Summary Statement. A study to evaluate biofilm development on different coatings of UHMWPE was performed. We observed a species-specific effect, with S. aureus affected mainly by DLC-F and S. epidermidis by DLC. These data correlates with previous adherence studies. Introduction. Prosthetic joint infection is intimately related to bacterial biofilms on implant biomaterials. Recently, diamond-like carbon (DLC) coating has been suggested to improve the antibacterial performance of medical grade GUR1050 ultra high molecular weight polyethylene (UHMWPE) supplied by Orthoplastics bacup, UK versus collection and clinical staphylococcal strains. The aim of this study was to make an approximation towards the actual impact of such coatings in biofilm formation. Material and Methods. Biofilm formation by two collection laboratory strains (S. aureus 15981[4] and S. epidermidis ATCC 35984) was evaluated with raw UHMWPE and two UHMWPEs coated with DLC, and fluorine doped DLC (F-DLC). The coated surfaces were obtained by plasma enhanced chemical vapour deposition, as previously described. All the sterilised surfaces were exposed to ≈10. 8. colony forming units/mL during 48 hours at 35° C, with total medium exchange at 24 hours without shaking. Surfaces were carefully washed with PBS (X 3) and then stained with Backlight. ©. live/dead stain for 15 minutes. Confocal Laser Scanning Microscopy was used for sampling the surfaces and studying biofilm, for which eight random series of photographs (Named SERIES) and four predefined biofilm series (Named BIOFILM) were taken. Biofilm thickness (microns) and covered surface by live/dead bacteria (%) were determined for both SERIES and BIOFILM. Assays were made in triplicates. Photographs were analyzed by ImageJ software, and data, by a Mann-Withney test. Results. Biofilm thickness and bacterial coverage per surface type in SERIES as well as BIOFILM for S. aureus and S.epidermidis, respectively is shown. A diminution of these two variables was observed in the coated surfaces versus raw UHWMPE with statistically significant reductions (p≤0.0001). F-DLC was the most effective coated surface versus S. aureus, with the least biofilm thickness and the highest proportional percentage of dead bacteria, and so DLC was versus S. epidermidis. Of interest, the proportion of dead S. epidermidis was higher in raw UHMWPE. Discussion & Conclusions. Staphylococcal biofilm formation on UHMWPE surfaces is irregular. Both biofilm thicknesses as bacterial coverage were lower in DLC and F-DLC. These preliminary data correlate to our previous bacterial adherence findings and support the better anti-adherence performance of DLC coated UHMWPEs. Fluorine is suggested to exhibit a bacteria-dependant behavior, but at present its role is quite far to be known. Further studies using clinical strains of both species are needed to evaluate the accuracy of these results

Summary

Staphylococcus aureus isolates from Fracture fixation device related infections contained fewer isolates that form a strong biofilm in comparison with isolates from Prosthetic joint infections. Both orthopaedic implant related infection groups possessed fnbB and sdrE more frequently than the non-implant related infection groups.

Introduction and Objective. Found in bone-associated prosthesis, Cutibacterium acnes (C. acnes) is isolated in more than 50% of osteoarticular prosthesis infections, particularly those involving shoulder prostheses. Ongoing controversies exist concerning the origin of C. acnes infection. Few reports construct a reasonable hypothesis about probable contaminant displaced from the superficial skin into the surgical wound. Indeed, despite strict aseptic procedures, transecting the sebaceous glands after incision might result in C. acnes leakage into the surgical wound. More recently, the presence of commensal C. acnes in deep intra-articular tissues was reported. C. acnes was thus detected in the intracellular compartment of macrophages and stromal cells in 62.5% of the tested patients who did not undergo skin penetration. Among bone stromal cells, mesenchymal stem cells (MSCs) are predominantly found in bone marrow and periosteum. MSCs are the source of osteogenic lines of cells capable of forming bone matter. In this study, the pathogenicity of C. acnes in bone repair context was investigated. Materials and Methods. Human bone marrow derived MSCs were challenged with C. acnes clinical strains harvested from non-infected bone site (Cb). The behaviour of Cb strain was compared to C. acnes took from orthopaedic implant-associated infection (Ci). The infective capabilities of both strains was determined following gentamicin-based antibiotic protection assay. The morphology and ultrastructural analysis of infected MSCs was performed respectively through CLSM pictures of Phalloidin. ®. stained MSCs cytoskeleton and DAPI labelled Cb, and transmission and scanning electron microscopies. The virulence of intracellular Ci and Cb (Ci-MSCs and Cb-MSCs) was investigated by biofilm formation on non-living bone materials; and the immunomodulatory response of infected MSCs was investigated (PGE-2 and IDO secretion detected by ELISA). Bone cells (osteoblasts and PMA differentiated macrophages) were then challenged with Cb-MSCs and Ci-MSCs. Intracellular accumulation of ROS within infected macrophages was assessed by flow cytometry after 2 h of infection and the catalase production by Cb-MSC and Ci-MSC was evaluated. Statistical analyses were performed using Mann & Whitney test. Results. Following MSCs infection by C. acnes, the rate of viable bacteria inside MSCs was about 4% and 6% for Cb and Ci, respectively. Cb showed however a lower invasiveness in comparison to Ci (0.6-fold, p=0.01), confirming the higher pathogenicity of Ci. The ultrastructural and morphology analysis of infected MSCs confirmed the presence of bacteria free in MSCs cytoplasm, localized between F-actin fibers of MSCs, which preserved their elongated morphology. Considering the high level of secreted immunomodulatory mediators (PGE-2 and IDO), our results suggest that Cb-infected MSCs could promote a transition of macrophages from a primarily pro-inflammatory M1 to a more anti-inflammatory M2 phenotype. In comparison with Cb, Cb-MSCs increased significantly the formation of biofilm on TA6V and PEEK but reduced the biofilm formation on 316L SS. Ci-MSCs showed a significant increase in biofilm formation on PEEK vs Ci, while no difference in biofilm formation was noticed on TA6V and 316L SS. Regarding the ability of MSCs bacteria to infect osteoblasts, our results showed a higher infective capabilities of Cb-MSCs versus Cb (>2-fold, p=0.02), while no difference was noticed between Ci and Ci-MSCs. Along with an increase in catalase production by Cb-MSCs, we noticed its higher persistence to macrophage degradation. Conclusions. Taken together, our results demonstrate a shift in commensal Cb to pathogenic following infection. Indeed, Cb- MSCs acquires features that (i) increase biofilm formation on orthopedic based materials, (ii) increase the osteoblast infection and (iii) develop resistance to the macrophage degradation, through the increase of catalase production. Overall, these results showed a direct impact of C. acnes on bone marrow derived MSCs, providing new insights into the development of C. acnes during implant-associated infections

Prosthetic joint infections represent complications connected to the implantation of biomedical devices. Bacterial biofilm is one of the main issues causing infections from contaminated orthopaedic prostheses. Biofilm is a structured community of microbial cells that are firmly attached to a surface and have unique metabolic and physiological attributes that induce improved resistance to environmental stresses including toxic compounds like antimicrobial molecules (e.g. antibiotics). Therefore, there is increasing need to develop methods/treatments exerting antibacterial activities not only against planktonic (suspended) cells but also against adherent cells of pathogenic microorganisms forming biofilms. In this context, metal-based coatings with antibacterial activities have been widely investigated and used in the clinical practice. However, traditional coatings exhibit some drawbacks related to the insufficient adhesion to the substrate, scarce uniformity and scarce control over the toxic metal release reducing the biofilm formation prevention efficacy. Additionally, standardized and systematic approaches to test antibacterial activity of newly developed coatings are still missing, while standard microbiological tests (e.g. soft-agar assays) are typically used that are limited in terms of simultaneous conditions that can be tested, potentially leading to scarce reproducibility and reliability of the results. In this work, we combined the Calgary Biofilm Device (CBD) as a device for high-throughput screening, together with a novel plasma-assisted technique named Ionized Jet Deposition (IJD), to generate and test new generation of nanostructured silver- and zinc-based films as coatings for biomedical devices with antibacterial and antibiofilm properties. During the experiments we tested both planktonic and biofilm growth of four bacterial strains, two gram-positive and two gram-negative bacterial strains, i.e. Staphylococcus aureus ATCC 6538P, Enterococcus faecalis DP1122 and Escherichia coli ATCC 8739 and Pseudomonas aeruginosa PAO1, respectively. The use of CBD that had the only wells covered with the metal coatings while the biofilm supports (pegs) were not sheltered allowed to selectively define the toxic effect of the metal release (from the coating) against biofilm development in addition to the toxic activity exerted by contact killing mechanism (on biofilms formed on the coating). The results indicated that the antibacterial and antibiofilm effects of the metal coatings was at least partly gram staining dependent. Indeed, Gram negative bacterial strains showed high sensitivity toward silver in both planktonic growth and biofilm formation, whereas zinc coatings provided a significant inhibitory activity against Gram positive bacterial strains. Furthermore, the coatings showed the maximal activity against biofilms directly forming on them, although, Zn coating showed a strong effect against biofilms of gram-positive bacteria also formed on uncoated pegs. We conclude that the metal-based coatings newly developed and screened in this work are efficient against bacterial growth and adherence opening possible future applications for orthopedic protheses manufacturing

Infection in orthopedics is a challenge, since it has high incidence (rates can be up to 15-20%, also depending on the surgical procedure and on comorbidities), interferes with osseointegration and brings severe complications to the patients and high societal burden. In particular, infection rates are high in oncologic surgery, when biomedical devices are used to fill bone gaps created to remove tumors. To increase osseointegration, calcium phosphates coatings are used. To prevent infection, metal- and mainly silver-based coatings are the most diffused option. However, traditional techniques present some drawbacks, including scarce adhesion to the substrate, detachments, and/or poor control over metal ions release, all leading to cytotoxicity and/or interfering with osteointegration. Since important cross-relations exist among infection, osseointegration and tumors, solutions capable of addressing all would be a breakthrough innovation in the field and could improve clinical practice. Here, for the first time, we propose the use antimicrobial silver-based nanostructured thin films to simultaneously discourage infection and bone metastases. Coatings are obtained by Ionized Jet Deposition, a plasma-assisted technique that permits to manufacture films of submicrometric thickness having a nanostructured surface texture. These characteristics, in turn, allow tuning silver release and avoid delamination, thus preventing toxicity. In addition, to mitigate interference with osseointegration, here silver composites with bone apatite are explored. Indeed, capability of bone apatite coatings to promote osseointegration had been previously demonstrated in vitro and in vivo. Here, antibacterial efficacy and biocompatibility of silver-based films are tested in vitro and in vivo. Finally, for the first time, a proof-of-concept of antitumor efficacy of the silver-based films is shown in vitro. Coatings are obtained by silver and silver-bone apatite composite targets. Both standard and custom-made (porous) vertebral titanium alloy prostheses are used as substrates. Films composition and morphology depending on the deposition parameters are investigated and optimized. Antibacterial efficacy of silver films is tested in vitro against gram+ and gram- species (E. coli, P. aeruginosa, S. aureus, E. faecalis), to determine the optimal coatings characteristics, by assessing reduction of bacterial viability, adhesion to substrate and biofilm formation. Biocompatibility is tested in vitro on fibroblasts and MSCs and, in vivo on rat models. Efficacy is also tested in an in vivo rabbit model, using a multidrug resistant strain of S. aureus (MRSA, S. aureus USA 300). Absence of nanotoxicity is assessed in vivo by measuring possible presence of Ag in the blood or in target organs (ICP-MS). Then, possible antitumor effect of the films is preliminary assessed in vitro using MDA-MB-231 cells, live/dead assay and scanning electron microscopy (FEG-SEM). Statistical analysis is performed and data are reported as Mean ± standard Deviation at a significance level of p <0.05. Silver and silver-bone apatite films show high efficacy in vitro against all the tested strains (complete inhibition of planktonic growth, reduction of biofilm formation > 50%), without causing cytotoxicity. Biocompatibility is also confirmed in vivo. In vivo, Ag and Ag-bone apatite films can inhibit the MRSA strain (>99% and >86% reduction against ctr, respectively). Residual antibacterial activity is retained after explant (at 1 month). These studies indicate that IJD films are highly tunable and can be a promising route to overcome the main challenges in orthopedic prostheses

Prosthetic joint infections represent complications connected to the implantation of biomedical devices, they have high incidence, interfere with osseointegration, and lead to a high societal burden. The microbial biofilm, which is a complex structure of microbial cells firmly attached to a surface, is one of the main issues causing infections. Biofilm- forming bacteria are acquiring more and more resistances to common clinical treatments due to the abuse of antibiotics administration. Therefore, there is increasing need to develop alternative methods exerting antibacterial activities against multidrug-resistant biofilm-forming bacteria. In this context, metal-based coatings with antimicrobial activities have been investigated and are currently used in the clinical practice. However, traditional coatings exhibit some drawbacks related to the insufficient adhesion to the substrate, scarce uniformity and scarce control over the toxic metal release reducing their efficacy. Here, we propose the use of antimicrobial silver-based nanostructured thin films to discourage bacterial infections. Coatings are obtained by Ionized Jet Deposition, a plasma-assisted technique that permits to manufacture films of submicrometric thickness having a nanostructured surface texture, allow tuning silver release, and avoid delamination. To mitigate interference with osseointegration, here silver composites with bone apatite and hydroxyapatite were explored. The antibacterial efficacy of silver films was tested in vitro against gram- positive and gram-negative species to determine the optimal coatings characteristics by assessing reduction of bacterial viability, adhesion to substrate, and biofilm formation. Efficacy was tested in an in vivo rabbit model, using a multidrug-resistant strain of Staphylococcus aureus showing significant reduction of the bacterial load on the silver prosthesis both when coated with the metal only (>99% reduction) and when in combination with bone apatite (>86% reduction). These studies indicate that IJD films are highly tunable and can be a promising route to overcome the main challenges in orthopedic prostheses

An increasing elderly population means joint replacement surgery numbers are projected to increase, with associated complications such as periprosthetic joint infections (PJI) also rising. PJI are particularly challenging due to antimicrobial resistant biofilm development on implant surfaces and surrounding tissues, with treatment typically involving invasive surgeries and systemic antibiotic delivery. Consequently, functionalisation of implant surfaces to prevent biofilm formation is a major research focus. This study characterises clinically relevant antimicrobials including gentamicin, clindamycin, daptomycin, vancomycin and caspofungin within a silica-based, biodegradable sol-gel coating for prosthetic devices. Antimicrobial activity of the coatings against clinically relevant microorganisms was assessed via disc diffusion assays, broth microdilution culture methods and the MBEC assay used to determine anti-biofilm activity. Human and bovine cells were cultured in presence of antimicrobial sol-gel to determine cytotoxicity using Alamar blue and antibiotic release was measured by LC-MS. Biodegradability in physiological conditions was assayed by FT-IR, ICP-MS and measuring mass change. Effect of degradation products on osteogenesis were studied by culturing mesenchymal stem cells in the presence of media in which sol-gel samples had been immersed. Antimicrobial-loaded coatings showed strong activity against a wide range of clinically relevant bacterial and fungal pathogens with no loss of activity from antibiotic alone. The sol-gel coating demonstrated controlled release of antimicrobials and initial sol-gel coatings showed no loss of viability on MSCs with gentamicin containing coatings. Current work is underway investigating cytotoxicity of sol-gel compositions against MG-63 cells and primary osteoblasts. This research forms part of an extended study into a promising antimicrobial delivery strategy to prevent PJI. The implant coating has potential to advance PJI infection prevention, reducing future burden upon healthcare costs and patient wellbeing

Prosthetic joint infections represent complications connected to the implantation of biomedical devices, they have high incidence, interfere with osseointegration, and lead to a high societal burden. The microbial biofilm, which is a complex structure of microbial cells firmly attached to a surface, is one of the main issues causing infections. Biofilm- forming bacteria are acquiring more and more resistances to common clinical treatments due to the abuse of antibiotics administration. Therefore, there is increasing need to develop alternative methods exerting antibacterial activities against multidrug-resistant biofilm-forming bacteria. In this context, metal-based coatings with antimicrobial activities have been investigated and are currently used in the clinical practice. However, traditional coatings exhibit some drawbacks related to the insufficient adhesion to the substrate, scarce uniformity and scarce control over the toxic metal release reducing their efficacy. Here, we propose the use of antimicrobial silver-based nanostructured thin films to discourage bacterial infections. Coatings are obtained by Ionized Jet Deposition, a plasma-assisted technique that permits to manufacture films of submicrometric thickness having a nanostructured surface texture, allow tuning silver release, and avoid delamination. To mitigate interference with osseointegration, here silver composites with bone apatite and hydroxyapatite were explored. The antibacterial efficacy of silver films was tested in vitro against gram- positive and gram-negative species to determine the optimal coatings characteristics by assessing reduction of bacterial viability, adhesion to substrate, and biofilm formation. Efficacy was tested in an in vivo rabbit model, using a multidrug-resistant strain of Staphylococcus aureus showing significant reduction of the bacterial load on the silver prosthesis both when coated with the metal only (>99% reduction) and when in combination with bone apatite (>86% reduction). These studies indicate that IJD films are highly tunable and can be a promising route to overcome the main challenges in orthopedic prostheses

Infection of implanted medical devices (biomaterials), like titanium orthopaedic implants, can have disastrous consequences, including removal of the device. These so-called biomaterial-associated infections (BAI) are mainly caused by Staphylococcus aureus and Staphylococcus epidermidis. To prevent biofilm formation using a non-antibiotic based strategy, we aimed to develop a novel permanently fixed antimicrobial coating for titanium devices based on stable immobilized quaternary ammonium compounds (QACs). Medical grade titanium implants were dip-coated in subsequent solutions of hyperbranched polymer, polyethyleneimine and 10 mM sodium iodide, and ethanol. The QAC-coating was characterized using water contact angle measurements, scanning electron microscopy, FTIR, AFM and XPS. The antimicrobial activity of the coating was evaluated against S. aureus strain JAR060131 and S. epidermidis strain ATCC 12228 using the JIS Z 2801:2000 surface microbicidal assay. Lastly, we assessed the in vivo antimicrobial activity in a mouse subcutaneous implant infection model with S. aureus administered locally on the QAC-coated implants prior to implantation to mimic contamination during surgery. Detailed material characterization of the titanium samples showed the presence of a homogenous and stable coating layer at the titanium surface. Moreover, the coating successfully killed S. aureus and S. epidermidis in vitro. The QAC-coating strongly reduced S. aureus colonization of the implant surface as well as of the surrounding tissue, with no apparent macroscopic signs of toxicity or inflammation in the peri-implant tissue at 1 and 4 days after implantation. An antimicrobial coating with stable quaternary ammonium compounds on titanium has been developed which holds promise to prevent BAI. Non-antibiotic-based antimicrobial coatings have great significance in guiding the design of novel antimicrobial coatings in the present, post-antibiotic era. Acknowledgements: This research was financially supported by the Health∼Holland/LSH-TKI call 2021–2022, project 25687, NACQAC: ‘Novel antimicrobial coatings with stable non-antibiotic Quaternary Ammonium Compounds and photosensitizer technology'

Prosthetic Joint Infections (PJIs) are increasing with the use of orthopedic devices on an ageing population. Cutibacterium acnes is a commensal organism that plays an important role in the ecosystem healthy human skin, yet this species is also recognized as a pathogen in foreign body infection: endocarditis, prostatitis and specifically in PJIs. C. acnes is able to escape the immune system. This phenomenon could reflect two bacterial behaviour: the bacterial internalization by host cells and the biofilm formation. In this study, we studied different clinical strains of C. acnes. We noticed that C. acnes isolated from PJIs form 2 fold-more biofilm than the strains isolated from a normal skin in two models (Crystal violet staining and fluorescent microscopy (p=0.04 and p=0.02, respectively, Mann-Whitney test). We did not observe any difference in the internalization rate of those strains by osteoblasts. However, the quantity of biofilm formed by C. acnes before and after the internalization was compared. A significant increase in biofilm formation was observed for the strains isolated from the skin (x2.3±0.07; p=0.008, Mann-Whitney test). However, the hydrophobicity of the skin strains is significantly less important than for the PJIs strains (24.8±13% vs 56.6±12% respectively; p=0.003, Mann-Whitney test) but this did not change after internalization suggesting that there is no cell wall evolution. In conclusion, we studied for the first time the impact of bacterial internalization by osteoblasts on the virulent behaviour of C. acnes, which could explain the hided pathogenicity of this commensal bacterium

The most common bacteria in orthopaedic prosthetic infections are Staphylococcus, namely Staphylococcus Epidermidis (SE) and Staphylococcus Aureus (SA). Infection causes implant failure due to biofilm production. Biofilms are produced by bacteria once they have adhered to a surface. Nanotopography has major effects on cell behaviour. Our research focuses on bacterial adhesion and biofilm formation on nanofabricated materials. Bacteria studied were clinically relevant from an orthopaedic perspective, SA and SE. We hypothesise that that nanosurfaces can modulate bacterial adherence and biofilm formation and may reduce orthopaedic implant infection rate. Isolated bacteria were grown and growth conditions optimised. Bacterial concentrations were calculated by using qPCR. Statistical analysis allowed identification of optimal biofilm growth conditions. These were refined on standard, non-nanopatterned surfaces, and then control and nanopatterned polystyrene (nanopits) and titanium plates (nanowires). Adhesion analysis was performed using fluorescence imaging and quantitative PCR. 4 bacterial strains were isolated and cultured. Growth kinetics based on 24hr cultures allowed isolation of optimal media for biofilm conditions (Dulbecco's Modified Eagle Medium with additional supplements). Highest bacterial concentrations were found following 2hrs incubation with Lysozyme during qPCR. Bacterial concentration significantly increased between 30, 60 and 90 minutes incubation. Differences in percentage coverage on different polysyrene nanosurfaces (nanopits) were noted varying. This was confirmed by qPCR extractions that showed different bacterial concentrations on different nanopatterns. Titanium nanowire surfaces significantly increased bacterial adhesion (P<0.05). Our study cultured and quantified bacterial biofilm and suggests that by altering nanotopography, bacterial adhesion and therefore biofilm formation can be affected. Specific nanopatterned surfaces may reduce implant infection associated morbidity and mortality. Clearly this is of significant benefit to the patient, the surgeon and the NHS, and may well extend far beyond the realms of orthopaedics

Prosthetic joint infections (PJI) occur infrequently, but they represent the most devastating complication with high morbidity and substantial cost. Staphylococcus aureus and coagulase-negative S. epidermidis are the most common infecting agents associated with PJI. During the past decades, novel materials have been developed to improve osseointegration of implants. Recently has been demonstrated that by using nanosized hydroxyapatite (HA) coatings, since it combines nanoroughness and bone-like chemistry in a synergistic effect, it promotes better osseointegration when compared to uncoated metal implants. In a further step, due to the known bactericidal properties of fluor, the aim of this study is to evaluate the biofilm development on fluorohydroxyapatite (FHA) compared to HA. Coatings were grown on stainless steel substrates by Pulsed Laser Deposition (PLD) technique using fluorohydroxyapatite targets of marine origin. A comprehensive physicochemical characterization of the coatings was performed using SEM, EDS, XPS and XRD. Biological in vitro tests using the pre-osteoblastic cell line (MC3T3-E1) demonstrated the non-cytotoxicity of FHA coatings, the healthy cell proliferation and their osteogenic activity. The S. aureus 15981 (Valle et al.) and S. epidermidis ATCC 35984 strains adherence study was performed introducing each probe in a well of 96-well plate with 200 µl containing 106 colony forming units (CFU/mL) intryptic soy broth supplemented with 1% glucose and was incubated at 37°C 5% CO2 for 24 hours. After incubation, the medium was removed and three washes with 0.9% NaCl sterile saline were performed. The biofilm was disrupted by sonication at 50–60 Hz for 5 min. The CFU/cm2 was estimated by drop plate method. All of the experiments were performed in triplicate. Statistical analysis was performed by non-parametric unilateral Wilcoxon”s test with a level of statistical significance of 0.05. The results showed a significant (p=0.02475) 2.4-fold reduction in S. epidermidis biofilm formation on FHA (logUFC/cm2 = 6.87) compared to HA (logUFC/cm2 = 7.25); and also a significant (p=0.042) 3.7-fold reduction in S. aureus 15981 biofilm formation. In conclusion, according our results FHA is a promising biomaterial that promotes osseointegration and decreases the staphylococcal biofilm that could avoid PJI. Further studies will be necessary

Infections are among the main complications connected to implantation of biomedical devices, having high incidence rate and severe outcome. Since their treatment is challenging, prevention must be preferred. For this reason, solutions capable of exerting suitable efficacy while not causing toxicity and/or development of resistant bacterial strains are needed. To address infection, inorganic antibacterial coatings, and in particular silver coatings, have been extensively studied and used in the clinical practice, but some drawbacks have been evidenced, such as scarce adhesion to the substrate, delamination, or scarce control over silver release. Here, antibacterial nanostructured silver-based thin films are proposed, obtained by a novel plasma-assisted technique, Ionized Jet Deposition (IJD). Coatings are obtained by deposition of metallic silver targets. Films thickness is selected based on previous results aimed at measuring extent and duration of silver release and at evaluating toxicity to host cells (fibroblasts). Here, composition (grazing incidence XRD) and morphology (SEM) of the obtained coatings are characterized for deposition onto different substrates, both metallic and polymeric. For heat sensitive substrates, possible alterations caused by coatings deposition in terms of morphology (SEM) and composition (FT-IR) is assessed. Then, a proof-of-concept study of the capability of these films to inhibit microbial biofilm formation is performed by using two different supports i.e., the Calgary Biofilm Device and the microplates. To the best of the Authors knowledge, this is the first study describing the application of specific anti-biofilm analyses to nanostructured coatings. In particular, anti-biofilm activities are tested against the following pathogenic strains: Escherichia (E.) coli NCTC12923, Staphylococcus (S.) aureus ATCC29213 and S. aureus 86. Among these, the strain 86 is not only pathogen but it also possesses several antibiotic resistance genes, allowing the evaluation of the utilization of nanostructured coatings as an alternative anti-microbial system to face the global threat of antibiotic resistance. Results indicate that films deposited from silver targets are composed of nanosized aggregates of metallic silver, indicating a perfect transfer of composition from the deposition target to the coatings. Results obtained here indicate that the films have significant antibacterial and antibiofilm activity. In addition, they prove that the system can be successfully applied for evaluation of coatings antibacterial efficacy for biomedical applications

The most challenging complications in orthopaedic trauma surgery are fracture-related infections (FRI). The incidence ranges from approximately 1% after closed fractures or joint replacement, to more than 30% in complex open limb fractures. Despite tremendous efforts with prolonged antibiotic therapy and multiple revision surgeries, these complications are associated with considerable rates of recurrent infections as well as permanent functional impairment. The primary aim for the clinician is to prevent infection, because once established, an infection is difficult to eradicate. The main reason for this is biofilm formation on the implanted device, which allows pathogens to protect themselves from host immune response and antimicrobial therapy. In open fractures with a considerable wound contamination and soft- tissue damage, systemically-delivered antibiotics may not reach sufficient local concentrations to eradicate the bacteria. Locally delivered antibiotics can overcome this problem by providing high local concentrations. Currently, several antibiotic loaded biomaterials for local infection prophylaxis and/or treatment are available. In this talk, next to the diagnostic challenges of FRIs, the currently available antimicrobial-loaded biomaterials will be described. Against a backdrop of increasing infection and antimicrobial resistance, the prudent use and availability of such materials will become even more important

Implant infection is an increasing problem in orthopedic surgery, especially due to progressive antibiotic resistance and an aging population with rising numbers of implantations. As a consequence, new strategies for infection prevention are necessary. In the previous study it was hypothesized that laser-structured implant surfaces favor cellular adhesion while hindering bacterial ongrowth and therewith contribute to reduce implant infections. Cuboid titanium implants (0.8 × 0.8 × 12 mm. 3. , n=34) were used. Seventeen were laser-structured by ultra-short pulsed laser ablation to create a spike structure; the others were polished and served as controls. In general anesthesia, implants were inserted in rat tibiae and infected with a S. aureus suspension. During a 21 day postoperative follow-up, daily clinical control was performed. Radiographs were taken at day 14 and day 21. After euthanasia, bacterial load and biofilm formation on the implant surface was evaluated semi quantitatively by confocal laser scanning microscopy and computational acquisition of bacteria and cells by Imaris®-software. Additionally, histology of the surrounding bone was performed. Clinically, no differences were observed between the groups. However, contrary to our hypothesis, bacterial load was increased in the laser-structured implant group although cellular adhesion was even more pronounced. Radiographical and histological evaluations showed increased bone alterations in the group with laser-structured implants compared to the control group. These findings did not confirm prior in vitro studies, where a reduction of bacterial load was found for similar surfaces and demonstrate the necessity of in vivo trials prior to the clinical use of new materials

The aim of the work is to develop innovative antibacterial surface modification treatments for titanium capable to limit the bacterial adhesion and proliferation as weel as the biofilm formation while maintaining an high osteointegrative potential. The goal is to contrast the infections which represent a serius complication related to the use of implantable devices. Introduction. Titanium and titanium alloy are considered the golden standard materials for the applications in contact with bone especially for dental and orthopaedic applications. To extend the implantable component lifetime and increase their clinical performance some surface modifications are required, to promote and speed up the osteointegration process increasing the rate of bone bonding. Unfortunately, among the different complications related to the use of titanium implantable devices the infections represent the most serious, often leading to implant failure and revision. The use of surface modification with specific metal ions represents a promising approach to fight implant-related infections. In particular gallium has recently shown efficacy in the treatment of infections: exploiting the chemical similarity of Ga. 3+. with Fe. 3+. , it can interfere in the iron metabolism for a wide range of bacteria. The aim of this work is to develop and characterise new biocompatible biomimetic treatments with anodic spark deposition (ASD) technique on titanium characterised by antibacterial properties maintaining high osteointegrative potential. Experimental Methods. Three surfaces were developed using titanium grade 2 samples (12 mm diam., 0.5 mm thick): i) SiB-Na: ASD treatment performed in an electrolytic solution containing Ca, P, Si and Na. 1. used as control; ii) GaOss: ASD treatment performed in the SiB-Na solution enriched with gallium nitrate and oxalic acid; iii) GaCis: ASD treatment performed in the SiB-Na solution enriched with with gallium nitrate and L-cysteine. The ASD was carried out in galvano-static condition with a current density of 10 mA/cm. 2. reaching 295V (for SiB-Na, GaCis) and 310V for GaOss. Untreated Ti was used as control. The surface morphology and chemistry were analysed using SEM, EDS and XPS. Ga release in D-PBS was studied up to 21 days using ICP/OES analysis. The structure of the titanium oxide was investigated using XRD while the surface wettability was studied using OCA measurements. The coating mechanical stability was evaluated using scratch test and three-point bending test. Human osteoblastic cells (Saos2) indirect citotoxicity was asessed using Alamar Blue assay. Saos2 morphology and adhesion to the treated surfaces were evaluated using SEM and actin staining. Saos2 viability was assessed up to 21 of cell cultured in direct contact with antibacterial surfaces while the Saos2 alkaline phosphatase activity (ALP) was evaluated up to 21 day as a marker of new bone formation. The antibacterial properties were assessed with S. mutans, S. epidermidis and E. coli bacterial strains even after 21 days of the antibacterial agents release to test the long lasting antibacterial activity. Also the effectiveness in limiting biofilm formation was evaluated against S. epidermidis and A. baumanni biofilm producers. Results and discussion. The developed surfaces showed a microporous morphology without the presence of any delamination. The EDS showed the presence of Ga, Si, P and Ca for GaCis and GaOss. Ga-based treatments revealed a similar concentration of the antimicrobial agent although the Ga released from GaOss was extremely higher than on GaCis. XRD analysis revealed the presence of the anatase cristallographic form which is associated with an higher surface wettability than Ti. The coatings showed a good mechanical stability both after three point bending test and scratch test. The antibacterial surfaces did not show any indirect citotoxicity for Saos2. Also the cell morphology and viability were not negatively affected by the presence of the antibacterial agent: GaOss treatment displayed a stimulating effect on ALP activity of osteoblastic cells than controls. A strong reduction of bacterial adhesion and proliferation for both of the Ga-based treatments especially for GaOss (≈ 40% vs Ti) was observed as well as a long-lasting antibaterial activity. Finally, a significative reduction of S. epidermidis and A. baumanni biofilm production than Ti was observed for GaOss and GaCis treatments. Conclusion. The treatments developed in the present study represent a promising class of antibacterial and osteointegrative coatings for titanium in particular for dental and orthopaedic applications

Nanotopographical cues on Ti surfaces have been shown to elicit different cell responses such as differentiation and selective growth. Bone remodelling is a continuous process requiring specific cues for optimal bone growth and implant fixation. In addition, the prevention of biofilm formation on surgical implants is a major challenge. We have identified nanopatterns on Ti surfaces that would be optimal for both bone remodelling and for reducing risk of bacterial infection. We used primary human osteoblast/osteoclast co-cultures and seeded them on flat Ti and three Ti nanosurfaces with increasing degrees of roughness, manufactured using anodisation under alkaline conditions (for 2, 2.5 and 3 hours). Cell growth and behaviour was assessed by scanning electron microscopy (SEM), immunofluorescence microscopy, histochemistry and quantitative RT-PCR methods. Bacterial growth on the nanowire surfaces was also assessed by confocal microscopy and SEM. From the three surfaces tested, the 2 h nanowire surface supported osteoblast and, to a lesser extent, osteoclast growth and differentiation. Bacterial viability was significantly reduced on the 2h surface. Hence the 2 h surface provided optimal bone remodelling conditions while reducing infection risk, making it a favourable candidate for future implant surfaces. This work was funded by EPSRC grant EP/K034898/1

One of the most common bacteria in orthopaedic prosthetic infections is Staphylococcus Aureus. Infection causes implant failure due to biofilm production. Biofilms are produced by bacteria once they have adhered to a surface. Nanotopography has major effects on cell behaviour. Our research focuses on bacterial adhesion on nanofabricated materials. We hypothesise that surface nanotopography impacts the differential ability of staphylococci species to adhere via altered metabolomics and may reduce orthopaedic implant infection rate. Bacteria were grown and growth conditions optimised. Polystyrene and titanium (Ti) nanosurfaces were studied. The polystyrene surfaces had different nanopit arrays, while the Ti surfaces expressed different nanowire structures. Adhesion analysis was performed using fluorescence imaging, quantitative PCR and bacterial percentage coverage calculations. Further substitution with ‘heavy’ labelled glucose into growth medium allowed for bacterial metabolomic analysis and identification of any up-regulated metabolites and pathways. Our data demonstrates reduced bacterial adhesion on specific nanopit polystyrene arrays, while nanowired titanium showed increased bacterial adhesion following qPCR (P<0.05) and percentage coverage calculations (P<0.001). Further metabolomic analysis identified significantly increased intensity counts of specific metabolites (Pyruvate, Aspartate, Alanine and Carbamoyl aspartate). Our study shows that by altering nanotopography, bacterial adhesion and therefore biofilm formation can be affected. Specific nanopatterned surfaces may reduce implant infection associated morbidity and mortality. The identification of metabolic pathways involved in adhesion may allow for a targeted approach to biofilm eradication in S. aureus. This is of significant benefit to both the patient and the surgeon, and may well extend far beyond the realms of orthopaedics

INTRODUCTION. Staphylococci species account for ∼80 % of osteomyelitis cases. While the most severe infections are caused by Staphylococcus aureus (S. aureus), the clinical significance of coagulase negative Staphylococcus epidermidis (S. epidermidis) infections remain controversial. In general, S. epidermidis was known to be a protective commensal bacterium. However, recent studies have shown that intra-operative low-grade S. epidermidis contamination prevents bone healing. Thus, the purpose of this study is to compare the pathogenic features of S. aureus and S. epidermidis in an established murine model of implant-associated osteomyelitis. METHODS. All animal experiments were performed on IACUC approved protocols. USA300LAC (MRSA) and RP62A(S. epidermidis) were used as prototypic bacterial strains. After sterilization, stainless steel pins were implanted into the tibiae of BALB/c mice (n=5 each) with or without Staphylococci. Mice were euthanized on day 14, and the implants were removed for scanning electron microscopy (SEM). Tibiae were fixed for mCT prior to decalcification for histology. RESULTS. The histology of S. aureus infected tibiae demonstrated massive osteolysis and abscesses formation. In contrast, the histology from S. epidermidis infected tibiae was indistinguishable from uninfected controls. Gross mCT analyses revealed massive bone defects around the infected implant with reactive bone formation only in the S. aureus group. The osteolysis findings were confirmed by quantitative analysis, as the medial hole area of S. aureus infected tibiae (1.67 ± 0.37 mm2) was larger than uninfected (0.15 ± 0.10 mm2) (p < 0.001) and S. epidermidis (0.19 ± 0.14 mm2) (p < 0.001) groups. Consistently, the %biofilm area on the implants of the S. aureus group (39.0 ± 13.7 %) was significantly larger than uninfected (6.3 ± 2.3 %) (p < 0.001) and S. epidermidis (12.9 ± 7.4 %) (p < 0.001). Although the amount of biofilm of S. epidermidis was much smaller than S. aureus, the presence of bacteria on the implant were confirmed by SEM. In addition, the empty lacunae, which is a feature of mature biofilm and evidence of bacterial emigration, were also present on both S. epidermidis and S. aureus infected implants. DISCUSSION. In this study, we confirmed the aggressive pathologic features S. aureus on host bone, soft tissues and biofilm formation. In contrast, we show that S. epidermidis is incapable of inducing osteolysis, reactive bone formation or soft tissue abscesses, even though it colonizes the implant in small biofilms. Collectively, the results support a potential role for S. epidermidis in implant loosening and fracture non-unions, as the bacteria can form small biofilms that could interfere with osseous integration and bone healing. However, future studies are warranted to assess the effects of S. epidermidis biofilm on implant loosening

Adhered bacteria on titanium surfaces are able to decrease its corrosion potential and impedance values at the lowest frequencies. This result points to the detrimental influence of the biofilm on the passive film formed on the surfaces, independently on the surface finishes. Titanium is one of the most used metallic biomaterials for biological and implant applications. The spontaneous formation of a protective passive film around 2–5 nm thick, make titanium unique as a biomaterial for implants. Its composition has been described by a three-layer model: TiO2/Ti2O3/TiO and its stability is ultimately responsible for the success of osseointegrated titanium implants. The cases of breakdown of the protective passive film are associated with highly acidic environments induced by bacterial biofilms and/or inflammatory processes that lead to localized corrosion of titanium and, in extreme cases, implant failure. Bearing in mind that the surface design of a titanium implant is a key element involved in the healing mechanisms at the bone-implant interface, the surface modifications have sought to enhance the biomechanical anchorage of the implant and promote osseointegration at the cell-biomolecular level. However, little attention has been paid to the effects of these surface modifications in the microbiologically induced corrosion (MIC). The aim of this work is to evaluate the potential for MIC of titanium in the short term under viable bacterial cells of Streptococcus mutansas a representative microorganism of oral biofilm considered to be a highly cariogenic pathogen. Discs of 64 mm. 2. surface area of commercially pure titanium, grade 4, were supplied by Biotechnology Institute (BTI, Vitoria, Spain). Four surface treatments were studied: two acid etchings (low roughness, opN and high roughness, opV). In addition, acid etched plus anodic oxidation (opNT). For comparative purposes, two surface finishes have been included: high roughness – corresponding with sandblasting-large grit plus acid (SLA); and, as-machined titanium (mach). The oral strain used for assessing the biofilm formation on the corrosion behavior of Ti surfaces was Streptococus mutansATCC 25175, obtained from the Spanish Type Culture Collection (CECT). The study of MIC from Streptococcus mutanson surfaces of Ti was carried out in an electrochemical cell specifically designed and patented by some of the present authors [1]. A three set up configuration of the electrochemical cell was used in the experiments. The measurement of the corrosion potential and electrochemical impedance was performed at different periods of incubation of bacteria: 2, 7, 15, 21 and 28 days. Out Slight but continuous decrease in the corrosion potential and impedance values at the lowest frequencies indicate the deleterious influence of the biofilm on the passive film formed on the surfaces, independently on the surface finishes. This research suggests that the most appropriate surface modification for the dental implant portion at the bone level would be the acid etched of high roughness (opV) surface