in absolute wear values. The median absolute linear wear was significantly higher in the pseudotumour implant group:

21.05um (range 2.74–164.80um) vs. 4.44um (range 1.50–8.80um) for the femoral component, p=0.005; and

Wear on the acetabular cup components in the pseudotumour group always involved the edge, indicating edge-loading of the bearing. In contrast, edge-loading was observed in only one acetabular component in the non-pseudotumour group of implants. The deepest wear was observed well within the bearing surface for the rest of the non-pseudotumour group. The difference in the incidence of edge-loading between the two groups was statistically significant (Fisher’s exact test, p=0.03).

Discussion: Significantly greater linear wear rates of the MoMHRA implants revised due to pseudotumour support the in vivo elevated metal ion concentrations in patients with pseudotumours. This study provides the first direct evidence to confirm that pseudotumour is associated with increased wear at the MoM articulation. Furthermore, edge-loading with the loss of fluid film lubrication may be the dominant wear generation mechanism in patients with pseudotumour.

Introduction: Metal on metal hip resurfacing arthroplasty-induced pseudotumours are a serious complication, which occur in 4% of patients who undergo this procedure. The aim of this study was to measure the 3D in vivo wear on the surface of resurfacing components revised for pseudotumour, compared to a control group.

Method: Thirty-nine hip resurfacing implants were examined; these were sourced from our institutions prosthesis retrieval bank. They were divided into two groups; 22 patients with a clinical and histopathological diagnosis of pseudotumour and 17 controls. Patient demographics and time to revision were known. Three dimensional contactless metrology (Redlux™ Ltd) was used to scan the surface of the femoral and acetabular components, to a resolution of 20 nanometers. The location, depth and area of the wear scar was determined for each component. Volumetric wear was determined, along with the presence of absence of edge-loading. A separate blinded analysis to determine the presence of absence of impingement was performed by one of the authors. ANOVA was used to test for differences in wear and Fishers Exact test was used to compare the incidence of edge-loading between the groups.

Results: The volumetric wear rate for femoral component of the pseudotumour group was 4.7mm3/yr (SD3.5) and 1.7 mm3/yr (SD1.5) for the control group (p=0.03). In the pseudotumour group, the volumetric wear rate of the acetabular component was 3.5 mm3/yr (SD3.6) compared to 0.02 mm3/yr (SD0.07) for the control group (p=0.01). Edge-loading was detected in 74% of acetabular components in the pseudotumour group and 22% of those in the control group (p=0.01). Anterior or posterior edge-loading, consistent with impingement was present on the femoral components of 73% of patients in the pseudotumour group and 22% in the control group (p=0.01).

Discussion: This work demonstrates that implants revised for pseudotumour have significantly higher volumetric wear rates than controls. They also have a significantly higher incidence of edge-loading and impingement than controls. Edge-loading significantly increases wear. We suggest that pseudotumours are caused by high concentrations of metal wear debris, which have been shown to have a toxic effect on osteocytes and macrophages. This is the one of the first studies to demonstrate a clear link between pseudotumours and increased bearing surface wear. It is also the first to demonstrate that edge-loading, due to impingement, occurs in a significant number of patients who develop this condition. Improved implantation techniques and resurfacing designs may help avoid this serious complication of hip resurfacing.

Introduction: The use of second generation highly cross-linked polyethylene (HXLPE) is now commonplace for total hip arthroplasty, however there is no long-term data to support its use. Hip simulator studies suggest that the wear rate of HXLPE is ten times less than conventional polyethylene (UHMWPE). The outcomes of hip simulator studies are not always reproducible in vivo. Long term clinical data is required, as there is emerging clinical data, which suggests that some types of second generation HXLPE may have increased wear after 5 years.

Method: A prospective double blind randomised control trial was conducted using Radiostereometric analysis (RSA). Fifty-four subjects were randomised to receive hip replacements with either UHMWPE liners or HXLPE liners. All subjects received a cemented CPT stem and uncemented Trilogy acetabular component (Zimmer, Warsaw, IN, USA). The 3D penetration of the head into the socket was determined to a minimum of 7 years.

Results: The total liner penetration was significantly different at 7 years (p=0.01) with values of 0.33mm (SD 0.17mm) for the HXLPE group and 0.51mm (SD 0.14mm) for the UHMWPE group. The steady state wear rate from 1 year onwards was significantly lower for HXLPE (0.003 mm/yr, SD 0.04 mm/yr) than for UHMWPE (0.03 mm/yr, SD 0.03 mm/yr) (p=0.01). The direction of wear was in the antero-medial direction in both groups.

Conclusion: We have previously demonstrated that the penetration in the first year is creep-dominated, from one year onwards the majority of penetration is due to wear. The wear rate of this second generation HXLPE approaches that of metal on metal bearings. Second-generation HXLPE may have the potential to reduce the risk of revision surgery, due to wear debris induced osteolysis.

Introduction: Metal-on-metal hip resurfacing arthroplasty (MoMHRA) has gained popularity as an alternative to THR for younger patients with osteoarthritis. A growing concern has been the association of MoMHRA with the development of inflammatory pseudotumours (IP), especially in women. These have been linked to metal-on-metal wear, which can be related to metal ion concentrations. Elevated metal wear debris levels may result from impingement, rim contact and edge loading. Head-neck ratio (HNR) is a predetermining factor for range of movement and impingement. Neck thinning is a recognised phenomenon post-MoMHRA and we have found an association of IP with increased neck thinning based on a case control study. Our aims were to identify HNR changes a hip undergoes when resurfaced and at follow up; and whether greater neck thinning at follow-up could be associated with the presence of elevated metal ions.

Methods: A cohort of 91 patients (57M:34F) with unilateral MoMHRAs were included in this study. Blood tests were obtained at a mean follow up of 3.9 years (range 1.7–7 years) and serum (Co:Cr) ion levels were measured (ICPMS). High metal ion concentrations were defined as Co> 4.1ppb and Cr> 5.2ppb. For all patients, head-neck ratio (HNR) was measured on plain anterio-posterior pelvic radiographs pre-operatively, immediately post-operatively and at follow-up.

Results: Female patients had significantly bigger HNR pre-op (mean=1.35, range:1.22–1.64) compared to males(mean=1.22, range:1.05–1.38) (p< 0.01). Immediately post-op, female HNRs (mean: 1.26, range: 1.14–1.34) were not different to male patients(mean=1.24, range=1.11–1.38) (p=0.11). At follow-up HNR was once again significantly bigger (p< 0.01) in females (mean=1.35, range: 1.21–1.49), compare to males (mean=1.27, range:1.11–1.38). HNR alterations with operation (p=0.00) and at follow-up (p< 0.01) were significantly bigger in female patients. Furthermore, there was a significant correlation between high ion levels and HNR change at follow-up for both Co (p=0.02) and Cr (p< 0.01).

Conclusion: This study identified gender-specific changes in HNR that resurfaced hips undergo, not previously documented. Female hips have greater HNR pre-operatively, compared to male hips, and appear to be biomechanically disadvantaged when resurfaced. A decrease in HNR with resurfacing could result in impingement and lead to processes, known to be more prevalent in females, such as neck thinning, increased wear and IP development. In addition, we highlight a correlation between high ion levels and greater neck thinning at follow-up. Increased neck thinning in symptomatic MoMHRA hips could be secondary to increased wear and should be investigated further radiologically for the presence of IP.

From 2004–2006, in an attempt to reduce the waiting time for patients listed for total knee and total hip arthroplasty at Cardiff and Vale NHS Trust, 156 total hip replacements (THRs) were performed by Swedish Orthopaedic surgeons at an NHS treatment centre in England.

All patients were contacted and invited to a review appointment with a Consultant specialising in hip and revision hip replacement. Oxford Hip Scores and clinical and radiographic evaluation were performed. Patients who declined an appointment were sent a postal questionnaire. Radiographs were analysed for component position, radiolucent lines, medial floor breach, leg length discrepancy.

One hundred and thirteen hips were reviewed at a mean 23 month follow-up. The mean Oxford score was 26. Mean age at surgery was 69. Cemented THR was performed in 104 hips; hybrid in 7; cementless in 2. The Exeter stem and Cenator cemented cup were used in the majority of cases. 16% had acetabular inclination greater than 55 degrees. Radiolucent lines around the cup were seen in 76/113 hips. Femoral stem position was greater than 4 degrees varus in 47/113. Medial floor breach seen in 13/113. 10/113 had leg length discrepancy > 1cm. There were 3 dislocations, 1 femoral fracture, 1 pulmonary embolus, 3 deep infections, 2 superficial infections.

Revision surgery has been performed in 18/113 – the majority for a painful loose acetabular component. A further 5/113 have been recommended for surgery. The further surgery rate was 12% at 2 year follow-up.

The revision rate far exceeds the 0.5% 5-year failure rate reported in the Swedish Registry for the components used. This initiative has left a legacy of unhappy patients, and increased the workload required in our unit to correct the problems. The lack of long-term ownership of patients may be an important factor.