In this prospective study we studied the effect of the inclination angle of the acetabular component on polyethylene wear and component migration in cemented acetabular sockets using radiostereometric analysis. A total of 120 patients received either a cemented Reflection All-Poly ultra-high-molecular-weight polyethylene or a cemented Reflection All-Poly highly cross-linked polyethylene acetabular component, combined with either cobalt–chrome or Oxinium femoral heads. Femoral head penetration and migration of the acetabular component were assessed with repeated radiostereometric analysis for two years. The inclination angle was measured on a standard post-operative anteroposterior pelvic radiograph. Linear regression analysis was used to determine the relationship between the inclination angle and femoral head penetration and migration of the acetabular component. We found no relationship between the inclination angle and penetration of the femoral head at two years’ follow-up (p = 0.9). Similarly, our data failed to reveal any statistically significant correlation between inclination angle and migration of these cemented acetabular components (p = 0.07 to p = 0.9)

Highly cross-linked polyethylene (HXLPE) has decreased wear and revision rates in total hip replacement (THR) at a long-term. However, the effect of HXLPE manufacturing characteristics on femoral head penetration has not been clearly defined yet. We report this single-institution study to investigate the clinical and radiological results of different HXLPE liners in THR. In this retrospective cohort analysis of our prospective database, we identified 904 THRs performed between 2000 and 2013. Seven different HXLPE liner types were assessed: remelted (3), annealed (2), sequentially annealed (1) and vitamin E-infused (1). The linear femoral head penetration rate was measured at six weeks, one year, and annually thereafter, using the Roman Software v1.70 package. Thirty hips were revised for the following reasons: aseptic loosening (11), dislocation (12), periprosthetic femoral fracture (6), and infection (1). No hip was revised for wear or osteolysis. 741 THRs were evaluated for a mean follow-up of 15 years (range, 10 to 20). The mean total penetration 15 years after THR was 0.17 mm in the sequentially annealed, and 0.16 mm in the vitamin E-infused groups, whereas it was 0.26 mm in the melted 95 kGy, 0.27 mm in the melted 5 Mrad and 0.25 mm in the melted 100 kGy groups (p=0.001). From one to 15 years after surgery, the mean wear was 0.206 mm in cups with an acetabular inclination greater than 50º and 0.105 mm in those placed between 35º and 50º (p<0.001). Although HXLPE characteristics can result in a different wear performance in patients undergoing THR at a mean follow-up of 15 years, the clinical results are excellent. The position of the acetabular component can influence on the femoral head penetration of modern HXLPEs. Nevertheless, these patients should continue to be monitored to detect future problems

Aims. The primary outcome was investigating differences in wear, as measured by femoral head penetration, between cross-linked vitamin E-diffused polyethylene (vE-PE) and cross-linked polyethylene (XLPE) acetabular component liners and between 32 and 36 mm head sizes at the ten-year follow-up. Secondary outcomes included acetabular component migration and patient-reported outcome measures (PROMs) such as the EuroQol five-dimension questionnaire, 36-Item Short-Form Health Survey, Harris Hip Score, and University of California, Los Angeles Activity Scale (UCLA). Methods. A single-blinded, multi-arm, 2 × 2 factorial randomized controlled trial was undertaken. Patients were recruited between May 2009 and April 2011. Radiostereometric analyses (RSAs) were performed from baseline to ten years. Of the 220 eligible patients, 116 underwent randomization, and 82 remained at the ten-year follow-up. Eligible patients were randomized into one of four interventions: vE-PE acetabular liner with either 32 or 36 mm femoral head, and XLPE acetabular liner with either 32 or 36 mm femoral head. Parameters were otherwise identical except for acetabular liner material and femoral head size. Results. A total of 116 patients participated, of whom 77 were male. The median ages of the vE-PE 32 mm and 36 mm groups were 65 (interquartile range (IQR) 57 to 67) and 63 years (IQR 56 to 66), respectively, and of the XLPE 32 mm and 36 mm groups were 64 (IQR 58 to 66) and 61 years (IQR 54 to 66), respectively. Mean total head penetration was significantly lower into vE-PE acetabular liner groups than into XLPE acetabular liner groups (-0.219 mm (95% confidence interval -0.348 to -0.090); p = 0.001). There were no differences in wear according to head size, acetabular component migration, or PROMs, except for UCLA. There were no cases of aseptic loosening or failures requiring revision at long-term follow-up. Conclusion. Significantly lower wear was observed in vE-PE acetabular liners than in XLPE acetabular liners. No difference in wear was observed between different head size or PROMs except for the UCLA at ten years. Cite this article: Bone Joint J 2023;105-B(10):1052–1059

Aims. The most frequent indication for revision surgery in total hip arthroplasty (THA) is aseptic loosening. Aseptic loosening is associated with polyethylene liner wear, and wear may be reduced by using vitamin E-doped liners. The primary objective of this study was to compare proximal femoral head penetration into the liner between a) two cross-linked polyethylene (XLPE) liners (vitamin E-doped (vE-PE)) versus standard XLPE liners, and b) two modular femoral head diameters (32 mm and 36 mm). Methods. Patients scheduled for a THA were randomized to receive a vE-PE or XLPE liner with a 32 mm or 36 mm metal head (four intervention groups in a 2 × 2 factorial design). Head penetration and acetabular component migration were measured using radiostereometric analysis at baseline, three, 12, 24, and 60 months postoperatively. The Harris Hip Score, University of California, Los Angeles (UCLA) Activity Score, EuroQol five-dimension questionnaire (EQ-5D), and 36-Item Short-Form Health Survey questionnaire (SF-36) were assessed at baseline, three, 12, 36, and 60 months. Results. Of 220 screened patients, 127 were included in this study. In all, 116 received the allocated intervention, and 94 had their results analyzed at five years. Head penetration was similar between liner materials and head sizes at five years, vE-PE versus XLPE was -0.084 mm (95% confidence interval (CI) -0.173 to 0.005; p = 0.064), and 32 mm versus 36 mm was -0.020 mm (95% CI -0.110 to 0.071; p = 0.671), respectively. No differences were found in acetabular component migration or in the patient-reported outcome measures. Conclusion. No significant difference in head penetration was found at five years between vE-PE and XLPE liners, nor between 32 mm and 36 mm heads. Cite this article: Bone Joint J 2020;102-B(10):1303–1310

We carried out a prospective randomised study designed to compare the penetration rate of acetabular polyethylene inserts of identical design but different levels of cross-linking at a minimum of four years follow-up. A total of 102 patients (102 hips) were randomised to receive either highly cross-linked Durasul, or contemporary Sulene polyethylene inserts at total hip replacement. A single blinded observer used the Martell system to assess penetration of the femoral head. At a mean follow-up of 4.9 years (4.2 to 6.1) the mean femoral head penetration rate was 0.025 mm/year (. sd. 0.128) in the Durasul group compared with 0.106 mm/year (. sd. 0.109) in the Sulene group (Mann-Whitney test, p = 0.0027). The mean volumetric penetration rate was 29.24 mm. 3. /year (. sd. 44.08) in the Durasul group compared with 53.32 mm. 3. /year (. sd. 48.68) in the Sulene group. The yearly volumetric penetration rate was 55% lower in the Durasul group (Mann-Whitney test, p = 0.0058). Longer term results are needed to investigate whether less osteolysis will occur

Introduction. Dual-mobility (DM) articulations may be useful for patients at increased risk for instability in primary and revision THA. While DM articulations are becoming increasingly popular, its routine use in primary THA is more uncertain. Even less is known about femoral head penetration in DM designs manufactured with highly cross-linked polyethylene infused with Vitamin E (E-HXLPE). The purpose of this study was to evaluate the early clinical results and femoral head penetration rates of primary THA implanted with DM E-HXLPE. Methods. Between 2012 and 2017, 105 primary DM THAs were performed using a one-piece acetabular shell, 28mm ceramic head, coupled with an E-HXLPE outer bearing via a standard posterior approach. Three patients refused follow-up after six months. 102 hips (92 patients) were available for review. The diagnosis was 99% OA. Average age was 65.7 years (33–90 years). 56% of patients were female. The most common femoral head size was 50mm (range, 44–60mm). The average thickness of the E-HXLPE outer bearing was 22.7mm (range, 16–32mm). Patients were followed at two months (baseline radiograph), six months, one, three, five, and seven years. Harris hip scores (HHS), UCLA activity score, and femoral head penetration (Martell method) were obtained at each visit beyond two months. Follow-up averaged 3 years (range, 1–7 years). Results. Average HHS improved from 43 to 95 points (50–100) at final follow-up. Similarly, average Harris pain scores improved from 10 to 42 points (20–44) with 78% of patients pain free and one patient, each, reporting groin and thigh pain (1%). Average UCLA activity scores was 8.1 (range, 5–10). There were no dislocations, revisions, or loose cups. The average femoral head penetration (including bedding-in) was 0.25mm/yr (s.d. 0.2mm/yr) at seven years. Discussion/Conclusion. The theoretical benefits of DM designs in diminishing wear include a smaller inner head, lower frictional torque with motion, less micro-separation, and less wear with impingement. The early clinical results of primary DM THA are promising. Although the early femoral head penetration using DM E-HXLPE appears to be less than other DM designs, it was greater than that of conventional THA using HXLPE and E-HXLPE inserts. The additional outer bearing surface, while affording additional stability, may actually enhance polyethylene creep and wear. For any tables or figures, please contact the authors directly

We have compared four computer-assisted methods to measure penetration of the femoral head into the acetabular component in total hip replacement. These were the Martell Hip Analysis suite 7.14, Rogan HyperOrtho, Rogan View Pro-X and Roman v1.70. The images used for the investigation comprised 24 anteroposterior digital radiographs and 24 conventional acetate radiographs which were scanned to provide digital images. These radiographs were acquired from 24 patients with an uncemented total hip replacement with a follow-up of approximately eight years (mean 8.1; 6.3 to 9.1). Each image was measured twice by two blinded observers. The mean annual rates of penetration of the femoral head measured in the eight-year single image analysis were: Martell, 0.24 (SD 0.19); HyperOrtho, 0.12 (SD 0.08); View Pro-X, 0.12 (SD 0.06); Roman, 0.12 (SD 0.07). In paired analysis of the six-month and eight-year radiographs: Martell, 0.35 (SD 0.22); HyperOrtho, 0.15 (SD 0.13); View Pro-X, 0.11 (SD 0.06); Roman, 0.11 (SD 0.07). The intra- and inter-observer variability for the paired analysis was best for View Pro-X and Roman software, with intraclass correlations of 0.97, 0.87 and 0.96, 0.87, respectively, and worst for HyperOrtho and Martell, with intraclass correlations of 0.46, 0.13 and 0.33, 0.39, respectively. The Roman method proved the most precise and the most easy to use in clinical practice and the software is available free of charge. The Martell method showed the lowest precision, indicating a problem with its edge detection algorithm on digital images

Aims. A significant reduction in wear at five and ten years was previously reported when comparing Durasul highly cross-linked polyethylene with nitrogen-sterilized Sulene polyethylene in total hip arthroplasty (THA). We investigated whether the improvement observed at the earlier follow-up continued, resulting in decreased osteolysis and revision surgery rates over the second decade. Methods. Between January 1999 and December 2001, 90 patients underwent surgery using the same acetabular and femoral components with a 28 mm metallic femoral head and either a Durasul or Sulene liner. A total of 66 hips of this prospective randomized study were available for a minimum follow-up of 20 years. The linear femoral head penetration rate was measured at six weeks, one year, and annually thereafter, using the Dorr method on digitized radiographs with a software package. Results. In the Durasul group, no patients underwent revision due to loosening or showed radiological evidence of osteolysis. In the Sulene group, four patients (four hips) were revised due to femoral component loosening. The 20-year cumulative failure incidence in the presence of the competing event of death for revision surgery was 4.5% (95% confidence interval (CI) 0.8 to 13.6) in the Durasul group, and 8.9% (95% CI 2.8 to 19.5) in the Sulene group. The mean wear one year after surgery was 0.09 mm (SD 0.007) in the Durasul group and 0.24 (SD 0.015) in the Sulene group (p < 0.001). From one to 20 years after surgery, the mean total penetration was 0.32 mm (SD 0.045) in the Durasul group and 1.07 mm (SD 0.13) in the Sulene group (p < 0.001). Mean femoral head penetration at 20 years was approximately 70.0% less in the Durasul group than the Sulene group. Conclusion. The significant reduction in femoral head penetration obtained with the Durasul compared with Sulene in uncemented THA resulted in lower osteolysis and revision rates after 20 years. Cite this article: Bone Joint J 2022;104-B(9):1032–1038

Aims. Radiostereometric analysis (RSA) studies of vitamin E-doped, highly crosslinked polyethylene (VEPE) liners show low head penetration rates in cementless acetabular components. There is, however, currently no data on cemented VEPE acetabular components in total hip arthroplasty (THA). The aim of this study was to evaluate the safety of a new cemented VEPE component, compared with a conventional polyethylene (PE) component regarding migration, head penetration, and clinical results. Patients and Methods. We enrolled 42 patients (21 male, 21 female) with osteoarthritis and a mean age of 67 years (. sd. 5), in a double-blinded, noninferiority, randomized controlled trial. The subjects were randomized in a 1:1 ratio to receive a reverse hybrid THA with a cemented component of either argon-gas gamma-sterilized PE component (controls) or VEPE, with identical geometry. The primary endpoint was proximal implant migration of the component at two years postoperatively measured with RSA. Secondary endpoints included total migration of the component, penetration of the femoral head into the component, and patient-reported outcome measurements. Results. In total, 19 control implants and 18 implants in the VEPE group were analyzed for the primary endpoint. We found a continuous proximal migration of the component in the VEPE group that was significantly higher with a difference at two years of a mean 0.21 mm (95% confidence interval (CI) 0.05 to 0.37; p = 0.013). The total migration was also significantly higher in the VEPE group, but femoral head penetration was lower. We found no difference in clinical outcomes between the groups. Conclusion. At two years, this cemented VEPE component, although having a low head penetration and excellent clinical results, failed to meet noninferiority compared with the conventional implant by a proximal migration above the proposed safety threshold of RSA. The early proximal migration pattern of the VEPE component is a reason for continued monitoring, although a specific threshold for proximal migration and risk for later failure cannot be defined and needs further study. Cite this article: Bone Joint J 2019;101-B:1192–1198

Aims. Radiostereometric analysis (RSA) is the most accurate radiological method to measure in vivo wear of highly cross-linked polyethylene (XLPE) acetabular components. We have previously reported very low wear rates for a sequentially irradiated and annealed X3 XLPE liner (Stryker Orthopaedics, USA) when used in conjunction with a 32 mm femoral heads at ten-year follow-up. Only two studies have reported the long-term wear rate of X3 liners used in conjunction with larger heads using plain radiographs which have poor sensitivity. The aim of this study was to measure the ten-year wear of thin X3 XLPE liners against larger 36 or 40 mm articulations with RSA. Methods. We prospectively reviewed 19 patients who underwent primary cementless THA with the XLPE acetabular liner (X3) and a 36 or 40 mm femoral head with a resultant liner thickness of at least 5.8 mm. RSA radiographs at one week, six months, and one, two, five, and ten years postoperatively and femoral head penetration within the acetabular component were measured with UmRSA software. Of the initial 19 patients, 12 were available at the ten-year time point. Results. The median proximal, 2D, and 3D wear rates calculated between one and ten years were all less than 0.005 mm/year, with no patient recording a proximal wear rate of more than 0.021 mm/year. Importantly, there was no increase in the wear rate between five and ten years. Conclusion. The very low wear rate of X3 XLPE liners with larger articulations remains encouraging for the future clinical performance of this material. Cite this article: Bone Jt Open 2023;4(11):839–845

Aims. We aimed to investigate if the use of the largest possible cobalt-chromium head articulating with polyethylene acetabular inserts would increase the in vivo wear rate in total hip arthroplasty. Methods. In a single-blinded randomized controlled trial, 96 patients (43 females), at a median age of 63 years (interquartile range (IQR) 57 to 69), were allocated to receive either the largest possible modular femoral head (36 mm to 44 mm) in the thinnest possible insert or a standard 32 mm head. All patients received a vitamin E-doped cross-linked polyethylene insert and a cobalt-chromium head. The primary outcome was proximal head penetration measured with radiostereometric analysis (RSA) at two years. Secondary outcomes were volumetric wear, periacetabular radiolucencies, and patient-reported outcomes. Results. At two years, 44 patients in each group were available for RSA assessment. The median total two-year proximal head penetration was -0.02 mm (IQR -0.09 to 0.07; p = 0.548) for the largest possible head and -0.01 mm (IQR -0.07 to 0.10; p = 0.525) for 32 mm heads. Their difference was not statistically significant (p = 0.323). Neither group demonstrated a bedding-in period. The median steady-state volumetric wear rates were 6.1 mm. 3. /year (IQR -59 to 57) and 3.5 mm. 3. /year (-21 to 34) respectively, and did not differ between the groups (p = 0.848). There were no statistically significant differences in periacetabular radiolucencies or patient-reported outcomes. Conclusion. The use of the largest possible metal head did not increase vitamin E-doped cross-linked polyethylene wear compared with 32 mm heads at two years. Linear wear was negligible and volumetric wear rates were very low in both head size groups. There was a tendency towards higher values of volumetric wear in large heads that warrants longer-term evaluation before any definite conclusions about the association between head size and wear can be drawn. Cite this article: Bone Joint J 2021;103-B(7):1206–1214

Aims. This paper describes the methodology, validation and reliability of a new computer-assisted method which uses models of the patient’s bones and the components to measure their migration and polyethylene wear from radiographs after total hip arthroplasty (THA). Materials and Methods. Models of the patient’s acetabular and femoral component obtained from the manufacturer and models of the patient’s pelvis and femur built from a single computed tomography (CT) scan, are used by a computer program to measure the migration of the components and the penetration of the femoral head from anteroposterior and lateral radiographs taken at follow-up visits. The program simulates the radiographic setup and matches the position and orientation of the models to outlines of the pelvis, the acetabular and femoral component, and femur on radiographs. Changes in position and orientation reflect the migration of the components and the penetration of the femoral head. Validation was performed using radiographs of phantoms simulating known migration and penetration, and the clinical feasibility of measuring migration was assessed in two patients. Results. Migration of the acetabular and femoral components can be measured with limits of agreement (LOA) of 0.37 mm and 0.33 mm, respectively. Penetration of the femoral head can be measured with LOA of 0.161 mm. Conclusion. The migration of components and polyethylene wear can be measured without needing specialised radiographs. Accurate measurement may allow earlier prediction of failure after THA. Cite this article: Bone Joint J 2017;99-B:1290–7

The purpose of this study was to precisely measure the 10-year polyethylene wear rate of primary total hips using Radiostereometric analysis (RSA) comparing Oxidized Zirconium (OxZi) to cobalt chrome (CoCr) femoral heads articulating with highly cross-linked polyethylene (XLPE). RSA was performed on 46 patients who underwent total hip arthroplasty − 23 who received OxZi femoral heads and 23 who received CoCr heads in combination with XLPE at a minimum of 10 years follow-up. All patients had identical THR systems implanted except for the femoral head utilized. The Centre Index method was utilised to assess total wear rates (from index surgery until final evaluation) using a dedicated RSA Software program (UmRSA Digital Measure v.2.2.1). In addition, the Martell technique was used to subtract head penetration occurring in the first 1–2 years (i.e. bedding-in phase) to allow calculation of the ‘steady state’ wear rates. There were no significant differences in demographics (i.e age, BMI, gender) between the groups. The average time from surgery of the RSA examinations was 11.7 and 12.6 years for the CoCr and OxZi groups respectively. Using the Centre Index Method to calculate total head penetration, wear rates were slightly higher in the OxZi group (0.048 +/− 0.021mm/year) compared to the CoCr group (0.035 +/− 0.017mm/year) with no statistical difference between the groups (p= 0.02). After correction for the bedding-in period, there was no statistically significant difference in mean ‘steady-state’ wear rate between OxZi (0.031 +/− 0.021mm/year) and CoCr (0.024 +/− 0.019mm/year) at 10 year follow up (p= 0.24). A comparison of preoperative and postoperative SF12, HHS, and WOMAC scores showed no statistical difference between the groups. RSA demonstrated the 10 year in-vivo wear rates of both bearing combinations to be well below the threshold for osteolysis. There was no significant difference between either the total or ‘steady-state’ wear rates of the OxZi and CoCr groups at 10 years

Vitamin E-doped cross-linked polyethylene (VEPE) has encouraged the use of larger heads in thinner liners in total hip arthroplasty (THA). However, there are concerns about wear and mechanical failure of the thin liner, especially when metal heads are used. The aim of this randomized controlled trial was to investigate if the use of a large metal head in a thin VEPE liner would increase polyethylene wear compared with a standard 32-mm metal head and to compare periacetabular radiolucencies and patient-reported outcomes in THA. 96 candidates for uncemented THA were randomly allocated to either the largest possible metal head (36–44 mm) that could be fitted in the thinnest available VEPE liner (intervention group) or a standard 32-mm metal head (control group). The primary outcome was proximal head penetration (PHP) measured with model-based radiostereometric analysis (RSA). Secondary outcomes were periacetabular radiolucencies and patient-reported outcomes. The mid-term results of the trial at 5 years are presented. Median total PHP (interquartile range) was -0.04 mm (−0.12 to 0.02) in the intervention group and -0.03 mm (=0.14 to 0.05) in the control group (p=0.691). The rates of periacetabular radiolucencies were 1/44 and 4/42 (p=0.197), respectively. Patient-reported hip function and health-related quality of life did not differ between the groups, but participants in the intervention group reported a higher level of activity (median UCLA rank 7 vs 6, p=0.020). There were 5 revisions caused by dislocations (2), periprosthetic fracture (1), stem subsidence (1), or iliopsoas impingement (1). Large metal heads in thin VEPE liners did not increase liner wear and were not associated with liner failure 5 years after THA

Aims. We previously reported the long-term results of the cementless Duraloc-Profile total hip arthroplasty (THA) system in a 12- to 15-year follow-up study. In this paper, we provide an update on the clinical and radiological results of a previously reported cohort of patients at 23 to 26 years´ follow-up. Patients and Methods. Of the 99 original patients (111 hips), 73 patients (82 hips) with a mean age of 56.8 years (21 to 70) were available for clinical and radiological study at a minimum follow-up of 23 years. There were 40 female patients (44 hips) and 33 male patients (38 hips). Results. All acetabular and femoral components were well fixed and showed signs of bone ingrowth. Nine acetabular components were revised due to wear-osteolysis-related problems and four due to late dislocation. The probability of not having component revision at 25 years was 83.2% (95% confidence interval (CI) 74.5 to 91.8; number at risk 41). Acetabular osteolysis was observed in ten hips. The mean femoral head penetration was 1.52 mm (. sd. 0.8) at 15 years and 1.92 mm (. sd. 1.2) at 25 years. Receiver operating characteristic (ROC) analysis revealed that mean femoral penetration with a value of 0.11 mm/year or more was associated with the appearance of osteolysis. The 25-year Kaplan–Meier survival with different endpoints was 89.9% for acetabular osteolysis (95% CI 83.3 to 96.5), 92.1% for proximal femoral osteolysis (95% CI 86.1 to 98.2), and 75.5% for femoral osteopenia (95% CI 66.5 to 84.5). Conclusion. The Duraloc-Profile THA system showed excellent long-term bone fixation. Nevertheless, monitoring is recommended in order to detect wear and late dislocations in this population that was relatively young at the time of surgery. Cite this article: Bone Joint J 2019;101-B:378–385

Dual Mobility (DM) Total Hip Replacements (THRs) were introduced to reduce dislocation risk, which is the most common cause of early revision. The in-vivo mechanics of these implants is not well understood, despite their increased use in both elective and trauma settings. Therefore, the aim of this study was to comprehensively assess retrieved DM polyethylene liners for signs of damage using visual inspection and semi-quantitative geometric assessment techniques. Retrieved DM liners (n=20) were visually inspected for the presence of seven established modes of polyethylene damage. If embedded debris was identified on the external surface, its material composition was characterised using energy-dispersive x-ray analysis (EDX). Additionally, each liner was geometrically assessed for signs of wear/deformation using a validated methodology. Visual inspection of the liners revealed that scratching and pitting were the most common damage modes on either surface. Burnishing was observed on 50% and 15% of the internal and external surfaces, respectively. In addition, embedded debris was identified on 25% of the internal and 65% of the external surfaces. EDX analysis of the debris identified several materials including iron, titanium, cobalt-chrome, and tantalum. Geometric analysis demonstrated highly variable damage patterns across the liners. The results of this study provide insight into the in-vivo mechanics of DM bearings. For example, the results suggest that the internal bearing (i.e., between the head and liner) acts as the primary articulation site for DM-THRs as evidenced by a higher incidence of burnishing and larger, more concentrated regions of penetration across the liners’ internal surfaces. Furthermore, circumferential, and crescent-shaped damage patterns were identified on the articulating surfaces of the liners thus providing evidence that these components can rotate within the acetabular shell with varying degrees of mobility. The mechanics of DM bearings are complex and may be influenced by several factors (e.g., soft tissue fibrosis, patient activities) and thus further investigation is warranted. Finally, the results of this study suggest that DM liners may be susceptible to ex-vivo surface damage and thus caution is advised when handling and/or assessing these types of components

The significance of periprosthetic fractures about a total hip arthroplasty (THA) is becoming increasingly important. Recent studies have demonstrated post-operative periprosthetic fracture rates are higher amongst cemented polished taper slip (PTS) stem designs compared to collared cementless (CC) designs. However, in the National Joint Registry, the rate of intra-operative periprosthetic femoral fractures (IOPFF) with cementless implant systems remains higher (0.87% vs 0.42%. p <0.001) potentially leading to more post-operative complications. This study identifies the incidence of IOPFF, the fracture subtype and compares functional outcomes and revision rates of CC femoral implants with an IOPFF to CC stems and PTS stems without a fracture. 5376 consecutive CC stem THA, carried out through a posterior approach were reviewed for IOPFF. Each fracture was subdivided into calcar fracture, greater trochanter (GT) fracture or shaft fracture. 1:1:1 matched analysis was carried out to compare Oxford scores at one year. Matching criteria included; sex (exact), age (± 1 year), American Society of Anaesthesiologists (ASA) grade (exact), and date of surgery (± 6 months). Electronic records were used to review revision rates. Following review of the CC stems, 44 (0.8%) were identified as having an IOPFF. Of these 30 (0.6%) were calcar fractures, 11 (0.2%) GT fractures and 3 (0.06%) were shaft fractures. There were no shaft penetrations. Overall, no significant difference in Oxford scores at one year were observed when comparing the CC IOPFF, CC non-IOPFF and PTS groups. There were no CC stems revised for any reason with either a calcar fracture or trochanteric fracture within the period of 8 years follow-up. IOPFF do occur more frequently in cementless systems than cemented. The majority are calcar and GT fractures. These fractures, when identified and managed intra-operatively, do not have worse functional outcomes or revision rates compared to matched non-IOPFF cases

It has been suggested that the wear of ultra-high molecular weight polyethylene (UHMWPE) in total hip replacement is substantially reduced when the femoral head is ceramic rather than metal. However, studies of alumina and zirconia ceramic femoral heads on the penetration of an UHMWPE liner in vivo have given conflicting results. The purpose of this study was to examine the surface characteristics of 30 alumina and 24 zirconia ceramic femoral heads and to identify any phase transformation in the zirconia heads. We also studied the penetration rate of alumina and zirconia heads into contemporary UHMWPE liners. The alumina heads had been implanted for a mean of 11.3 years (8.1 to 16.2) and zirconia heads for a mean of 9.8 years (7.5 to 15). The mean surface roughness values of the explanted alumina heads (Ra 40.12 nm and Rpm 578.34 nm) were similar to those for the explanted zirconia heads (Ra 36.21 nm and Rpm 607.34 nm). The mean value of the monoclinic phase of two control zirconia heads was 1% (0.8% to 1.5%) and 1.2% (0.9% to 1.3%), respectively. The mean value of the monoclinic phase of 24 explanted zirconia heads was 7.3% (1% to 26%). In the alumina group, the mean linear penetration rate of the UMWPE liner was 0.10 mm/yr (0.09 to 0.12) in hips with low Ra and Rpm values (13.22 nm and 85.91 nm, respectively). The mean linear penetration rate of the UHMWPE liner was 0.13 mm/yr (0.07 to 0.23) in hips with high Ra and Rpm values (198.72 nm and 1329 nm, respectively). This difference was significant (p = 0.041). In the zirconia head group, the mean linear penetration rate of the UHMWPE liner was 0.09 mm/yr (0.07 to 0.14) in hips with low Ra and Rpm values (12.78 nm and 92.99 nm, respectively). The mean linear penetration rate of the UHMWPE liner was 0.12 mm/yr (0.08 to 0.22) in hips with high Ra and Rpm values (199.21 nm and 1381 nm, respectively). This difference was significant (p = 0.039). The explanted zirconia heads which had a minimal phase transformation had similar surface roughness and a similar penetration rate of UHMWPE liner as the explanted alumina head

The creep and wear behaviour of highly cross-linked polyethylene and standard polyethylene liners were examined in a prospective, double-blind randomised, controlled trial using radiostereometric analysis. We randomised 54 patients to receive hip replacements with either highly cross-linked polyethylene or standard liners and determined the three-dimensional penetration of the liners over three years. After three years the mean total penetration was 0.35 mm (SD 0.14) for the highly cross-linked polyethylene group and 0.45 mm (SD 0.19) for the standard group. The difference was statistically significant (p = 0.0184). From the pattern of penetration it was possible to discriminate creep from wear. Most (95%) of the creep occurred within six months of implantation and nearly all within the first year. There was no difference in the mean degree of creep between the two types of polyethylene (highly cross-linked polyethylene 0.26 mm, SD 0.17; standard 0.27 mm, SD 0.2; p = 0.83). There was, however, a significant difference (p = 0.012) in the mean wear rate (highly cross-linked polyethylene 0.03 mm/yr, SD 0.06; standard 0.07 mm/yr, SD 0.05). Creep and wear occurred in significantly different directions (p = 0.01); creep was predominantly proximal whereas wear was anterior, proximal and medial. We conclude that penetration in the first six months is creep-dominated, but after one year virtually all penetration is due to wear. Highly cross-linked polyethylene has a 60% lower rate of wear than standard polyethylene and therefore will probably perform better in the long term

Aims. Our aim in this study was to describe a continuing review of 11 total hip arthroplasties using 22.225 mm Alumina ceramic femoral heads on a Charnley flanged femoral component, articulating against a silane crosslinked polyethylene. Patients and Methods. Nine patients (11 THAs) were reviewed at a mean of 27.5 years (26 to 28) post-operatively. Outcome was assessed using the d’Aubigne and Postel, and Charnley scores and penetration was recorded on radiographs. In addition, the oxidation of a 29-year-old shelf-aged acetabular component was analysed. Results. The mean clinical outcome scores remained excellent at final follow-up. The mean total penetration remained 0.41 mm (0.40 to 0.41). There was no radiographic evidence of acetabular or femoral loosening or osteolysis. There was negligible oxidation in the shelf-aged sample despite gamma irradiation and storage in air. Conclusion. These results highlight the long-term stability and durability of this type of crosslinked, antioxidant containing polyethylene when used in combination with a small diameter alumina ceramic femoral head. Cite this article: Bone Joint J 2017;99-B:1286–9