The creep and wear behaviour of highly cross-linked polyethylene and standard polyethylene liners were examined in a prospective, double-blind randomised, controlled trial using radiostereometric analysis.

We randomised 54 patients to receive hip replacements with either highly cross-linked polyethylene or standard liners and determined the three-dimensional penetration of the liners over three years.

After three years the mean total penetration was 0.35 mm (SD 0.14) for the highly cross-linked polyethylene group and 0.45 mm (SD 0.19) for the standard group. The difference was statistically significant (p = 0.0184). From the pattern of penetration it was possible to discriminate creep from wear. Most (95%) of the creep occurred within six months of implantation and nearly all within the first year. There was no difference in the mean degree of creep between the two types of polyethylene (highly cross-linked polyethylene 0.26 mm, SD 0.17; standard 0.27 mm, SD 0.2; p = 0.83). There was, however, a significant difference (p = 0.012) in the mean wear rate (highly cross-linked polyethylene 0.03 mm/yr, SD 0.06; standard 0.07 mm/yr, SD 0.05). Creep and wear occurred in significantly different directions (p = 0.01); creep was predominantly proximal whereas wear was anterior, proximal and medial.

We conclude that penetration in the first six months is creep-dominated, but after one year virtually all penetration is due to wear. Highly cross-linked polyethylene has a 60% lower rate of wear than standard polyethylene and therefore will probably perform better in the long term.

Few independent studies have reported the outcome of resurfacing arthroplasty of the hip. The aim of this study was to report the five-year clinical outcome and seven-year survival of an independent series.

A total of 610 Birmingham Hip Resurfacing arthroplasties were performed in 532 patients with a mean age of 51.8 years (16.5 to 81.6). They were followed for between two and eight years; 107 patients (120 hips) had been followed up for more than five years. Two patients were lost to follow-up. At a minimum of five years’ follow-up, 79 of 85 hips (93%) had an excellent or good outcome according to the Harris hip score. The mean Oxford hip score was 16.1 points (sd 7.7) and the mean University of California Los Angeles activity score was 6.6 points (sd 1.9). There were no patients with definite radiological evidence of loosening or of narrowing of the femoral neck exceeding 10% of its width. There were 23 revisions (3.8%), giving an overall survival of 95% (95% confidence interval 85.3 to 99.2) at seven years. Fractured neck of femur in 12 hips was the most common indication for revision, followed by aseptic loosening in four. In three hips (three patients) (0.5%), failure was possibly related to metal debris.

Considering that these patients are young and active these results are good, and support the use of resurfacing. Further study is needed to address the early failures, particularly those related to fracture and metal debris.

In 12 patients, we measured the oxygen concentration in the femoral head-neck junction during hip resurfacing through the anterolateral approach. This was compared with previous measurements made for the posterior approach. For the anterolateral approach, the oxygen concentration was found to be highly dependent upon the position of the leg, which was adjusted during surgery to provide exposure to the acetabulum and femoral head. Gross external rotation of the hip gave a significant decrease in oxygenation of the femoral head. Straightening the limb led to recovery in oxygen concentration, indicating that the blood supply was maintained. The oxygen concentration at the end of the procedure was not significantly different from that at the start.

The anterolateral approach appears to produce less disruption to the blood flow in the femoral head-neck junction than the posterior approach for patients undergoing hip resurfacing. This may be reflected subsequently in a lower incidence of fracture of the femoral neck and avascular necrosis.

Resurfacing arthroplasty of the hip is being used increasingly as an alternative to total hip replacement, especially for young active patients. There is concern about necrosis of the femoral head after resurfacing which can result in fracture and loosening. Most systems use a cemented femoral component, with the potential for thermal necrosis of the cancellous bone of the reamed femoral head. We used thermal probes to record temperatures close to the cement-bone interface during resurfacing arthroplasty.

The maximum temperature recorded at the cement-bone interface in four cases was approximately 68°C which was higher than that reported to kill osteocytes. A modified surgical technique using insertion of a suction cannula into the lesser trochanter, generous pulsed lavage and early reduction of the joint significantly reduced the maximum recorded cancellous bone temperature to approximately 36°C in five cases (p = 0.014).

We recommend the modified technique since it significantly reduces temperatures at the cement-bone interface.

We performed a clinical and radiological study to determine the rate of failure of the Charnley Elite-Plus femoral component. Our aim was to confirm or refute the predictions of a previous roentgen stereophotogrammetric analysis study in which 20% of the Charnley Elite-Plus stems had shown rapid posterior head migration. It was predicted that this device would have a high early rate of failure.

We examined 118 patients at a mean of nine years after hip replacement, including the 19 patients from the original roentgen stereophotogrammetric study. The number of revision procedures was recorded and clinical and radiological examinations were performed.

The rate of survival of the femoral stems at ten years was 83% when revision alone was considered to be a failure. It decreased to 59% when a radiologically loose stem was also considered to be a failure. All the patients previously shown in the roentgen stereophotogrammetric study to have high posterior head migration went on to failure. There was a highly significant difference (p = 0.002) in posterior head migration measured at two years after operation between failed and non-failed femoral stems, but there was no significant difference in subsidence between these two groups.

Our study has shown that the Charnley Elite-Plus femoral component has an unacceptably high rate of failure. It confirms that early evaluation of new components is important and that roentgen stereophotogrammetric is a good tool for this. Our findings have also shown that rapid posterior head migration is predictive of premature loosening and a better predictor than subsidence.

We inserted an electrode up the femoral neck into the femoral head of ten patients undergoing a metal-on-metal hip resurfacing arthroplasty through a posterior surgical approach and measured the oxygen concentration during the operation. In every patient the blood flow was compromised during surgery, but the extent varied. In three patients, the oxygen concentration was zero at the end of the procedure. The surgical approach caused a mean 60% drop (p < 0.005) in oxygen concentration while component insertion led to a further 20% drop (p < 0.04). The oxygen concentration did not improve significantly on wound closure. This study demonstrates that during hip resurfacing arthroplasty, patients experience some compromise to their femoral head blood supply and some have complete disruption.

Polished, tapered stems are now widely used for cemented total hip replacement and many such designs have been introduced. However, a change in stem geometry may have a profound influence on stability. Stems with a wide, rectangular proximal section may be more stable than those which are narrower proximally. We examined the influence of proximal geometry on stability by comparing the two-year migration of the Exeter stem with a more recent design, the CPS-Plus, which has a wider shoulder and a more rectangular cross-section. The hypothesis was that these design features would increase rotational stability.

Both stems subsided approximately 1 mm relative to the femur during the first two years after implantation. The Exeter stem was found to rotate into valgus (mean 0.2°, sd 0.42°) and internally rotate (mean 1.28°, sd 0.99°). The CPS-Plus showed no significant valgus rotation (mean 0.2°, sd 0.42°) or internal rotation (mean −0.03°, sd 0.75°). A wider, more rectangular cross-section improves rotational stability and may have a better long-term outcome.

The Birmingham hip resurfacing (BHR) arthroplasty is a metal-on-metal prosthesis for which no medium- or long-term results have been published. Despite this, it is increasing in popularity as an alternative to stemmed prostheses for younger patients. Since the fixation of the socket is conventional, the major concern is long-term failure of the femoral component. This can be predicted by the use of roentgen stereophotogrammetric analysis (RSA). We have therefore undertaken such a study of the BHR femoral component over a period of two years.

Twenty patients (22 hips) underwent a standard BHR procedure. Migration of the femoral component was measured by RSA at intervals of three, six, 12 and 24 months. At 24 months the total three-dimensional migration of the head was 0.2 mm. This was not statistically significant. Previous studies have shown that implants which loosen quickly have rapid early migration. Our results therefore suggest that the BHR femoral component is an inherently stable device which is likely to perform well in the long term.