Aims. The risk of mechanical failure of modular revision hip stems is frequently mentioned in the literature, but little is currently known about the actual clinical failure rates of this type of prosthesis. The current retrospective long-term analysis examines the distal and modular failure patterns of the Prevision hip stem from 18 years of clinical use. A design improvement of the modular taper was introduced in 2008, and the data could also be used to compare the original and the current design of the modular connection. Methods. We performed an analysis of the Prevision modular hip stem using the manufacturer’s vigilance database and investigated different mechanical failure patterns of the hip stem from January 2004 to December 2022. Results. Two mechanical failure patterns were identified: fractures in the area of the distal fluted profile (distal stem fracture) and failure of the modular taper (modular fracture). A failure rate of 0.07% was observed for distal stem fracture, and modular fracture rates of 1.74% for the original and 0.013% for the current taper design. Conclusion. A low risk of mechanical failure for both fracture types was observed compared to other known complications in revision hip arthroplasty. In addition, the data show that a design change did significantly reduce the risk of a modular fracture. Cite this article: Bone Joint J 2024;106-B(2):151–157

Aims. There are limited long-term studies reporting on outcomes of the Zimmer Modular Revision (ZMR) stem, and concerns remain regarding failure. Our primary aim was to determine long-term survival free from all-cause revision and stem-related failure for this modular revision stem in revision total hip arthroplasty (THA). Secondary aims included evaluating radiological and functional outcomes. Methods. We retrospectively identified all patients in our institutional database who underwent revision THA using the ZMR system from January 2000 to December 2007. We included 106 patients (108 hips) with a mean follow-up of 14.5 years (2.3 to 22.3). Mean patient age was 69.2 years (37.0 to 89.4), and 51.9% were female (n = 55). Indications for index revision included aseptic loosening (73.1%), infection (16.7%), fracture (9.3%), and stem fracture (0.9%). Kaplan-Meier analysis was used to determine the all-cause and stem-related failure revision-free survival. At most recent follow-up, Oxford Hip Scores (OHS) were collected, and radiological stem stability was determined using the Engh classification. Results. A total of 17 hips (15.7%) underwent re-revision of any component. Indications for re-revision were stem failure (35.3%; n = 6), infection (29.4%; n = 5), instability (29.4%; n = 5), and acetabular aseptic loosening (5.9%; n = 1). The five- and 15-year all-cause survival was 89.7% (95% confidence interval (CI) 86.7 to 92.7) and 83.3% (95% CI 79.6 to 87.0), respectively. There were six re-revisions (5.6%) for stem failure; five for stem fracture and one for aseptic loosening. The five- and 15-year survival free from stem-related failure was 97.2% (95% CI 95.6 to 98.8) and 94.0% (95% CI 91.6 to 96.4), respectively. At final follow-up, the mean OHS was 36.9 (8.0 to 48.0) and 95.7% (n = 66) of surviving modular revision stems were well-fixed in available radiographs. Conclusion. Femoral revision with the ZMR offers satisfactory long-term all-cause revision-free survival, good survival free of stem-related failure, and favourable clinical outcomes. Stem fracture was the most common reason for stem-related failure and occurred both early and late. This highlights the importance of both early and long-term surveillance for stem-related failure. Cite this article: Bone Joint J 2024;106-B(5 Supple B):112–117

A modular femoral head–neck junction has practical advantages in total hip replacement. Taper fretting and corrosion have so far been an infrequent cause of revision. The role of design and manufacturing variables continues to be debated. Over the past decade several changes in technology and clinical practice might result in an increase in clinically significant taper fretting and corrosion. Those factors include an increased usage of large diameter (36 mm) heads, reduced femoral neck and taper dimensions, greater variability in taper assembly with smaller incision surgery, and higher taper stresses due to increased patient weight and/or physical activity. Additional studies are needed to determine the role of taper assembly compared with design, manufacturing and other implant variables. . Cite this article: Bone Joint J 2013;95-B, Supple A:3–6

Aims. Prior studies have identified that malseating of a modular dual mobility liner can occur, with previous reported incidences between 5.8% and 16.4%. The aim of this study was to determine the incidence of malseating in dual mobility implants at our institution, assess for risk factors for liner malseating, and investigate whether liner malseating has any impact on clinical outcomes after surgery. Methods. We retrospectively reviewed the radiographs of 239 primary and revision total hip arthroplasties with a modular dual mobility liner. Two independent reviewers assessed radiographs for each patient twice for evidence of malseating, with a third observer acting as a tiebreaker. Univariate analysis was conducted to determine risk factors for malseating with Youden’s index used to identify cut-off points. Cohen’s kappa test was used to measure interobserver and intraobserver reliability. Results. In all, 12 liners (5.0%), including eight Stryker (6.8%) and four Zimmer Biomet (3.3%), had radiological evidence of malseating. Interobserver reliability was found to be 0.453 (95% confidence interval (CI) 0.26 to 0.64), suggesting weak inter-rater agreement, with strong agreement being greater than 0.8. We found component size of 50 mm or less to be associated with liner malseating on univariate analysis (p = 0.031). Patients with malseated liners appeared to have no associated clinical consequences, and none required revision surgery at a mean of 14 months (1.4 to 99.2) postoperatively. Conclusion. The incidence of liner malseating was 5.0%, which is similar to other reports. Component size of 50 mm or smaller was identified as a risk factor for malseating. Surgeons should be aware that malseating can occur and implant design changes or changes in instrumentation should be considered to lower the risk of malseating. Although further follow-up is needed, it remains to be seen if malseating is associated with any clinical consequences. Cite this article: Bone Jt Open 2021;2(10):858–864

Aims. The aim of this study was to investigate the safety and efficacy of 3D-printed modular prostheses in patients who underwent joint-sparing limb salvage surgery (JSLSS) for malignant femoral diaphyseal bone tumours. Methods. We retrospectively reviewed 17 patients (13 males and four females) with femoral diaphyseal tumours who underwent JSLSS in our hospital. Results. In all, 17 patients with locally aggressive bone tumours (Enneking stage IIB) located in the femoral shaft underwent JSLSS and reconstruction with 3D-printed modular prostheses between January 2020 and June 2022. The median surgical time was 153 minutes (interquartile range (IQR) 117 to 248), and the median estimated blood loss was 200ml (IQR 125 to 400). Osteosarcoma was the most common pathological type (n = 12; 70.6%). The mean osteotomy length was 197.53 mm (SD 12.34), and the median follow-up was 25 months (IQR 19 to 38). Two patients experienced local recurrence and three developed distant metastases. Postoperative complications included wound infection in one patient and screw loosening in another, both of which were treated successfully with revision surgery. The median Musculoskeletal Tumor Society score at the final follow-up was 28 (IQR 27 to 28). Conclusion. The 3D-printed modular prosthesis is a reliable and feasible reconstruction option for patients with malignant femoral diaphyseal tumours. It helps to improve the limb salvage rate, restore limb function, and achieve better short-term effectiveness. Cite this article: Bone Jt Open 2024;5(4):317–323

Aims. Dual mobility (DM) implants have been shown to reduce the dislocation rate after total hip arthroplasty (THA), but there remain concerns about the use of cobalt chrome liners inserted into titanium shells. The aim of this study was to assess the clinical outcomes, metal ion levels, and periprosthetic femoral bone mineral density (BMD) at mid-term follow-up in young, active patients receiving a modular DM THA. Methods. This was a prospective study involving patients aged < 65 years, with a BMI of < 35 kg/m. 2. , and University of California, Los Angeles activity score of > 6 who underwent primary THA with a modular cobalt chrome acetabular liner, highly cross-linked polyethylene mobile bearing, and a cementless titanium femoral stem. Patient-reported outcome measures, whole blood metal ion levels (μg/l), and periprosthetic femoral BMD were measured at baseline and at one, two, and five years postoperatively. The results two years postoperatively for this cohort have been previously reported. Results. A total of 43 patients were enrolled. At minimum follow-up of five years, 23 (53.4%) returned for clinical and radiological review, 25 (58.1%) had metal ion analysis performed, 19 (44.2%) underwent dual energy x-ray absorptiometry scans, and 25 (58%) completed a pain-drawing questionnaire. The mean modified Harris Hip Scores improved significantly from 54.8 (SD 19) preoperatively to 93.08 (SD 10.5) five years postoperatively (p < 0.001). One patient was revised for aseptic acetabular loosening. The mean cobalt levels increased from 0.065 μg/l (SD 0.03) to 0.08 (SD 0.05) and the mean titanium levels increased from 0.35 (SD 0.13) to 0.78 (SD 0.29). The femoral BMD ratio decreased in Gruen Zone 1 (91.9%) at five years postoperatively compared with the baseline scores at six weeks potoperatively. The femoral BMD ratio was maintained in Gruen zones 2 to 7. Conclusion. The use of a modular DM component and a cementless, tapered femoral stem shows excellent mid-term survivorship with minimal concerns for corrosion and metal ion release in a cohort of young, active patients undergoing primary THA. Cite this article: Bone Joint J 2021;103-B(7 Supple B):73–77

Aims. The aim of this meta-analysis is to assess the association between exchange of modular parts in debridement, antibiotics, and implant retention (DAIR) procedure and outcomes for hip and knee periprosthetic joint infection (PJI). Methods. We conducted a systematic search on PubMed, Embase, Web of Science, and Cochrane library from inception until May 2021. Random effects meta-analyses and meta-regression was used to estimate, on a study level, the success rate of DAIR related to component exchange. Risk of bias was appraised using the (AQUILA) checklist. Results. We included 65 studies comprising 6,630 patients. The pooled overall success after DAIR for PJI was 67% (95% confidence interval (CI) 63% to 70%). This was 70% (95% CI 65% to 75%) for DAIR for hip PJI and 63% (95% CI 58% to 69%) for knee PJI. In studies before 2004 (n = 27), our meta-regression analysis showed a 3.5% increase in success rates for each 10% increase in component exchange in DAIR for hip PJI and a 3.1% increase for each 10% increase in component exchange for knee PJI. When restricted to studies after 2004 (n = 37), this association changed: for DAIR for hip PJI a decrease in successful outcome by 0.5% for each 10% increase in component exchange and for DAIR for knee PJI this was a 0.01% increase in successful outcome for each 10% increase in component exchange. Conclusion. This systematic review and meta-regression found no benefit of modular component exchange on reduction of PJI failure. This limited effect should be weighed against the risks for the patient and cost on a case-by-case basis. The association between exchange of modular components and outcome changed before and after 2004. This suggests the effect seen after 2004 may reflect a more rigorous, evidence-based, approach to the infected implant compared to the years before. Level of Evidence: Level III. Cite this article: Bone Jt Open 2021;2(10):806–812

Aims. We evaluated a large database with mechanical failure of a single uncemented modular femoral component, used in revision hip arthroplasty, as the end point and compared them to a control group treated with the same implant. Patient- and implant-specific risk factors for implant failure were analyzed. . Methods. All cases of a fractured uncemented modular revision femoral component from one manufacturer until April 2017 were identified and the total number of implants sold until April 2017 was used to calculate the fracture rate. The manufacturer provided data on patient demographics, time to failure, and implant details for all notified fractured devices. Patient- and implant-specific risk factors were evaluated using a logistic regression model with multiple imputations and compared to data from a previously published reference group, where no fractures had been observed. The results of a retrieval analysis of the fractured implants, performed by the manufacturer, were available for evaluation. Results. There were 113 recorded cases with fracture at the modular junction, resulting in a calculated fracture rate of 0.30% (113/37,600). The fracture rate of the implant without signs of improper use was 0.11% (41/37,600). In 79% (89/113) of cases with a failed implant, either a lateralized (high offset) neck segment, an extralong head, or the combination of both were used. Logistic regression analysis revealed male sex, high body mass index (BMI), straight component design, and small neck segments were significant risk factors for failure. Investigation of the implants (76/113) showed at least one sign of improper use in 72 cases. Conclusion. Implant failure at the modular junction is associated with patient- and implant-specific risk factors as well as technical errors during implantation. Whenever possible, the use of short and lateralized neck segments should be avoided with this revision system. Implantation instructions and contraindications need to be adhered to and respected. Cite this article: Bone Joint J 2020;102-B(5):573–579

Aims. Uncemented implants are now commonly used at reimplantation of a two-stage revision total hip arthoplasty (THA) following periprosthetic joint infection (PJI). However, there is a paucity of data on the performance of the most commonly used uncemented femoral implants – modular fluted tapered (MFT) femoral components – in this setting. This study evaluated implant survival, radiological results, and clinical outcomes in a large cohort of reimplantation THAs using MFT components. Methods. We identified 236 reimplantation THAs from a single tertiary care academic institution from September 2000 to September 2020. Two designs of MFT femoral components were used as part of an established two-stage exchange protocol for the treatment of PJI. Mean age at reimplantation was 65 years (SD 11), mean BMI was 32 kg/m. 2. (SD 7), and 46% (n = 109) were female. Mean follow-up was seven years (SD 4). A competing risk model accounting for death was used. Results. The 15-year cumulative incidence of any revision was 24%. There were 48 revisions, with the most common reasons being dislocation (n = 25) and infection (n = 16). The 15-year cumulative incidence of any reoperation was 28%. Only 13 revisions involved the fluted tapered component (FTC), for a 15-year cumulative incidence of any FTC revision of 8%. Only two FTCs were revised for aseptic loosening, resulting in a 15-year cumulative incidence of FTC revision for aseptic loosening of 1%. Stem subsidence ≥ 5 mm occurred in 2% of unrevised cases. All stems were radiologically stable at most recent follow-up. Mean Harris Hip Score was 69 (SD 20) at most recent follow-up. Conclusion. This series demonstrated that MFT components were durable and reliable in the setting of two-stage reimplantation THA for infection. While the incidence of aseptic loosening was very low, the incidence of any revision was 24% at 15 years, primarily due to dislocation and recurrent PJI. Cite this article: Bone Joint J 2024;106-B(5 Supple B):125–132

Aims. Dual mobility implants in total hip arthroplasty are designed to increase the functional head size, thus decreasing the potential for dislocation. Modular dual mobility (MDM) implants incorporate a metal liner (e.g. cobalt-chromium alloy) in a metal shell (e.g. titanium alloy), raising concern for mechanically assisted crevice corrosion at the modular liner-shell connection. We sought to examine fretting and corrosion on MDM liners, to analyze the corrosion products, and to examine histologically the periprosthetic tissues. Methods. A total of 60 retrieved liners were subjectively scored for fretting and corrosion. The corrosion products from the three most severely corroded implants were removed from the implant surface, imaged using scanning electron microscopy, and analyzed using Fourier-transform infrared spectroscopy. Results. Fretting was present on 88% (53/60) of the retrieved liners, and corrosion was present on 97% (58/60). Fretting was most often found on the lip of the taper at the transition between the lip and the dome regions. Macrophages and particles reflecting an innate inflammatory reaction to corrosion debris were noted in six of the 48 cases for which periprosthetic tissues were examined, and all were associated with retrieved components that had high corrosion scores. Conclusion. Our results show that corrosion occurs at the interface between MDM liners and shells and that it can be associated with reactions in the local tissues, suggesting continued concern that this problem may become clinically important with longer-term use of these implants. Cite this article: Bone Joint J 2021;103-B(7):1238–1246

The advent of modular porous metal augments has ushered in a new form of treatment for acetabular bone loss. The function of an augment can be seen as reducing the size of a defect or reconstituting the anterosuperior/posteroinferior columns and/or allowing supplementary fixation. Depending on the function of the augment, the surgeon can decide on the sequence of introduction of the hemispherical shell, before or after the augment. Augments should always, however, be used with cement to form a unit with the acetabular component. Given their versatility, augments also allow the use of a hemispherical shell in a position that restores the centre of rotation and biomechanics of the hip. Progressive shedding or the appearance of metal debris is a particular finding with augments and, with other radiological signs of failure, should be recognized on serial radiographs. Mid- to long-term outcomes in studies reporting the use of augments with hemispherical shells in revision total hip arthroplasty have shown rates of survival of > 90%. However, a higher risk of failure has been reported when augments have been used for patients with chronic pelvic discontinuity. Cite this article: Bone Joint J 2024;106-B(4):312–318

Aims. Revision total hip arthroplasty in patients with Vancouver type B3 fractures with Paprosky type IIIA, IIIB, and IV femoral defects are difficult to treat. One option for Paprovsky type IIIB and IV defects involves modular cementless, tapered, revision femoral components in conjunction with distal interlocking screws. The aim of this study was to analyze the rate of reoperations and complications and union of the fracture, subsidence of the stem, mortality, and the clinical outcomes in these patients. Methods. A total of 46 femoral components in patients with Vancouver B3 fractures (23 with Paprosky type IIIA, 19 with type IIIB, and four with type IV defects) in 46 patients were revised with a transfemoral approach using a modular, tapered, cementless revision Revitan curved femoral component with distal cone-in-cone fixation and prospectively followed for a mean of 48.8 months (SD 23.9; 24 to 112). The mean age of the patients was 80.4 years (66 to 100). Additional distal interlocking was also used in 23 fractures in which distal cone-in-cone fixation in the isthmus was < 3 cm. Results. One patient (2.2%) died during the first postoperative year. After six months, 43 patients (93.5%) had osseous, and three had fibrous consolidation of the fracture and the bony flap, 42 (91.3%) had bony ingrowth and four had stable fibrous fixation of the stem. No patient had radiolucency around the interlocking screws and no screw broke. One patient had non-progressive subsidence and two had a dislocation. The mean Harris Hip Score increased from of 57.8 points (SD 7.9) three months postoperatively to 76.1 points (SD 10.7) 24 months postoperatively. Conclusion. The 2° tapered, fluted revision femoral component with distal cone-in-cone-fixation, combined with additional distal interlocking in patients with bony deficiency at the isthmus, led to reproducibly good results in patients with a Vancouver B3 fracture and Paprosky type IIIA, IIIB, and IV defects with regard to union of the fracture, subsidence or loosening of the stem, and clinical outcomes. Cite this article: Bone Joint J 2024;106-B(4):344–351

Following the recall of modular neck hip stems in July 2012, research into femoral modularity will intensify over the next few years. This review aims to provide surgeons with an up-to-date summary of the clinically relevant evidence. The development of femoral modularity, and a classification system, is described. The theoretical rationale for modularity is summarised and the clinical outcomes are explored. The review also examines the clinically relevant problems reported following the use of femoral stems with a modular neck. Joint replacement registries in the United Kingdom and Australia have provided data on the failure rates of modular devices but cannot identify the mechanism of failure. This information is needed to determine whether modular neck femoral stems will be used in the future, and how we should monitor patients who already have them implanted. Cite this article: Bone Joint J 2013;95-B:1011–21

Aims. Modular dual-mobility constructs reduce the risk of dislocation after revision total hip arthroplasty (THA). However, questions about metal ions from the cobalt-chromium (CoCr) liner persist, and are particularly germane to patients being revised for adverse local tissue reactions (ALTR) to metal. We determined the early- to mid-term serum Co and Cr levels after modular dual-mobility components were used in revision and complex primary THAs, and specifically included patients revised for ALTR. Patients and Methods. Serum Co and Cr levels were measured prospectively in 24 patients with a modular dual-mobility construct and a ceramic femoral head. Patients with CoCr heads or contralateral THAs with CoCr heads were excluded. The mean age was 63 years (35 to 83), with 13 patients (54%) being female. The mean follow-up was four years (2 to 7). Indications for modular dual-mobility were prosthetic joint infection treated with two-stage exchange and subsequent reimplantation (n = 8), ALTR revision (n = 7), complex primary THA (n = 7), recurrent instability (n = 1), and periprosthetic femoral fracture (n = 1). The mean preoperative Co and Cr in patients revised for an ALTR were 29.7 μg/l (2 to 146) and 21.5 μg/l (1 to 113), respectively. Results. Mean Co and Cr levels were 0.30 μg/l and 0.76 μg/l, respectively, at the most recent follow-up. No patient had a Co level ≥ 1 μg/l. Only one patient had a Cr level ≥ 1 μg/l. That patient’s Cr level was 12 μg/l at 57 months after revision THA for ALTR (and decreased ten-fold from a preoperative Cr of 113 μg/l). Conclusion. At a mean of four years, no patient with a modular dual-mobility construct and ceramic femoral head had elevated Co levels, including seven patients revised specifically for ALTR. While further studies are required, we support the selective use of a modular dual-mobility construct in revision and complex primary THAs for patients at high risk for instability. Cite this article: Bone Joint J 2019;101-B(6 Supple B):57–61

Aims. This combined clinical and in vitro study aimed to determine the incidence of liner malseating in modular dual mobility (MDM) constructs in primary total hip arthroplasties (THAs) from a large volume arthroplasty centre, and determine whether malseating increases the potential for fretting and corrosion at the modular metal interface in malseated MDM constructs using a simulated corrosion chamber. Methods. For the clinical arm of the study, observers independently reviewed postoperative radiographs of 551 primary THAs using MDM constructs from a single manufacturer over a three-year period, to identify the incidence of MDM liner-shell malseating. Multivariable logistic regression analysis was performed to identify risk factors including age, sex, body mass index (BMI), cup design, cup size, and the MDM case volume of the surgeon. For the in vitro arm, six pristine MDM implants with cobalt-chrome liners were tested in a simulated corrosion chamber. Three were well-seated and three were malseated with 6° of canting. The liner-shell couples underwent cyclic loading of increasing magnitudes. Fretting current was measured throughout testing and the onset of fretting load was determined by analyzing the increase in average current. Results. The radiological review identified that 32 of 551 MDM liners (5.8%) were malseated. Malseating was noted in all of the three different cup designs. The incidence of malseating was significantly higher in low-volume MDM surgeons than high-volume MDM surgeons (p < 0.001). Pristine well-seated liners showed significantly lower fretting current values at all peak loads greater than 800 N (p < 0.044). Malseated liner-shell couples had lower fretting onset loads at 2,400 N. Conclusion. MDM malseating remains an issue that can occur in at least one in 20 patients at a high-volume arthroplasty centre. The onset of fretting and increased fretting current throughout loading cycles suggests susceptibility to corrosion when this occurs. These results support the hypothesis that malseated liners may be at risk for fretting corrosion. Clinicians should be aware of this phenomenon. Cite this article: Bone Joint J 2020;102-B(7 Supple B):20–26

Aims. Femoral revision component subsidence has been identified as predicting early failure in revision hip surgery. This comparative cohort study assessed the potential risk factors of subsidence in two commonly used femoral implant designs. Methods. A comparative cohort study was undertaken, analyzing a consecutive series of patients following revision total hip arthroplasties using either a tapered-modular (TM) fluted titanium or a porous-coated cylindrical modular (PCM) titanium femoral component, between April 2006 and May 2018. Clinical and radiological assessment was compared for both treatment cohorts. Risk factors for subsidence were assessed and compared. Results. In total, 65 TM and 35 PCM cases were included. At mean follow-up of seven years (1 to 13), subsidence was noted in both cohorts during the initial three months postoperatively (p < 0.001) then implants stabilized. Subsidence noted in 58.7% (38/65 cases) of the TM cohort (mean 2.3 mm, SD 3.5 mm) compared to 48.8% (17/35) of PCM cohort (mean 1.9 mm, SD 2.6 mm; p = 0.344). Subsidence of PCM cohort were significantly associated with extended trochanteric osteotomy (ETO) (p < 0.041). Although the ETO was used less frequently in PCM stem cohort (7/35), subsidence was noted in 85% (6/7) of them. Significant improvement of the final mean Oxford Hip Score (OHS) was reported in both treatment groups (p < 0.001). Conclusion. Both modular TM and PCM revision femoral components subsided within the femur. TM implants subsided more frequently than PCM components if the femur was intact but with no difference in clinical outcomes. However, if an ETO is performed then a PCM component will subside significantly more and suggests the use of a TM implant may be advisable. Cite this article: Bone Joint J 2020;102-B(6):709–715

Objectives. Taper junctions between modular hip arthroplasty femoral heads and stems fail by wear or corrosion which can be caused by relative motion at their interface. Increasing the assembly force can reduce relative motion and corrosion but may also damage surrounding tissues. The purpose of this study was to determine the effects of increasing the impaction energy and the stiffness of the impactor tool on the stability of the taper junction and on the forces transmitted through the patient’s surrounding tissues. Methods. A commercially available impaction tool was modified to assemble components in the laboratory using impactor tips with varying stiffness at different applied energy levels. Springs were mounted below the modular components to represent the patient. The pull-off force of the head from the stem was measured to assess stability, and the displacement of the springs was measured to assess the force transmitted to the patient’s tissues. Results. The pull-off force of the head increased as the stiffness of the impactor tip increased but without increasing the force transmitted through the springs (patient). Increasing the impaction energy increased the pull-off force but also increased the force transmitted through the springs. Conclusions. To limit wear and corrosion, manufacturers should maximize the stiffness of the impactor tool but without damaging the surface of the head. This strategy will maximize the stability of the head on the stem for a given applied energy, without influencing the force transmitted through the patient’s tissues. Current impactor designs already appear to approach this limit. Increasing the applied energy (which is dependent on the mass of the hammer and square of the contact speed) increases the stability of the modular connection but proportionally increases the force transmitted through the patient’s tissues, as well as to the surface of the head, and should be restricted to safe levels. Cite this article: A. Krull, M. M. Morlock, N. E. Bishop. Maximizing the fixation strength of modular components by impaction without tissue damage. Bone Joint Res 2018;7:196–204. DOI: 10.1302/2046-3758.72.BJR-2017-0078.R2

Aims. To fully verify the reliability and reproducibility of an experimental method in generating standardized micromotion for the rat femur fracture model. Methods. A modularized experimental device has been developed that allows rat models to be used instead of large animal models, with the aim of reducing systematic errors and time and money constraints on grouping. The bench test was used to determine the difference between the measured and set values of the micromotion produced by this device under different simulated loading weights. The displacement of the fixator under different loading conditions was measured by compression tests, which was used to simulate the unexpected micromotion caused by the rat’s ambulation. In vivo preliminary experiments with a small sample size were used to test the feasibility and effectiveness of the whole experimental scheme and surgical scheme. Results. The bench test showed that a weight loading < 500 g did not affect the operation of experimental device. The compression test demonstrated that the stiffness of the device was sufficient to keep the uncontrollable motion between fracture ends, resulting from the rat’s daily activities, within 1% strain. In vivo results on 15 rats prove that the device works reliably, without overburdening the experimental animals, and provides standardized micromotion reproductively at the fracture site according to the set parameters. Conclusion. Our device was able to investigate the effect of micromotion parameters on fracture healing by generating standardized micromotion to small animal models. Cite this article: Bone Joint Res 2021;10(11):714–722

Objectives. The objective of this study was to assess all evidence comparing the Thompson monoblock hemiarthroplasty with modular unipolar implants for patients requiring hemiarthroplasty of the hip with respect to mortality and complications. Methods. A literature search was performed to identify all relevant literature. The population consisted of patients undergoing hemiarthroplasty of the hip for fracture. The intervention was hemiarthroplasty of the hip with a comparison between Thompson and modular unipolar prostheses. Pubmed, Embase, CINAHL, Web of Science, PROSPERO and the Cochrane Central Register of Controlled Trials. The study designs included were randomised controlled trials (RCTs), well designed case control studies and retrospective or prospective cohort studies. Studies available in any language, published at any time until September 2015 were considered. Studies were included if they contained mortality or complications. Results. The initial literature search identified 4757 items for examination. Four papers were included in the final review. The pooled odds ratio for mortality was 1.3 (95% confidence Interval 0.78 to 2.46) favouring modular designs. The pooled odds ratio for post-operative complications was 1.1 (95% CI 0.79 to 1.55) favouring modular designs. Outcomes were reported at 12 or six months. These papers all contained potential sources of bias and significant clinical heterogeneity. Conclusion. The current evidence comparing monoblock versus modular implants in patients undergoing hemiarthroplasty is weak. Confidence intervals around the pooled odds ratios are broad and incorporate a value of one. Direct comparison of outcomes from these papers is fraught with difficulty and, as such, may well be misleading. A well designed randomised controlled trial would be helpful to inform evidence-based implant selection. Cite this article: A. L. Sims, A. J. Farrier, M. R. Reed, T. A. Sheldon. Thompson hemiarthroplasty versus modular unipolar implants for patients requiring hemiarthroplasty of the hip: A systematic review of the evidence. Bone Joint Res 2017;6:–513. DOI: 10.1302/2046-3758.68.BJR-2016-0256.R1

Aims. Modular dual mobility (DM) prostheses in which a cobalt-chromium liner is inserted into a titanium acetabular shell (vs a monoblock acetabular component) have the advantage of allowing supplementary screw fixation, but the potential for corrosion between the liner and acetabulum has raised concerns. While DM prostheses have shown improved stability in patients deemed ‘high-risk’ for dislocation undergoing total hip arthroplasty (THA), their performance in young, active patients has not been reported. This study’s purpose was to assess clinical outcomes, metal ion levels, and periprosthetic femoral bone mineral density (BMD) in young, active patients receiving a modular DM acetabulum and recently introduced titanium, proximally coated, tapered femoral stem design. Patients and Methods. This was a prospective study of patients between 18 and 65 years of age, with a body mass index (BMI) < 35 kg/m. 2. and University of California at Los Angeles (UCLA) activity score > 6, who received a modular cobalt-chromium acetabular liner, highly crosslinked polyethylene mobile bearing, and cementless titanium femoral stem for their primary THA. Patients with a history of renal disease and metal hardware elsewhere in the body were excluded. A total of 43 patients (30 male, 13 female; mean age 52.6 years (. sd. 6.5)) were enrolled. All patients had a minimum of two years’ clinical follow-up. Patient-reported outcome measures, whole blood metal ion levels (ug/l), and periprosthetic femoral BMD were measured at baseline, as well as at one and two years postoperatively. Power analysis indicated 40 patients necessary to demonstrate a five-fold increase in cobalt levels from baseline (alpha = 0.05, beta = 0.80). A mixed model with repeated measures was used for statistical analysis. Results. Mean Harris Hip Scores improved from 54.1 (. sd. 20.5) to 91.2 (. sd. 10.8) at two years postoperatively (p < 0.001). All patients had radiologically well-fixed components, no patients experienced any instability, and no patients required any further intervention. Mean cobalt levels increased from 0.065 ug/l (. sd. 0.03) preoperatively to 0.30 ug/l (. sd. 0.51) at one year postoperatively (p = 0.01) but decreased at two years postoperatively to 0.16 ug/l (. sd. 0.23; p = 0.2). Four patients (9.3%) had a cobalt level outside the reference range (0.03 ug/l to 0.29 ug/l) at two years postoperatively, with values from 0.32 ug/l to 0.94 ug/l. The mean femoral BMD ratio was maintained in Gruen zones 2 to 7 at both one and two years postoperatively using this stem design. At two years postoperatively, mean BMD in the medial calcar was 101.5% of the baseline value. Conclusion. Use of a modular DM prosthesis and cementless, tapered femoral stem has shown encouraging results in young, active patients undergoing primary THA. Elevation in mean cobalt levels and the presence of four patients outside the reference range at two years postoperatively demonstrates the necessity of continued surveillance in this cohort. Cite this article: Bone Joint J 2019;101-B:365–371