Metal-on-metal bearings for total hip replacement (THR) are becoming increasingly popular. Improved wear characteristics mean that these articulations are being inserted into younger patients in the form of THR and resurfacing procedures. This has led to concerns regarding potential carcinogenicity because of the increased exposure to metal ions that the procedure brings. We have studied the serum cobalt and chromium concentrations in patients who had primary, well-fixed Ring metal-on-metal THRs for more than 30 years. The levels of cobalt and chromium were elevated by five and three times, respectively compared with those in our reference groups. Metal-on-metal articulations appear to be the source of metal ions throughout the life of the prosthesis. In three patients who had undergone revision of a previous metal-on-metal THR to a metal-on-polyethylene replacement the levels of metal ions were within the normal range. The elevations of cobalt and chromium ions seen in our study were comparable with those in patients with modern metal-on-metal THRs

Objectives. Alarm over the reported high failure rates for metal-on-metal (MoM) hip implants as well as their potential for locally aggressive Adverse Reactions to Metal Debris (ARMDs) has prompted government agencies, internationally, to recommend the monitoring of patients with MoM hip implants. Some have advised that a blood ion level >7 µg/L indicates potential for ARMDs. We report a systematic review and meta-analysis of the performance of metal ion testing for ARMDs. Methods. We searched MEDLINE and EMBASE to identify articles from which it was possible to reconstruct a 2 × 2 table. Two readers independently reviewed all articles and extracted data using explicit criteria. We computed a summary receiver operating curve using a Bayesian random-effects hierarchical model. Results. Our literature search returned 575 unique articles; only six met inclusion criteria defined a priori. The discriminative capacity of ion tests was homogeneous across studies but that there was substantial cut-point heterogeneity. Our best estimate of the “true” area under curve (AUC) for metal ion testing is 0.615, with a 95% credible interval of 0.480 to 0.735, thus we can state that the probability that metal ion testing is actually clinically useful with an AUC ≥ 0.75 is 1.7%. Conclusion. Metal ion levels are not useful as a screening test for identifying high risk patients because ion testing will either lead to a large burden of false positive patients, or otherwise marginally modify the pre-test probability. With the availability of more accurate non-invasive tests, we did not find any evidence for using blood ion levels to diagnose symptomatic patients. Cite this article: M. Pahuta, J. M. Smolders, J. L. van Susante, J. Peck, P. R. Kim, P. E. Beaule. Blood metal ion levels are not a useful test for adverse reactions to metal debris: a systematic review and meta-analysis. Bone Joint Res 2016;5:379–386. DOI: 10.1302/2046-3758.59.BJR-2016-0027.R1

We retrospectively analysed concentrations of chromium and cobalt ions in samples of synovial fluid and whole blood taken from a group of 92 patients with failed current-generation metal-on-metal hip replacements. We applied acid oxidative digestion to our trace metal analysis protocol, which found significantly higher levels of metal ion concentrations in blood and synovial fluid than a non-digestive method. Patients were subcategorised by mode of failure as either ‘unexplained pain’ or ‘defined causes’. Using this classification, chromium and cobalt ion levels were present over a wider range in synovial fluid and not as strongly correlated with blood ion levels as previously reported. There was no significant difference between metal ion concentrations and manufacturer of the implant, nor femoral head size below or above 50 mm. There was a moderately positive correlation between metal ion levels and acetabular component inclination angle as measured on three-dimensional CT imaging. Our results suggest that acid digestion of samples of synovial fluid samples is necessary to determine metal ion concentrations accurately so that meaningful comparisons can be made between studies

There have been no large comparative studies of the blood levels of metal ions after implantation of commercially available hip resurfacing devices which have taken into account the effects of femoral size and inclination and anteversion of the acetabular component. We present the results in 90 patients with unilateral articular surface replacement (ASR) hip resurfacings (mean time to blood sampling 26 months) and 70 patients with unilateral Birmingham Hip Resurfacing (BHR) implants (mean time 47 months). The whole blood and serum chromium (Cr) and cobalt (Co) concentrations were inversely related to the size of the femoral component in both groups (p < 0.05). Cr and Co were more strongly influenced by the position of the acetabular component in the case of the ASR, with an increase in metal ions observed at inclinations > 45° and anteversion angles of < 10° and > 20°. These levels were only increased in the BHR group when the acetabular component was implanted with an inclination > 55°. A significant relationship was identified between the anteversion of the BHR acetabular component and the levels of Cr and Co (p < 0.05 for Co), with an increase observed at anteversion angles < 10° and > 20°. The median whole blood and serum Cr concentrations of the male ASR patients were significantly lower than those of the BHR men (p < 0.001). This indicates that reduced diametral clearance may equate to a reduction in metal ion concentrations in larger joints with satisfactory orientation of the acetabular component

We report serum metal ion level data in patients with unilateral and bilateral hip resurfacing over a ten-year period. In these patients there is an increase in both cobalt and chromium levels above the accepted reference ranges during the first 18 months after operation. Metal ion levels remain elevated, but decline slowly for up to five years. However, the levels then appear to start rising again in some patients up to the ten-year mark. There was no significant difference in cobalt or chromium levels between men and women. These findings appear to differ from much of the current literature. The clinical significance of a raised metal ion level remains under investigation

Aims. We have previously demonstrated raised cobalt and chromium levels in patients with larger diameter femoral heads, following metal-on-polyethylene uncemented total hip arthroplasty. Further data have been collected, to see whether these associations have altered with time and to determine the long-term implications for these patients and our practice. Methods. Patients from our previous study who underwent Trident-Accolade primary total hip arthroplasties using a metal-on-polyethylene bearing in 2009 were reviewed. Patients were invited to have their cobalt and chromium levels retested, and were provided an Oxford Hip Score. Serum ion levels were then compared between groups (28 mm, 36 mm, and 40 mm heads) and over time. Results. Metal ion levels were repeated in 33 patients. When comparing the results of serum metal ion levels over time, regardless of head size, there was a significant increase in both cobalt and chromium levels (p < 0.001). Two patients with larger head sizes had undergone revision arthroplasty with evidence of trunnion damage at surgery. Two patients within the 40 mm subgroup had metal ion levels above the MHRA (Medicines and Healthcare Products Regulatory Agency) threshold for detailed investigation. The increase in cobalt and chromium, when comparing the 36 mm and 40 mm groups with those of the 28 mm group, was not significant (36 mm vs 28 mm; p = 0.092/p = 0.191; 40 mm vs 28 mm; p = 0.200/p = 0.091, respectively). There was no difference, between femoral head sizes, when comparing outcome as measured by the Oxford Hip Score. Conclusion. This study shows an increase in cobalt and chromium levels over time for all modular femoral head sizes in patients with metal-on-polyethylene bearings, with two patients demonstrating ion levels above the MHRA threshold for failure, and a further two patients requiring revision surgery. These results may have clinical implications regarding longer term follow-up of patients and future implant choice, particularly among younger patients. Cite this article: Bone Joint J 2020;102-B(7):832–837

Objectives. The aims of this piece of work were to: 1) record the background concentrations of blood chromium (Cr) and cobalt (Co) concentrations in a large group of subjects; 2) to compare blood/serum Cr and Co concentrations with retrieved metal-on-metal (MoM) hip resurfacings; 3) to examine the distribution of Co and Cr in the serum and whole blood of patients with MoM hip arthroplasties; and 4) to further understand the partitioning of metal ions between the serum and whole blood fractions. Methods. A total of 3042 blood samples donated to the local transfusion centre were analysed to record Co and Cr concentrations. Also, 91 hip resurfacing devices from patients who had given pre-revision blood/serum samples for metal ion analysis underwent volumetric wear assessment using a coordinate measuring machine. Linear regression analysis was carried out and receiver operating characteristic curves were constructed to assess the reliability of metal ions to identify abnormally wearing implants. The relationship between serum and whole blood concentrations of Cr and Co in 1048 patients was analysed using Bland-Altman charts. This relationship was further investigated in an in vitro study during which human blood was spiked with trivalent and hexavalent Cr, the serum then separated and the fractions analysed. Results. Only one patient in the transfusion group was found to have a blood Co > 2 µg/l. Blood/Serum Cr and Co concentrations were reliable indicators of abnormal wear. Blood Co appeared to be the most useful clinical test, with a concentration of 4.5 µg/l showing sensitivity and specificity for the detection of abnormal wear of 94% and 95%, respectively. Generated metal ions tended to fill the serum compartment preferentially in vivo and this was replicated in the in vitro study when blood was spiked with trivalent Cr and bivalent Co. Conclusions. Blood/serum metal ion concentrations are reliable indicators of abnormal wear processes. Important differences exist however between elements and the blood fraction under study. Future guidelines must take these differences into account

Increased concentrations of metal ions after metal-on-metal resurfacing arthroplasty of the hip remain a concern. Although there has been no proven link to long-term health problems or early prosthetic failure, variables associated with high metal ion concentrations should be identified and, if possible, corrected. Our study provides data on metal ion levels from a series of 76 consecutive patients (76 hips) after resurfacing arthroplasty with the Articular Surface Replacement. Chromium and cobalt ion concentrations in the whole blood of patients with smaller (≤ 51 mm) femoral components were significantly higher than in those with the larger (≥ 53 mm) components (p < 0.01). Ion concentrations in the former group were significantly related to the inclination (p = 0.01) and anteversion (p = 0.01) of the acetabular component. The same relationships were not significant in the patients with larger femoral components (p = 0.61 and p = 0.49, respectively). Accurate positioning of the acetabular component intra-operatively is essential in order to reduce the concentration of metal ions in the blood after hip resurfacing arthroplasty with the Articular Surface Replacement implant

We examined the relationships between the serum levels of chromium and cobalt ions and the inclination angle of the acetabular component and the level of activity in 214 patients implanted with a metal-on-metal resurfacing hip replacement. Each patient had a single resurfacing and no other metal in their body. All serum measurements were performed at a minimum of one year after operation. The inclination of the acetabular component was considered to be steep if the abduction angle was greater than 55°. There were significantly higher levels of metal ions in patients with steeply-inclined components (p = 0.002 for chromium, p = 0.003 for cobalt), but no correlation was found between the level of activity and the concentration of metal ions. A highly significant (p < 0.001) correlation with the arc of cover was found. Arcs of cover of less than 10 mm were correlated with a greater risk of high concentrations of serum metal ions. The arc of coverage was also related to the design of the component and to size as well as to the abduction angle of the acetabular component. Steeply-inclined acetabular components, with abduction angles greater than 55°, combined with a small size of component are likely to give rise to higher serum levels of cobalt and chromium ions. This is probably due to a greater risk of edge-loading

Metal ions generated from joint replacements are a cause for concern. There is no consensus on the best surrogate measure of metal ion exposure. This study investigates whether serum and whole blood concentrations can be used interchangeably to report results of cobalt and chromium ion concentrations. Concentrations of serum and whole blood were analysed in 262 concurrent specimens using high resolution inductively-coupled plasma mass-spectrometry. The agreement was assessed with normalised scatterplots, mean difference and the Bland and Altman limits of agreement. The wide variability seen in the normalised scatterplots, in the Bland and Altman plots and the statistically significant mean differences between serum and whole blood concentrations suggest that they cannot be used interchangeably. A bias was demonstrated for both ions in the Bland-Altman plots. Regression analysis provided a possible conversion factor of 0.71 for cobalt and 0.48 for chromium. However, even when the correction factors were applied, the limits of agreement were greater than ±67% for cobalt and greater than ±85% for chromium, suggesting that serum and whole blood cannot be used interconvertibly. This suggests that serum metal concentrations are not useful as a surrogate measure of systemic metal ion exposure

Objectives. We have encountered patients who developed large joint fluid collections with massive elevations in chromium (Cr) and cobalt (Co) concentrations following metal-on-metal (MoM) hip arthroplasties. In some cases, retrieval analysis determined that these ion concentrations could not be explained simply by the wear rates of the components. We hypothesized that these effects may be associated with aseptic lymphocyte-dominated vasculitis-associated lesion (ALVAL). Patients and Methods. We examined the influence of the ALVAL grade on synovial fluid Co and Cr concentrations following adjustment for patient and device variables, including volumetric wear rates. Initially restricting the analysis to include only patients with one MoM hip resurfacing device, we performed multiple regression analyses of prospectively collected data. We then repeated the same statistical approach using results from a larger cohort with different MoM designs, including total hip arthroplasties. Results. In the resurfacing cohort (n = 76), the statistical modelling indicated that the presence of severe ALVAL and a large fluid collection were associated with greater joint fluid Co concentrations after adjustment for volumetric wear rates (p = 0.005). These findings were replicated in the mixed implant group (n = 178), where the presence of severe ALVAL and a large fluid collection were significantly associated with greater fluid Co concentrations (p < 0.001). Conclusion. The development of severe ALVAL is associated with elevations in metal ion concentrations far beyond those expected from the volumetric loss from the prosthetic surfaces. This finding may aid the understanding of the sequence of events leading to soft-tissue reactions following MoM hip arthroplasties. Cite this article: D. J. Langton, R. P. Sidaginamale, T. J. Joyce, J. G. Bowsher, J. P. Holland, D. Deehan, A. V. F. Nargol, S. Natu. Aseptic lymphocyte-dominated vasculitis-associated lesions are related to changes in metal ion handling in the joint capsules of metal-on-metal hip arthroplasties. Bone Joint Res 2018;7:388–396. DOI: 10.1302/2046-3758.76.BJR-2018-0037

We describe the findings at six years in an ongoing prospective clinicoradiological and metal ion study in a cohort of 26 consecutive male patients with unilateral Birmingham Hip Resurfacing arthroplasties with one of two femoral head sizes (50 mm and 54 mm). Their mean age was 52.9 years (29 to 67). We have previously shown an early increase in the 24-hour urinary excretion of metal ions, reaching a peak at six months (cobalt) and one year (chromium) after operation. Subsequently there is a decreasing trend in excretion of both cobalt and chromium. The levels of cobalt and chromium in whole blood also show a significant increase at one year, followed by a decreasing trend until the sixth year

Metal-on-metal hip bearings are being implanted into younger patients. The consequence of elevated levels of potentially carcinogenic metal ions is therefore a cause for concern. We have determined the levels of cobalt (Co), chromium (Cr), titanium (Ti) and vanadium (Va) in the urine and whole blood of patients who had had metal-on-metal and metal-on-polyethylene articulations in situ for more than 30 years. We compared these with each other and with the levels for a control group of subjects. We found significantly elevated levels of whole blood Ti, Va and urinary Cr in all arthroplasty groups. The whole blood and urine levels of Co were grossly elevated, by a factor of 50 and 300 times respectively in patients with loose metal-on-metal articulations when compared with the control group. Stable metal-on-metal articulations showed much lower levels. Elevated levels of whole blood or urinary Co may be useful in identifying metal-on-metal articulations which are loose

Aims. We investigated whether blood metal ion levels could effectively identify patients with bilateral Birmingham Hip Resurfacing (BHR) implants who have adverse reactions to metal debris (ARMD). Patients and Methods. Metal ion levels in whole blood were measured in 185 patients with bilateral BHRs. Patients were divided into those with ARMD who either had undergone a revision for ARMD or had ARMD on imaging (n = 30), and those without ARMD (n = 155). Receiver operating characteristic analysis was used to determine the optimal thresholds of blood metal ion levels for identifying patients with ARMD. Results. The maximum level of cobalt or chromium ions in the blood was the parameter which produced the highest area under the curve (91.0%). The optimal threshold for distinguishing between patients with and without ARMD was 5.5 µg/l (83.3% sensitivity, 88.4% specificity, 58.1% positive and 96.5% negative predictive values). Similar results were obtained in a subgroup of 111 patients who all underwent cross-sectional imaging. Between 3.2% and 4.3% of patients with ARMD were missed if United Kingdom (7 µg/l) and United States (10 µg/l) authority thresholds were used respectively, compared with 2.7% if our implant specific threshold was used, though these differences did not reach statistical significance (p ≥ 0.248). Conclusion. Patients with bilateral BHRs who have blood metal ion levels below our implant specific threshold were at low-risk of having ARMD. Cite this article: Bone Joint J 2016;98-B:1455–62

A retrospective study was conducted to investigate the changes in metal ion levels in a consecutive series of Birmingham Hip Resurfacings (BHRs) at a minimum ten-year follow-up. We reviewed 250 BHRs implanted in 232 patients between 1998 and 2001. Implant survival, clinical outcome (Harris hip score), radiographs and serum chromium (Cr) and cobalt (Co) ion levels were assessed. Of 232 patients, 18 were dead (five bilateral BHRs), 15 lost to follow-up and ten had been revised. The remaining 202 BHRs in 190 patients (136 men and 54 women; mean age at surgery 50.5 years (17 to 76)) were evaluated at a minimum follow-up of ten years (mean 10.8 years (10 to 13.6)). The overall implant survival at 13.2 years was 92.4% (95% confidence interval 90.8 to 94.0). The mean Harris hip score was 97.7 (median 100; 65 to 100). Median and mean ion levels were low for unilateral resurfacings (Cr: median 1.3 µg/l, mean 1.95 µg/l (< 0.5 to 16.2); Co: median 1.0 µg/l, mean 1.62 µg/l (< 0.5 to 17.3)) and bilateral resurfacings (Cr: median 3.2 µg/l, mean 3.46 µg/l (< 0.5 to 10.0); Co: median 2.3 µg/l, mean 2.66 µg/l (< 0.5 to 9.5)). In 80 unilateral BHRs with sequential ion measurements, Cr and Co levels were found to decrease significantly (p < 0.001) from the initial assessment at a median of six years (4 to 8) to the last assessment at a median of 11 years (9 to 13), with a mean reduction of 1.24 µg/l for Cr and 0.88 µg/l for Co. Three female patients had a > 2.5 µg/l increase of Co ions, associated with head sizes ≤ 50 mm, clinical symptoms and osteolysis. Overall, there was no significant difference in change of ion levels between genders (Cr, p = 0.845; Co, p = 0.310) or component sizes (Cr, p = 0.505; Co, p = 0.370). Higher acetabular component inclination angles correlated with greater change in ion levels (Cr, p = 0.013; Co, p = 0.002). Patients with increased ion levels had lower Harris hip scores (p = 0.038). In conclusion, in well-functioning BHRs the metal ion levels decreased significantly at ten years. An increase > 2.5 µg/l was associated with poor function. Cite this article: Bone Joint J 2013;95-B:1332–8

Plasma levels of cobalt and chromium ions and Metal Artefact Reduction Sequence (MARS)-MRI scans were performed on patients with 209 consecutive, unilateral, symptomatic metal-on-metal (MoM) hip arthroplasties. There was wide variation in plasma cobalt and chromium levels, and MARS-MRI scans were positive for adverse reaction to metal debris (ARMD) in 84 hips (40%). There was a significant difference in the median plasma cobalt and chromium levels between those with positive and negative MARS-MRI scans (p < 0.001). Compared with MARS-MRI as the potential reference standard for the diagnosis of ARMD, the sensitivity of metal ion analysis for cobalt or chromium with a cut-off of > 7 µg/l was 57%. The specificity was 65%, positive predictive value was 52% and the negative predictive value was 69% in symptomatic patients. A lowered threshold of > 3.5 µg/l for cobalt and chromium ion levels improved the sensitivity and negative predictive value to 86% and 74% but at the expense of specificity (27%) and positive predictive value (44%). Metal ion analysis is not recommended as a sole indirect screening test in the surveillance of symptomatic patients with a MoM arthroplasty. The investigating clinicians should have a low threshold for obtaining cross-sectional imaging in these patients, even in the presence of low plasma metal ion levels

We have studied the relationship between metal ion levels and lymphocyte counts in patients with metal-on-metal hip resurfacings. Peripheral blood samples were analysed for lymphocyte subtypes and whole blood cobalt and chromium ion levels in 68 patients (34 with metal-on-metal hip resurfacings and 34 with standard metal-on-polyethylene total hip replacements). All hip components were radiologically well-fixed and the patients were asymptomatic. Cobalt and chromium levels were significantly elevated in the patients with metal-on-metal hip resurfacings, compared with the patients with standard metal-on-polyethylene designs (p < 0.0001). There was a statistically significant decrease in the level of CD8. +. cells (T-cytotoxic/suppressor) (p = 0.005) in the metal-on-metal hip resurfacing group. A threshold level of blood cobalt and chromium ions was associated with reduced CD8. +. T-cell counts. We have no evidence that our patients suffered as a result of this reduced level of CD8. +. T-cells

We present a series of 35 patients (19 men and 16 women) with a mean age of 64 years (36.7 to 75.9), who underwent total hip replacement using the ESKA dual-modular short stem with metal on-polyethylene bearing surfaces. This implant has a modular neck section in addition to the modular head. Of these patients, three presented with increasing post-operative pain due to pseudotumour formation that resulted from corrosion at the modular neck-stem junction. These patients underwent further surgery and aseptic lymphocytic vaculitis associated lesions were demonstrated on histological analysis. Retrieval analysis of two modular necks showed corrosion at the neck-stem taper. Blood cobalt and chromium levels were measured at a mean of nine months (3 to 28) following surgery. These were compared with the levels in seven control patients (three men and four women) with a mean age of 53.4 years (32.1 to 64.1), who had an identical prosthesis and articulation but with a prosthesis that had no modularity at neck-stem junction. The mean blood levels of cobalt in the study group were raised at 50.75 nmol/l (5 to 145) compared with 5.6 nmol/l (2 to 13) in control patients. Corrosion at neck-stem tapers has been identified as an important source of metal ion release and pseudotumour formation requiring revision surgery. Finite element modelling of the dual modular stem demonstrated high stresses at the modular stem-neck junction. Dual modular cobalt-chrome hip prostheses should be used with caution due to these concerns

This is a longitudinal study of the daily urinary output and the concentrations in whole blood of cobalt and chromium in patients with metal-on-metal resurfacings over a period of four years. Twelve-hour urine collections and whole blood specimens were collected before and periodically after a Birmingham hip resurfacing in 26 patients. All ion analyses were carried out using a high-resolution inductively-coupled plasma mass spectrometer. Clinical and radiological assessment, hip function scoring and activity level assessment revealed excellent hip function. There was a significant early increase in urinary metal output, reaching a peak at six months for cobalt and one year for chromium post-operatively. There was thereafter a steady decrease in the median urinary output of cobalt over the following three years, although the differences are not statistically significant. The mean whole blood levels of cobalt and chromium also showed a significant increase between the pre-operative and one-year post-operative periods. The blood levels then decreased to a lower level at four years, compared with the one-year levels. This late reduction was statistically significant for chromium but not for cobalt. The effects of systemic metal ion exposure in patients with metal-on-metal resurfacing arthroplasties continue to be a matter of concern. The levels in this study provide a baseline against which the in vivo wear performance of newer bearings can be compared

The issues surrounding raised levels of metal ions in the blood following large head metal-on-metal total hip replacement (THR), such as cobalt and chromium, have been well documented. Despite the national popularity of uncemented metal-on-polyethylene (MoP) THR using a large-diameter femoral head, few papers have reported the levels of metal ions in the blood following this combination. Following an isolated failure of a 44 mm Trident–Accolade uncemented THR associated with severe wear between the femoral head and the trunnion in the presence of markedly elevated levels of cobalt ions in the blood, we investigated the relationship between modular femoral head diameter and the levels of cobalt and chromium ions in the blood following this THR. A total of 69 patients received an uncemented Trident–Accolade MoP THR in 2009. Of these, 43 patients (23 men and 20 women, mean age 67.0 years) were recruited and had levels of cobalt and chromium ions in the blood measured between May and June 2012. The patients were then divided into three groups according to the diameter of the femoral head used: 12 patients in the 28 mm group (controls), 18 patients in the 36 mm group and 13 patients in the 40 mm group. A total of four patients had identical bilateral prostheses in situ at phlebotomy: one each in the 28 mm and 36 mm groups and two in the 40 mm group. There was a significant increase in the mean levels of cobalt ions in the blood in those with a 36 mm diameter femoral head compared with those with a 28 mm diameter head (p = 0.013). The levels of cobalt ions in the blood were raised in those with a 40 mm diameter head but there was no statistically significant difference between this group and the control group (p = 0.152). The levels of chromium ions in the blood were normal in all patients. The clinical significance of this finding is unclear, but we have stopped using femoral heads with a diameter of ≤ 36 mm, and await further larger studies to clarify whether, for instance, this issue particularly affects this combination of components. Cite this article: Bone Joint J 2014;96-B:43–7

We have updated our previous randomised controlled trial comparing release of chromium (Cr) and cobalt (Co) ions and included levels of titanium (Ti) ions. We have compared the findings from 28 mm metal-on-metal total hip replacement, performed using titanium CLS/Spotorno femoral components and titanium AlloFit acetabular components with Metasul bearings, with Durom hip resurfacing using a Metasul articulation or bearing and a titanium plasma-sprayed coating for fixation of the acetabular component. Although significantly higher blood ion levels of Cr and Co were observed at three months in the resurfaced group than in total hip replacement, no significant difference was found at two years post-operatively for Cr, 1.58 μg/L and 1.62 μg/L respectively (p = 0.819) and for Co, 0.67 μg/L and 0.94 μg/L respectively (p = 0.207). A steady state was reached at one year in the resurfaced group and after three months in the total hip replacement group. Interestingly, Ti, which is not part of the bearing surfaces with its release resulting from metal corrosion, had significantly elevated ion levels after implantation in both groups. The hip resurfacing group had significantly higher Ti levels than the total hip replacement group for all periods of follow-up. At two years the mean blood levels of Ti ions were 1.87 μg/L in hip resurfacing and and 1.30 μg/L in total hip replacement (p = 0.001). The study confirms even with different bearing diameters and clearances, hip replacement and 28 mm metal-on-metal total hip replacement produced similar Cr and Co metal ion levels in this randomised controlled trial study design, but apart from wear on bearing surfaces, passive corrosion of exposed metallic surfaces is a factor which influences ion concentrations. Ti plasma spray coating the acetabular components for hip resurfacing produces significantly higher release of Ti than Ti grit-blasted surfaces in total hip replacement

Aims. The Birmingham Hip Resurfacing (BHR) arthroplasty has been used as a surgical treatment of coxarthrosis since 1997. We present 20-year results of 234 consecutive BHRs performed in our unit. Methods. Between 1999 and 2001, there were 217 patients: 142 males (65.4%), mean age 52 years (18 to 68) who had 234 implants (17 bilateral). They had patient-reported outcome measures collected, imaging (radiograph and ultrasound), and serum metal ion assessment. Survivorship analysis was performed using Kaplan-Meier estimates. Revision for any cause was considered as an endpoint for the analysis. Results. Mean follow-up was 20.9 years (19.3 to 22.4). Registry data revealed that 19 hips (8.1%) had been revised and 26 patients (12%) had died from causes unrelated to the BHR. Among the remaining 189 hips, 61% were available for clinical follow-up at 20 years (n = 115) and 70% of patients had biochemical follow-up (n = 132). The cumulative implant survival rate at 20 years for male patients was 96.5% (95% confidence interval (CI) 93.5 to 99.6), and for female patients 87% (95% CI 79.7 to 94.9). The difference was statistically significant (p = 0.029). The mean Oxford Hip Score, Hip disability and Osteoarthritis Outcome Score, and Forgotten Joint Score were 45 (29 to 48), 89 (43 to 100), and 84 (19 to 100), respectively. The mean scores for each of the five domains of the EuroQol five-dimension three-level questionnaire were 1.2, 1.0, 1.2, 1.3, and 1.1, and mean overall score 82.6 (50 to 100). Ultrasound showed no pseudotumour. Mean cobalt and chromium levels were 32.1 nmol/l (1 to 374) and 45.5 nmol/l (9 to 408), respectively. Conclusion. This study shows that BHRs provide excellent survivorship and functional outcomes in young male patients. At 20 years, soft-tissue imaging and serum metal ion studies suggest that a metal-on-metal resurfacing implant can be well tolerated in a group of young patients. Cite this article: Bone Joint J 2023;105-B(9):946–952

Aims. To establish the survivorship, function, and metal ion levels in an unselected series of metal-on-metal hip resurfacing arthroplasties (HRAs) performed by a non-designer surgeon. Methods. We reviewed 105 consecutive HRAs in 83 patients, performed by a single surgeon, at a mean follow-up of 14.9 years (9.3 to 19.1). The cohort included 45 male and 38 female patients, with a mean age of 49.5 years (SD 12.5). Results. At the time of review 13 patients with 15 hips had died from causes unrelated to the hip operation, and 14 hips had undergone revision surgery, giving an overall survival rate of rate of 86.7% (95% confidence interval (CI) 84.2 to 89.1). The survival rate in men was 97.7% (95% CI 96.3 to 98.9) and in women was 73.4% (95% CI 70.6 to 75.1). The median head size of the failed group was 42 mm (interquartile range (IQR) 42 to 44), and in the surviving group was 50 mm (IQR 46 to 50). In all, 13 of the 14 revised hips had a femoral component measuring ≤ 46 mm. The mean blood levels of cobalt and chromium ions were 26.6 nmol/l (SD 24.5) and 30.6 nmol/l (SD 15.3), respectively. No metal ion levels exceeded the safe limit. The mean Oxford Hip Score was 41.5 (SD 8.9) and Harris Hip Score was 89.9 (14.8). In the surviving group, four patients had radiolucent lines around the stem of the femoral component, and one had lysis around the acetabular component; eight hips demonstrated heterotopic ossification. Conclusion. Our results confirm the existing understanding that HRA provides good long-term survival and function in patients with adequate-sized femoral heads. This is evidenced by a 97.7% survival rate among men (larger heads) in our series at a mean follow-up of 14.9 years. Failure is closely related to head sizes ≤ 46 cm. Cite this article: Bone Jt Open 2022;3(1):68–76

Aims. Dual mobility (DM) implants have been shown to reduce the dislocation rate after total hip arthroplasty (THA), but there remain concerns about the use of cobalt chrome liners inserted into titanium shells. The aim of this study was to assess the clinical outcomes, metal ion levels, and periprosthetic femoral bone mineral density (BMD) at mid-term follow-up in young, active patients receiving a modular DM THA. Methods. This was a prospective study involving patients aged < 65 years, with a BMI of < 35 kg/m. 2. , and University of California, Los Angeles activity score of > 6 who underwent primary THA with a modular cobalt chrome acetabular liner, highly cross-linked polyethylene mobile bearing, and a cementless titanium femoral stem. Patient-reported outcome measures, whole blood metal ion levels (μg/l), and periprosthetic femoral BMD were measured at baseline and at one, two, and five years postoperatively. The results two years postoperatively for this cohort have been previously reported. Results. A total of 43 patients were enrolled. At minimum follow-up of five years, 23 (53.4%) returned for clinical and radiological review, 25 (58.1%) had metal ion analysis performed, 19 (44.2%) underwent dual energy x-ray absorptiometry scans, and 25 (58%) completed a pain-drawing questionnaire. The mean modified Harris Hip Scores improved significantly from 54.8 (SD 19) preoperatively to 93.08 (SD 10.5) five years postoperatively (p < 0.001). One patient was revised for aseptic acetabular loosening. The mean cobalt levels increased from 0.065 μg/l (SD 0.03) to 0.08 (SD 0.05) and the mean titanium levels increased from 0.35 (SD 0.13) to 0.78 (SD 0.29). The femoral BMD ratio decreased in Gruen Zone 1 (91.9%) at five years postoperatively compared with the baseline scores at six weeks potoperatively. The femoral BMD ratio was maintained in Gruen zones 2 to 7. Conclusion. The use of a modular DM component and a cementless, tapered femoral stem shows excellent mid-term survivorship with minimal concerns for corrosion and metal ion release in a cohort of young, active patients undergoing primary THA. Cite this article: Bone Joint J 2021;103-B(7 Supple B):73–77

Aims. In metal-on-metal (MoM) hip arthroplasties and resurfacings, mechanically induced corrosion can lead to elevated serum metal ions, a local inflammatory response, and formation of pseudotumours, ultimately requiring revision. The size and diametral clearance of anatomical (ADM) and modular (MDM) dual-mobility polyethylene bearings match those of Birmingham hip MoM components. If the acetabular component is satisfactorily positioned, well integrated into the bone, and has no surface damage, this presents the opportunity for revision with exchange of the metal head for ADM/MDM polyethylene bearings without removal of the acetabular component. Methods. Between 2012 and 2020, across two centres, 94 patients underwent revision of Birmingham MoM hip arthroplasties or resurfacings. Mean age was 65.5 years (33 to 87). In 53 patients (56.4%), the acetabular component was retained and dual-mobility bearings were used (DM); in 41 (43.6%) the acetabulum was revised (AR). Patients underwent follow-up of minimum two-years (mean 4.6 (2.1 to 8.5) years). Results. In the DM group, two (3.8%) patients underwent further surgery: one (1.9%) for dislocation and one (1.9%) for infection. In the AR group, four (9.8%) underwent further procedures: two (4.9%) for loosening of the acetabular component and two (4.9%) following dislocations. There were no other dislocations in either group. In the DM group, operating time (68.4 vs 101.5 mins, p < 0.001), postoperative drop in haemoglobin (16.6 vs 27.8 g/L, p < 0.001), and length of stay (1.8 vs 2.4 days, p < 0.001) were significantly lower. There was a significant reduction in serum metal ions postoperatively in both groups (p < 0.001), although there was no difference between groups for this reduction (p = 0.674 (cobalt); p = 0.186 (chromium)). Conclusion. In selected patients with Birmingham MoM hips, where the acetabular component is well-fixed and in a satisfactory position with no surface damage, the metal head can be exchanged for polyethylene ADM/MDM bearings with retention of the acetabular prosthesis. This presents significant benefits, with a shorter procedure and a lower risk of complications. Cite this article: Bone Jt Open 2024;5(6):514–523

Aims. The present study investigated the five-year interval changes in pseudotumours and measured serum metal ions at long-term follow-up of a previous report of 28 mm diameter metal-on-metal (MoM) total hip arthroplasty (THA). Patients and Methods. A total of 72 patients (mean age 46.6 years (37 to 55); 43 men, 29 women; 91 hips) who underwent cementless primary MoM THA with a 28 mm modular head were included. The mean follow-up duration was 20.3 years (18 to 24). All patients had CT scans at a mean 15.1 years (13 to 19) after the index operation and subsequent follow-up at a mean of 20.2 years (18 to 24). Pseudotumour volume, type of mass, and new-onset pseudotumours were evaluated using CT scanning. Clinical outcomes were assessed by Harris Hip Score (HHS) and the presence of groin pain. Serum metal ion (cobalt (Co) and chromium (Cr)) levels were measured at the latest follow-up. Results. At final follow-up, pseudotumours were observed in 26/91 hips (28.6%). There was an increase in volume of the pseudotumour in four hips (15.4%), no change in volume in 21 hips (80.8%), and a decrease in volume in one hip (3.8%). There were no new-onset pseudotumours. There was no significant difference in HHS between patients with and without pseudotumours. At final follow-up, mean serum Co ion levels and median Co:Cr ratios were significantly greater in patients with pseudotumours, but the serum Cr ion levels were not significantly different. Conclusion. At a mean 20 years of follow-up, pseudotumours were observed in 26/91 hips (28.6%) with no new-onset pseudotumours during subsequent follow-up. Most pseudotumours in small-head MoM THA were static in volume and asymptomatic with normal serum metal ion levels. Cite this article: Bone Joint J 2019;101-B:317–324

Aims. Our first aim was to determine whether there are significant changes in the level of metal ions in the blood at mid-term follow-up, in patients with an Articular Surface Replacement (ASR) arthroplasty. Secondly, we sought to identify risk factors for any increases. Patients and Methods. The study involved 435 patients who underwent unilateral, metal-on-metal (MoM) hip resurfacing (HRA) or total hip arthroplasty (THA). These patients all had one measurement of the level of metal ions in the blood before seven years had passed post-operatively (early evaluation) and one after seven years had passed post-operatively (mid-term evaluation). Changes in ion levels were tested using a Wilcoxon signed-rank test. We identified subgroups at the highest risk of increase using a multivariable linear logistic regression model. Results. There were significant increases in the levels of metal ions for patients who underwent both MoM HRA (Chromium (Cr): 0.5 parts per billion (ppb); Cobalt (Co): 1.1 ppb) and MoM THA (Cr: 0.5 ppb; Co: 0.7 ppb). In a multivariable model considering MoM HRAs, the change in the levels of metal ions was influenced by female gender (Co: Odds Ratio (OR) 1.42; p = 0.002 and Cr: OR 1.08; p = 0.006). The change was found to be irrespective of the initial level for the MoM HRAs, whereas there was a negative relationship between the initial level and the change in the level for those with a MoM THA (Co: OR -0.43; p <  0.001 and Cr: OR -0.14; p = 0.033). Conclusion. The levels of metal ions in the blood increase significantly over the period until mid-term follow-up in patients with both a MoM HRA and those with a MoM THA. We recommend that the levels of metal ions be measured most frequently for women with a MoM HRA. While those with a MoM THA appear to stabilise at a certain level, the accuracy of this trend is not yet clear. Vigilant follow-up is still recommended. . Cite this article: Bone Joint J 2017;99-B(4 Supple B):33–40

Aims. The purpose of this study was to compare two different types of metal-on-metal (MoM) bearing for total hip arthroplasty (THA): one with a large femoral head (38 mm to 52 mm) and the other with a conventional femoral head (28 mm or 32 mm). We compared clinical outcome, blood metal ion levels, and the incidence of pseudotumour in the two groups. Patients and Methods. Between December 2009 and December 2011, 62 patients underwent MoM THA with a large femoral head (Magnum group) and 57 patients an MoM THA with a conventional femoral head (conventional group). Clinical outcome was assessed using the Harris Hip score, University of California, Los Angeles (UCLA) activity score and EuroQol-5D (EQ-5D). Blood metal ion levels were measured and MRI scans were analyzed at a minimum of five years postoperatively. Results. No acetabular component was implanted with more than 50° of inclination in either group. The Harris Hip Score, UCLA activity score, and EQ-5D improved postoperatively in both groups; no significant clinical differences were noted between the groups. The blood cobalt ion levels in the conventional group continued to rise postoperatively to five years while reaching a plateau at two years postoperatively in the Magnum group. At five years, the mean cobalt ion level of 1.16 μg/l (. sd. 1.32) in the Magnum group was significantly lower than the 3.77 μg/l (. sd. 9.80) seen in the conventional group (p = 0.0015). The incidence of moderate to severe pseudotumour was 4.7% in the Magnum group and 20.6% in the conventional group. There were no dislocations in the Magnum group and two in the conventional group. One patient in the Magnum group underwent revision for pseudotumour at 4.7 years postoperatively. Conclusion. At five years, a well-positioned large head MoM THA has a significantly lower level of metal ion release and a lower incidence of moderate to severe pseudotumour than a MoM bearing of conventional size. Cite this article: Bone Joint J 2018;100-B:1018–24

Aims. The Birmingham Hip Resurfacing (BHR) was introduced in 1997 to address the needs of young active patients using a historically proven large-diameter metal-on-metal (MoM) bearing. A single designer surgeon’s consecutive series of 130 patients (144 hips) was previously reported at five and ten years, reporting three and ten failures, respectively. The aim of this study was to extend the follow-up of this original cohort at 25 years. Methods. The study extends the reporting on the first consecutive 144 resurfacing procedures in 130 patients for all indications. All operations were undertaken between August 1997 and May 1998. The mean age at operation was 52.1 years (SD 9.93; 17 to 76), and included 37 female patients (28.5%). Failure was defined as revision of either component for any reason. Kaplan-Meier survival analysis was performed. Routine follow-up with serum metal ion levels, radiographs, and Oxford Hip Scores (OHSs) was undertaken. Results. Overall implant survival was 83.50% (95% confidence interval (CI) 0.79 to 0.90) at 25 years, and the number at risk was 79. Survival in male patients at 25 years was 89.5% (95% CI 0.83 to 0.96) compared to 66.9% for female patients (95% CI 0.51 to 0.83). Ten additional failures occurred in the period of ten to 25 years. These involved an adverse reaction to metal debris in four patients, a periprosthetic femoral neck fracture affecting five patients, and aseptic loosening in one patient. The median chromium levels were 49.50 nmol/l (interquartile range (IQR) 34 to 70), and the median cobalt serum levels were 42 nmol/l (IQR 24.50 to 71.25). The median OHS at last follow-up was 35 (IQR 10 to 48). During the 25-year study period, 29 patients died. Patient survival at 25 years was 75.10% (95% CI 0.67 to 0.83). Conclusion. This study demonstrates that MoM hip resurfacing using the BHR provides a durable alternative to total hip arthroplasty (THA), particularly in younger male patients with osteoarthritis wishing to maintain a high level of function. These results compare favourably to the best results for THAs. Cite this article: Bone Joint J 2024;106-B(6):540–547

Aims. Head-taper corrosion is a cause of failure in total hip arthroplasty (THA). Recent reports have described an increasing number of V40 taper failures with adverse local tissue reaction (ALTR). However, the real incidence of V40 taper damage and its cause remain unknown. The aim of this study was to evaluate the long-term incidence of ALTR in a consecutive series of THAs using a V40 taper and identify potentially related factors. Methods. Between January 2006 and June 2007, a total of 121 patients underwent THA using either an uncemented (Accolade I, made of Ti. 12. Mo. 6. Zr. 2. Fe; Stryker, USA) or a cemented (ABG II, made of cobalt-chrome-molybdenum (CoCrMo); Stryker) femoral component, both with a V40 taper (Stryker). Uncemented acetabular components (Trident; Stryker) with crosslinked polyethylene liners and CoCr femoral heads of 36 mm diameter were used in all patients. At a mean folllow-up of 10.8 years (SD 1.1), 94 patients (79%) were eligible for follow-up (six patients had already undergone a revision, 15 had died, and six were lost to follow-up). A total of 85 THAs in 80 patients (mean age 61 years (24 to 75); 47 (56%) were female) underwent clinical and radiological evaluation, including the measurement of whole blood levels of cobalt and chrome. Metal artifact reduction sequence MRI scans of the hip were performed in 71 patients. Results. A total of 20 ALTRs were identified on MRI, with an incidence of 26%. Patients with ALTR had significantly higher median Co levels compared with those without ALTR (2.96 μg/l (interquartile range (IQR) 1.35 to 4.98) vs 1.44 μg/l (IQR 0.79 to 2.5); p = 0.019). Radiological evidence of osteolysis was also significantly associated with ALTR (p = 0.014). Median Cr levels were not significantly higher in those with ALTR compared with those without one (0.97 μg/l (IQR 0.72 to 1.9) v 0.67 μg/l (IQR 0.5 to 1.19; p = 0.080). BMI, sex, age, type of femoral component, head length, the inclination of the acetabular component, and heterotopic ossification formation showed no significant relationship with ALTR. Conclusion. Due to the high incidence of local ALTR in our cohort after more than ten years postoperatively, we recommend regular follow-up investigation even in asymptomatic patients with V40 taper and metal heads. As cobalt levels correlate with ALTR occurrence, routine metal ion screening and consecutive MRI investigation upon elevation could be discussed. Cite this article: Bone Joint J 2022;104-B(7):852–858

Aims. Cardiac magnetic resonance (CMR) was used to assess whether cardiac function or tissue composition was affected in patients with well-functioning metal-on-metal hip resurfacing arthroplasties (MoMHRA) when compared with a group of controls, and to assess if metal ion levels correlated with any of the functional or structural parameters studied. Patients and Methods. In all, 30 participants with no significant cardiac history were enrolled: 20 patients with well-functioning MoMHRA at mean follow-up of 8.3 years post-procedure (ten unilateral, ten bilateral; 17 men, three women) and a case-matched control group of ten non-MoM total hip arthroplasty patients (six men, four women). The mean age of the whole cohort (study group and controls) at the time of surgery was 50.6 years (41.0 to 64.0). Serum levels of cobalt and chromium were measured, and all patients underwent CMR imaging, including cine, T2* measurements, T1 and T2 mapping, late gadolinium enhancement, and strain measurements. Results. None of the MoMHRA patients showed clinically significant cardiac functional abnormality. The MoMHRA patients had larger indexed right and left end diastolic volumes (left ventricular (LV): 74 ml/m. 2. vs 67 ml/m. 2. , p = 0.045; right ventricular: 80 ml/m. 2. vs 71 ml/m. 2. , p = 0.02). There was a small decrease in T2 time in the MoMHRA patients (median 49 ms vs 54 ms; p = 0.0003). Higher metal ion levels were associated with larger LV volumes and with shorter T2 time. Conclusion. Although cardiac function is not clinically adversely affected in patients with well-functioning MoMHRA, modern imaging is able to demonstrate subtle changes in structure and function of the heart. As these changes correlate with systemic ion measurements, they may be consequences of wear debris deposition. Longer, longitudinal studies are necessary to determine whether cardiac function will become affected. . Cite this article: Bone Joint J 2019;101-B:540–546

Aims. Metal-on-metal hip resurfacing (MoM-HR) has seen decreased usage due to safety and longevity concerns. Joint registries have highlighted the risks in females, smaller hips, and hip dysplasia. This study aimed to identify if reported risk factors are linked to revision in a long-term follow-up of MoM-HR performed by a non-designer surgeon. Methods. A retrospective review of consecutive MoM hip arthroplasties (MoM-HRAs) using Birmingham Hip Resurfacing was conducted. Data on procedure side, indication, implant sizes and orientation, highest blood cobalt and chromium ion concentrations, and all-cause revision were collected from local and UK National Joint Registry records. Results. A total of 243 hips (205 patients (163 male, 80 female; mean age at surgery 55.3 years (range 25.7 to 75.3)) with MoM-HRA performed between April 2003 and October 2020 were included. Mean follow-up was 11.2 years (range 0.3 to 17.8). Osteoarthritis was the most common indication (93.8%), and 13 hips (5.3%; 7M:6F) showed dysplasia (lateral centre-edge angle < 25°). Acetabular cups were implanted at a median of 45.4° abduction (interquartile range 41.9° - 48.3°) and stems neutral or valgus to the native neck-shaft angle. In all, 11 hips (4.5%; one male, ten females) in ten patients underwent revision surgery at a mean of 7.4 years (range 2.8 to 14.2), giving a cumulative survival rate of 94.8% (95% confidence interval (CI) 91.6% to 98.0%) at ten years, and 93.4% (95% CI 89.3% to 97.6%) at 17 years. For aseptic revision, male survivorship was 100% at 17 years, and 89.6% (95% CI 83.1% to 96.7%) at ten and 17 years for females. Increased metal ion levels were implicated in 50% of female revisions, with the remaining being revised for unexplained pain or avascular necrosis. Conclusion. The Birmingham MoM-HR showed 100% survivorship in males, exceeding the National Institute for Health and Care Excellence ‘5% at ten years’ threshold. Female sex and small component sizes are independent risk factors. Dysplasia alone is not a contraindication to resurfacing. Cite this article: Bone Jt Open 2023;4(11):853–858

This study compared component wear rates and pre-revision blood metal ions levels in two groups of failed metal-on-metal hip arthroplasties: hip resurfacing and modular total hip replacement (THR). There was no significant difference in the median rate of linear wear between the groups for both acetabular (p = 0.4633) and femoral (p = 0.0872) components. There was also no significant difference in the median linear wear rates when failed hip resurfacing and modular THR hips of the same type (ASR and Birmingham hip resurfacing (BHR)) were compared. Unlike other studies of well-functioning hips, there was no significant difference in pre-revision blood metal ion levels between hip resurfacing and modular THR. Edge loading was common in both groups, but more common in the resurfacing group (67%) than in the modular group (57%). However, this was not significant (p = 0.3479). We attribute this difference to retention of the neck in resurfacing of the hip, leading to impingement-type edge loading. This was supported by visual evidence of impingement on the femur. These findings show that failed metal-on-metal hip resurfacing and modular THRs have similar component wear rates and are both associated with raised pre-revision blood levels of metal ions

Aims. To determine whether there is any association between glomerular filtration rate (GFR) and blood cobalt (Co) and chromium (Cr) levels in patients with metal-on-metal (MoM) hip arthroplasty. Patients and Methods. We identified 179 patients with a unilateral 36 mm diameter head as part of a stemmed Summit-Pinnacle MoM hip arthroplasty. GFR was calculated using the Modification of Diet in Renal Disease formula. Results. Normal renal function (GFR ≥ 90 ml/min/1.73 m. 2. ) was seen in 74 patients. Mild renal insufficiency (GFR 60 to 89 ml/min/1.73 m. 2. ) was seen in 90 patients and moderate renal insufficiency (GFR 30 to 59 ml/min/1.73 m. 2. ) in 15. There was no statistical difference in Co and Cr levels between patients with normal renal function and those with mild or moderate renal insufficiency. No correlation was seen between creatinine and blood metal ion levels or between GFR and blood metal ion levels. Linear regression analysis did not show any association between Co and Cr levels and GFR. Conclusion. We did not find any association between GFR and blood metal ion levels. Consequently, the accumulation of Co and Cr in blood due to renal insufficiency does not seem to be a major risk in patients with mild or moderate renal insufficiency. Cite this article Bone Joint J 2017;99-B:1147–52

Aims. Modular dual mobility (DM) prostheses in which a cobalt-chromium liner is inserted into a titanium acetabular shell (vs a monoblock acetabular component) have the advantage of allowing supplementary screw fixation, but the potential for corrosion between the liner and acetabulum has raised concerns. While DM prostheses have shown improved stability in patients deemed ‘high-risk’ for dislocation undergoing total hip arthroplasty (THA), their performance in young, active patients has not been reported. This study’s purpose was to assess clinical outcomes, metal ion levels, and periprosthetic femoral bone mineral density (BMD) in young, active patients receiving a modular DM acetabulum and recently introduced titanium, proximally coated, tapered femoral stem design. Patients and Methods. This was a prospective study of patients between 18 and 65 years of age, with a body mass index (BMI) < 35 kg/m. 2. and University of California at Los Angeles (UCLA) activity score > 6, who received a modular cobalt-chromium acetabular liner, highly crosslinked polyethylene mobile bearing, and cementless titanium femoral stem for their primary THA. Patients with a history of renal disease and metal hardware elsewhere in the body were excluded. A total of 43 patients (30 male, 13 female; mean age 52.6 years (. sd. 6.5)) were enrolled. All patients had a minimum of two years’ clinical follow-up. Patient-reported outcome measures, whole blood metal ion levels (ug/l), and periprosthetic femoral BMD were measured at baseline, as well as at one and two years postoperatively. Power analysis indicated 40 patients necessary to demonstrate a five-fold increase in cobalt levels from baseline (alpha = 0.05, beta = 0.80). A mixed model with repeated measures was used for statistical analysis. Results. Mean Harris Hip Scores improved from 54.1 (. sd. 20.5) to 91.2 (. sd. 10.8) at two years postoperatively (p < 0.001). All patients had radiologically well-fixed components, no patients experienced any instability, and no patients required any further intervention. Mean cobalt levels increased from 0.065 ug/l (. sd. 0.03) preoperatively to 0.30 ug/l (. sd. 0.51) at one year postoperatively (p = 0.01) but decreased at two years postoperatively to 0.16 ug/l (. sd. 0.23; p = 0.2). Four patients (9.3%) had a cobalt level outside the reference range (0.03 ug/l to 0.29 ug/l) at two years postoperatively, with values from 0.32 ug/l to 0.94 ug/l. The mean femoral BMD ratio was maintained in Gruen zones 2 to 7 at both one and two years postoperatively using this stem design. At two years postoperatively, mean BMD in the medial calcar was 101.5% of the baseline value. Conclusion. Use of a modular DM prosthesis and cementless, tapered femoral stem has shown encouraging results in young, active patients undergoing primary THA. Elevation in mean cobalt levels and the presence of four patients outside the reference range at two years postoperatively demonstrates the necessity of continued surveillance in this cohort. Cite this article: Bone Joint J 2019;101-B:365–371

Aims. To find out if there is an inverse association between estimated glomerular filtration rate (eGFR) and whole blood cobalt (Co) and chromium (Cr) levels in patients with metal-on-metal (MoM) hip arthroplasties and renal insufficiency, suggesting that renal insufficiency could cause accumulation of Co and Cr in blood. Methods. Out of 2,520 patients with 3,013 MoM hip arthroplasties, we identified 1,244 patients with whole blood Co, Cr, and creatinine measured within no more than a one-year interval. We analyzed the correlation of blood metal ion levels and eGFR to identify a potential trend of accumulating Co or Cr with decreasing eGFR. Results. Of the 1,244 patients, 112 had normal renal function (eGFR > 90 ml/min/1.73 m. 2. ), 715 had mild renal insufficiency (eGFR 60 to 89), 384 had moderate renal insufficiency (eGFR 30 to 59), 27 had severe renal insufficiency (eGFR 15 to 29), and six had end-stage renal insufficiency (eGFR < 15). Median eGFR was 68 ml/min/1.73 m. 2. (interquartile range (IQR) 56 to 82), median whole blood Co was 3.3 µg/l (IQR 1.1 to 9.9), and median Cr was 2.0 µg/l (IQR 1.2 to 3.6). We did not observe an association between decreased eGFR and increased whole blood Co and Cr concentrations, but instead both increased Co and Cr were associated with higher eGFR, indicating better kidney function. Conclusion. As patients with MoM hip arthroplasties get older, the prevalence of renal insufficiency among them will increase, and orthopaedic surgeons will increasingly have to evaluate whether or not this affects patient follow-up. The USA Food and Drug Administration suggests that closer follow-up may be needed for MoM patients with renal insufficiency. We did not observe accumulation of blood Co or Cr in MoM hip arthroplasty patients with mild to severe renal insufficiency. Cite this article: Bone Joint J 2021;103-B(7):1231–1237

Objectives. This study aimed to characterise and qualitatively grade the severity of the corrosion particles released into the hip joint following taper corrosion. Methods. The 26 cases examined were CoC/ABG Modular (n = 13) and ASR/SROM (n = 13). Blood serum metal ion levels were collected before and after revision surgery. The haematoxylin and eosin tissue sections were graded on the presence of fibrin exudates, necrosis, inflammatory cells and corrosion products. The corrosion products were identified based on visible observation and graded on abundance. Two independent observers blinded to the clinical patient findings scored all cases. Elemental analysis was performed on corrosion products within tissue sections. X-Ray diffraction was used to identify crystalline structures present in taper debris. Results. The CoC/ABG Modular patients had a mean age of 64.6 years (49.4 to 76.5) and ASR/SROM patients had a mean age of 58.2 years (33.3 to 85.6). The mean time in situ for CoC/ABG was 4.9 years (2 to 6.4) and ASR/SROM was 6.1 years (2.5 to 8.1). The blood serum metal ion concentrations reduced following revision surgery with the exception of Cr levels within CoC/ABG. The grading of tissue sections showed that the macrophage response and metal debris were significantly higher for the ASR/SROM patients (p < 0.001). The brown/red particles were significantly higher for ASR/SROM (p < 0.001). The taper debris contained traces of titanium oxide, chromium oxide and aluminium nitride. Conclusion. This study characterised and qualitatively graded the severity of the corrosion particles released into the hip joint from tapers that had corrosion damage. Cite this article: S. Munir, R. A. Oliver, B. Zicat, W. L. Walter, W. K. Walter, W. R. Walsh. The histological and elemental characterisation of corrosion particles from taper junctions. Bone Joint Res 2016;5:370–378. DOI: 10.1302/2046-3758.59.2000507

Aims. This study aimed to determine if macrophages can attach and directly affect the oxide layers of 316L stainless steel, titanium alloy (Ti6Al4V), and cobalt-chromium-molybdenum alloy (CoCrMo) by releasing components of these alloys. Methods. Murine peritoneal macrophages were cultured and placed on stainless steel, CoCrMo, and Ti6Al4V discs into a 96-well plate. Cells were activated with interferon gamma and lipopolysaccharide. Macrophages on stainless steel discs produced significantly more nitric oxide (NO) compared to their control counterparts after eight to ten days and remained elevated for the duration of the experiment. Results. On stainless steel, both nonactivated and activated cell groups were shown to have a significant increase in metal ion release for Cr, Fe, and Ni (p < 0.001, p = 0.002, and p = 0.020 respectively) compared with medium only and showed macrophage-sized corrosive pits on the stainless steel surface. On titanium alloy discs there was a significant increase in aluminum (p < 0.001) among all groups compared with medium only. Conclusion. These results indicated that macrophages were able to attach to and affect the oxide surface of stainless steel and titanium alloy discs. Cite this article: Bone Joint J 2020;102-B(7 Supple B):116–121

The Articular Surface Replacement (ASR) hip resurfacing arthroplasty has a failure rate of 12.0% at five years, compared with 4.3% for the Birmingham Hip Resurfacing (BHR). We analysed 66 ASR and 64 BHR explanted metal-on-metal hip replacements with the aim of understanding their mechanisms of failure. We measured the linear wear rates of the acetabular and femoral components and analysed the clinical cause of failure, pre-revision blood metal ion levels and orientation of the acetabular component. There was no significant difference in metal ion levels (chromium, p = 0.82; cobalt, p = 0.40) or head wear rate (p = 0.14) between the two groups. The ASR had a significantly increased rate of wear of the acetabular component (p = 0.03) and a significantly increased occurrence of edge loading (p < 0.005), which can be attributed to differences in design between the ASR and BHR. The effects of differences in design on the in vivo wear rates are discussed: these may provide an explanation as to why the ASR is more sensitive to suboptimal positioning than the BHR

We prospectively assessed the efficacy of a ceramic-on-metal (CoM) hip bearing with uncemented acetabular and femoral components in which cobalt­–chrome acetabular liners and alumina ceramic heads were used. The cohort comprised 94 total hip replacements (THRs) in 83 patients (38 women and 45 men) with a mean age of 58 years (42 to 70). Minimum follow-up was two years. All patients had pre- and post-operative assessment using the Western Ontario and McMaster Universities osteoarthritis index (WOMAC), Oxford hip score and Short-Form 12 scores. All showed a statistically significant improvement from three months post-operatively onwards (all p < 0.001). After two years whole blood metal ion levels were measured and chromosomal analysis was performed. The levels of all metal ions were elevated except vanadium. Levels of chromium, cobalt, molybdenum and titanium were significantly higher in patients who underwent bilateral THR compared with those undergoing unilateral THR (p < 0.001). Chromosomal analysis demonstrated both structural and aneuploidy mutations. There were significantly more breaks and losses than in the normal population (p < 0.001). There was no significant difference in chromosomal aberration between those undergoing unilateral and bilateral procedures (all analyses p ≥ 0.62). The use of a CoM THR is effective clinically in the short-term, with no concerns, but the significance of high metal ion levels and chromosomal aberrations in the long-term remains unclear. Cite this article: Bone Joint J 2013;95-B:1040–44

The recent resurgence in the use of metal-on-metal bearings has led to fresh concerns over metal wear and elevated systemic levels of metal ions. In order to establish if bearing diameter influences the release of metal ions, we compared the whole blood levels of cobalt and chromium (at one year) and the urinary cobalt and chromium output (at one to three and four to six years) following either a 50 mm or 54 mm Birmingham hip resurfacing or a 28 mm Metasul total hip replacement. The whole blood concentrations and daily output of cobalt and chromium in these time periods for both bearings were in the same range and without significant difference

Objectives. Pseudotumours (abnormal peri-prosthetic soft-tissue reactions) following metal-on-metal hip resurfacing arthroplasty (MoMHRA) have been associated with elevated metal ion levels, suggesting that excessive wear may occur due to edge-loading of these MoM implants. This study aimed to quantify in vivo edge-loading in MoMHRA patients with and without pseudotumours during functional activities. Methods. The duration and magnitude of edge-loading in vivo was quantified during functional activities by combining the dynamic hip joint segment contact force calculated from the three-dimensional (3D) motion analysis system with the 3D reconstruction of orientation of the acetabular component and each patient’s specific hip joint centre, based on CT scans. Results. Edge-loading in the hips with pseudotumours occurred with a four-fold increase in duration and magnitude of force compared with the hips without pseudotumours (p = 0.02). Conclusions. The study provides the first in vivo evidence to support that edge-loading is an important mechanism that leads to localised excessive wear (edge-wear), with subsequent elevation of metal ion levels in MoMHRA patients with pseudotumours

Peri-articular soft-tissue masses or ‘pseudotumours’ can occur after large-diameter metal-on-metal (MoM) resurfacing of the hip and conventional total hip replacement (THR). Our aim was to assess the incidence of pseudotumour formation and to identify risk factors for their formation in a prospective cohort study. A total of 119 patients who underwent 120 MoM THRs with large-diameter femoral heads between January 2005 and November 2007 were included in the study. Outcome scores, serum metal ion levels, radiographs and CT scans were obtained. Patients with symptoms or an identified pseudotumour were offered MRI and an ultrasound-guided biopsy. There were 108 patients (109 hips) eligible for evaluation by CT scan at a mean follow-up of 3.6 years (2.5 to 4.5); 42 patients (39%) were diagnosed with a pseudotumour. The hips of 13 patients (12%) were revised to a polyethylene acetabular component with small-diameter metal head. Patients with elevated serum metal ion levels had a four times increased risk of developing a pseudotumour. This study shows a substantially higher incidence of pseudotumour formation and subsequent revisions in patients with MoM THRs than previously reported. Because most revision cases were identified only after an intensive screening protocol, we recommend close monitoring of patients with MoM THR

We evaluated the concentrations of chromium and cobalt ions in blood after metal-on-metal surface replacement arthroplasty using a wrought-forged, high carbon content chromium-cobalt alloy implant in 64 patients. At one year, mean whole blood ion levels were 1.61 μg/L (0.4 to 5.5) for chromium and 0.67 μg/L (0.23 to 2.09) for cobalt. The pre-operative ion levels, component size, female gender and the inclination of the acetabular component were inversely proportional to the values of chromium and/or cobalt ions at one year postoperatively. Other factors, such as age and level of activity, did not correlate with the levels of metal ions. We found that the levels of the ions in the serum were 1.39 and 1.37 times higher for chromium and cobalt respectively than those in the whole blood. The levels of metal ions obtained may be specific to the hip resurfacing implant and reflect its manufacturing process

Aims. The aim of this study was to evaluate blood metal ion levels, leucocyte profiles, and serum cytokines in patients with a total hip arthroplasty (THA) involving modular dual-mobility components. Patients and Methods. A total of 39 patients were recruited, with clinical follow-up of up to two years. Outcome was assessed using the Harris Hip Score (HHS, the 12-Item Short-Form Health Survey (SF-12), the Western Ontario and McMaster Universities Osteoarthritis Index (WOMAC), and a visual analogue scale (VAS) for pain. Blood concentrations of cobalt (Co), chromium (Cr), and serum cytokines were measured. Subpopulations of leucocytes were analyzed by flow cytometry. Results. The clinical performance was good. Blood Co levels (ref 1.0 µg/l) were mildly elevated in seven patients at three months, and two patients at two years’ follow-up. The preoperative Cr levels were normal except for one patient with a detectable Cr (1.2 µg/l). Cr levels were detectable in three patients at three months, two patients at one year, and three patients at two years’ follow-up. No patients had symptoms suggestive of failure. Although flow cytometry showed constant circulating leucocyte profiles, there was a significant reduction of serum interleukin (IL)-4, IL-5, and interferon gamma (IFNγ) postoperatively compared with the preoperative levels (p < 0.05). Conclusion. These results suggest that THA using modular dual-mobility components is safe. This allows an opportunity to use a large femoral head and a thick polyethylene bearing surface, which is especially useful in revision procedures or high-risk situations when added stability is required. Cite this article: Bone Joint J 2019;101-B:1035–1041

Metal-on-metal bearings are being increasingly used in young patients. The potential adverse effects of systemic metal ion elevation are the subject of ongoing investigation. The purpose of this study was to investigate whether cobalt and chromium ions cross the placenta of pregnant women with a metal-on-metal hip resurfacing and reach the developing fetus. Whole blood levels were estimated using high-resolution inductively-coupled plasma mass spectrometry. Our findings showed that cobalt and chromium are able to cross the placenta in the study patients with metal-on-metal hip resurfacings and in control subjects without any metal implants. In the study group the mean concentrations of cobalt and chromium in the maternal blood were 1.39 μg/l (0.55 to 2.55) and 1.28 μg/l (0.52 to 2.39), respectively. The mean umbilical cord blood concentrations of cobalt and chromium were comparatively lower, at 0.839 μg/l (0.42 to 1.75) and 0.378 μg/l (0.14 to 1.03), respectively, and this difference was significant with respect to chromium (p < 0.05). In the control group, the mean concentrations of cobalt and chromium in the maternal blood were 0.341 μg/l (0.18 to 0.54) and 0.199 μg/l (0.12 to 0.33), and in the umbilical cord blood they were 0.336 μg/l (0.17 to 0.5) and 0.194 μg/l (0.11 to 0.56), respectively. The differences between the maternal and umbilical cord blood levels in the controls were marginal, and not statistically significant (p > 0.05). The mean cord blood level of cobalt in the study patients was significantly greater than that in the control group (p < 0.01). Although the mean umbilical cord blood chromium level was nearly twice as high in the study patients (0.378 μg/l) as in the controls (0.1934 μg/l), this difference was not statistically significant. (p > 0.05). The transplacental transfer rate was in excess of 95% in the controls for both metals, but only 29% for chromium and 60% for cobalt in study patients, suggesting that the placenta exerts a modulatory effect on the rate of metal ion transfer

Aims. The aim of this study was to assess the functional gain achieved following hip resurfacing arthroplasty (HRA). Patients and Methods. A total of 28 patients (23 male, five female; mean age, 56 years (25 to 73)) awaiting Birmingham HRA volunteered for this prospective gait study, with an age-matched control group of 26 healthy adults (16 male, ten female; mean age, 56 years (33 to 84)). The Oxford Hip Score (OHS) and gait analysis using an instrumented treadmill were used preoperatively and more than two years postoperatively to measure the functional change attributable to the intervention. Results. The mean OHS improved significantly from 27 to 46 points (p < 0.001) at a mean of 29 months (12 to 60) after HRA. The mean metal ion levels at a mean 32 months (13 to 60) postoperatively were 1.71 (0.77 to 4.83) µg/l (ppb) and 1.77 (0.68 to 4.16) µg/l (ppb) for cobalt and chromium, respectively. When compared with healthy controls, preoperative patients overloaded the contralateral good hip, limping significantly. After HRA, patients walked at high speeds, with symmetrical gait, statistically indistinguishable from healthy controls over almost all characteristics. The control group could only be distinguished by an increased push-off force at higher speeds, which may reflect the operative approach. Conclusion. Patients undergoing HRA improved their preoperative gait pattern of a significant limp to a symmetrical gait at high speeds and on inclines, almost indistinguishable from normal controls. HRA with an approved device offers substantial functional gains, almost indistinguishable from healthy controls. Cite this article: Bone Joint J 2019;101-B:1423–1430

Aims. Modular dual-mobility constructs reduce the risk of dislocation after revision total hip arthroplasty (THA). However, questions about metal ions from the cobalt-chromium (CoCr) liner persist, and are particularly germane to patients being revised for adverse local tissue reactions (ALTR) to metal. We determined the early- to mid-term serum Co and Cr levels after modular dual-mobility components were used in revision and complex primary THAs, and specifically included patients revised for ALTR. Patients and Methods. Serum Co and Cr levels were measured prospectively in 24 patients with a modular dual-mobility construct and a ceramic femoral head. Patients with CoCr heads or contralateral THAs with CoCr heads were excluded. The mean age was 63 years (35 to 83), with 13 patients (54%) being female. The mean follow-up was four years (2 to 7). Indications for modular dual-mobility were prosthetic joint infection treated with two-stage exchange and subsequent reimplantation (n = 8), ALTR revision (n = 7), complex primary THA (n = 7), recurrent instability (n = 1), and periprosthetic femoral fracture (n = 1). The mean preoperative Co and Cr in patients revised for an ALTR were 29.7 μg/l (2 to 146) and 21.5 μg/l (1 to 113), respectively. Results. Mean Co and Cr levels were 0.30 μg/l and 0.76 μg/l, respectively, at the most recent follow-up. No patient had a Co level ≥ 1 μg/l. Only one patient had a Cr level ≥ 1 μg/l. That patient’s Cr level was 12 μg/l at 57 months after revision THA for ALTR (and decreased ten-fold from a preoperative Cr of 113 μg/l). Conclusion. At a mean of four years, no patient with a modular dual-mobility construct and ceramic femoral head had elevated Co levels, including seven patients revised specifically for ALTR. While further studies are required, we support the selective use of a modular dual-mobility construct in revision and complex primary THAs for patients at high risk for instability. Cite this article: Bone Joint J 2019;101-B(6 Supple B):57–61

Aims . The primary aim of this independent prospective randomised trial was to compare serum metal ion levels for ceramic-on-metal (CoM) and metal-on-metal (MoM) bearing surfaces in total hip arthroplasty (THA). Our one-year results demonstrated elevation in metal ion levels above baseline with no significant difference between the CoM and MoM groups. This paper reviews the five-year data. Patients and Methods. The implants used in each patient differed only in respect to the type of femoral head (ceramic or metal). At five-year follow-up of the 83 enrolled patients, data from 67 (36 CoM, 31 MoM) was available for comparison. Results. The mean serum cobalt (Co) and chromium (Cr) ion levels remained above baseline in both groups (CoM: Co 1.16 μg/l (0.41 to 14.67), Cr 1.05 μg/l (0.16 to 12.58); MoM: Co 2.93 μg/l (0.35 to 30.29), Cr 1.85 μg/l (0.36 to 17.00)) but the increase was significantly less in the CoM cohort (Co difference p = 0.001, Cr difference p = 0.002). These medium-term results, coupled with lower revision rates from national joint registries, suggest that the performance of CoM THA may be superior to that of MoM. . Conclusion. While both bearing combinations have since been withdrawn these results provide useful information for planning clinical surveillance of CoM THAs and warrants continued monitoring. Cite this article: Bone Joint J 2017;99-B:1298–1303

Aims. A contact patch to rim (CPR) distance of < 10 mm has been associated with edge-loading and excessive wear. However, not all arthroplasties with a low CPR distance show problems with wear. Therefore, CPR distance may not be the only variable affecting the post-operative metal ion concentrations. Patients and Methods. We used multiple logistic regression to determine what variables differed between the patients who had high and low cobalt (CoS) and chromium (CrS) serum ion concentrations within a cohort of patients with low (< 10 mm) CPR distances. A total of 56 patients treated with unilateral hip resurfacing arthroplasty (HRA) had CoS and CrS ion studies performed more than one year after surgery. The mean age of the patients at the time of surgery was 51.7 years (29 to 70), with 38 women (68%) and 18 men (32%). Results. It was seen that 47 patients had low ion levels (< 7µg/L) and nine had high ion levels (≥ 7µg/L). We found increased risks of high wear with decreasing CPR distance. Conclusion. The use of CPR distance measurements to predict hips at risk for elevated wear is needed for all patients with HRA. We recommend that patients with low CPR distances have at least one serum ion study performed while patients with CPR distance > 10 mm do not need routine ion studies. We believe that patients with low CPR distance and low ions do not need repeat ion studies unless the patient becomes symptomatic or has substantial radiographic changes. Cite this article: Bone Joint J 2017;99-B:865–71