Background

Children suffering from primary bone cancer necessitating resection of growth plates, may suffer progressive leg length discrepancy, which can be attenuated with extendable prostheses. A serious complication is catastrophic implant failure. Over time, bone will remodel, altering the stress pattern in the implant. By using finite element analysis we can model different bone remodeling conditions to ascertain the effect that this will have on stress distribution and magnitude.

A finite element analysis was performed. Simplified computer generated models were designed of a cemented femoral Stanmore growing massive endoprosthesis. Three scenarios were designed, modelled on post-operative radiographs. Scenario 1 had a gap between the end of the femur and the implant collar, scenario 2 had no gap, but with no bone attachment into the collar, and scenario 3 had growth of the bone over the length of the collar with attachment. Physiological loading conditions were applied. The resultant stress in the implant for each scenario was measured, and compared to the strength of the material. Peak stresses were recorded at the stem-collar junction.

The maximum stress recorded in the implant in scenario 1 was 3104.2Mpa, compared to 1054.4Mpa in scenario 2, and 321.2Mpa in scenario 3.

A complete cement mantle is important for the longevity of a total hip replacement. In the minimally-invasive direct anterior approach used at the Innsbruck University hospital, the femoral component has to be inserted into the femoral canal by an angulated movement. In a cadaver study, the quality and the extent of the cement mantle surrounding 13 Exeter femoral components implanted straight through a standard anterolateral transgluteal approach were compared with those of 13 similar femoral components implanted in an angulated fashion through a direct anterior approach. A third-generation cementing technique was used. The inner and outer contours of the cement mantles was traced from CT scans and the thickness and cross-sectional area determined. In no case was the cement mantle incomplete. The total mean thickness of the cement mantle was 3.62 mm (95% confidence interval 3.59 to 3.65). The mean thickness in the group using the minimally-invasive approach was 0.16 mm less than that in the anterolateral group. The distribution of the thickness was similar in the two groups. The mean thickness was less on the anteromedial and anterolateral aspect than on the posterior aspect of the femur. There is no evidence that the angulated introduction of Exeter femoral components in the direct anterior approach in cadavers compromises the quality, extent or thickness of the cement mantle

Trochlear geometry of modern femoral implants is designed for mechanical alignment (MA) technique for TKA. The biomechanical goal is to create a proximalised and more valgus trochlea to better capture the patella and optimize tracking. In contrast, Kinematic alignment (KA) technique for TKA respects the integrity of the soft tissue envelope and therefore aims to restore native articular surfaces, either femoro-tibial or femoro-patellar. Consequently, it is possible that current implant designs are not suitable for restoring patient specific trochlea anatomy when they are implanted using the kinematic technique, this could cause patellar complications, either anterior knee pain, instability or accelerated wear or loosening. The aim of our study is therefore to explore the extent to which native trochlear geometry is restored when the Persona. ®. implant (Zimmer, Warsaw, USA) is kinematically aligned. A retrospective study of a cohort of 15 patients with KA-TKA was performed with the Persona. ®. prosthesis (Zimmer, Warsaw, USA). Preoperative knee MRIs and postoperative knee CTs were segmented to create 3D femoral models. MRI and CT segmentation used Materialise Mimics and Acrobot Modeller software, respectively. Persona. ®. implants were laser scanned to generate 3D implant models. Those implant models have been overlaid on the 3D femoral implant model (generated via segmentation of postoperative CTs) to replicate, in silico, the alignment of the implant on the post-operative bone and to reproduce in the computer models the features of the implant lost due to CT metal artefacts. 3D models generated from post-operative CT and pre-operative MRI were registered to the same coordinate geometry. A custom written planner was used to align the implant, as located on the CT, onto the pre-operative MRI based model. In house software enabled a comparison of trochlea parameters between the native trochlea and the performed prosthetic trochlea. Parameters assessed included 3D trochlear axis and anteroposterior offset from medial facet, central groove, and lateral facet. Sulcus angle at 30% and 40% flexion was also measured. Inter and intra observer measurement variabilities have been assessed. Varus-valgus rotation between the native and prosthetic trochleae was significantly different (p<0.001), with the prosthetic trochlear groove being on average 7.9 degrees more valgus. Medial and lateral facets and trochlear groove were significantly understuffed (3 to 6mm) postoperatively in the proximal two thirds of the trochlear, with greatest understuffing for the lateral facet (p<0.05). The mean medio-lateral translation and internal-external rotation of the groove and the sulcus angle showed no statistical differences, pre and postoperatively. Kinematic alignment of Persona. ®. implants poorly restores native trochlear geometry. Its clinical impact remains to be defined

Introduction. Despite decades of clinical research in artificial joints and underlying failure mechanisms, systematical and reproducible identification of reasons for complications in total knee replacements (TKR) remains difficult. Due to the complex dynamic interaction of implant system and biological situs, malfunction eventually leading to failure is multifactorial and remains not fully understood. The aim of present study was to evaluate different TKR designs and positions with regard to joint kinematics and stability under dynamic conditions by using a robot-based hardware-in-the-loop (HiL) setup. Material & methods. An industrial 6-axis robot with 6-axis force-torque sensor mounted into its end-effector moved and loaded real, commercially available TKR (bicondylar, cruciate-retaining) that were in virtual interaction with a subject-specific computational multibody model representing the anatomical situs of the knee joint while performing passive seated deep knee flexion. The subject-specific musculoskeletal multibody model (MMB) included rigid bones of the lower right extremity. Bone and cartilage geometries were reconstructed from MRT/ CT data sets preserving anatomical landmarks and allowing for the calculation of inertial properties. M. quadriceps femoris was modeled as single passive tensile force elements. Knee ligaments were modelled as elastic spring elements with a nonlinear force-displacement characteristic. Providing the flexion angle, the robot moved and loaded the mounted femoral implant component with respect to the tibial component while being in continuous interaction with the MMB. Several influencing parameters like implant position (internal/external rotation, varus/valgus alignment) and design (fixed vs. mobile bearing, tibia-insert height) as well as ligament insufficiency and joint loading on joint kinematics and stability was systematically analysed. Results. Improper implant positioning caused joint instability, which was demonstrated in higher magnitudes of the relative kinematics. Negative effects by incorrect implant positioning could be partially compensated by a mobile bearing design. However, this was accompanied with an increase in tibiofemoral contact forces. High correlation of tibia-insert height on ligament and contact force was found. After releasing ligament structures, lower tibiofemoral contact forces and joint opening during deep knee flexion were observed. Conclusion. By means of HiL simulation different clinical and technical parameters of TKR were evaluated in a systematical and reproducible fashion under physiological-like boundary conditions with regard to joint kinematics and stability. The proposed HiL test setup combining robot-based testing with MMBs can contribute to deeper understanding of knee joint function and improvement of total knee implant systems. Acknowledgement. The authors would like to thank the Deutsche Forschungsgemeinschaft (grant numbers: WO WO 452/8-1, BA 3347/3-1 and KL 2327/4-1) for supporting the project

Post-mortem retrieval of canine, cemented femoral components was analysed to assess the performance of these implants in the dog as a model for human total hip replacement (THR). Mechanical testing and radiological analysis were performed to determine the stability of the implant and the quality of the cement. Thirty-eight implants from 29 dogs were retrieved after time intervals ranging from 0.67 to 11.67 years. The incidence of aseptic loosening was 63.2%, much higher than in human patients (6% in post-mortem studies). Failure of the femoral implants began with debonding at the cement-metal interface, similar to that in implants in man. The incidence of aseptic loosening was much lower in bilateral than in unilateral implants. Significant differences were observed for three different designs of implant. While the dog remains the animal model of choice for THR, results from this study provide insight into interspecies differences in the performance of implants. For example, the performance of THR in dogs should be compared with that in young rather than in elderly human patients

Financial and human cost effectiveness is an increasing evident outcome measure of surgical innovation. Considering the human element, the aim is to restore the individual to their “normal” state by sparing anatomy without compromising implant performance. Gait lab studies have shown differences between different implants at top walking speed, but none to our knowledge have analysed differing total hip replacement patients through the entire range of gait speed and incline to show differences. The purpose of this gait study was to 1) determine if a new short stem femoral implant would return patients back to normal 2) compare its performance to established hip resurfacing and long stem total hip replacement (THR) implants. 110 subjects were tested on an instrumented treadmill (Kistler Gaitway, Amherst, NY), 4 groups (short-stem THR, long-stem THR, hip resurfacing and healthy controls) of 28, 29, 27, and 26 respectively. The new short femoral stem patients (Furlong Evolution, JRI) were taken from the ongoing Evolution Hip trial that have been tested on the treadmill with minimum 12months postop. The long stem total hip replacements and hip resurfacing groups were identified from out 800 patient gait database. They were only chosen if they were 12 months postop and had no other joint disease or medical comorbidities which would affect gait performance. All subjects were tested through their entire range of gait speeds and incline after having a 5 minute habituation period. Speed intervals were at 0.5kms increments until maximum walking speed achieved and inclines at 4kms for 5, 10, 15%. At all incremental intervals of speed, the vertical component of the ground reaction forces, center of pressure and temporal measurements were collected for both limbs with a sampling frequency of 100Hz. Body weight scaling was applied to correct for mass differences and a symmetry index to compare the implanted hip to the contralateral normal hip. All variables for each subject group were compared to each other using an analysis of variance (ANOVA) with Tukey post hoc test with significance set at α=0.05. The four experimental groups were reasonably matched for demographics and the implant groups for PROMs. Hip resurfacing had a clear top walking speed advantage, but when assessing the symmetry index on all speeds and incline, all groups were not significantly different. Push-off and step length was statistically less favourable for the short/long THR group (p=0.005–0.05) depending on speed/incline. The primary aim of this study was determine if implant design affected gait symmetry and performance. Interestingly, irrespective of implant design, symmetry with regards to weight acceptance, impulse, push-off and step length was returned to normal when comparing to healthy controls. However individual implant performance on the flat and incline, showed inferior (p<0.05) push-off force and step length in the short stem and long stem THR groups when compared to controls. Age and gender may have played a part for the short stem group. It appears that the early gait outcomes for the short stem device are promising. Assessment at the 3 year mark should be conclusive

Summary Statement. In young, active patients cementless THR demonstrates excellent prosthetic stability by RSA and outstanding clinical outcomes at 5 years using a tapered titanium femoral stem, crosslinked polyethylene liners and either titanium or tantalum shells. Introduction. Early femoral implant stability is essential to long-term success in total hip replacement. Radiostereometric analysis (RSA) provides precise measurements of micromotion of the stem relative to the femur that are otherwise not detectable by routine radiographs. This study characterised micromotion of a tapered, cementless femoral stem and tantalum porous-coated vs. titanium acetabular shells in combination with highly cross-linked UHMWPE or conventional polyethylene liners using radiostereometric analysis (RSA) for 5 years following THR. Patients and Methods. This IRB-approved, prospective, double randomised, blinded study, involved 46 patients receiving a primary THR by a single surgeon. Each patient was randomised to receive a titanium (23) (Trilogy, Zimmer) or tantalum (23) (Modular Tantalum shell, Zimmer) uncemented hemispheric shell and either a highly-crosslinked or conventional polyethylene liner. Tantalum RSA markers were implanted in each patient. All patients had a Dorr A or B femoral canal and received a cementless, porous-coated titanium tapered stem (M/L Taper, Zimmer). All final femoral broaches were stable to rotational and longitudinal stress. RSA examinations, Harris Hip, UCLA, WOMAC, SF-12 scores were obtained at 10 days, 6 months, and annually through 5 years. Results. All patients demonstrated statistically significant improvement in Harris Hip, WOMAC, and SF-12 PCS scores post-operatively. Evaluation of polyethylene wear demonstrated that median penetration measurements were significantly greater in the conventional compared to the HXPLE liner cohorts at 1 year through 5 years follow-up (p<0.003). At 5 years, conventional liners showed 0.38 ± 0.05mm vertical wear whereas HXLPE liners showed 0.08 ± 0.02mm (p<0.003). Evaluation of the femoral stems demonstrated that the rate of subsidence was highest in the first 6 months (0.09mm/yr), with no other detectable motion through 5 years. Two outlying patients had significantly higher stem subsidence values at 6 months (0.7 mm and 1.0mm). One stem stabilised without further subsidence after 6 months (0.7mm), and the other stem stabilised at 1 year (1.5mm). Neither patient has clinical evidence of loosening. Evaluation of acetabular shells demonstrated less median vertical translation in tantalum than titanium shells at each time-point except at 3-years follow-up, however due to large standard errors, there was no significant difference between the two designs (p>0.05). These large standard errors were predominantly caused by two outliers, neither of which had clinical evidence of loosening. Discussion/Conclusion. In this RSA study of young THR patients, cementless tapered femoral stems, highly crosslinked polyethylene liners, and tantalum or titanium acetabular shells all demonstrated excellent performance through 5 years follow-up. Highly crosslinked polyethylene liners demonstrated significantly less wear than conventional liners. The femoral stem showed excellent stability through 5 years, with no clinical or radiologic episodes of failure. The small amount of micromotion seen is less than that previously reported for similar tapered, cementless stems and approaches the accuracy of RSA (0.05mm). Both acetabular shells demonstrated excellent stability with minimal micromotion at 5 years without significant differences in migration. All patients demonstrated significant clinical improvement in pain and function and additional RSA evaluation of these patients is planned

CT and advanced computer-aided design techniques offer the means for designing customised femoral stems. Our aim was to determine the Hounsfield (HU) value of the bone at the corticocancellous interface, as part of the criteria for the design algorithm. We obtained transverse CT images from eight human cadaver femora. The proximal femoral canal was rasped until contact with dense cortical bone was achieved. The femora were cut into several sections corresponding to the slice positions of the CT images. After obtaining a computerised image of the anatomical sections using a scanner, the inner cortical contour was outlined and transferred to the corresponding CT image. The pixels beneath this contour represent the CT density of the bone remaining after surgical rasping. Contours were generated automatically at nine HU levels from 300 to 1100 and the mean distance between the transferred contour and each of the HU-generated contours was computed. The contour generated along the 600-HU pixels was closest to the inner cortical contour of the rasped femur and therefore 600 HU seem to be the CT density of the corticocancellous interface in the proximal part of cadaver femora. Generally, femoral bone with a CT density beyond 600 HU is not removable by conventional reamers. Thus, we recommend the 600 HU threshold as one of several criteria for the design of custom femoral implants from CT data

Summary. From a large 3D Caucasian bone data base, female population had significantly larger acetabular anatomical anteversion angle and combined acetabular-femoral anteversion angle than that of male population. There was no significant difference in femoral neck anteversion angles between the groups. Introduction. Combined Anteversion (CA) angle of acetabular component and femoral neck is an important parameter for a successful Total Hip Arthroplasty (THA). The purpose of this study was to electronically measure the version angles of native acetabulum and femur in matured normal Caucasian population from large 3D CT data base. Our question was if there was any significant difference in CA between male and female population. Methods. 221 anonymous (134 males and 87 females) CT paired pelvic and femoral scans from normal Caucasian population with age range of 30–93 years old were analyzed. CT data was converted to virtual bones using custom CT analytical software. 1. (SOMA. TM. V.3.2). Acetabular Anatomical Anteversion (AA) angle as defined by Murray. 2. was selected. The acetabular rim plane was constructed by selecting 3 bony land marks from pubis, ilium and ischium. The AA was measured against pelvic frontal plane. Femoral neck Anteversion (FA) was measured between neck axis plane and the Coronal plane which was defined by posterior condyles. The neck axis plane was defined as being the plane passing through femoral neck axis and being perpendicular to the transverse plane which is defined by distal femoral condyles. The CA angle in standing position was computed as the summation of AA and FNA angles. All the measurements were performed for total, male and female populations. Student's t tests were performed to compare gender difference with an assumed 95% confidence level. The relationship between AA and FA for each gender was studied by the plot of AA and a function of FA. Results. The mean AA angle for total population was 25.8°, SD=6.52°. (male 24.8°, SD=5.91°, female was 27.3°, SD=7.12°. P=0.006). The mean FA angle for total population was 14.3°, SD=7.95°. (male 13.4°, SD=7.99°, female 15.6°, SD=7.76°. P=0.051). The mean CA angle for total population was 40.1°, SD=10.76°. (male 38.2° SD= 10.38 °, female 42.9° SD= 10.79 °. P=.0002). The plot of AA as a function FA is shown. The frequency distribution of CA angle is plotted for males and females. Discussion/Conclusion. The results showed both AA and CA angles were significantly smaller in the male than that in female. However there was no significant difference in FA between male and female. The plot of AA as a function of FA showed no correlation (R. 2. <.09) between the two angles for both male (R. 2. =.0097) and female (R. 2. =.0029). The FA angle of a femoral stem implant in THA may be smaller than that of natural femur, therefore a higher AA or higher posterior build up may be required for the acetabular component to achieve optimal function of a THA. This may be a more significant issue in female population. The limitations of this study was that this population did not have pathological conditions which could lead to THA. However, it should provide reference guidance comparing normal anatomy between male and female

Objectives

Taper junctions between modular hip arthroplasty femoral heads and stems fail by wear or corrosion which can be caused by relative motion at their interface. Increasing the assembly force can reduce relative motion and corrosion but may also damage surrounding tissues. The purpose of this study was to determine the effects of increasing the impaction energy and the stiffness of the impactor tool on the stability of the taper junction and on the forces transmitted through the patient’s surrounding tissues.

We designed an in vivo study to determine if the superimposition of a microtexture on the surface of sintered titanium beads affected the extent of bone ingrowth. Cylindrical titanium intramedullary implants were coated with titanium beads to form a porous finish using commercial sintering techniques. A control group of implants was left in the as-sintered condition. The test group was etched in a boiling acidic solution to create an irregular surface over the entire porous coating. Six experimental dogs underwent simultaneous bilateral femoral intramedullary implantation of a control implant and an acid etched implant. At 12 weeks, the implants were harvested in situ and the femora processed for undecalcified, histological examination. Eight transverse serial sections for each implant were analysed by backscattered electron microscopy and the extent of bone ingrowth was quantified by computer-aided image analysis. The extent of bone ingrowth into the control implants was 15.8% while the extent of bone ingrowth into the etched implants was 25.3%, a difference of 60% that was statistically significant. These results are consistent with other research that documents the positive effect of microtextured surfaces on bone formation at an implant surface. The acid etching process developed for this study represents a simple method for enhancing the potential of commonly available porous coatings for biological fixation

Objectives

Infection of implants is a major problem in elective and trauma surgery. Heating is an effective way to reduce the bacterial load in food preparation, and studies on hyperthermia treatment for cancer have shown that it is possible to heat metal objects with pulsed electromagnetic fields selectively (PEMF), also known as induction heating. We therefore set out to answer the following research question: is non-contact induction heating of metallic implants effective in reducing bacterial load in vitro?

Objectives

This study tests the biomechanical properties of adjacent locked plate constructs in a femur model using Sawbones. Previous studies have described biomechanical behaviour related to inter-device distances. We hypothesise that a smaller lateral inter-plate distance will result in a biomechanically stronger construct, and that addition of an anterior plate will increase the overall strength of the construct.

Hydroxyapatite-coated standard anatomical and customised femoral stems are designed to transmit load to the metaphyseal part of the proximal femur in order to avoid stress shielding and to reduce resorption of bone. In a randomised in vitro study, we compared the changes in the pattern of cortical strain after the insertion of hydroxyapatite-coated standard anatomical and customised stems in 12 pairs of human cadaver femora. A hip simulator reproduced the physiological loads on the proximal femur in single-leg stance and stair-climbing. The cortical strains were measured before and after the insertion of the stems.

Significantly higher strain shielding was seen in Gruen zones 7, 6, 5, 3 and 2 after the insertion of the anatomical stem compared with the customised stem. For the anatomical stem, the hoop strains on the femur also indicated that the load was transferred to the cortical bone at the lower metaphyseal or upper diaphyseal part of the proximal femur.

The customised stem induced a strain pattern more similar to that of the intact femur than the standard, anatomical stem.

The aim of our study was to investigate whether placing of the femoral component of a hip resurfacing in valgus protected against spontaneous fracture of the femoral neck.

We performed a hip resurfacing in 20 pairs of embalmed femora. The femoral component was implanted at the natural neck-shaft angle in the left femur and with a 10° valgus angle on the right. The bone mineral density of each femur was measured and CT was performed. Each femur was evaluated in a materials testing machine using increasing cyclical loads.

In specimens with good bone quality, the 10° valgus placement of the femoral component had a protective effect against fractures of the femoral neck. An adverse effect was detected in osteoporotic specimens.

When resurfacing the hip a valgus position of the femoral component should be achieved in order to prevent fracture of the femoral neck. Patient selection remains absolutely imperative. In borderline cases, measurement of bone mineral density may be indicated.

Dislocation remains a major concern after total hip replacement, and is often attributed to malposition of the components. The optimum position for placement of the components remains uncertain. We have attempted to identify a relatively safe zone in which movement of the hip will occur without impingement, even if one component is positioned incorrectly. A three-dimensional computer model was designed to simulate impingement and used to examine 125 combinations of positioning of the components in order to allow maximum movement without impingement. Increase in acetabular and/or femoral anteversion allowed greater internal rotation before impingement occurred, but decreases the amount of external rotation. A decrease in abduction of the acetabular components increased internal rotation while decreasing external rotation. Although some correction for malposition was allowable on the opposite side of the joint, extreme degrees could not be corrected because of bony impingement.

We introduce the concept of combined component position, in which anteversion and abduction of the acetabular component, along with femoral anteversion, are all defined as critical elements for stability.

We investigated the effect of stimulation with a pulsed electromagnetic field on the osseointegration of hydroxyapatite in cortical bone in rabbits. Implants were inserted into femoral cortical bone and were stimulated for six hours per day for three weeks.

Electromagnetic stimulation improved osseointegration of hydroxyapatite compared with animals which did not receive this treatment in terms of direct contact with the bone, the maturity of the bone and mechanical fixation. The highest values of maximum push-out force (F_max) and ultimate shear strength (σ_u) were observed in the treated group and differed significantly from those of the control group at three weeks (F_max; p < 0.0001; σ_u, p < 0.0005).

Interfacial defects between the cement mantle and a hip implant may arise from constrained shrinkage of the cement or from air introduced during insertion of the stem. Shrinkage-induced interfacial porosity consists of small pores randomly located around the stem, whereas introduced interfacial gaps are large, individual and less uniformly distributed areas of stem-cement separation. Using a validated CT-based technique, we investigated the extent, morphology and distribution of interfacial gaps for two types of stem, the Charnley-Kerboul and the Lubinus SPII, and for two techniques of implantation, line-to-line and undersized.

The interfacial gaps were variable and involved a mean of 6.43% (sd 8.99) of the surface of the stem. Neither the type of implant nor the technique of implantation had a significant effect on the regions of the gaps, which occurred more often over the flat areas of the implant than along the corners of the stems, and were more common proximally than distally for Charnley-Kerboul stems cemented line-to-line. Interfacial defects could have a major effect on the stability and survival of the implant.