Objectives

Taper junctions between modular hip arthroplasty femoral heads and stems fail by wear or corrosion which can be caused by relative motion at their interface. Increasing the assembly force can reduce relative motion and corrosion but may also damage surrounding tissues. The purpose of this study was to determine the effects of increasing the impaction energy and the stiffness of the impactor tool on the stability of the taper junction and on the forces transmitted through the patient’s surrounding tissues.

Aims

The aim of this study was to determine whether patients with metal-on-metal (MoM) arthroplasties of the hip have an increased risk of cardiac failure compared with those with alternative types of arthroplasties (non-MoM).

Resurfacing of the humeral head is commonly used within the UK to treat osteoarthritis (OA) of the shoulder. We present the results of a small prospective randomised study of this procedure using the Global CAP prosthesis with two different coatings, Porocoat and DuoFix hydroxyapatite (HA). We followed two groups of ten patients with OA of the shoulder for two years after insertion of the prosthesis with tantalum marker beads, recording pain, Constant–Murley and American Shoulder and Elbow Surgeons (ASES) outcome scores, and using radiostereometric analysis to assess migration. The outcomes were similar to those of other series, with significant reductions in pain (p = 0.003) and an improvement in the Constant (p = 0.001) and ASES scores (p = 0.006). The mean migration of the prosthesis three months post-operatively was 0.78 mm (0.51 to 1.69) and 0.72 mm (0.33 to 1.45) for the Porocoat and DuoFix groups, respectively. Analysis of variance indicated that the rate of migration reached a plateau after three months post-operatively in both groups. At follow-up of two years the mean migration was 1 mm (sd 1 (0.25 to 3.32)); in the Porocoat group and 0.8 mm (sd 0.4 (0.27 to 1.45)) in the DuoFix HA group. Significant migration of the prosthesis was seen in one patient who had received an anterior humeral bone graft. This prosthesis was later revised after 2.7 years.

The addition of a coating of HA to the sintered surface does not improve fixation of this prosthesis.

Cite this article: Bone Joint J 2014;96-B:1077–81.

Aims

We wished to investigate the influence of metal debris exposure on the subsequent immune response and resulting soft-tissue injury following metal-on-metal (MoM) hip arthroplasty. Some reports have suggested that debris generated from the head-neck taper junction is more destructive than equivalent doses from metal bearing surfaces.

The MAGnetic Expansion Control (MAGEC) system is used increasingly in the management of early-onset scoliosis. Good results have been published, but there have been recent reports identifying implant failures that may be associated with significant metallosis surrounding the implants. This article aims to present the current knowledge regarding the performance of this implant, and the potential implications and strategies that may be employed to identify and limit any problems.

We urge surgeons to apply caution to patient and construct selection; engage in prospective patient registration using a spine registry; ensure close clinical monitoring until growth has ceased; and send all explanted MAGEC rods for independent analysis.

The MAGEC system may be a good instrumentation system for the treatment of early-onset scoliosis. However, it is innovative and like all new technology, especially when deployed in a paediatric population, robust systems to assess long-term outcome are required to ensure that patient safety is maintained.

Cite this article: Bone Joint J 2017;99-B:708–13.

Aims

Our aim was to report survivorship data and lessons learned with the Corail/Pinnacle cementless total hip arthroplasty (THA) system.

Bioengineering reasons for increased wear and failure of metal-on-metal (MoM) bearings in hip prostheses have been described. Low wear occurs in MoM hips when the centre of the femoral head is concentric with the centre of the acetabular component and the implants are correctly positioned. Translational or rotational malpositioning of the components can lead to the contact-patch of the femoral component being displaced to the rim of the acetabular component, resulting in a ten- to 100-fold increase in wear and metal ion levels. This may cause adverse tissue reactions, loosening of components and failure of the prosthesis.

Lately, concerns have arisen following the use of large metal-on-metal bearings in hip replacements owing to reports of catastrophic soft-tissue reactions resulting in implant failure and associated complications. This review examines the literature and contemporary presentations on current clinical dilemmas in metal-on-metal hip replacement.

Objectives

High failure rates of metal-on-metal hip arthroplasty implants have highlighted the need for more careful introduction and monitoring of new implants and for the evaluation of the safety of medical devices. The National Joint Registry and other regulatory services are unable to detect failing implants at an early enough stage. We aimed to identify validated surrogate markers of long-term outcome in patients undergoing primary total hip arthroplasty (THA).

Objectives

The aims of this piece of work were to: 1) record the background concentrations of blood chromium (Cr) and cobalt (Co) concentrations in a large group of subjects; 2) to compare blood/serum Cr and Co concentrations with retrieved metal-on-metal (MoM) hip resurfacings; 3) to examine the distribution of Co and Cr in the serum and whole blood of patients with MoM hip arthroplasties; and 4) to further understand the partitioning of metal ions between the serum and whole blood fractions.

Modern metal-on-metal hip resurfacing has been widely performed in the United Kingdom for over a decade. However, the literature reports conflicting views of the benefits: excellent medium- to long-term results with some brands in specific subgroups, but high failure rates and local soft-tissue reactions in others. The National Joint Registry for England and Wales (NJR) has collected data on all hip resurfacings performed since 2003. This retrospective cohort study recorded survival time to revision from a resurfacing procedure, exploring risk factors independently associated with failure. All patients with a primary diagnosis of osteoarthritis who underwent resurfacing between 2003 and 2010 were included in the analyses. Cox’s proportional hazard models were used to analyse the extent to which the risk of revision was related to patient, surgeon and implant covariates.

A total of 27 971 hip resurfacings were performed during the study period, of which 1003 (3.59%) underwent revision surgery. In the final adjusted model, we found that women were at greater risk of revision than men (hazard ratio (HR) = 1.30, p = 0.007), but the risk of revision was independent of age. Of the implant-specific predictors, five brands had a significantly greater risk of revision than the Birmingham Hip Resurfacing (BHR) (ASR: HR = 2.82, p < 0.001, Conserve: HR = 2.03, p < 0.001, Cormet: HR = 1.43, p = 0.001, Durom: HR = 1.67, p < 0.001, Recap: HR = 1.58, p = 0.007). Smaller femoral head components were also significantly more likely to require revision (≤ 44 mm: HR = 2.14, p < 0.001, 45 to 47 mm: HR = 1.48, p = 0.001) than medium or large heads, as were operations performed by low-volume surgeons (HR = 1.36, p <  0.001). Once these influences had been removed, in 4873 male patients < 60 years old undergoing resurfacing with a BHR, the five-year estimated risk of revision was 1.59%.

In summary, after adjustment for a range of covariates we found that there were significant differences in the rate of failure between brands and component sizes. Younger male patients had good five-year implant survival when the BHR was used.

The purpose of this study was twofold: first, to determine whether the five-year results of hip resurfacing arthroplasty (HRA) in Canada justified the continued use of HRA; and second, to identify whether greater refinement of patient selection was warranted.

This was a retrospective cohort study that involved a review of 2773 HRAs performed between January 2001 and December 2008 at 11 Canadian centres. Cox’s proportional hazards models were used to analyse the predictors of failure of HRA. Kaplan–Meier survival analysis was performed to predict the cumulative survival rate at five years. The factors analysed included age, gender, body mass index, pre-operative hip pathology, surgeon’s experience, surgical approach, implant sizes and implant types. The most common modes of failure were also analysed.

The 2773 HRAs were undertaken in 2450 patients: 2127 in men and 646 in women. The mean age at operation was 50.5 years (sd 8.72; 18 to 82) and mean follow-up was 3.4 years (sd 2.1; 2.0 to 10.1). At the last follow-up a total of 101 HRAs (3.6%) required revision. Using revision for all causes of failure as the endpoint, Kaplan–Meier survival analysis showed a cumulative survival of 96.4% (95% confidence interval (CI) 96.1 to 96.9) at five years. With regard to gender, the five-year overall survival was 97.4% in men (95% CI 97.1 to 97.7) and 93.6% in women (95% CI 92.6 to 94.6). Female gender, smaller femoral components, specific implant types and a diagnosis of childhood hip problems were associated with higher rates of failure. The most common cause of failure was fracture of the femoral neck, followed by loosening of the femoral component.

The failure rates of HRA at five years justify the ongoing use of this technique in men. Female gender is an independent predictor of failure, and a higher failure rate at five years in women leads the authors to recommend this technique only in exceptional circumstances for women.

Cite this article: Bone Joint J 2013;95-B:1044–50.

We present the results of 62 consecutive acetabular revisions using impaction bone grafting and a cemented polyethylene acetabular component in 58 patients (13 men and 45 women) after a mean follow-up of 27 years (25 to 30). All patients were prospectively followed. The mean age at revision was 59.2 years (23 to 82).

We performed Kaplan–Meier (KM) analysis and also a Competing Risk (CR) analysis because with long-term follow-up, the presence of a competing event (i.e. death) prevents the occurrence of the endpoint of re-revision.

A total of 48 patients (52 hips) had died or had been re-revised at final review in March 2011. None of the deaths were related to the surgery. The mean Harris hip score of the ten surviving hips in ten patients was 76 points (45 to 99).

The KM survivorship at 25 years for the endpoint ‘re-revision for any reason’ was 58.0% (95% confidence interval (CI) 38 to 73) and for ‘re-revision for aseptic loosening’ 72.1% (95% CI 51 to 85). With the CR analysis we calculated the KM analysis overestimates the failure rate with respectively 74% and 93% for these endpoints. The current study shows that acetabular impaction bone grafting revisions provide good clinical results at over 25 years.

Cite this article: Bone Joint J 2015;97-B:1338–44.

Aims

The aims of this study were to compare the diagnostic test characteristics of ultrasound alone, metal artefact reduction sequence MRI (MARS-MRI) alone, and ultrasound combined with MARS-MRI for identifying intra-operative pseudotumours in metal-on-metal hip resurfacing (MoMHR) patients undergoing revision surgery.

Radiostereometric analysis (RSA) can detect early micromovement in unstable implant designs which are likely subsequently to have a high failure rate. In 2010, the Articular Surface Replacement (ASR) was withdrawn because of a high failure rate. In 19 ASR femoral components, the mean micromovement over the first two years after implantation was 0.107 mm (sd 0.513) laterally, 0.055 mm (sd 0.204) distally and 0.150 mm (sd 0.413) anteriorly. The mean backward tilt around the x-axis was -0.08° (sd 1.088), mean internal rotation was 0.165° (sd 0.924) and mean varus tilt 0.238° (sd 0.420). The baseline to two-year varus tilt was statistically significant from zero movement, but there was no significant movement from one year onwards.

We conclude that the ASR femoral component achieves initial stability and that early migration is not the mode of failure for this resurfacing arthroplasty.

Plasma levels of cobalt and chromium ions and Metal Artefact Reduction Sequence (MARS)-MRI scans were performed on patients with 209 consecutive, unilateral, symptomatic metal-on-metal (MoM) hip arthroplasties. There was wide variation in plasma cobalt and chromium levels, and MARS-MRI scans were positive for adverse reaction to metal debris (ARMD) in 84 hips (40%). There was a significant difference in the median plasma cobalt and chromium levels between those with positive and negative MARS-MRI scans (p < 0.001). Compared with MARS-MRI as the potential reference standard for the diagnosis of ARMD, the sensitivity of metal ion analysis for cobalt or chromium with a cut-off of > 7 µg/l was 57%. The specificity was 65%, positive predictive value was 52% and the negative predictive value was 69% in symptomatic patients. A lowered threshold of > 3.5 µg/l for cobalt and chromium ion levels improved the sensitivity and negative predictive value to 86% and 74% but at the expense of specificity (27%) and positive predictive value (44%).

Metal ion analysis is not recommended as a sole indirect screening test in the surveillance of symptomatic patients with a MoM arthroplasty. The investigating clinicians should have a low threshold for obtaining cross-sectional imaging in these patients, even in the presence of low plasma metal ion levels.

Arthroplasty registries are important for the surveillance of joint replacements and the evaluation of outcome. Independent validation of registry data ensures high quality. The ability for orthopaedic implant retrieval centres to validate registry data is not known. We analysed data from the National Joint Registry for England, Wales and Northern Ireland (NJR) for primary metal-on-metal hip arthroplasties performed between 2003 and 2013. Records were linked to the London Implant Retrieval Centre (RC) for validation. A total of 67 045 procedures on the NJR and 782 revised pairs of components from the RC were included. We were able to link 476 procedures (60.9%) recorded with the RC to the NJR successfully. However, 306 procedures (39.1%) could not be linked. The outcome recorded by the NJR (as either revised, unrevised or death) for a primary procedure was incorrect in 79 linked cases (16.6%). The rate of registry-retrieval linkage and correct assignment of outcome code improved over time. The rates of error for component reference numbers on the NJR were as follows: femoral head category number 14/229 (5.0%); femoral head batch number 13/232 (5.3%); acetabular component category number 2/293 (0.7%) and acetabular component batch number 24/347 (6.5%).

Registry-retrieval linkage provided a novel means for the validation of data, particularly for component fields. This study suggests that NJR reports may underestimate rates of revision for many types of metal-on-metal hip replacement. This is topical given the increasing scope for NJR data. We recommend a system for continuous independent evaluation of the quality and validity of NJR data.

Cite this article: Bone Joint J 2015;97-B:10–18.