Femoral stems with exchangeable (modular) necks were introduced
to offer surgeons an increased choice when determining the version,
offset and length of the femoral neck during total hip arthroplasty
(THA). It was hoped that this would improve outcomes and reduce
complications, particularly dislocation. In 2010, the Australian Orthopaedic
Association National Joint Replacement Registry (AOANJRR) first
reported an increased rate of revision after primary THA using femoral
stems with an exchangeable neck. The aim of this study was to provide
a more comprehensive up-to-date analysis of primary THA using femoral
stems with exchangeable and fixed necks. The data included all primary THA procedures performed for osteoarthritis
(OA), reported to the AOANJRR between 01 September 1999 and 31 December
2014. There were 9289 femoral stems with an exchangeable neck and
253 165 femoral stems with a fixed neck. The characteristics of
the patients and prostheses including the bearing surface and stem/neck
metal combinations were examined using Cox proportional hazard ratios
(HRs) and Kaplan-Meier estimates of survivorship. Aims
Materials and Methods
The use of ceramic femoral heads in total hip arthroplasty (THA) has increased due to their proven low bearing wear characteristics. Ceramic femoral heads are also thought to reduce wear and corrosion at the head-stem junction with titanium (Ti) stems when compared with metal heads. We sought to evaluate taper damage of ceramic compared with metal heads when paired with cobalt chromium (CoCr) alloy stems in a single stem design. This retrieval study involved 48 total hip arthroplasties (THAs) with CoCr V40 trunnions paired with either CoCr (n = 21) or ceramic (n = 27) heads. The taper junction of all hips was evaluated for fretting/corrosion damage and volumetric material loss using a roundness-measuring machine. We used linear regression analysis to investigate taper damage differences after adjusting for potential confounding variables.Objectives
Methods
The aim of this study was to identify patient- and surgery-related
risk factors for sustaining an early periprosthetic fracture following
primary total hip arthroplasty (THA) performed using a double-tapered
cementless femoral component (Bi-Metric femoral stem; Biomet Inc.,
Warsaw, Indiana). A total of 1598 consecutive hips, in 1441 patients receiving
primary THA between January 2010 and June 2015, were retrospectively
identified. Level of pre-operative osteoarthritis, femoral Dorr
type and cortical index were recorded. Varus/valgus placement of
the stem and canal fill ratio were recorded post-operatively. Periprosthetic
fractures were identified and classified according to the Vancouver
classification. Regression analysis was performed to identify risk
factors for early periprosthetic fracture.Aims
Patients and Methods
To determine the effect of a change in design of a cementless
ceramic acetabular component in fixation and clinical outcome after
total hip arthroplasty We compared 342 hips (302 patients) operated between 1999 and
2005 with a relatively smooth hydroxyapatite coated acetabular component
(group 1), and 337 hips (310 patients) operated between 2006 and
2011 using a similar acetabular component with a macrotexture on
the entire outer surface of the component (group 2). The mean age of
the patients was 53.5 (14 to 70) in group 1 and 53.0 (15 to 70)
in group 2. The mean follow-up was 12.7 years (10 to 17) for group
1 and 7.2 years (4 to 10) for group 2.Aims
Patients and Methods
We compared the incidence of pseudotumours after
large head metal-on-metal (MoM) total hip arthroplasty (THA) with
that after conventional metal-on-polyethylene (MoP) THA and assessed
the predisposing factors to pseudotumour formation. From a previous randomised controlled trial which compared large
head (38 mm to 60 mm) cementless MoM THA with conventional head
(28 mm) cementless MoP THA, 93 patients (96 THAs: 41 MoM (21 males,
20 females, mean age of 64 years, standard deviation ( The incidence of pseudotumours, measured using a standardised
CT protocol was 22 (53.7%) after MoM THA and 12 (21.8%) after MoP
THA. Women with a MoM THA were more likely to develop a pseudotumour
than those with a MoP THA (15 Contrary to popular belief, pseudotumours occur frequently around
MoP THAs. Women with a MoM THA and an elevated cobalt level are
at greatest risk. In this study, pseudotumours had no effect on
the functional outcome after either large head MoM or conventional
MoP THA. Cite this article:
The aims of this retrospective study were to report the feasibility
of using 3D-printing technology for patients with a pelvic tumour
who underwent reconstruction. A total of 35 patients underwent resection of a pelvic tumour
and reconstruction using 3D-printed endoprostheses between September
2013 and December 2015. According to Enneking’s classification of
bone defects, there were three Type I lesions, 12 Type II+III lesions,
five Type I+II lesions, two Type I+II+III lesions, ten type I+II+IV
lesions and three type I+II+III+IV lesions. A total of three patients
underwent reconstruction using an iliac prosthesis, 12 using a standard
hemipelvic prosthesis and 20 using a screw-rod connected hemipelvic
prosthesis.Aims
Patients and Methods
Little biomechanical information is available about kinematically aligned (KA) total knee arthroplasty (TKA). The purpose of this study was to simulate the kinematics and kinetics after KA TKA and mechanically aligned (MA) TKA with four different limb alignments. Bone models were constructed from one volunteer (normal) and three patients with three different knee deformities (slight, moderate and severe varus). A dynamic musculoskeletal modelling system was used to analyse the kinematics and the tibiofemoral contact force. The contact stress on the tibial insert, and the stress to the resection surface and medial tibial cortex were examined by using finite element analysis.Objectives
Materials and Methods
We report on the outcome of the Synergy cementless femoral stem
with a minimum follow-up of 15 years (15 to 17). A retrospective review was undertaken of a consecutive series
of 112 routine primary cementless total hip arthroplasties (THAs)
in 102 patients (112 hips). There were 60 female and 42 male patients
with a mean age of 61 years (18 to 82) at the time of surgery. A
total of 78 hips in the 69 patients remain Aims
Patients and Methods
Studies reporting specifically on squeaking in total hip arthroplasty have focused on cementless, and not on hybrid, fixation. We hypothesised that the cement mantle of the femur might have a damping effect on the sound transmitted through the metal stem. The objective of this study was to test the effect of cement on sound propagation along different stem designs and under different fixation conditions. An Objectives
Methods
Tribocorrosion at the head–neck taper interface
– so-called ‘taperosis’ – may be a source of metal ions and particulate
debris in metal-on-polyethylene total hip arthroplasty (THA). We examined the effect of femoral head length on fretting and
corrosion in retrieved head–neck tapers Head length was observed to affect fretting (p = 0.03), with
28 mm + 8 mm femoral heads showing greater total fretting scores
than all other head lengths. The central zone of the femoral head
bore taper was subject to increased fretting damage (p = 0.01),
regardless of head length or stem offset. High-offset femoral stems
were associated with greater total fretting of the bore taper (p
= 0.04). Increased fretting damage is seen with longer head lengths and
high-offset femoral stems, and occurs within a central concentric
zone of the femoral head bore taper. Further investigation is required
to determine the effect of increased head size, and variations in
head–neck taper design. Cite this article:
One method of femoral head preservation following avascular necrosis
(AVN) is core decompression and insertion of a tantalum rod. However,
there may be a high failure rate associated with this procedure.
The purpose of this study was to document the clinical and radiological
outcomes following total hip arthroplasty (THA) subsequent to failed
tantalum rod insertion. A total of 37 failed tantalum rods requiring total hip arthroplasty
were identified from a prospective database. There were 21 hips
in 21 patients (12 men and nine women, mean age 37 years, 18 to
53) meeting minimum two year clinical and radiographic follow-up
whose THAs were carried out between November 2002 and April 2013
(mean time between tantalum rod implantation and conversion to a
THA was 26 months, 6 to 72). These were matched by age and gender
to individuals (12 men, nine women, mean age 40 years, 18 to 58)
receiving THA for AVN without prior tantalum rod insertion.Aims
Patients and Methods
Periprosthetic femoral fractures (PFF) following total hip arthroplasty
(THA) are devastating complications that are associated with functional
limitations and increased overall mortality. Although cementless
implants have been associated with an increased risk of PFF, the
precise contribution of implant geometry and design on the risk
of both intra-operative and post-operative PFF remains poorly investigated.
A systematic review was performed to aggregate all of the PFF literature
with specific attention to the femoral implant used. A systematic search strategy of several journal databases and
recent proceedings from the American Academy of Orthopaedic Surgeons
was performed. Clinical articles were included for analysis if sufficient
implant description was provided. All articles were reviewed by
two reviewers. A review of fundamental investigations of implant
load-to-failure was performed, with the intent of identifying similar
conclusions from the clinical and fundamental literature.Aims
Patients and Methods
Symptomatic cobalt toxicity from a failed total
hip replacement is a rare but devastating complication. It has been reported
following revision of fractured ceramic components, as well as in
patients with failed metal-on-metal articulations. Potential clinical
findings include fatigue, weakness, hypothyroidism, cardiomyopathy,
polycythaemia, visual and hearing impairment, cognitive dysfunction,
and neuropathy. We report a case of an otherwise healthy 46-year-old
patient, who developed progressively worsening symptoms of cobalt
toxicity beginning approximately six months following synovectomy
and revision of a fractured ceramic-on-ceramic total hip replacement
to a metal-on-polyethylene bearing. The whole blood cobalt levels
peaked at 6521 µg/l. The patient died from cobalt-induced cardiomyopathy.
Implant retrieval analysis confirmed a loss of 28.3 g mass of the
cobalt–chromium femoral head as a result of severe abrasive wear
by ceramic particles embedded in the revision polyethylene liner.
Autopsy findings were consistent with heavy metal-induced cardiomyopathy. We recommend using new ceramics at revision to minimise the risk
of wear-related cobalt toxicity following breakage of ceramic components. Cite this article:
We conducted a case-control study to examine
the merit of silver-coated tumour prostheses. We reviewed 85 patients
with Agluna-treated (silver-coated) tumour implants treated between
2006 and 2011 and matched them with 85 control patients treated
between 2001 and 2011 with identical, but uncoated, tumour prostheses. In all, 106 men and 64 women with a mean age of 42.2 years (18.4
to 90.4) were included in the study. There were 50 primary reconstructions
(29.4%); 79 one-stage revisions (46.5%) and 41 two-stage revisions
for infection (24.1%). The overall post-operative infection rate of the silver-coated
group was 11.8% compared with 22.4% for the control group (p = 0.033,
chi-square test). A total of seven of the ten infected prostheses
in the silver-coated group were treated successfully with debridement,
antibiotics, and implant retention compared with only six of the
19 patients (31.6%) in the control group (p = 0.048, chi-square
test). Three patients in the silver-coated group (3.5%) and 13 controls
(15.3%) had chronic periprosthetic infection (p = 0.009, chi-square
test). The overall success rates in controlling infection by two-stage
revision in the silver-coated group was 85% (17/20) compared with
57.1% (12/21) in the control group (p = 0.05, chi-square test).
The Agluna-treated endoprostheses were associated with a lower rate
of early periprosthetic infection. These silver-treated implants
were particularly useful in two-stage revisions for infection and
in those patients with incidental positive cultures at the time
of implantation of the prosthesis. Debridement with antibiotic treatment and retention of the implant
appeared to be more successful with silver-coated implants. Cite this article:
Computed tomography (CT) plays an important role in evaluating wear and periacetabular osteolysis (PAO) in total hip replacements. One concern with CT is the high radiation exposure since standard pelvic CT provides approximately 3.5 millisieverts (mSv) of radiation exposure, whereas a planar radiographic examination with three projections totals approximately 0.5 mSv. The objective of this study was to evaluate the lowest acceptable radiation dose for dual-energy CT (DECT) images when measuring wear and periacetabular osteolysis in uncemented metal components. A porcine pelvis with bilateral uncemented hip prostheses and with known linear wear and acetabular bone defects was examined in a third-generation multidetector DECT scanner. The examinations were performed with four different radiation levels both with and without iterative reconstruction techniques. From the high and low peak kilo voltage acquisitions, polychrmoatic images were created together with virtual monochromatic images of energies 100 kiloelectron volts (keV) and 150 keV.Objectives
Materials and Methods
Following the recall of modular neck hip stems
in July 2012, research into femoral modularity will intensify over
the next few years. This review aims to provide surgeons with an
up-to-date summary of the clinically relevant evidence. The development
of femoral modularity, and a classification system, is described.
The theoretical rationale for modularity is summarised and the clinical
outcomes are explored. The review also examines the clinically relevant problems
reported following the use of femoral stems with a modular neck. Joint replacement registries in the United Kingdom and Australia
have provided data on the failure rates of modular devices but cannot
identify the mechanism of failure. This information is needed to
determine whether modular neck femoral stems will be used in the
future, and how we should monitor patients who already have them implanted. Cite this article:
Modular junctions are ubiquitous in contemporary hip arthroplasty. The head-trunnion junction is implicated in the failure of large diameter metal-on-metal (MoM) hips which are the currently the topic of one the largest legal actions in the history of orthopaedics (estimated costs are stated to exceed $4 billion). Several factors are known to influence the strength of these press-fit modular connections. However, the influence of different head sizes has not previously been investigated. The aim of the study was to establish whether the choice of head size influences the initial strength of the trunnion-head connection. Ti-6Al-4V trunnions (n = 60) and two different sizes of cobalt-chromium (Co-Cr) heads (28 mm and 36 mm; 30 of each size) were used in the study. Three different levels of assembly force were considered: 4 kN; 5 kN; and 6 kN (n = 10 each). The strength of the press-fit connection was subsequently evaluated by measuring the pull-off force required to break the connection. The statistical differences in pull-off force were examined using a Kruskal–Wallis test and two-sample Mann–Whitney U test. Finite element and analytical models were developed to understand the reasons for the experimentally observed differences.Objectives
Materials and Methods
Until now, there has been no consensus as to whether stemmed
acetabular components are appropriate for use in patients undergoing
revision total hip arthroplasty (THA) who have major acetabular
defects or pelvic discontinuity. We wished to address this deficiency
in the literature. We carried out a retrospective study of 35 patients (six men
and 29 women) with a mean age of 68 years (37 to 87), with major
acetabular defects who underwent revision THA between 2000 and 2012.Aim
Patients and Methods
We wished to investigate the influence of metal debris exposure
on the subsequent immune response and resulting soft-tissue injury
following metal-on-metal (MoM) hip arthroplasty. Some reports have
suggested that debris generated from the head-neck taper junction
is more destructive than equivalent doses from metal bearing surfaces. We investigated the influence of the source and volume of metal
debris on chromium (Cr) and cobalt (Co) concentrations in corresponding
blood and hip synovial fluid samples and the observed agglomerated
particle sizes in excised tissues using multiple regression analysis
of prospectively collected data. A total of 199 explanted MoM hips
(177 patients; 132 hips female) were analysed to determine rates
of volumetric wear at the bearing surfaces and taper junctions. Aims
Patients and Methods
A 70-year-old man with an uncemented metal-on-polyethylene
total hip prosthesis underwent revision arthroplasty 33 months later
because of pain, swelling and recurrent dislocation. There appeared
to be corrosion and metal release from the prosthetic head, resulting
in pseudotumour formation and severe local soft-tissue destruction.
The corrosion occurred at the junction between the titanium-molybdenum-zirconium-iron
taper and the cobalt-chrome-molybdenum head, but the mechanism was unproven.