Osteoarthritis (OA) is a degenerative disease resulting from progressive joint destruction caused by many factors. Its pathogenesis is complex and has not been elucidated to date. Advanced glycation end products (AGEs) are a series of irreversible and stable macromolecular complexes formed by reducing sugar with protein, lipid, and nucleic acid through a non-enzymatic glycosylation reaction (Maillard reaction). They are an important indicator of the degree of ageing. Currently, it is considered that AGEs accumulation in vivo is a molecular basis of age-induced OA, and AGEs production and accumulation in vivo is one of the important reasons for the induction and acceleration of the pathological changes of OA. In recent years, it has been found that AGEs are involved in a variety of pathological processes of OA, including extracellular matrix degradation, chondrocyte apoptosis, and autophagy. Clearly, AGEs play an important role in regulating the expression of OA-related genes and maintaining the chondrocyte phenotype and the stability of the intra-articular environment. This article reviews the latest research results of AGEs in a variety of pathological processes of OA, to provide a new direction for the study of OA pathogenesis and a new target for prevention and treatment.

Cite this article: Bone Joint Res 2022;11(5):292–300.

Introduction. Highly crosslinked, ultra-high molecular weight polyethylene (HXLPE) acetabular liners inherently have a risk of fatigue failure associated with femoral neck impingement. One of the potential reasons for liner failure was reported as crosslinking formulations of polyethylene, increasing the brittleness and structural rigidity. In addition, the acetabular component designs greatly affect the mechanical loading scenario, such as the offset (lateralized) liners with protruded rim above the metal shells, which commonly induce a weak resistance to rim impingement. The purpose of the present study was to compare the influence of the liner offset length on the impingement resistance in the annealed (first generation) and vitamin E-blended (second-generation) HXLPE liners with a commercial design. Materials and Methods. The materials tested were the 95-kGy irradiated annealed GUR1020, and the 300-kGy irradiated vitamin E-blended GUR1050 HXLPE offset liners, which were referred to as “20_95” and “50E_300”, respectively. These liners had 2, 3, 4-mm rim offset, 2.45-mm rim thickness, and 36-mm internal diameter. Their rims were protruded above the metal rim at 2, 3, 4mm. Rim impingement testing was performed using an electrodynamic axial-torsional machine. The cyclic impingement load of 25–250N was applied on the rims through the necks of the femoral stems at 1Hz. The rotational torque was simultaneously generated by swinging the stem necks on the rims at 1Hz and its rotational angle was set at the range of 0–10˚. The percent crystallinity was analyzed on the as-received (intact) and impinged HXLPE acetabular rims by confocal Raman microspectroscopy. Results. The number of cycles to failure was dependent on the offset length (2, 3, 4-mm) in 20_95 and 50E_300 liners. Our results showed that the shorter the rim offset, the shorter the number of cycles to failure. In both HXLPEs, accumulation of impingement damages significantly decreased crystallinity in their near-surfaces, indicating the occurrence of crystallographic breakdown. In each offset length tested, the fracture always occurred much earlier in 50E_300 than 20_95. However, the magnitudes of the microstructural changes at the time of failure were much less in 50E_300 than 20_95. Conclusions. Although it is known that vitamin E blend into HXLPE can improve the fatigue resistance of HXLPE, the impingement resistance of 50E_300 was lower than vitamin-E free 20_95, indicating a larger negative contribution of high-dose radiation (300kGy) over a positive contribution of the vitamin E blend in 50E_300. Our results implied that the reduction of the protruded rim length in the offset liners may increase the neck-rim contact stresses at the time of impingement, causing a decrease in the fatigue durability. Therefore, if HXLPE offset liner is used, surgeons should take special care in maximizing the volume of the protruded lip section

Objectives. Modular junctions are ubiquitous in contemporary hip arthroplasty. The head-trunnion junction is implicated in the failure of large diameter metal-on-metal (MoM) hips which are the currently the topic of one the largest legal actions in the history of orthopaedics (estimated costs are stated to exceed $4 billion). Several factors are known to influence the strength of these press-fit modular connections. However, the influence of different head sizes has not previously been investigated. The aim of the study was to establish whether the choice of head size influences the initial strength of the trunnion-head connection. Materials and Methods. Ti-6Al-4V trunnions (n = 60) and two different sizes of cobalt-chromium (Co-Cr) heads (28 mm and 36 mm; 30 of each size) were used in the study. Three different levels of assembly force were considered: 4 kN; 5 kN; and 6 kN (n = 10 each). The strength of the press-fit connection was subsequently evaluated by measuring the pull-off force required to break the connection. The statistical differences in pull-off force were examined using a Kruskal–Wallis test and two-sample Mann–Whitney U test. Finite element and analytical models were developed to understand the reasons for the experimentally observed differences. Results. 36 mm diameter heads had significantly lower pull-off forces than 28 mm heads when impacted at 4 kN and 5 kN (p < 0.001; p < 0.001), but not at 6 kN (p = 0.21). Mean pull-off forces at 4 kN and 5 kN impaction forces were approximately 20% larger for 28 mm heads compared with 36 mm heads. Finite element and analytical models demonstrate that the differences in pull-off strength can be explained by differences in structural rigidity and the resulting interface pressures. Conclusion. This is the first study to show that 36 mm Co-Cr heads have up to 20% lower pull-off connection strength compared with 28 mm heads for equivalent assembly forces. This effect is likely to play a role in the high failure rates of large diameter MoM hips. Cite this article: A. R. MacLeod, N. P. T. Sullivan, M. R. Whitehouse, H. S. Gill. Large-diameter total hip arthroplasty modular heads require greater assembly forces for initial stability. Bone Joint Res 2016;5:338–346. DOI: 10.1302/2046-3758.58.BJR-2016-0044.R1

Introduction. The majority of primary total hip arthroplasty (THA) procedures performed throughout the world use modular junctions, such as the trunnion-head interface; however, the failure of these press-fit junctions is currently a key issue that may be exacerbated by the use of large diameter heads. Several factors are known to influence the strength of the initial connection, however, the influence of different head sizes has not previously been investigated. The aim of the study was to establish whether the choice of head size influences the initial strength of the trunnion-head connection. Methods. Ti-6Al-4V trunnions (n = 60) and two different sizes of Co-Cr heads (28 mm and 36 mm) were used in the study. Three different levels of assembly force were considered; 4, 5 and 6 kN (n = 10 each). The strength of the press-fit connection was subsequently evaluated by measuring the pull-off force required to break the connection. Finite element and analytical models were also developed to better understand the mechanics of the problem. Results. We report that 36 mm diameter heads had significantly lower pull-off forces when impacted at 4 and 5 kN (p < 0.001; p < 0.001) but not at 6 kN (p = 0.21) compared to 28 mm heads. Mean pull-off forces at 4 and 5 kN impaction forces were 20% lower for 36 mm heads compared to 28 mm heads. Discussion. This is the first study to demonstrate that the head-trunnion connection strength of larger diameter heads is compromised at the point of assembly. Our finite element and analytical models show that the differences in pull-off strength can be explained by differences in structural rigidity and the resulting interface pressures. It should be noted that this effect is likely to be even more pronounced for head diameters larger than 36 mm. Conclusion. We recommend that surgeons use 20% larger impaction forces for 36 mm heads than they would ordinarily use for 28 mm heads

The December 2015 Oncology Roundup³⁶⁰ looks at: Amputation may not be the best option; Growing golf balls bad news!; How close is safe? Radiotherapy and surgery; Lymphocyte: monocyte ratio in osteosarcoma; Are borderline cartilage tumours really borderline?; Boosting algorithms improves survival estimates; CT better than Mirels?

Previously, we showed that case-specific non-linear finite element (FE) models are better at predicting the load to failure of metastatic femora than experienced clinicians. In this study we improved our FE modelling and increased the number of femora and characteristics of the lesions. We retested the robustness of the FE predictions and assessed why clinicians have difficulty in estimating the load to failure of metastatic femora. A total of 20 femora with and without artificial metastases were mechanically loaded until failure. These experiments were simulated using case-specific FE models. Six clinicians ranked the femora on load to failure and reported their ranking strategies. The experimental load to failure for intact and metastatic femora was well predicted by the FE models (R² = 0.90 and R² = 0.93, respectively). Ranking metastatic femora on load to failure was well performed by the FE models (τ = 0.87), but not by the clinicians (0.11 < τ < 0.42). Both the FE models and the clinicians allowed for the characteristics of the lesions, but only the FE models incorporated the initial bone strength, which is essential for accurately predicting the risk of fracture. Accurate prediction of the risk of fracture should be made possible for clinicians by further developing FE models.

Objectives. This study aims to assess the correlation of CT-based structural rigidity analysis with mechanically determined axial rigidity in normal and metabolically diseased rat bone. Methods. A total of 30 rats were divided equally into normal, ovariectomized, and partially nephrectomized groups. Cortical and trabecular bone segments from each animal underwent micro-CT to assess their average and minimum axial rigidities using structural rigidity analysis. Following imaging, all specimens were subjected to uniaxial compression and assessment of mechanically-derived axial rigidity. Results. The average structural rigidity-based axial rigidity was well correlated with the average mechanically-derived axial rigidity results (R. 2. = 0.74). This correlation improved significantly (p < 0.0001) when the CT-based Structural Rigidity Analysis (CTRA) minimum axial rigidity was correlated to the mechanically-derived minimum axial rigidity results (R. 2. = 0.84). Tests of slopes in the mixed model regression analysis indicated a significantly steeper slope for the average axial rigidity compared with the minimum axial rigidity (p = 0.028) and a significant difference in the intercepts (p = 0.022). The CTRA average and minimum axial rigidities were correlated with the mechanically-derived average and minimum axial rigidities using paired t-test analysis (p = 0.37 and p = 0.18, respectively). Conclusions. In summary, the results of this study suggest that structural rigidity analysis of micro-CT data can be used to accurately and quantitatively measure the axial rigidity of bones with metabolic pathologies in an experimental rat model. It appears that minimum axial rigidity is a better model for measuring bone rigidity than average axial rigidity