The aims of this study were to review the surgical technique for a combined femoral head reduction osteotomy (FHRO) and periacetabular osteotomy (PAO), and to report the short-term clinical and radiological results of a combined FHRO/PAO for the treatment of selected severe femoral head deformities. Between 2011 and 2016, six female patients were treated with a combined FHRO and PAO. The mean patient age was 13.6 years (12.6 to 15.7). Clinical data, including patient demographics and patient-reported outcome scores, were collected prospectively. Radiologicalally, hip morphology was assessed evaluating the Tönnis angle, the lateral centre to edge angle, the medial offset distance, the extrusion index, and the alpha angle.Aims
Patients and Methods
Ceramic-on-ceramic (CoC) bearings in total hip arthroplasty (THA)
are commonly used, but concerns exist regarding ceramic fracture.
This study aims to report the risk of revision for fracture of modern
CoC bearings and identify factors that might influence this risk,
using data from the National Joint Registry (NJR) for England, Wales, Northern
Ireland and the Isle of Man. We analysed data on 223 362 bearings from 111 681 primary CoC
THAs and 182 linked revisions for bearing fracture recorded in the
NJR. We used implant codes to identify ceramic bearing composition
and generated Kaplan-Meier estimates for implant survivorship. Logistic
regression analyses were performed for implant size and patient specific
variables to determine any associated risks for revision.Aims
Patients and Methods
Instability remains a challenging problem in both primary and
revision total hip arthroplasty (THA). Dual mobility components
confer increased stability, but there are concerns about the unique
complications associated with these designs, as well as the long-term
survivorship. We performed a systematic review of all English language articles
dealing with dual mobility THAs published between 2007 and 2016
in the MEDLINE and Embase electronic databases. A total of 54 articles
met inclusion criteria for the final analysis of primary and revision
dual mobility THAs and dual mobility THAs used in the treatment
of fractures of the femoral neck. We analysed the survivorship and
rates of aseptic loosening and of intraprosthetic and extra-articular
dislocation.Aims
Materials and Methods
Our aim in this study was to describe a continuing review of
11 total hip arthroplasties using 22.225 mm Alumina ceramic femoral
heads on a Charnley flanged femoral component, articulating against
a silane crosslinked polyethylene. Nine patients (11 THAs) were reviewed at a mean of 27.5 years
(26 to 28) post-operatively. Outcome was assessed using the d’Aubigne
and Postel, and Charnley scores and penetration was recorded on
radiographs. In addition, the oxidation of a 29-year-old shelf-aged
acetabular component was analysed.Aims
Patients and Methods
The primary aim of this independent prospective randomised trial
was to compare serum metal ion levels for ceramic-on-metal (CoM)
and metal-on-metal (MoM) bearing surfaces in total hip arthroplasty
(THA). Our one-year results demonstrated elevation in metal ion
levels above baseline with no significant difference between the
CoM and MoM groups. This paper reviews the five-year data. The implants used in each patient differed only in respect to
the type of femoral head (ceramic or metal). At five-year follow-up
of the 83 enrolled patients, data from 67 (36 CoM, 31 MoM) was available
for comparison.Aims
Patients and Methods
Modular junctions are ubiquitous in contemporary hip arthroplasty. The head-trunnion junction is implicated in the failure of large diameter metal-on-metal (MoM) hips which are the currently the topic of one the largest legal actions in the history of orthopaedics (estimated costs are stated to exceed $4 billion). Several factors are known to influence the strength of these press-fit modular connections. However, the influence of different head sizes has not previously been investigated. The aim of the study was to establish whether the choice of head size influences the initial strength of the trunnion-head connection. Ti-6Al-4V trunnions (n = 60) and two different sizes of cobalt-chromium (Co-Cr) heads (28 mm and 36 mm; 30 of each size) were used in the study. Three different levels of assembly force were considered: 4 kN; 5 kN; and 6 kN (n = 10 each). The strength of the press-fit connection was subsequently evaluated by measuring the pull-off force required to break the connection. The statistical differences in pull-off force were examined using a Kruskal–Wallis test and two-sample Mann–Whitney U test. Finite element and analytical models were developed to understand the reasons for the experimentally observed differences.Objectives
Materials and Methods
Our aim was to evaluate the radiographic characteristics of patients
undergoing total hip arthroplasty (THA) for the potential of posterior
bony impingement using CT simulations. Virtual CT data from 112 patients who underwent THA were analysed.
There were 40 men and 72 women. Their mean age was 59.1 years (41
to 76). Associations between radiographic characteristics and posterior
bony impingement and the range of external rotation of the hip were
evaluated. In addition, we investigated the effects of pelvic tilt
and the neck/shaft angle and femoral offset on posterior bony impingement.Aims
Patients and Methods
Long-term clinical outcomes for ceramic-on-ceramic (CoC) bearings
are encouraging. However, there is a risk of squeaking. Guidelines
for the orientation of the acetabular component are defined from
static imaging, but the position of the pelvis and thus the acetabular
component during activities associated with edge-loading are likely
to be very different from those measured when the patient is supine.
We assessed the functional orientation of the acetabular component. A total of 18 patients with reproducible squeaking in their CoC
hips during deep flexion were investigated with a control group
of 36 non-squeaking CoC hips. The two groups were matched for the
type of implant, the orientation of the acetabular component when
supine, the size of the femoral head, ligament laxity, maximum hip
flexion and body mass index. Aims
Patients and Methods
We evaluated the short-term functional outcome and prevalence
of bearing-specific generation of audible noise in 301 patients
(336 hips) operated on with fourth generation (Delta) medium diameter
head, ceramic-on-ceramic (CoC) total hip arthroplasties (THAs). There were 191 female (63%) and 110 male patients (37%) with
a mean age of 61 years (29 to 78) and mean follow-up of 2.1 years
(1.3 to 3.4). Patients completed three questionnaires: Oxford Hip
Score (OHS), Research and Development 36-item health survey (RAND-36)
and a noise-specific symptom questionnaire. Plain radiographs were also
analysed. A total of three hips (0.9%) were revised. Aims
Patients and Methods
The use of large-diameter metal-on-metal (MoM)
components in total hip arthroplasty (THA) is associated with an increased
risk of early failure due to adverse local tissue reaction to metal
debris (ARMD) in response to the release of metal ions from the
bearing couple and/or head-neck taper corrosion. The aim of this
paper was to present a review of the incidence and natural history
of ARMD and the forms of treatment, with a focus on the need for
and extent of resection or debulking of the pseudotumour. An illustrative
case report is presented of a patient with an intra-pelvic pseudotumour
associated with a large diameter MoM THA, which was treated successfully
with revision of the bearing surface to a dual mobility couple and
retention of the well-fixed acetabular and femoral components. The
pseudotumour was left Cite this article:
We conducted a prospective study of a delta ceramic total hip
arthroplasty (THA) to determine the rate of ceramic fracture, to
characterise post-operative noise, and to evaluate the mid-term
results and survivorship. Between March 2009 and March 2011, 274 patients (310 hips) underwent
cementless THA using a delta ceramic femoral head and liner. At
each follow-up, clinical and radiological outcomes were recorded.
A Kaplan-Meier analysis was undertaken to estimate survival.Aims
Patients and Methods
Femoral stems with exchangeable (modular) necks were introduced
to offer surgeons an increased choice when determining the version,
offset and length of the femoral neck during total hip arthroplasty
(THA). It was hoped that this would improve outcomes and reduce
complications, particularly dislocation. In 2010, the Australian Orthopaedic
Association National Joint Replacement Registry (AOANJRR) first
reported an increased rate of revision after primary THA using femoral
stems with an exchangeable neck. The aim of this study was to provide
a more comprehensive up-to-date analysis of primary THA using femoral
stems with exchangeable and fixed necks. The data included all primary THA procedures performed for osteoarthritis
(OA), reported to the AOANJRR between 01 September 1999 and 31 December
2014. There were 9289 femoral stems with an exchangeable neck and
253 165 femoral stems with a fixed neck. The characteristics of
the patients and prostheses including the bearing surface and stem/neck
metal combinations were examined using Cox proportional hazard ratios
(HRs) and Kaplan-Meier estimates of survivorship. Aims
Materials and Methods
There is increasing global awareness of adverse
reactions to metal debris and elevated serum metal ion concentrations
following the use of second generation metal-on-metal total hip
arthroplasties. The high incidence of these complications can be
largely attributed to corrosion at the head-neck interface. Severe
corrosion of the taper is identified most commonly in association
with larger diameter femoral heads. However, there is emerging evidence
of varying levels of corrosion observed in retrieved components
with smaller diameter femoral heads. This same mechanism of galvanic
and mechanically-assisted crevice corrosion has been observed in
metal-on-polyethylene and ceramic components, suggesting an inherent
biomechanical problem with current designs of the head-neck interface. We provide a review of the fundamental questions and answers
clinicians and researchers must understand regarding corrosion of
the taper, and its relevance to current orthopaedic practice. Cite this article:
The use of ceramic femoral heads in total hip arthroplasty (THA) has increased due to their proven low bearing wear characteristics. Ceramic femoral heads are also thought to reduce wear and corrosion at the head-stem junction with titanium (Ti) stems when compared with metal heads. We sought to evaluate taper damage of ceramic compared with metal heads when paired with cobalt chromium (CoCr) alloy stems in a single stem design. This retrieval study involved 48 total hip arthroplasties (THAs) with CoCr V40 trunnions paired with either CoCr (n = 21) or ceramic (n = 27) heads. The taper junction of all hips was evaluated for fretting/corrosion damage and volumetric material loss using a roundness-measuring machine. We used linear regression analysis to investigate taper damage differences after adjusting for potential confounding variables.Objectives
Methods
Our first aim was to determine whether there are significant
changes in the level of metal ions in the blood at mid-term follow-up,
in patients with an Articular Surface Replacement (ASR) arthroplasty.
Secondly, we sought to identify risk factors for any increases. The study involved 435 patients who underwent unilateral, metal-on-metal
(MoM) hip resurfacing (HRA) or total hip arthroplasty (THA). These
patients all had one measurement of the level of metal ions in the
blood before seven years had passed post-operatively (early evaluation)
and one after seven years had passed post-operatively (mid-term evaluation).
Changes in ion levels were tested using a Wilcoxon signed-rank test.
We identified subgroups at the highest risk of increase using a
multivariable linear logistic regression model.Aims
Patients and Methods