The long term biological effects of wear products following total hip arthroplasty (THA) are unclear. However, the indications for THA are expanding, with increasingly younger patients undergoing the procedure.

This prospective, randomised study compared two groups of patients undergoing THA after being randomised to receive one of two different bearing surfaces: metal-on-polyethylene (MoP) n = 22 and metal-on-metal (MoM) n = 23. We investigated the relationship between three variables: bearing surface (MoP vs MoM), whole blood levels of chromium (Cr) and cobalt (Co) and chromosomal aberrations in peripheral lymphocyte pre-operatively and at one, two and five years post-surgery.

Our results demonstrated significantly higher mean cobalt and chromium (Co and Cr) blood levels in the MoM group at all follow-up points following surgery (p < 0.01), but there were no significant differences in the chromosomal aberration indices between MoM and MoP at two or five years (two years: p = 0.56, p = 0.08, p = 0.91, p = 0.51 and five years: p = 0.086, p = 0.73, p = 0.06, p = 0.34) for translocations, breaks, loss and gain of chromosomes respectively. Regression analysis showed a strong linear relationship between Cr levels and the total chromosomal aberration indices in the MoM group (R² = 0.90016), but this was not as strong for Co (R² = 0.68991). In the MoP group, the analysis revealed a poor relationship between Cr levels and the total chromosomal aberration indices (R² = 0.23908) but a slightly stronger relationship for Co (R² = 0.64292). Across both groups, Spearman’s correlation detected no overall association between Co and Cr levels and each of the studied chromosomal aberrations. There remains no clear indication which THA bearing couple is the most biocompatible, especially in young active patients. While THA continues to be very successful at alleviating pain and restoring function, the long-term biological implications of the procedure still require further scrutiny.

Cite this article: Bone Joint J 2015;97-B:1183–91.

Metallosis after shoulder replacement has not previously been described in the literature. We report a patient who developed extensive metallosis after implantation of an uncemented Nottingham shoulder replacement. He underwent a revision procedure.

Examination of the retrieved prosthesis showed that the titanium porous coating was separating from the humeral stem and becoming embedded in the ultra-high-molecular-weight polyethylene glenoid component, resulting in abrasive wear of the humeral component. There was metallosis despite exchange of the modular humeral head. Both components had to be exchanged to resolve the problem.

Increased concentrations of metal ions after metal-on-metal resurfacing arthroplasty of the hip remain a concern. Although there has been no proven link to long-term health problems or early prosthetic failure, variables associated with high metal ion concentrations should be identified and, if possible, corrected. Our study provides data on metal ion levels from a series of 76 consecutive patients (76 hips) after resurfacing arthroplasty with the Articular Surface Replacement. Chromium and cobalt ion concentrations in the whole blood of patients with smaller (≤ 51 mm) femoral components were significantly higher than in those with the larger (≥ 53 mm) components (p < 0.01). Ion concentrations in the former group were significantly related to the inclination (p = 0.01) and anteversion (p = 0.01) of the acetabular component. The same relationships were not significant in the patients with larger femoral components (p = 0.61 and p = 0.49, respectively). Accurate positioning of the acetabular component intra-operatively is essential in order to reduce the concentration of metal ions in the blood after hip resurfacing arthroplasty with the Articular Surface Replacement implant.

The August 2012 Knee Roundup³⁶⁰ looks at: meniscal defects and a polyurethane scaffold; which is best between a single or double bundle; OA of the knee; how to resolve anterior knee pain; whether yoga can be bad for your menisci; metal ions in the serum; whether ACI is any good; the ACL; whether hyaluronic acid delays collagen degradation; and hyaluronan and patellar tendinopathy.

We report a case of a male patient presenting with bilateral painful but apparently well-positioned and -fixed large-diameter metal-on-metal hip replacements four years post-operatively. Multiple imaging modes revealed a thick-walled, cystic expansile mass in communication with the hip joint (a pseudotumour). Implant retrieval analysis and tissue culture eliminated high bearing wear or infection as causes for the soft-tissue reaction, but noted marked corrosion of the modular neck taper adaptor and corrosion products in the tissues. Therefore, we believe corrosion products from the taper caused by mismatch of the implant components led to pseudotumour formation requiring revision.

Objectives

Recent studies have shown that modulating inflammation-related lipid signalling after a bone fracture can accelerate healing in animal models. Specifically, decreasing 5-lipoxygenase (5-LO) activity during fracture healing increases cyclooxygenase-2 (COX-2) expression in the fracture callus, accelerates chondrogenesis and decreases healing time. In this study, we test the hypothesis that 5-LO inhibition will increase direct osteogenesis.

We present a case of early retrieval of an Oxinium femoral head and corresponding polyethylene liner where there was significant surface damage to the head and polyethylene. The implants were retrieved at the time of revision surgery to correct leg-length discrepancy just 48 hours after the primary hip replacement. Appropriate analysis of the retrieved femoral head demonstrated loss of the Oxinium layer with exposure of the underlying substrate and transfer of titanium from the acetabular shell at the time of a reduction of the index total hip replacement. In addition, the level of damage to the polyethylene was extensive despite only 48 hours in situ.

The purpose of this report is to highlight the care that is required at the time of reduction, especially with these hard femoral counter-faces such as Oxinium. To our knowledge, the damage occurring at the time of reduction has not been previously reported following the retrieval of an otherwise well-functioning hip replacement.

Retrieval studies of total hip replacements with highly cross-linked ultra-high-molecular-weight polyethylene liners have shown much less surface damage than with conventional ultra-high-molecular-weight polyethylene liners. A recent revision hip replacement for recurrent dislocation undertaken after only five months revealed a highly cross-linked polyethylene liner with a large area of visible delamination. In order to determine the cause of this unusual surface damage, we analysed the bearing surfaces of the cobalt-chromium femoral head and the acetabular liner with scanning electron microscopy, energy dispersive x-ray spectroscopy and optical profilometry. We concluded that the cobalt-chromium modular femoral head had scraped against the titanium acetabular shell during the course of the dislocations and had not only roughened the surface of the femoral head but also transferred deposits of titanium onto it. The largest deposits were 1.6 μm to 4.3 μm proud of the surrounding surface and could lead to increased stresses in the acetabular liner and therefore cause accelerated wear and damage.

This case illustrates that dislocations can leave titanium deposits on cobalt-chromium femoral heads and that highly cross-linked ultra-high-molecular-weight polyethylene remains susceptible to surface damage.

We report serum metal ion level data in patients with unilateral and bilateral hip resurfacing over a ten-year period. In these patients there is an increase in both cobalt and chromium levels above the accepted reference ranges during the first 18 months after operation. Metal ion levels remain elevated, but decline slowly for up to five years. However, the levels then appear to start rising again in some patients up to the ten-year mark. There was no significant difference in cobalt or chromium levels between men and women. These findings appear to differ from much of the current literature.

The clinical significance of a raised metal ion level remains under investigation.

This paper considers the increased risk of the development of lymphoma in patients with chronic inflammatory disease who undergo metal-on-metal arthroplasty.

This study reports on ceramic-on-metal (CoM) bearings in total hip replacement. Whole blood metal ion levels were measured. The median increase in chromium and cobalt at 12 months was 0.08 μg/1 and 0.22 μg/1, respectively, in CoM bearings. Comparable values for metal-on-metal (MoM) were 0.48 μg/1 and 0.32 μg/1. The chromium levels were significantly lower in CoM than in MoM bearings (p = 0.02). The cobalt levels were lower, but the difference was not significant. Examination of two explanted ceramic heads revealed areas of thin metal transfer. CoM bearings (one explanted head and acetabular component, one explanted head and new acetabular component, and three new heads and acetabular components) were tested in a hip joint simulator. The explanted head and acetabular component had higher bedding-in. However, after one million cycles all the wear rates were the same and an order of magnitude less than that reported for MoM bearings. There were four outliers in each clinical group, primarily related to component malposition.

The recent resurgence in the use of metal-on-metal bearings has led to fresh concerns over metal wear and elevated systemic levels of metal ions.

In order to establish if bearing diameter influences the release of metal ions, we compared the whole blood levels of cobalt and chromium (at one year) and the urinary cobalt and chromium output (at one to three and four to six years) following either a 50 mm or 54 mm Birmingham hip resurfacing or a 28 mm Metasul total hip replacement. The whole blood concentrations and daily output of cobalt and chromium in these time periods for both bearings were in the same range and without significant difference.