Objectives

Third-body wear is believed to be one trigger for adverse results with metal-on-metal (MOM) bearings. Impingement and subluxation may release metal particles from MOM replacements. We therefore challenged MOM bearings with relevant debris types of cobalt–chrome alloy (CoCr), titanium alloy (Ti6Al4V) and polymethylmethacrylate bone cement (PMMA).

The role of vacuum mixing on the reduction of porosity and on the clinical performance of cemented total hip replacements remains uncertain. We have used paired femoral constructs prepared with either hand-mixed or vacuum-mixed cement in a cadaver model which simulated intra-operative conditions during cementing of the femoral component. After the cement had cured, the distribution of its porosity was determined, as was the strength of the cement-stem and cement-bone interfaces.

The overall fraction of the pore area was similar for both hand-mixed and vacuum-mixed cement (hand 6%; vacuum 5.7%; paired t-test, p = 0.187). The linear pore fractions at the interfaces were also similar for the two techniques. The pore number-density was much higher for the hand-mixed cement (paired t-test, p = 0.0013). The strength of the cement-stem interface was greater with the hand-mixed cement (paired t-test, p = 0.0005), while the strength of the cement-bone interface was not affected by the conditions of mixing (paired t-test, p = 0.275). The reduction in porosity with vacuum mixing did not affect the porosity of the mantle, but the distribution of the porosity can be affected by the technique of mixing used.

Synthetic bone substitutes provide an alternative to autograft but do not give equivalent clinical results. Their performance may be enhanced by adding osteogenic growth factors. In this study, TGFβ1 was absorbed on to a carrier of β tricalcium phosphate and Gelfoam® and used to fill a defect around a tibial implant in a rat model of revision arthoplasty.

We added 0.0, 0.02 μg, 0.1 μg or 1.0 μg of TGFβ1 to the carrier and then implanted it around an hydroxyapatite-coated stainless-steel pin in the proximal tibia of rats. The tibiae were harvested at three, six or 26 weeks and the amount of bone formation and ceramic resorption were assessed.

TGFβ1 had no effect on the amount of bone in the defect, the amount of fluorescent label incorporated or the rate of mineral apposition. The growth factor did not significantly affect the amount of β TCP remaining in the tissue at any of the time points.

Metal-on-metal (MOM) bearings for hip arthroplasty are increasing in popularity. Concern remains, however, regarding the potential toxicological effects of the metal ions which these bearings release.

The serum levels of cobalt and chromium in 22 patients who had undergone MOM resurfacing arthroplasty were compared with a matched group of 22 patients who had undergone 28 mm MOM total hip arthroplasty (THA).

At a median of 16 months (7 to 56) after resurfacing arthroplasty, we found the median serum levels of cobalt and chromium to be 38 nmol/l (14 to 44) and 53 nmol/l (23 to 165) respectively. These were significantly greater than the levels after 28 mm MOM THA which were 22 nmol/l (15 to 87, p = 0.021) and 19 nmol/l (2 to 58, p < 0.001) respectively.

Since the upper limit for normal patients without implants is typically 5 nmol/l, both groups had significantly raised levels of metal ions. MOM bearings of large diameter, however, result in a greater systemic exposure of cobalt and chromium ions than bearings of small diameter. This may be of relevance for potential long-term side-effects. It is not known to what extent this difference is due to corrosion of the surfaces of the component or of the wear particles produced.

Chondrocytes at the lower zone of the growth plate must be eliminated to facilitate longitudinal growth; this is generally assumed to involve apoptosis. We attempted to provide definitive electron-microscopic evidence of apoptosis in chondrocytes of physes and chondroepiphyses in the rabbit. We were, however, unable to find a single chondrocyte with the ultrastructure of ‘classical’ apoptosis in vivo, although such a cell was found in vitro. Instead, condensed chondrocytes had a convoluted nucleus with patchy chromatin condensations while the cytoplasm was dark with excessive amounts of endoplasmic reticulum. These cells were termed ‘dark chondrocytes’. A detailed study of their ultrastructure combined with localisation methods in situ suggested a different mechanism of programmed cell death. In addition, another type of death was identified among the immature chondrocytes of the chondroepiphysis. These cells had the same nucleus as dark chondrocytes, but the lumen of the endoplasmic reticulum had expanded to fill the entire non-nuclear space, and all cytoplasm and organelles had been reduced to dark, worm-like inclusions. Since these cells appeared to be ‘in limbo’, they were termed ‘paralysed’ cells. It is proposed that ‘dark chondrocytes’ and ‘paralysed cells’ are examples of physiological cell death which does not involve apoptosis. It is possible that the confinement of chondrocytes within their lacunae, which would prevent phagocytosis of apoptotic bodies, necessitates different mechanisms of elimination.