The rate and mode of early failure in 463 Birmingham hip resurfacings in a two-centre, multisurgeon series were examined. Of the 463 patients two have died and three were lost to follow-up. The mean radiological and clinical follow-up was for 43 months (6 to 90). We have revised 13 resurfacings (2.8%) including seven for pain, three for fracture, two for dislocation and another for sepsis. Of these, nine had macroscopic and histological evidence of metallosis. The survival at five years was 95.8% (95% confidence interval (CI) 94.1 to 96.8) for revision for all causes and 96.9% (95% CI 95.5 to 98.3) for metallosis. The rate of metallosis related revision was 3.1% at five years. Risk factors for metallosis were female gender, a small femoral component, a high abduction angle and obesity. We do not advocate the use of the Birmingham Hip resurfacing procedure in patients with these risk factors

Aims. The purpose of this study was to directly compare the Modular Dual Mobility (MDM) Mobile Bearing Hip System (Stryker, USA) and large femoral heads (LFHs) in revision total hip arthroplasties (THAs) at mid-term follow-up, with specific emphasis on survival free of re-revision for dislocation, any re-revision, dislocation, and the risk of metal-related complications. Methods. We identified 299 revision THAs performed at a single tertiary care academic institution from March 2011 to July 2014. Aseptic loosening of the acetabular component (n = 65), dislocation (n = 58), and reimplantation as part of a two-stage exchange protocol (n = 57) were the most common reasons for index revision. MDM constructs were used in 123 cases, and LFHs were used in 176 cases. Mean age was 66 years (28 to 93), mean BMI was 31 kg/m. 2. (18 to 55), and 45% (n = 136) were female. Mean follow-up was seven years (2 to 12). Results. The ten-year survival free of re-revision for dislocation was 99% (95% CI 95 to 100) in the MDM cohort and 91% (95% CI 84 to 96) in the LFH cohort, with a significantly increased risk of re-revision for dislocation in the LFH cohort (HR 7.1 (95% CI 1.3 to 40.8); p = 0.023). The ten-year survival free of any re-revision was 92% (95% CI 82 to 99%) in the MDM cohort and 84% (95% CI 74 to 90) in the LFH cohort with a significantly increased risk of any re-revision in the LFH cohort (HR 2.6 (95% CI 1.1 to 5.9); p = 0.024). The ten-year survival free of any dislocation was 95% (95% CI 85 to 99) in the MDM cohort and 87% (95% CI 78 to 92) in the LFH cohort with a significantly increased risk of any dislocation in the LFH cohort (HR 2.7 (95% CI 1.1 to 6.3); p = 0.028). There were no re-revisions or reoperations for metallosis or corrosion in the MDM cohort. Conclusion. In this head-to-head comparison, revision THAs with a MDM construct safely and effectively lowered the risk of re-revision for dislocation, any re-revision, and any dislocation compared to LFH at mid-term follow-up. There were no re-revisions or reoperations for metallosis or corrosion in the MDM cohort. Cite this article: Bone Joint J 2025;107-B(1):58–64

We describe three prostheses with cemented titanium-alloy stems and Al. 2. O. 3. ceramic femoral heads which had to be revised after a mean period of implantation of 78 months. In each case, the neck of the prosthesis had been so severely worn that the profile was elliptical rather than circular. There was severe metallosis of the periprosthetic tissues. Metal particles isolated from the tissues were approximately one nanometre in size and the ratios of titanium, aluminium and vanadium in the particles were the same as in the original alloy. Histologically, the high concentration of metal particles masked the presence of high-density polyethylene (HDP) debris, but again particles about one nanometre in size were isolated from the tissues. The severe necrobiosis and necrosis noted were consistent with other reports of the presence of extensive wear particles in periprosthetic tissues. Wear is presumed to have occurred as a result of mismatch between the shape or size of the taper cone and the femoral head, or to changes in the geometry of loading due to migration of the cup. To facilitate early intervention, patients with this design of prosthesis should be monitored radiologically

Previous reports on the outcomes of isolated head and liner exchange in revision total hip arthroplasty have found high rates of instability following these surgeries. Most reports have studied constructs using ≤28mm femoral heads. The purpose of this study was to determine if modern techniques with the use of larger head sizes can improve the rate of instability after head and liner exchange. We identified 138 hips in 132 patients who underwent isolated head and liner exchange for polyethylene wear/osteolysis (57%), acute infection (27%), metallosis (13%), or other (2%). All patients underwent revision with either 32mm (23%), 36mm (62%), or 40mm (15%) diameter heads. Crosslinked polyethylene was used in all revisions. Lipped and/or offset liners were used in 104 (75%) hips. Average follow up was 3.5 (1.0–9.1) years. Statistical analyses were performed with significance set at p<0.05. Revision-free survivorship for any cause was 94.6% and for aseptic causes was 98.2% at 5 years. 11 (8%) hips experienced a complication with 7 (5%) hips requiring additional revision surgery. Following revision, 4 (3%) hips experienced dislocation, 5 (4%) hips experienced infection, and 1 (1%) hip was revised for trunnionosis. No demographic or surgical factors significantly affected outcomes. Our study shows that isolated head and liner exchange using large femoral heads and modern liners provides for better stability than previous reports. The most common complication was infection. We did not identify specific patient, surgical or implant factors that reduced the risk of instability or other complication

Mechanical irritation or impingement of the iliopsoas tendon accounts for 2–6% of persistent postoperative pain cases after total hip arthroplasty (THA). The most common trigger is anterior cup overhang. CT-scan can be used to identify and measure this overhang; however, no threshold exists for symptomatic anterior iliopsoas impingement. We conducted a case–control study in which CT-scan was used to define a threshold that differentiates patients with iliopsoas impingement from asymptomatic patients after THA. We analyzed the CT-scans of 622 patients (758 CT-scans) between 2011 and 2020. Out of this population we identified 136 patients with symptoms suggestive of iliopsoas impingement. Among them, 6 were subsequently excluded: three because the diagnosis was reestablished intra-operatively (one metallosis, two anterior instability related to posterior prosthetic impingement) and three because they had another obvious cause of impingement (one protruding screw, one protruding cement plug, one stem collar), leaving 130 patients in the study (impingement) group. They were matched to a control group of 138 patients who were asymptomatic after THA. The anterior cup overhang (anterior margin of cup not covered by anterior wall) was measured by an observer (without knowledge of the clinical status) on an axial CT slice based on anatomical landmarks (orthogonal to pelvic axis). The impingement group had a median overhang of 8 mm [IQR: 5 to 11] versus 0 mm [IQR: 0 to 4] for the control group (p<.001). Using ROC curves, an overhang threshold of 4 mm was best correlated with a diagnosis of impingement (sensitivity 79%, specificity 85%, PPV = 75%, NPV = 85%). Pain after THA related to iliopsoas impingement can be reasonably linked to acetabular overhang if it exceeds 4 mm on a CT scan. Below this threshold, it seems logical to look for another cause of iliopsoas irritation or another reason for the pain after THA before concluding impingement is present

Ceramic-on-ceramic (CoC) articulations in total hip arthroplasty (THA) have low wear, but the unique risk of fracture. After revision for CoC fracture, ceramic third bodies can lead to runaway wear of cobalt chrome (CoCr) causing extremely elevated blood cobalt. We present five cases of ceramic liner fractures revised to a CoCr head associated with the rapid development of severe cobalt toxicity. We identified 5 cases of fractured CoC THA treated with revision to CoCr on highly cross-linked polyethylene (HXLPE) – three to conventional bearings and two to modular dual mobility bearings (CoCr acetabular liner, CoCr femoral head, and HXLPE). Mean follow up was 2.5 years after CoCr/HXLPE re-revision. Symptoms of cobalt toxicity occurred at average 9.5 months after revision for ceramic fracture (range 6–12). All patients developed vision and hearing loss, balance difficulties, and peripheral neuropathy. Several had cardiomyopathy, endocrinopathy, and local skin discoloration. Two reported hip pain. Re-revision for cobalt toxicity occurred at an average of 22 months (range 10–36) after revision for ceramic fracture. Average serum cobalt level at re-revision was 991 μg/L (range 734–1302, normal <1 μg/L). All CoCr heads exhibited massive wear with asphericity; deep tissues exhibited prominent metallosis. Treatment consisted of debridement and revision to a ceramic head with HXLPE. Serum cobalt improved to an average of 25 μg/L at final follow up. All patients reported partial improvement in vision and hearing; peripheral neuropathy and balance did not recover. Systemic cobalt toxicity is a rare but devastating complication of ceramic fracture in THA treated with cobalt-alloy bearings. Cobalt alloy bearings should be avoided in this setting. The diagnosis of systemic cobalt toxicity requires a high index of suspicion and was typically delayed following systemic symptoms. Debridement and revision to a ceramic-on-HXLPE leads to improvement but not resolution of cobalt toxicity complications

Pre-operative definitive diagnosis of infection in painful total hip arthroplasty (THA) is not always easy to be established, making the intra-operative decision-making process crucial in management of revision hip surgery. Calprotectin is a promising point-of-care novel biomarker that has displayed high accuracy in detecting PJIs. From November 2020 to December 2022, 105 patients with painful primary THA were treated with revision THA in 3 orthopaedic departments. Pre-operatively, 23 were considered infected and treated with two-stage revision THA. The remaining 82 were likely infected according to the 2019 EBJIS criteria. The suspicion of low-grade infection was based on clinical (rest and/or night pain), laboratory (CRP, ESR, WBC – normal or slightly elevated) and radiological evaluation (loosening). Hip aspiration under CT imaging was performed in these cases and 34 of them yielded positive culture and were treated with two-stage revision. Aspiration was ineffective in the remaining 48 cases (33 negative, 15 unsuccessful attempts). Intra-operatively, calprotectin was measured with lateral flow immunoassay test in these patients. Cases with calprotectin levels ≥ 50 mg/L were treated with 2-stage revision THA; otherwise, they were considered not-infected and one-stage revision was performed. Synovial fluid and tissue samples were collected for analysis. Implants were sent for sonication fluid cultures. Calprotectin was positive (≥ 50 mg/L) in 27 cases and negative in 21 cases. There was 1 false negative case with positive tissue cultures. Out of the 27 positive cases, 25 had positive tissue cultures and sonication. However, 2 cases with high calprotectin levels (>200 mg/L) were not infected. The false positive result was attributed to severe metallosis. Calprotectin sensitivity was 96.2%, specificity 90.9%, PPV 92.6%, NPV 95.2%, AUC 0.935. The results of this ongoing study indicate that calprotectin seems to be a valuable tool in facilitating the intra-operative decision-making process in cases that low-grade infection is suspected and diagnosis cannot be established pre-operatively

Despite the increasing interest and subsequent published literature on hip resurfacing arthroplasty, little is known about the prevalence of its complications and in particular the less common modes of failure. The aim of this study was to identify the prevalence of failure of hip resurfacing arthroplasty and to analyse the reasons for it. From a multi-surgeon series (141 surgeons) of 5000 Birmingham hip resurfacings we have analysed the modes, prevalence, gender differences and times to failure of any hip requiring revision. To date 182 hips have been revised (3.6%). The most common cause for revision was a fracture of the neck of the femur (54 hips, prevalence 1.1%), followed by loosening of the acetabular component (32 hips, 0.6%), collapse of the femoral head/avascular necrosis (30 hips, 0.6%), loosening of the femoral component (19 hips, 0.4%), infection (17 hips, 0.3%), pain with aseptic lymphocytic vascular and associated lesions (ALVAL)/metallosis (15 hips, 0.3%), loosening of both components (five hips, 0.1%), dislocation (five hips, 0.1%) and malposition of the acetabular component (three hips, 0.1%). In two cases the cause of failure was unknown. Comparing men with women, we found the prevalence of revision to be significantly higher in women (women = 5.7%; men = 2.6%, p < 0.001). When analysing the individual modes of failure women had significantly more revisions for loosening of the acetabular component, dislocation, infection and pain/ALVAL/metallosis (p < 0.001, p = 0.004, p = 0.008, p = 0.01 respectively). The mean time to failure was 2.9 years (0.003 to 11.0) for all causes, with revision for fracture of the neck of the femur occurring earlier than other causes (mean 1.5 years, 0.02 to 11.0). There was a significantly shorter time to failure in men (mean 2.1 years, 0.4 to 8.7) compared with women (mean 3.6 years, 0.003 to 11.0) (p < 0.001)

Hip resurfacing has been proposed as an alternative to traditional total hip arthroplasty in young, active patients. Much has been learned following the introduction of metal-on-metal resurfacing devices in the 1990s. The triad of a well-designed device, implanted accurately, in the correct patient has never been more critical than with these implants. . Following Food and Drug Administration approval in 2006, we studied the safety and effectiveness of one hip resurfacing device (Birmingham Hip Resurfacing) at our hospital in a large, single-surgeon series. We report our early to mid–term results in 1333 cases followed for a mean of 4.3 years (2 to 5.7) using a prospective, observational registry. The mean patient age was 53.1 years (12 to 84); 70% were male and 91% had osteoarthritis. Complications were few, including no dislocations, no femoral component loosening, two femoral neck fractures (0.15%), one socket loosening (0.08%), three deep infections (0.23%), and three cases of metallosis (0.23%). There were no destructive pseudotumours. Overall survivorship at up to 5.7 years was 99.2%. Aseptic survivorship in males under the age of 50 was 100%. We believe this is the largest United States series of a single surgeon using a single resurfacing system. Cite this article: Bone Joint J 2016;98-B (1 Suppl A):10–13

Surface hip replacement (SHR) is generally used in younger, active patients as an alternative conventional total hip replacement in part because of the ability to preserve femoral bone. This major benefit of surface replacement will only hold true if revision procedures of SHRs are found to provide good clinical results. A retrospective review of SHR revisions between 2007 and 2012 was presented, and the type of revision and aetiologies were recorded. There were 55 SHR revisions, of which 27 were in women. At a mean follow-up of 2.3 years (0.72 to 6.4), the mean post-operative Harris hip score (HHS) was 94.8 (66 to 100). Overall 23 were revised for mechanical reasons, nine for impingement, 13 for metallosis, nine for unexplained pain and one for sepsis. Of the type of revision surgery performed, 14 were femoral-only revisions; four were acetabular-only revisions, and 37 were complete revisions. We did not find that clinical scores were significantly different between gender or different types of revisions. However, the mean post-operative HHS was significantly lower in patients revised for unexplained pain compared with patients revised for mechanical reasons (86.9 (66 to 100) versus 99 (96 to 100); p = 0.029). There were two re-revisions for infection in the entire cohort. Based on the overall clinical results, we believe that revision of SHR can have good or excellent results and warrants a continued use of the procedure in selected patients. Close monitoring of these patients facilitates early intervention, as we believe that tissue damage may be related to the duration of an ongoing problem. There should be a low threshold to revise a surface replacement if there is component malposition, rising metal ion levels, or evidence of soft-tissue abnormalities. Cite this article: Bone Joint J 2013;95-B, Supple A:88–91

We have reviewed 42 patients who had revision of metal-on-metal resurfacing procedures, mostly because of problems with the acetabular component. The revisions were carried out a mean of 26.2 months (1 to 76) after the initial operation and most of the patients (30) were female. Malpositioning of the acetabular component resulted in 27 revisions, mostly because of excessive abduction (mean 69.9°; 56° to 98°) or insufficient or excessive anteversion. Seven patients had more than one reason for revision. The mean increase in the diameter of the component was 1.8 mm (0 to 4) when exchange was needed. Malpositioning of the components was associated with metallosis and a high level of serum ions. The results of revision of the femoral component to a component with a modular head were excellent, but four patients had dislocation after revision and four required a further revision

Introduction. MDM implants can enhance stability in total hip replacement (THR), but complications include malseated liners and corrosion between the cobalt-chrome liner and titanium acetabular shell increased systemic metal ion levels. The liner-shell junction has the potential for fretting corrosion, and the corrosion could be exacerbated in malseated liners. We determined the potential for fretting corrosion in malseated versus well-seated liners using a mechanical electrochemical corrosion chamber. Methods. Four pristine MDM liners and shells were tested. Two liners were well-seated into their shells; two were canted at 6°. The liner-shell couples were assembled with a 2kN force after wetting the surfaces to promote a crevice environment conducive to corrosion. Couples were fixed in an electrochemical chamber at 40° inclination/20° anteversion to the load axis. The chamber was filled with phosphate buffered saline and setup as a three-electrode configuration: the shell as the working, a saturated calomel electrode as the reference, and a carbon rod as the counter electrode. A potentiostat held the system at −50mV throughout testing. After equilibration, couples underwent cyclic loading of increasing magnitudes from 100 to 3400N at 3 Hz. Fretting current was measured throughout, and the onset load for fretting was determined from the increase in average current. Results. Well-seated liners showed lower fretting current values at all peak compressive loads greater than 800 N (p<0.05). Canted liners demonstrated a fretting onset load of 2400 N, and fretting currents at greater than 2400 N were larger than those at lower peak compressive loads (p<0.05). Conclusion. The clinical consequences of MDM liner malseating remain unknown, but our results demonstrate earlier fretting current onset at lower peak loads when compared to well-seated liners. The onset loads were consistent with physiologic loads for daily activities. Our findings are significant given the potential for metallosis and adverse local tissue reactions. For any tables or figures, please contact the authors directly

Aims

The aims of this study were to determine if an increasing serum cobalt (Co) and/or chromium (Cr) concentration is correlated with a decreasing Harris Hip Score (HHS) and Hip disability and Osteoarthritis Outcome Score (HOOS) in patients who received the Articular Surface Replacement (ASR) hip resurfacing arthroplasty (HRA), and to evaluate the ten-year revision rate and show if sex, inclination angle, and Co level influenced the revision rate.

Aims

The aims of the study were to report for a cohort aged younger than 40 years: 1) indications for HRA; 2) patient-reported outcomes in terms of the modified Harris Hip Score (HHS); 3) dislocation rate; and 4) revision rate.

Aims

The Birmingham Hip Resurfacing (BHR) was introduced in 1997 to address the needs of young active patients using a historically proven large-diameter metal-on-metal (MoM) bearing. A single designer surgeon’s consecutive series of 130 patients (144 hips) was previously reported at five and ten years, reporting three and ten failures, respectively. The aim of this study was to extend the follow-up of this original cohort at 25 years.

Aims

The prevalence of obesity is increasing substantially around the world. Elevated BMI increases the risk of complications following total hip arthroplasty (THA). We sought to evaluate trends in BMI and complication rates of obese patients undergoing primary THA over the last 30 years.

Aims

This study aims to assess the relationship between history of pseudotumour formation secondary to metal-on-metal (MoM) implants and periprosthetic joint infection (PJI) rate, as well as establish ESR and CRP thresholds that are suggestive of infection in these patients. We hypothesized that patients with a pseudotumour were at increased risk of infection.

Aims

Our objective was describing an algorithm to identify and prevent vascular injury in patients with intrapelvic components.

Aims

The aim of this study was to evaluate the incidence of liner malseating in two commonly used dual-mobility (DM) designs. Secondary aims included determining the risk of dislocation, survival, and clinical outcomes.

Serum and blood cobalt (Co) and chromium (Cr) ion levels are used to monitor patients at risk for adverse reaction to metal debris (ARMD) following metal-on-metal (MoM) total hip arthroplasty (THA). However, these levels often do not correlate with the degree of local soft-tissue reaction and damage observed at the time of revision. The purpose of this study was to analyze synovial fluid metal ion concentrations in patients with a failed THA in the setting of an ARMD and determine if these levels can be more predictive of soft-tissue destruction than serum or whole blood levels. Synovial, blood and serum samples were prospectively collected from patients undergoing revision THA with ARMD (n=29) and those undergoing aseptic revision without ARMD (n=29). There was no difference in mean age (P=0.50), BMI (P=0.18), sex distribution (P=0.18), serum creatinine (P=0.74), or time to revision THA (P=0.13) between the cohorts. In the AMRD cohort, the components included MoM THA (n=18), hip resurfacing (n=5), dual-modular taper THA (n=4) and MoM and dual-modular taper THA (n=2). At the time of revision THA, 26 (90%) patients in the metal reaction cohort had gross evidence of metallosis in the soft-tissues, the remaining 3 (10%) had evidence of corrosion of the dual taper neck or MoM bearing. In the non ARMD cohort the bearing surfaces included metal-on-polyethylene (n=19) and ceramic-on-polyethylene (n=10). The indications for revision included isolated acetabular loosening (n=11), isolated femoral component loosening (n=11), polyethylene wear (n=5), recurrent dislocation (n=1) and combined femoral and acetabular component loosening (n=1). None had a clinical diagnosis or gross evidence of taper corrosion. Pre-revision, 21 (72%) patients in the metal reaction group had periarticular fluid collections or a mass on MRI. Mean cyst size was 202.9±71.6 cm3 and masses were grouped into Type I (cyst wall <3 mm, n=10), Type II (cyst wall ≥3 mm, n=8) and Type III (mainly solid, n=3). At the time of revision THA, the mean Co levels were elevated in patients with ARMD compared to those without in synovial fluid (1,833 ppb vs. 12.3 ppb, P=0.008), whole blood (22.6 ppb vs 0.5 ppb, P=0.005)) and serum (19.6 vs. 0.6, P=0.001). Likewise, mean Cr levels were significantly elevated in patients with an ARMD compared to those undergoing revision without in synovial fluid (3,128 ppb vs. 10.3 ppb, P=0.01), whole blood (8.9 ppb vs. 0.5 ppb, P=0.009) and serum (14.1 ppb vs. 0.5 ppb, P=0.005). The synovial fluid Co levels were the most accurate test for detecting pseudotumor (AUC 0.951) and adverse local tissue reaction (AUC 0.826). At a synovial fluid Cr level of 110 ppb, the synovial fluid metal ion analysis was 94% sensitive and 86% specific for pseudotumor formation. In this prospective study, synovial fluid analysis of metal ion levels was more accurate in predicting the presence and extent of pseudo-tumor or ALTR compared to blood or serum analysis. The addition of synovial aspiration with metal ion analysis may provide another helpful data point when risk stratifying these patients for need for revision THA