Abstract
Highly cross-linked polyethylene (HXLPE) has decreased wear and revision rates in total hip replacement (THR) at a long-term. However, the effect of HXLPE manufacturing characteristics on femoral head penetration has not been clearly defined yet. We report this single-institution study to investigate the clinical and radiological results of different HXLPE liners in THR.
In this retrospective cohort analysis of our prospective database, we identified 904 THRs performed between 2000 and 2013. Seven different HXLPE liner types were assessed: remelted (3), annealed (2), sequentially annealed (1) and vitamin E-infused (1). The linear femoral head penetration rate was measured at six weeks, one year, and annually thereafter, using the Roman Software v1.70 package.
Thirty hips were revised for the following reasons: aseptic loosening (11), dislocation (12), periprosthetic femoral fracture (6), and infection (1). No hip was revised for wear or osteolysis. 741 THRs were evaluated for a mean follow-up of 15 years (range, 10 to 20). The mean total penetration 15 years after THR was 0.17 mm in the sequentially annealed, and 0.16 mm in the vitamin E-infused groups, whereas it was 0.26 mm in the melted 95 kGy, 0.27 mm in the melted 5 Mrad and 0.25 mm in the melted 100 kGy groups (p=0.001). From one to 15 years after surgery, the mean wear was 0.206 mm in cups with an acetabular inclination greater than 50º and 0.105 mm in those placed between 35º and 50º (p<0.001).
Although HXLPE characteristics can result in a different wear performance in patients undergoing THR at a mean follow-up of 15 years, the clinical results are excellent. The position of the acetabular component can influence on the femoral head penetration of modern HXLPEs. Nevertheless, these patients should continue to be monitored to detect future problems.