Methodology

Porcine NC cells were incorporated into three injectable hydrogels: NPgel (a L-pNIPAM-co-DMAc hydrogel), NPgel with decellularized NC-matrix powder (dNCM) and Albugel (an albumin/ hyaluronan hydrogel). The NCs and biomaterials constructs were cultured for up to four weeks under 5% oxygen (n=3 biological repeats). Histological, immunohistochemical and glycosaminoglycans (GAG) analysis were performed to investigate NC viability, phenotype and extracellular matrix synthesis and deposition.

Methodology

Bovine and Human Nucleus pulpous tissue explants were injected with Bgel with and without MSCs. Tissue samples were cultured under hypoxia (5%) in standard culture media for 4 weeks. Cell viability, histological assessment of matrix deposition, calcium formation, and cell phenotype analysis using immunohistochemistry for NP matrix and bone markers.

Methodology

Cadaveric human discs were used to calculate disc height and to determine Youngs Modulus during simulated walking pre and post injection of NPgel, extrusion testing performed. Whole human IVDs were injected with NPgel +/− human BMPCs and maintained in culture under physiological loading regime for 4 weeks. Pre and post culture MRI imaging and in line biomechanical characteristics determined. Histology and immunochemistry performed for anabolic and catabolic factors.

Methods and Results

We have been working to develop a new thermoresponsive injectable biomaterial hydrogel (NPgel) for the treatment of intervertebral disc (IVD) disease. A large part of the IMPD requires information on how the hydrogel physical properties change over time in bodily conditions. We have been studying 6 batches of NPgel over 18 months, tracking the materials wet/ dry weight, structure and composition. To date we have found that NPgel in liquids more similar to the body (with protein and salts) appear to be stable and safe, whilst those in distilled water swell and disintegrate over time. Subtle long-term changes to the material composition were found and we are currently investigating its ramifications.

Methods

IVD tissue obtained from patients undergoing discectomy, or cadaveric samples, were cultured within a novel explant device. The hydrogel was injected, with and without mesenchymal stem cells (MSCs), and cultured under hypoxia, to mimic the degenerate IVD environment, for 4 weeks. Explants were embedded to wax and native cellular migration into the hydrogel was investigated, together with cellular phenotype and matrix deposition.

Methods and Results

We present an in vitro study looking at the effect of our Bgel hydrogel on mesenchymal stem cells (MSCs) and their bone forming capacity within lumbar cages: devices used to space the bones apart in the fusion operation, as a mechanism to improve fixation and intra cage bone formation. MSCs were isolated from human hip joint, expanded, seeded within Bgel, cast into well inserts or lumbar cages and cultured for 4 weeks. Using 3D X-ray imaging micro computed tomography (μCT) scans we show that the MSC in the presence Bgel begin to mineralise within the lumbar cages. Histology is currently ongoing and will be presented at the meeting.

Methods and Results

Human fat pad and bone marrow derived MSCs were isolated from femoral heads of patients undergoing hip replacement surgery for osteoarthritis with informed consent. MSCs were encapsulated into either NPgel or Bgel and cultured for up to 6 weeks in 5% (NPgel) or 21% (Bgel) O₂. Histology and immunohistochemistry was utilized to determine phenotype. Both fat and bone marrow derived MSCs, were able to differentiate into both cell lineages. NPgel culture conditions increased expression of matrix components such as collagen II and aggrecan and NP phenotypic markers FOXF1 and PAX1, whereas Bgel induced expression of collagen I and osteopontin, indicative of osteogenic differentiation.

Methods and Results

We present an injectable range of hydrogel biomaterials made from water, clay and polymer that set at 37°C. The materials were made at 80°C polymerised in water and stored at 70°C to remain liquid. The physical properties of the materials were assessed using various methods, including mechanical assessment using temperature-controlled rheometry to monitor the liquid-hydrogel transition.

Methods and Results

In seven goats, one disc was injected with chondroitinase ABC (mild degeneration) and after three months compared to control. Ex vivo, 50 caprine discs received physiological loading (50–150N) or overloading (50–400N) in a loaded disc culture system. To determine whether ECM degeneration is due to cell activity, half of the discs was subjected to freeze-thaw cycles. Spectroscopic images were collected at 1000–1300 cm⁻¹ and analyzed using multivariate curve resolution analysis.

In vivo, less proteoglycan was found in the degenerated group (p<0.05), especially in the nucleus. Collagen content was increased in the nucleus and anterior annulus, and had higher entropy (p<0.01), indicating matrix disorganization. In the ex vivo experiment, the proteoglycan/collagen ratio was decreased (p<0.05) in the vital group and there was an increase in collagen entropy (p<0.05). A significant interaction between loading and vitality was found in the amount of collagen (p<0.05), but not in the entropy.

Methods and Results

Goat discs were excised and cultured in a bioreactor under diurnal, simulated-physiological loading (SPL) conditions, following 3 days pre load, IVDs were degenerated enzymatically for 2hrs and subsequently loaded for 10 days under physiological loading. A PBS injected group was used as controls. Disc deformation was continuously monitored and changes in disc height recovery quantified using stretched-exponential fitting. Histological staining was performed on caprine discs to assess extracellular matrix production and immunohistochemistry performed to determine expression of catabolic protein expression.

The injection of collagenase and cABC induced mechanical behavior akin to that seen in human degeneration. A decrease in collagens and glycosaminoglycans (GAGs) was seen in enzyme injected discs, which was accompanied by increased cellular expression for degradative enzymes and catabolic cytokines.

Methods and Results

MSCs were cultured in NP gel under 5% O₂ in either: standard culture (DMEM, pH7.4); healthy disc (DMEM, pH7.1); degenerate disc (low glucose DMEM, pH6) or degenerate disc plus IL-1β. Following 4 weeks histological staining and immunohistochemical analysis investigated viability, ECM synthesis and matrix degrading enzyme expression.

Here we have shown that viability and NP cell differentiation of MSCs incorporated within NPgel was mostly unaffected by treatment with conditions such as low glucose, low pH and the presence of cytokines, all regarded as key contributors to disc degeneration. In addition, the NPgel was shown to prevent MSCs from displaying a catabolic phenotype with low expression of degradative enzymes, highlighting the potential of NPgel to differentiate hMSCs and protect them from the degenerate disc microenvironment.

Methods and Results

The NPgel integrated with bovine and human degenerate Nucleus Pulposus (NP) tissue and hMSCs produced matrix components: aggrecan, collagen type II and chondroitin sulphate in standard and degenerate culture conditions. Significantly increased cellular immunopositivty for aggrecan was observed within native NP cells surrounding the site where NPgel+MSCs were injected (P≤0.05). In NP explants a significant decrease in catabolic factors were observed where NPgel+MSCs was injected in comparison to controls.

Methods & Results

The effect of hydrogel wt./wt., clay and co-monomer percentages were assessed using a box-Behnken design. Rheometry, SEM, FTIR and swelling was used to measure changes in material properties in simulated physiological conditions. Rheometry revealed gelation temperature of hydrogel materials could be modified with dimethyl-acrylamide co-monomer; however, final maximum mechanical properties remained unaffected. Increasing the weight % and clay % increased resultant mechanical properties from ∼500–2500 G' (Pa), increased viscosity, but retained the ability to flow through a 26G needle at 39°C.

Methods

hMSCs were incorporated within liquid NPgel and injected into bovine NP explants alongside controls. Explants were cultured for 6 weeks under hypoxia (5%) with ± calcium 5.0mM CaCl₂ or IL-1β individually or in combination to mimic the degenerate microenvironment. Cell viability was assessed by caspase 3 immunohistochemistry. Histological and immunohistochemical analysis was performed to investigate altered matrix synthesis and matrix degrading enzyme expression.

Methods

Rat sub-cut analysis was performed to investigate safety in vivo. A rat femur defect model was performed to evaluate efficacy. Four groups were investigated: sham operated controls; acellular L-pNIPAM-co-DMAc hydrogel; acellular L-pNIPAM-co-DMAc hydrogel with HAPna; L-pNIPAM-co-DMAc hydrogel with rat MSCs and HAPna. Following 4 weeks, defect site and organs were histologically examined to determine integration, repair and inflammatory response, as well as Micro-CT to assess mineralisation.

Methods

hMSCs were encapsulated in NPgel and cultured for 4 weeks under hypoxia (5%) with ± calcium (2.5mM and 5.0mM CaCl₂), IL-1β and TNFα either individually or in combination to mimic the degenerate microenvironment. Cell viability was assessed by Alamar blue assay. Histological and immunohistochemical analysis investigated altered matrix and matrix degrading enzyme expression.

Methods

hMSCs were injected either alone or within NPgel, into bovine NP tissue explants and maintained at 5% O₂ for up to 6wks. Media alone and acellular NPgel were also injected into NP explants to serve as controls. Cell viability was assessed by Caspase 3 immunohistochemistry and the phenotype of injected hMSC was assessed by histology and immunohistochemistry. Mechanical properties were also assessed via dynamic mechanical analysis (DMA).