There are no recent studies comparing cable with wire for the fixation of osteotomies or fractures in total hip replacement (THR). Our objective was to evaluate the five-year clinical and radiological outcomes and complication rates of the two techniques. We undertook a review including all primary and revision THRs performed in one hospital between 1996 and 2005 using cable or wire fixation. Clinical and radiological evaluation was performed five years post-operatively. Cables were used in 51 THRs and wires in 126, and of these, 36 THRs with cable (71%) and 101 with wire (80%) were evaluated at follow-up. The five-year radiographs available for 33 cable and 91 wire THRs revealed rates of breakage of fixation of 12 of 33 (36%) and 42 of 91 (46%), respectively. With cable there was a significantly higher risk of metal debris (68% vs 9%; adjusted relative risk (RR) 6.6; 95% confidence interval (CI) 3.0 to 14.1), nonunion (36% vs 21%; adjusted RR 2.0; 95% CI 1.0 to 3.9) and osteolysis around the material, acetabulum or femur (61% vs 19%; adjusted RR 3.9; 95% CI 2.3 to 6.5). Cable breakage increased the risk of osteolysis to 83%. There was a trend towards foreign-body reaction and increased infection with cables. Clinical results did not differ between the groups.

In conclusion, we found a higher incidence of complications and a trend towards increased infection and foreign-body reaction with the use of cables.

Bioengineering reasons for increased wear and failure of metal-on-metal (MoM) bearings in hip prostheses have been described. Low wear occurs in MoM hips when the centre of the femoral head is concentric with the centre of the acetabular component and the implants are correctly positioned. Translational or rotational malpositioning of the components can lead to the contact-patch of the femoral component being displaced to the rim of the acetabular component, resulting in a ten- to 100-fold increase in wear and metal ion levels. This may cause adverse tissue reactions, loosening of components and failure of the prosthesis.

The aim of this study was to investigate the possible benefit of large-head metal-on-metal bearing on a stem for primary hip replacement compared with a 28 mm diameter conventional metal-on-polyethylene bearing in a prospective randomised controlled trial. We investigated cemented stem behaviour between these two different bearings using Einzel-Bild-Röntgen-Analyse, clinical and patient reported measures (Harris hip score, Western Ontario and McMaster Universities osteoarthritis index, Short Form-36 and satisfaction) and whole blood metal ion levels at two years. A power study indicated that 50 hips were needed in each group to detect subsidence of > 5 mm at two years with a p-value of < 0.05.

Significant improvement (p < 0.001) was found in the mean clinical and patient reported outcomes at two years for both groups. Comparison of outcomes between the groups at two years showed no statistically significant difference for mean stem migration, clinical and patient reported outcomes; except overall patient satisfaction which was higher for metal-on-metal group (p = 0.05). Metal ion levels were raised above the Medicines and Healthcare products Regulatory Agency advised safety level (7 µg per litre) in 20% of the metal-on-metal group and in one patient in metal-on-polyethylene group (who had a metal-on-metal implant on the contralateral side). Two patients in the metal-on-metal group were revised, one for pseudotumour and one for peri-prosthetic fracture.

Use of large modular heads is associated with a risk of raised whole blood metal ion levels despite using a proven bearing from resurfacing. The head-neck junction or excess stem micromotion are possibly the weak links warranting further research.

This systematic review of the literature summarises the clinical experience with ceramic-on-ceramic hip bearings over the past 40 years and discusses the concerns that exist in relation to the bearing combination. Loosening, fracture, liner chipping on insertion, liner canting and dissociation, edge-loading and squeaking have all been reported, and the relationship between these issues and implant design and surgical technique is investigated. New design concepts are introduced and analysed with respect to previous clinical experience.

We retrospectively analysed concentrations of chromium and cobalt ions in samples of synovial fluid and whole blood taken from a group of 92 patients with failed current-generation metal-on-metal hip replacements. We applied acid oxidative digestion to our trace metal analysis protocol, which found significantly higher levels of metal ion concentrations in blood and synovial fluid than a non-digestive method. Patients were subcategorised by mode of failure as either ‘unexplained pain’ or ‘defined causes’. Using this classification, chromium and cobalt ion levels were present over a wider range in synovial fluid and not as strongly correlated with blood ion levels as previously reported. There was no significant difference between metal ion concentrations and manufacturer of the implant, nor femoral head size below or above 50 mm. There was a moderately positive correlation between metal ion levels and acetabular component inclination angle as measured on three-dimensional CT imaging.

Our results suggest that acid digestion of samples of synovial fluid samples is necessary to determine metal ion concentrations accurately so that meaningful comparisons can be made between studies.

Between 1986 and 1991 we implanted 331 consecutive Furlong hydroxyapatite-coated femoral components of a total hip replacement in 291 patients. A cemented acetabular prosthesis was used in 217 hips and a hydroxyapatite-coated component in 114. We describe the long-term clinical and radiological survival of the femoral component at a mean follow-up of 17.5 years (15 to 21). Only two patients (0.68%) were lost to follow-up. With revision of the femoral component for any reason as the endpoint, the survival at a mean of 17 years was 97.4% (95% confidence interval 94.1 to 99.5), and with revision for aseptic loosening as the endpoint it was 100%. The survival at a maximum of 21 years with revision of the femoral component for any reason as the endpoint was 97.4% (95% confidence interval 81.0 or 99.5). These results compare favourably with the best long-term results of cemented or uncemented femoral components used in total hip replacement.

The management of bone loss in revision replacement of the knee remains a challenge despite an array of options available to the surgeon. Bone loss may occur as a result of the original disease, the design of the prosthesis, the mechanism of failure or technical error at initial surgery. The aim of revision surgery is to relieve pain and improve function while addressing the mechanism of failure in order to reconstruct a stable platform with transfer of load to the host bone. Methods of reconstruction include the use of cement, modular metal augmentation of prostheses, custom-made, tumour-type or hinged implants and bone grafting.

The published results of the surgical techniques are summarised and a guide for the management of bone defects in revision surgery of the knee is presented.

A clinical and radiological study was conducted on 97 total hip replacements performed for congenital hip dislocation in 79 patients between 1989 and 1998 using a three-dimensional custom-made cementless stem. The mean age at operation was 48 years (17 to 72) and the mean follow-up was for 123 months (83 to 182).

According to the Crowe classification, there were 37 class I, 28 class II, 13 class III and 19 class IV hips. The mean leg lengthening was 25 mm (5 to 58), the mean pre-operative femoral anteversion was 38.6° (2° to 86°) and the mean correction in the prosthetic neck was −23.6° (−71° to 13°). The mean Harris hip score improved from 58 (15 to 84) to 93 (40 to 100) points. A revision was required in six hips (6.2%). The overall survival rate was 89.5% (95% confidence interval 89.2 to 89.8) at 13 years when two hips were at risk.

This custom-made cementless femoral component, which can be accommodated in the abnormal proximal femur and will correct the anteversion and frontal offset, provided good results without recourse to proximal femoral corrective osteotomy.

We reviewed the initial post-operative radiographs of the Trident acetabulum and identified a problem with seating of the metal-backed ceramic liner. We identified 117 hips in 113 patients who had undergone primary total hip replacement using the Trident shell with a metal-backed alumina liner. Of these, 19 (16.4%) were noted to have incomplete seating of the liner, as judged by plain anteroposterior and lateral radiographs. One case of complete liner dissociation necessitating early revision was not included in the prevalence figures. One mis-seated liner was revised in the early post-operative period and two that were initially incompletely seated were found on follow-up radiographs to have become correctly seated. There may be technical issues with regard to the implanting of this prosthesis of which surgeons should be aware. However, there is the distinct possibility that the Trident shell deforms upon implantation, thereby preventing complete seating of the liner.

The treatment of bony defects of the tibia at the time of revision total knee replacement is controversial. The place of compacted morsellised bone graft is becoming established, particularly in contained defects. It has previously been shown that the initial stability of impaction-grafted trays in the contained defects is equivalent to that of an uncemented primary knee replacement. However, there is little biomechanical evidence on which to base a decision in the treatment of uncontained defects. We undertook a laboratory-based biomechanical study comparing three methods of graft containment in segmental medial tibial defects and compared them with the use of a modular metal augment to bypass the defect.

Using resin models of the proximal tibia with medial defects representing either 46% or 65% of the medial cortical rim, repair of the defect was accomplished using mesh, cement or a novel bag technique, after which impaction bone grafting was used to fill the contained defects and a tibial component was cemented in place. As a control, a cemented tibial component with modular metal augments was used in identical defects. All specimens were submitted to cyclical mechanical loading, during which cyclical and permanent tray displacement were determined.

The results showed satisfactory stability with all the techniques except the bone bag method. Using metal augments gave the highest initial stability, but obviously lacked any potential for bone restoration.

We have evaluated the results of total hip replacement in patients with congenital hip disease using 46 cemented all-polyethylene Charnley acetabular components implanted with the cotyloplasty technique in 34 patients (group A), and compared them with 47 metal-backed cementless acetabular components implanted without bone grafting in 33 patients (group B). Patients in group A were treated between 1988 and 1993 and those in group B between 1990 and 1995. The mean follow-up for group A was 16.6 years (12 to 18) and the mean follow-up for group B was 13.4 years (10 to 16).

Revision for aseptic loosening was undertaken in 15 hips (32.6%) in group A and in four hips (8.5%) in group B. When liner exchange was included, a total of 13 hips were revised in group B (27.7%). The mean polyethylene wear was 0.11 mm/yr (0.002 to 0.43) and 0.107 mm/yr (0 to 0.62) for groups A and B, respectively. Polyethylene wear in group A was associated with linear osteolysis, and in group B with expansile osteolysis.

In patients with congenital hip disease, when 80% cover of the implant can be obtained, a cementless acetabular component appears to be acceptable and provides durable fixation. However, because of the type of osteolysis arising with these devices, early exchange of a worn liner is recommended before extensive bone loss makes revision surgery more complicated.

Polished, tapered stems are now widely used for cemented total hip replacement and many such designs have been introduced. However, a change in stem geometry may have a profound influence on stability. Stems with a wide, rectangular proximal section may be more stable than those which are narrower proximally. We examined the influence of proximal geometry on stability by comparing the two-year migration of the Exeter stem with a more recent design, the CPS-Plus, which has a wider shoulder and a more rectangular cross-section. The hypothesis was that these design features would increase rotational stability.

Both stems subsided approximately 1 mm relative to the femur during the first two years after implantation. The Exeter stem was found to rotate into valgus (mean 0.2°, sd 0.42°) and internally rotate (mean 1.28°, sd 0.99°). The CPS-Plus showed no significant valgus rotation (mean 0.2°, sd 0.42°) or internal rotation (mean −0.03°, sd 0.75°). A wider, more rectangular cross-section improves rotational stability and may have a better long-term outcome.

Metal-on-metal hip bearings are being implanted into younger patients. The consequence of elevated levels of potentially carcinogenic metal ions is therefore a cause for concern. We have determined the levels of cobalt (Co), chromium (Cr), titanium (Ti) and vanadium (Va) in the urine and whole blood of patients who had had metal-on-metal and metal-on-polyethylene articulations in situ for more than 30 years. We compared these with each other and with the levels for a control group of subjects.

We found significantly elevated levels of whole blood Ti, Va and urinary Cr in all arthroplasty groups. The whole blood and urine levels of Co were grossly elevated, by a factor of 50 and 300 times respectively in patients with loose metal-on-metal articulations when compared with the control group. Stable metal-on-metal articulations showed much lower levels. Elevated levels of whole blood or urinary Co may be useful in identifying metal-on-metal articulations which are loose.