We investigated the fixation of fully-threaded cementless acetabular prostheses in 20 patients with osteoarthritis, measuring the migration of the cup using roentgen stereophotogrammetric analysis (RSA). All the cups migrated proximally, 13 moved laterally or medially, and nine moved anteriorly or posteriorly in the first two postoperative years, the average migration being 1.1 to 1.4 mm in either direction. Rotatory movements of up to 5.7 degrees were found in nine of the 13 hips where this analysis could be performed. Movements of cobalt-chrome (12) and titanium alloy (8) cups did not differ significantly. Seventeen of the 20 patients had some pain two years after the operation. The migration of the prostheses indicates that 'osseointegration' had not occurred. The combination of this with persistent pain suggests that the long-term results will be unfavourable

The membranes surrounding seven loose cementless acetabular implants were shown to contain polyethylene particles, birefringent in polarised light. Three of these implants were made of titanium alloy and the membranes around these contained titanium particles as well. There was no metallosis around the four implants made of chromium-cobalt-steel alloy. Both titanium and polyethylene particles caused migration, adherence and phagocytosis of CD11b-positive, peroxidase-negative macrophages. There were no histological signs of activation of the specific immune response; neither interleukin-2 receptor-positive activated T cells nor PCA-1 plasmablasts/plasma cells were present in the tissues. In cases of simple loosening, resident mesenchymal fibroblast-like cells were active. In aggressive granulomatosis, there were many macrophages and multinucleated giant cells but little fibroblast reaction. The clinical relevance of the findings is that the use of cementless prostheses is not a guarantee against adverse tissue reactions

We performed a histological and histomorphometric examination in five cadaver specimens of the femoral and acetabular components and the associated tissue which had been recovered between 3.3 and 6.2 years after primary total hip arthroplasty (THA) using a proximal hydroxyapatite (HA)-coated titanium alloy implant. All had functioned well during the patients’ life. All the stems were fixed in the femur and showed osseointegration of both the proximal and distal parts. The amount of residual HA was greatest in the distal metaphyseal sections, indicating that the rate of bone remodelling may be the main factor causing loss of HA. The level of activity of the patient was the only clinical factor which correlated with loss of coating. The percentage of bone-implant osseointegration was almost constant, regardless of the amount of HA residue, periprosthetic bone density or the time of implantation. HA debris was seldom observed and if present did not cause any adverse or inflammatory reaction. Partial debonding did occur in one case as a result of a polyethylene-induced inflammatory reaction

Total hip replacement using an alumina head and socket and a titanium alloy stem is evaluated in a series of patients under 50 years of age. Between April 1977 and December 1986, 86 such replacements were performed in 75 patients, but mainly because patients had difficulty travelling from Africa, only 71 hips were followed up adequately; of these, 56 were primary procedures and 15 revisions. Survivorship analysis showed that 98% of the prostheses were retained for 10 years. On clinical and radiological examination 51 of the 71 hips were stable and acceptable, 15 had radiological changes on the acetabular side, and one on the femoral side; four other cases had clinical and radiological changes suggesting impending failure, possibly because fixation of the socket was inadequate. There were no differences between the results of the primary procedures and those of revisions. In these young patients, the results seem better with alumina-on-alumina hips than with other varieties, possibly because of their remarkably low wear

Coating titanium alloy implants with titanium nitride (TiN) by the method of Powder Immersion Reaction Assisted Coating (PIRAC) produces a stable layer on their surface. We have examined the ability of the new TiN coating to undergo osseointegration. We implanted TiN-coated and uncoated Ti6Al4V alloy pins into the femora of six-month-old female Wistar rats. SEM after two months showed a bone collar around both TiN-coated and uncoated implants. Morphometrical analysis revealed no significant differences between the percentage of the implant-bone contact and the area and volume of the bone around TiN-coated compared with uncoated implants. Electron-probe microanalysis indicated the presence of calcium and phosphorus at the implant-bone interface. Mineralisation around the implants was also confirmed by labelling with oxytetracycline. Strong activity of alkaline phosphatase and weak activity of tartrate-resistant acid phosphatase were shown histochemically. Very few macrophages were detected by the non-specific esterase reaction at the site of implantation. Our findings indicate good biocompatibility and bone-bonding properties of the new PIRAC TiN coatings which are comparable to those of uncoated Ti6Al4V alloy implants

Aims

The purpose of this study was to determine whether there were long-term differences in outcomes of reverse shoulder arthroplasty (RSA) undertaken for acute proximal humeral fracture versus rotator cuff deficiency with a minimum follow-up of five years.

We have studied the beneficial effects of a hydroxyapatite (HA) coating on the prevention of the migration of wear debris along the implant-bone interface. We implanted a loaded HA-coated implant and a non-coated grit-blasted titanium alloy (Ti) implant in each distal femoral condyle of eight Labrador dogs. The test implant was surrounded by a gap communicating with the joint space and allowing access of joint fluid to the implant-bone interface. We injected polyethylene (PE) particles into the right knee three weeks after surgery and repeated this weekly for the following five weeks. The left knee received sham injections. The animals were killed eight weeks after surgery. Specimens from the implant-bone interface were examined under plain and polarised light. Only a few particles were found around HA-coated implants, but around Ti implants there was a large amount of particles. HA-coated implants had approximately 35% bone ingrowth, whereas Ti implants had virtually no bone ingrowth and were surrounded by a fibrous membrane. Our findings suggest that HA coating of implants is able to inhibit peri-implant migration of PE particles by creating a seal of tightly-bonded bone on the surface of the implant

We allocated randomly 27 patients undergoing 28 primary uncemented total hip replacements (THR) to receive prosthetic components of similar design with either plasma-sprayed titanium alloy (Ti) coating (n = 13) or hydroxyapatite (HA) coating (n = 15). After some exclusions, 15 of the patients (15 THR; 7 with HA- and 8 with Ti-coating) were followed by roentgen stereophotogrammetric analysis at 3, 6 and 12 months to measure migration of the femoral component. Twenty-six of the patients (26 THR) were followed clinically and by conventional radiography. All the femoral components had migrated at 3 months. From 3 to 12 months, the migration of Ti-coated components continued whereas the HA-coated components had stabilised. At 12 months there was significantly less migration of the HA-coated components (p < 0.05). The maximum subsidence was 0.2 mm in both groups. The Harris hip score was equal in the two groups preoperatively but at follow-up it was better in the HA-coated group (p < 0.05) and visual analogue scale scores showed that they had less pain (p < 0.05)

Between January 1988 and January 1991 we performed 100 consecutive cemented total hip replacements using a zirconia head, a titanium alloy stem and a polyethylene cup. We reviewed 78 of these hips in 61 patients in detail at a mean of 5.8 years (1 to 9). Aseptic loosening was seen in 11 hips (14%). Eight needed revision. In total, 37 cups (47.5%) showed radiolucent lines, all at the cement-bone interface, with 18 (23%) involving all the interface. Of the 78 femoral implants, 17 (21.7%) showed radiolucent lines, and two, which had a complete line of more than 1 mm thick, definite endocortical osteolyses. There was also an abnormally high incidence of osteolysis of more than 2 mm at the calcar. Survivorship analysis showed that only 63% were in situ at eight years. These worrying results led us to abandon the use of zirconia heads, since at the same hospital, using the same femoral stem, cement and polyethylene cup, but with alumina femoral heads, the survival rate was 93% at nine years. We discuss the possible reasons for the poor performance of zirconia ceramic

Between 1990 and 1992, we implanted 71 hybrid alumina-on-alumina hip arthroplasties in 62 consecutive patients under the age of 55 years, with a mean age of 46 years at surgery. There were 56 primary and 15 secondary procedures. The prostheses involved a cemented titanium alloy stem, a 32 mm alumina head, and a press-fit metal-backed socket with an alumina insert. Three patients (four hips) died from unrelated causes. Four hips had revision surgery for either deep infection, unexplained persistent pain, fracture of the alumina head, or aseptic loosening of the socket. The nine-year survival rate was 93.7% with revision for any cause as the end-point and 98.4% with revision for aseptic loosening as the end-point. The outcome in the surviving patients (50 patients, 57 hips) with a minimum five-year follow-up (mean eight years) was excellent in 47 hips (82.5%), very good in eight (14%), good in one and fair in one. A thin, partial, lucent line, mainly in zone III was present in 38% of the sockets and one socket had a complete lucency less than 1 mm thick. One stem had isolated femoral osteolysis. There was no detectable component migration nor acetabular osteolysis. This hybrid arthroplasty gave satisfactory medium-term results in active patients. The press-fit metal-backed socket appeared to have reliable fixation in alumina-on-alumina hip arthroplasty. The excellent results using cemented fixation of the stem may be related to the low production of wear debris

Reports of differing failure rates of total hip prostheses made of various metals prompted us to measure the size of metallic and polyethylene particulate debris around failed cemented arthroplasties. We used an isolation method, in which metallic debris was extracted from the tissues, and a non-isolation method of routine preparation for light and electron microscopy. Specimens were taken from 30 cases in which the femoral component was of titanium alloy (10), cobalt-chrome alloy (10), or stainless steel (10). The mean size of metallic particles with the isolation method was 0.8 to 1.0 microns by 1.5 to 1.8 microns. The non-isolation method gave a significantly smaller mean size of 0.3 to 0.4 microns by 0.6 to 0.7 microns. For each technique the particle sizes of the three metals were similar. The mean size of polyethylene particles was 2 to 4 microns by 8 to 13 microns. They were larger in tissue retrieved from failed titanium-alloy implants than from cobalt-chrome and stainless-steel implants. Our results suggest that factors other than the size of the metal particles, such as the constituents of the alloy, and the amount and speed of generation of debris, may be more important in the failure of hip replacements

Aims

To determine whether half-threaded screw holes in a new titanium locking plate design can substantially decrease the notch effects of the threads and increase the plate fatigue life.

Bone growth into cementless prosthetic components is compromised by osteoporosis, by any gap between the implant and the bone, by micromotion, and after the revision of failed prostheses. Recombinant human transforming growth factor-β1 (rhTGF-β1) has recently been shown to be a potent stimulator of bone healing and bone formation in various models in vivo. We have investigated the potential of rhTGF-β1, adsorbed on to weight-loaded tricalcium phosphate (TCP) coated implants, to enhance bone ongrowth and mechanical fixation. We inserted cylindrical grit-blasted titanium alloy implants bilaterally into the weight-bearing part of the medial femoral condyles of ten skeletally mature dogs. The implants were mounted on special devices which ensured stable weight-loading during each gait cycle. All implants were initially surrounded by a 0.75 mm gap and were coated with TCP ceramic. Each animal received two implants, one with 0.3 μg rhTGF-β1 adsorbed on the ceramic surface and the other without growth factor. Histological analysis showed that bone ongrowth was significantly increased from 22 ± 5.6% bone-implant contact in the control group to 36 ± 2.9% in the rhTGF-β stimulated group, an increase of 59%. The volume of bone in the gap was increased by 16% in rhTGF-β1-stimulated TCP-coated implants, but this difference was not significant. Mechanical push-out tests showed no difference in fixation of the implant between the two groups. Our study suggests that rhTGF-β1 adsorbed on TCP-ceramic-coated implants can enhance bone ongrowth

Periprosthetic osteolysis is a major cause of aseptic loosening in artificial joint replacement. It is assumed to occur in conjunction with the activation of macrophages. We have shown in vitro that human osteoblast-like cells, isolated from bone specimens obtained from patients undergoing hip replacement, phagocytose fine particles of titanium alloy (TiAlV). The human osteoblast-like cells were identified immunocytochemically by the presence of bone-specific alkaline phosphatase (BAP). With increasing duration of culture, a variable number of the osteoblastic cells became positive for the macrophage marker CD68, independent of the phagocytosis of particles, with a fine granular cytoplasmic staining which was coexpressed with BAP as revealed by immunodoublestaining. The metal particles were not toxic to the osteoblastic cells since even in culture for up to four weeks massively laden cells were vital and had a characteristic morphology. Cells of the human osteosarcoma cell line (HOS 58) were also able to phagocytose metal particles but had only a low expression of the CD68 antigen. Fluorescence-activated cell scanning confirmed our immunocytochemical results. Additionally, the cells were found to be negative for the major histocompatibility complex-II (MHC-II) which is a marker for macrophages and other antigen-presenting cells. Negative results of histochemical tests for tartrate-resistant acid phosphatase excluded the contamination by osteoclasts or macrophages in culture. Our observations suggest that the osteoblast can either change to a phagocytosing cell or that the phagocytosis is an underestimated property of the osteoblast. The detection of the CD68 antigen is insufficient to prove the monocytic lineage. In order to discriminate between macrophages and osteoblasts additional markers should be used. To our knowledge, this is the first demonstration of cells of an osteoblastic origin which have acquired a mixed phenotype of both osteoblasts and macrophages

Some of the component metals of the alloys used for total joint prostheses are toxic and dissolve in the body fluids. It is important to establish how toxic these metals are and to assess the risk of localised tissue necrosis around the prostheses. This has been investigated by incubating primary monolayer cultures of human synovial fibroblasts with various preparations of metals for periods up to 18 days. Morphological changes were evident after exposure to cobalt chloride at a concentration of 50 nanomoles per millilitre and to nickel chloride at 200 nanomoles per millilitre. Chromic chloride, ammonium molybdate and ferric chloride produced no changes up to 500 nanomoles per millilitre. Cultures exposed to particulate pure metals were poisoned by cobalt and vanadium but were not affected under the same conditions by nickel, chromium, molybdenum, titanium or aluminium. Particulate cobalt and vanadium were probably toxic due to their relatively high solubility (four and one micromoles per millilitre respectively after seven days incubation). Particulate nickel also dissolved (three nanomoles per millilitre after seven days) but not in sufficient quantities to be toxic. It appears, therefore, that potentially the most harmful components are cobalt from cobalt-chromium alloy, nickel from stainless steel, and vanadium from titanium alloy. As far as can be estimated, the only combination of materials which is likely to give rise to toxic levels of metal under clinical conditions, is cobalt-chromium alloy articulating against itself to produce relatively high levels of cobalt

The Alloclassic and Endoplus femoral stems have the same grit-blasted surface and are hot forged from the same titanium alloy. Only the external form of the implants differs slightly. It was our aim to examine the differences in radiographic bone response between the Alloclassic (second generation) and the Endoplus (third generation) femoral stems. We compared 79 prostheses in 70 matched patients studied over a minimum of two years. Radiolucent lines, adaptive bone remodelling, subsidence, heterotopic bone formation and lysis were recorded in the Gruen zones. Radiolucencies were mainly found in zones 1 and 7 but to a greater extent in the Endoplus than in the Alloclassic group (p < 0.001 in zone 1, p < 0.05 in zone 7). We found lucent lines in three or more Gruen zones in seven patients all of whom were in the Endoplus group (p < 0.05). Zones 2 and 6 had a significantly higher rate of lucencies in the Endoplus group (p < 0.001). We encountered a combination of proximal lucent lines in zones 1 and 7 with distal hypertrophy of the cortical bone in zones 2, 3, 5 and 6 in eight patients, all from the Endoplus group (p < 0.05). In other patients bone atrophy (stress shielding) in zones 2 and 6 was seen more frequently in the Endoplus than in the Alloclassic group (p < 0.001). In neither group was there radiological evidence of osteolysis. Heterotopic bone formation and subsidence occurred with similar frequency in both groups. Our study shows that a small change in the form of the femoral implant can result in statistically significant radiological changes in bone remodelling. Whether this will result in clinical compromise is unknown. However, it seems likely that the Endoplus femoral stem will perform differently from the Alloclassic

In previous studies, we have demonstrated a fibrocartilaginous membrane around hydroxyapatite-coated implants subjected to micromovement in contrast to the fibrous connective tissue which predominates around similarly loaded titanium alloy implants. In the present study, in mature dogs, we investigated the effect of immobilising titanium (Ti)- or hydroxyapatite (HA)-coated implants already surrounded by a movement-induced fibrous membrane and compared the results with those of similar implants in which continuous micromovement was allowed to continue. The implants were inserted in the medial femoral condyles of 14 dogs and subjected to 150 microns movements during each gait cycle. After four weeks (when a fibrous membrane had developed), half the implants were immobilised to prevent further micromovement. The dogs were killed at 16 weeks and the results were evaluated by push-out tests and histological analysis. The continuously loaded Ti-coated implants were surrounded by a fibrous membrane, whereas bridges of new bone anchored the HA-coated implants. The immobilised implants were surrounded by bone irrespective of the type of coating. Push-out tests of the continuously loaded implants showed better fixation of those with HA coating (p < 0.001). The immobilised Ti-coated implants had four times stronger fixation than did continuously loaded Ti-coated implants (p < 0.01) but there was no equivalent difference between the two groups of HA-coated implants. The amount of bone ingrowth was greater into immobilised HA-coated implants than into immobilised Ti-coated implants (p < 0.01). Two-thirds of the HA coating had been resorbed after 16 weeks of implantation, but 25% of this resorbed HA had been replaced by bone.(ABSTRACT TRUNCATED AT 250 WORDS)

Aims

The purpose of this study was to evaluate the biological fixation of a 3D printed porous implant, with and without different hydroxyapatite (HA) coatings, in a canine model.

Aims

This combined clinical and in vitro study aimed to determine the incidence of liner malseating in modular dual mobility (MDM) constructs in primary total hip arthroplasties (THAs) from a large volume arthroplasty centre, and determine whether malseating increases the potential for fretting and corrosion at the modular metal interface in malseated MDM constructs using a simulated corrosion chamber.

Aims

Commonly performed unicompartmental knee arthroplasty (UKA) is not designed for the lateral compartment. Additionally, the anatomical medial and lateral tibial plateaus have asymmetrical geometries, with a slightly dished medial plateau and a convex lateral plateau. Therefore, this study aims to investigate the native knee kinematics with respect to the tibial insert design corresponding to the lateral femoral component.