Aims. Radiostereometric analysis (RSA) is the most accurate radiological method to measure in vivo wear of highly cross-linked polyethylene (XLPE) acetabular components. We have previously reported very low wear rates for a sequentially irradiated and annealed X3 XLPE liner (Stryker Orthopaedics, USA) when used in conjunction with a 32 mm femoral heads at ten-year follow-up. Only two studies have reported the long-term wear rate of X3 liners used in conjunction with larger heads using plain radiographs which have poor sensitivity. The aim of this study was to measure the ten-year wear of thin X3 XLPE liners against larger 36 or 40 mm articulations with RSA. Methods. We prospectively reviewed 19 patients who underwent primary cementless THA with the XLPE acetabular liner (X3) and a 36 or 40 mm femoral head with a resultant liner thickness of at least 5.8 mm. RSA radiographs at one week, six months, and one, two, five, and ten years postoperatively and femoral head penetration within the acetabular component were measured with UmRSA software. Of the initial 19 patients, 12 were available at the ten-year time point. Results. The median proximal, 2D, and 3D wear rates calculated between one and ten years were all less than 0.005 mm/year, with no patient recording a proximal wear rate of more than 0.021 mm/year. Importantly, there was no increase in the wear rate between five and ten years. Conclusion. The very low wear rate of X3 XLPE liners with larger articulations remains encouraging for the future clinical performance of this material. Cite this article: Bone Jt Open 2023;4(11):839–845

The leading indication for revision total hip arthroplasty (THA) remains aseptic loosening owing to wear. The younger, more active patients currently undergoing THA present unprecedented demands on the bearings. Ceramic-on-ceramic (CoC) bearings have consistently shown the lowest rates of wear. The recent advances, especially involving alumina/zirconia composite ceramic, have led to substantial improvements and good results in vitro. Alumina/zirconia composite ceramics are extremely hard, scratch resistant and biocompatible. They offer a low co-efficient of friction and superior lubrication and lower rates of wear compared with other bearings. The major disadvantage is the risk of fracture of the ceramic. The new composite ceramic has reduced the risk of fracture of the femoral head to 0.002%. The risk of fracture of the liner is slightly higher (0.02%). Assuming that the components are introduced without impingement, CoC bearings have major advantages over other bearings. Owing to the superior hardness, they produce less third body wear and are less vulnerable to intra-operative damage. The improved tribology means that CoC bearings are an excellent choice for young, active patients requiring THA. Cite this article: Bone Joint J 2016;98-B(1 Suppl A):14–17

Aims. The aim of this study was to evaluate the performance of first-generation annealed highly cross-linked polyethylene (HXLPE) in cementless total hip arthroplasty (THA). Methods. We retrospectively evaluated 29 patients (35 hips) who underwent THA between December 2000 and February 2002. The survival rate was estimated using the Kaplan-Meier method. Hip joint function was evaluated using the Japanese Orthopaedic Association (JOA) score. Two-dimensional polyethylene wear was estimated using Martell’s Hip Analysis Suite. We calculated the wear rates between years 1 and 5, 5 and 10, 10 and 15, and 15 and final follow-up. Results. The mean follow-up period was 19.1 years (SD 0.6; 17.3 to 20.1). The 19-year overall survival rate with the end point of all-cause revision was 97.0% (95% confidence interval (CI) 91 to 100). The mean JOA score improved from 43.2 (SD 10.6; 30 to 76) before surgery to 90.2 (SD 6.4; 76 to 98) at the final follow-up (p < 0.001). There was no osteolysis or loosening of the acetabular or femoral components. The overall steady-state wear rate was 0.013 mm/year (SD 0.012). There was no hip with a steady-state wear rate of > 0.1 mm/year. There was no significant difference in wear rates for each period. We found no significant correlation between the wear rate and age, body weight, BMI, or cup inclination. Conclusion. First-generation annealed HXLPE shows excellent wear resistance and no acceleration of wear for approximately 20 years, with low all-cause revision rates. Cite this article: Bone Joint J 2022;104-B(2):200–205

Aims. Several short- and mid-term studies have shown minimal liner wear of highly cross-linked polyethylene (HXLPE) in total hip arthroplasty (THA), but the safety of using thinner HXLPE liners to maximize femoral head size remains uncertain. The objective of this study was to analyze clinical survival and radiological wear rates of patients with HXLPE liners, a 36 mm femoral head, and a small acetabular component with a minimum of ten years’ follow-up. Methods. We retrospectively identified 55 patients who underwent primary THA performed at a single centre, using HXLPE liners with 36 mm cobalt-chrome heads in acetabular components with an outer diameter of 52 mm or smaller. Patient demographic details, implant details, death, and all-cause revisions were recorded. Cox regression and Kaplan-Meier survival was used to determine all-cause and liner-specific revision. Of these 55 patients, 22 had a minimum radiological follow-up of seven years and were assessed radiologically for linear and volumetric wear. Results. Overall survival rate for all-cause revision was 94.5% (95% confidence interval (CI) 81.7% to 97.2%) at a mean follow-up of 12.8 years (10.9 to 18.7). Three patients were revised, none for liner wear, fracture, or dissociation. A total of 22 patients were included in the radiological analysis (mean follow-up 9.9 years (7.5 to 13.7)). Mean linear liner wear was 0.085 mm (95% CI -0.086 to 0.257) and the volumetric wear rate was 11.097 mm. 3. /year (95% CI -6.5 to 28.7). Conclusion. Using HXLPE liners with 36 mm heads in 52 mm acetabular components or smaller is safe, with excellent survival and low rates of linear and volumetric wear at medium-term follow-up. Patients did not require revision surgery for liner complications such as fracture, dissociation, or wear. Our results suggest that the advantages of using larger heads outweigh the potential risks of using thin HXLPE liners. Cite this article: Bone Joint J 2023;105-B(1):29–34

Aims. The optimum clearance between the bearing surfaces of hip arthroplasties is unknown. Theoretically, to minimize wear, it is understood that clearances must be low enough to maintain optimal contact pressure and fluid film lubrication, while being large enough to allow lubricant recovery and reduce contact patch size. This study aimed to identify the relationship between diametrical clearance and volumetric wear, through the analysis of retrieved components. Methods. A total of 81 metal-on-metal Pinnacle hips paired with 12/14 stems were included in this study. Geometrical analysis was performed on each component, using coordinate and roundness measuring machines. The relationship between their as-manufactured diametrical clearance and volumetric wear was investigated. The Mann-Whitney U test and unpaired t-test were used, in addition to calculating the non-parametric Spearman's correlation coefficient, to statistically evaluate the acquired data. Results. The hips in this study were found to have had a median unworn diametrical clearance of 90.31 μm (interquartile range (IQR) 77.59 to 97.40); 32% (n = 26) were found to have been below the manufacturing tolerance. There was no correlation found between clearance and bearing (r. s. = -0.0004, p = 0.997) or taper (r. s. = 0.0048, p = 0.966) wear rates. The wear performance of hips manufactured within and below these specifications was not significantly different (bearing: p = 0.395; taper: p = 0.653). Pinnacles manufactured from 2007 onwards had a greater prevalence of bearing clearance below tolerance (p = 0.004). Conclusion. The diametrical clearance of Pinnacle hips did not influence their wear performance, even when below the manufacturing tolerance. The optimum clearance for minimizing hip implant wear remains unclear. Cite this article: Bone Joint Res 2020;9(8):515–523

We reviewed the literature on the currently available choices of bearing surface in total hip replacement (THR). We present a detailed description of the properties of articulating surfaces review the understanding of the advantages and disadvantages of existing bearing couples. Recent technological developments in the field of polyethylene and ceramics have altered the risk of fracture and the rate of wear, although the use of metal-on-metal bearings has largely fallen out of favour, owing to concerns about reactions to metal debris. As expected, all bearing surface combinations have advantages and disadvantages. A patient-based approach is recommended, balancing the risks of different options against an individual’s functional demands. Cite this article: Bone Joint J 2014;96-B:147–56

Aims. We aimed to investigate if the use of the largest possible cobalt-chromium head articulating with polyethylene acetabular inserts would increase the in vivo wear rate in total hip arthroplasty. Methods. In a single-blinded randomized controlled trial, 96 patients (43 females), at a median age of 63 years (interquartile range (IQR) 57 to 69), were allocated to receive either the largest possible modular femoral head (36 mm to 44 mm) in the thinnest possible insert or a standard 32 mm head. All patients received a vitamin E-doped cross-linked polyethylene insert and a cobalt-chromium head. The primary outcome was proximal head penetration measured with radiostereometric analysis (RSA) at two years. Secondary outcomes were volumetric wear, periacetabular radiolucencies, and patient-reported outcomes. Results. At two years, 44 patients in each group were available for RSA assessment. The median total two-year proximal head penetration was -0.02 mm (IQR -0.09 to 0.07; p = 0.548) for the largest possible head and -0.01 mm (IQR -0.07 to 0.10; p = 0.525) for 32 mm heads. Their difference was not statistically significant (p = 0.323). Neither group demonstrated a bedding-in period. The median steady-state volumetric wear rates were 6.1 mm. 3. /year (IQR -59 to 57) and 3.5 mm. 3. /year (-21 to 34) respectively, and did not differ between the groups (p = 0.848). There were no statistically significant differences in periacetabular radiolucencies or patient-reported outcomes. Conclusion. The use of the largest possible metal head did not increase vitamin E-doped cross-linked polyethylene wear compared with 32 mm heads at two years. Linear wear was negligible and volumetric wear rates were very low in both head size groups. There was a tendency towards higher values of volumetric wear in large heads that warrants longer-term evaluation before any definite conclusions about the association between head size and wear can be drawn. Cite this article: Bone Joint J 2021;103-B(7):1206–1214

Aims. The aim of this study was to determine whether there is a difference in the rate of wear between acetabular components positioned within and outside the ‘safe zones’ of anteversion and inclination angle. Patients and Methods. We reviewed 100 hips in 94 patients who had undergone primary total hip arthroplasty (THA) at least ten years previously. Patients all had the same type of acetabular component with a bearing couple which consisted of a 28 mm cobalt-chromium head on a highly crosslinked polyethylene (HXLPE) liner. A supine radiostereometric analysis (RSA) examination was carried out which acquired anteroposterior (AP) and lateral paired images. Acetabular component anteversion and inclination angles were measured as well as total femoral head penetration, which was divided by the length of implantation to determine the rate of polyethylene wear. Results. The mean anteversion angle was 19.4° (-15.2° to 48°, . sd. 11.4°), the mean inclination angle 43.4° (27.3° to 60.5°, . sd. 6.6°), and the mean wear rate 0.055 mm/year (. sd. 0.060). Exactly half of the hips were positioned inside the ‘safe zone’. There was no difference (median difference, 0.012 mm/year; p = 0.091) in the rate of wear between acetabular components located within or outside the ‘safe zone’. When compared to acetabular components located inside the ‘safe zone’, the wear rate was no different for acetabular components that only achieved the target anteversion angle (median difference, 0.012 mm/year; p = 0.138), target inclination angle (median difference, 0.013 mm/year; p = 0.354), or neither target (median difference, 0.012 mm/year; p = 0.322). Conclusion. Placing the acetabular component within or outside the ‘safe zone’ did not alter the wear rate of HXLPE at long-term follow-up to a level that risked osteolysis. HXLPE appears to be a forgiving bearing material in terms of articular surface wear, but care must still be taken to position the acetabular component correctly so that the implant is stable. Cite this article: Bone Joint J 2018;100-B:891-7

Objectives. The determination of the volumetric polyethylene wear on explanted material requires complicated equipment, which is not available in many research institutions. Our aim in this study was to present and validate a method that only requires a set of polyetheretherketone balls and a laboratory balance to determine wear. Methods. The insert to be measured was placed on a balance, and a ball of the appropriate diameter was inserted. The cavity remaining between the ball and insert caused by wear was filled with contrast medium and the weight of the contrast medium was recorded. The volume was calculated from the known density of the liquid. The precision, inter- and intraobserver reliability, were determined by four investigators on four days using nine inserts with specified wear (0.094 ml to 1.626 ml), and the intra-class correlation coefficient was calculated. The feasibility of using this method in routine clinical practice and the time required for measurement were tested on 84 explanted inserts by one investigator. Results. In order to get the mean for all investigators and determinations, the deviation between the measured and specified wear was -0.08 ml . (sd. 0.12; -0.21 to 0.11). The interobserver reliability was 0.989 ml (95% confidence interval (CI) 0.964 to 0.997) and the intraobserver reliability was 0.941 for observer 1 (95% CI 0.846 to 0.985), 0.983 for observer 2 (95% CI 0.956 to 0.995), 0.939 for observer 3 (95% CI 0.855 to 0.984), and 0.934 for observer 4 (95% CI 0.790 to 0.984). The mean time required to examine the samples was two minutes . (sd. 2; 1 to 5). Conclusion. The method presented here was shown to be sufficiently precise for many settings and is a cost-effective and quick method of determining the volumetric wear of explanted acetabular components. However, the measurement of wear for scientific purposes will probably continue to involve more accurate and dedicated laboratory equipment. Cite this article: Bone Joint Res 2017;6:530–534

Objectives. Previous studies have suggested that metal-on-metal (MoM) Pinnacle (DePuy Synthes, Warsaw, Indiana) hip arthroplasties implanted after 2006 exhibit higher failure rates. This was attributed to the production of implants with reduced diametrical clearances between their bearing surfaces, which, it was speculated, were outside manufacturing tolerances. This study aimed to better understand the performance of Pinnacle Systems manufactured before and after this event. Methods. A total of 92 retrieved MoM Pinnacle hips were analyzed, of which 45 were implanted before 2007, and 47 from 2007 onwards. The ‘pre-2007’ group contained 45 implants retrieved from 21 male and 24 female patients, with a median age of 61.3 years (interquartile range (IQR) 57.1 to 65.5); the ‘2007 onwards’ group contained 47 implants retrieved from 19 male and 28 female patients, with a median age of 61.8 years (IQR 58.5 to 67.8). The volume of material lost from their bearing and taper surfaces was measured using coordinate and roundness measuring machines. These outcomes were then compared statistically using linear regression models, adjusting for potentially confounding factors. Results. There was no significant difference between the taper and bearing wear rates of the ‘pre-2007’ and ‘2007 onwards’ groups (p = 0.67 and p = 0.39, respectively). Pinnacles implanted from 2007 onwards were revised after a mean time of 50 months, which was significantly earlier than the ‘pre-2007’ hips (96 months) (p < 0.001). A reduction in the time to revision was present year on year from 2003 to 2011. Conclusion. We found no difference in the wear rate of these implants based on the year of implantation. The ‘pre-2007’ hips had a two-fold greater time to revision than those implanted after 2007; this may be due to the increased surveillance of MoM hips following UK regulatory advice and several high-profile failures. Interestingly, we observed a decreasing trend in the mean time to revision every year from 2003 onwards. Cite this article: S. Bergiers, H. S. Hothi, J. Henckel, A. Eskelinen, J. Skinner, A. Hart. Wear performance of retrieved metal-on-metal Pinnacle hip arthroplasties implanted before and after 2007. Bone Joint Res 2018;7:595–600. DOI: 10.1302/2046-3758.711.BJR-2018-0143.R1

We analysed 54 alumina ceramic-on-ceramic bearings from total hip replacements retrieved at one centre after a mean duration of 3.5 years (0.2 to 10.6) in situ. These implants were obtained from 54 patients (16 men and 38 women) with a mean age of 67 years (33 to 88) who underwent revision for a variety of reasons. Posterior edge loading was found in the majority of these retrievals (32 out of 54). Anterosuperior edge loading occurred less often but produced a higher rate of wear. Stripe wear on the femoral heads had a median volumetric wear rate of 0.2 mm. 3. /year (0 to 7.2). The wear volume on the femoral heads corresponded to the width of edge wear on the matching liner. Anteversion of the acetabular component was found to be a more important determinant than inclination for wear in ceramic bearings. Posterior edge loading may be considered to be a normal occurrence in ceramic-on-ceramic bearings, with minimal clinical consequences. Edge loading should be defined as either anterosuperior or posterior, as each edge loading mechanism may result in different clinical implications

The creep and wear behaviour of highly cross-linked polyethylene and standard polyethylene liners were examined in a prospective, double-blind randomised, controlled trial using radiostereometric analysis. We randomised 54 patients to receive hip replacements with either highly cross-linked polyethylene or standard liners and determined the three-dimensional penetration of the liners over three years. After three years the mean total penetration was 0.35 mm (SD 0.14) for the highly cross-linked polyethylene group and 0.45 mm (SD 0.19) for the standard group. The difference was statistically significant (p = 0.0184). From the pattern of penetration it was possible to discriminate creep from wear. Most (95%) of the creep occurred within six months of implantation and nearly all within the first year. There was no difference in the mean degree of creep between the two types of polyethylene (highly cross-linked polyethylene 0.26 mm, SD 0.17; standard 0.27 mm, SD 0.2; p = 0.83). There was, however, a significant difference (p = 0.012) in the mean wear rate (highly cross-linked polyethylene 0.03 mm/yr, SD 0.06; standard 0.07 mm/yr, SD 0.05). Creep and wear occurred in significantly different directions (p = 0.01); creep was predominantly proximal whereas wear was anterior, proximal and medial. We conclude that penetration in the first six months is creep-dominated, but after one year virtually all penetration is due to wear. Highly cross-linked polyethylene has a 60% lower rate of wear than standard polyethylene and therefore will probably perform better in the long term

Aims. Vitamin E-diffused, highly crosslinked polyethylene (VEPE) and porous titanium-coated (PTC) shells were introduced in total hip arthroplasty (THA) to reduce the risk of aseptic loosening. The purpose of this study was: 1) to compare the wear properties of VEPE to moderately crosslinked polyethylene; 2) to assess the stability of PTC shells; and 3) to report their clinical outcomes at seven years. Patients and Methods. A total of 89 patients were enrolled into a prospective study. All patients received a PTC shell and were randomized to receive a VEPE liner (n = 44) or a moderately crosslinked polyethylene (ModXLPE) liner (n = 45). Radiostereometric analysis (RSA) was used to measure polyethylene wear and component migration. Differences in wear were assessed while adjusting for body mass index, activity level, acetabular inclination, anteversion, and head size. Plain radiographs were assessed for radiolucency and patient-reported outcome measures (PROMs) were administered at each follow-up. Results. In total, 73 patients (82%) completed the seven-year visit. Mean seven-year linear proximal penetration was -0.07 mm (. sd. 0.16) and 0.00 mm (. sd. 0.22) for the VEPE and ModXLPE cohorts, respectively (p = 0.116). PROMs (p = 0.310 to 0.807) and radiolucency incidence (p = 0.330) were not different between the polyethylene cohorts. The mean proximal shell migration rate was 0.04 mm per year (. sd. 0.09). At seven years, patients with radiolucency (34%) demonstrated greater migration (mean difference: 0.6 mm (. sd. 0.2); p < 0.001). PROMs were lower for patients with radiolucency and greater proximal migration (p = 0.009 to p = 0.045). No implants were revised for aseptic loosening. Conclusion. This is the first randomized controlled trial to report seven-year RSA results for VEPE. All wear rates were below the previously reported osteolysis threshold (0.1 mm per year). PTC shells demonstrated acceptable primary stability through seven years, as indicated by low migration and lack of aseptic loosening. However, patients with acetabular radiolucency were associated with higher shell migration and lower PROM scores. Cite this article: Bone Joint J 2019;101-B:760–767

Aims. The increased in vivo resistance to wear of highly crosslinked polyethylene (HXLPE) in total hip arthroplasty (THA) has led to an increased use of larger articulations which have been shown to reduce the incidence of early dislocation. To date, there are few reports of the wear of larger articulations using second generation HXLPE liners. Our prospective cohort study measured the bedding-in and early wear of large (36 mm and 40 mm diameter) articulations involving a second generation X3 HXLPE liner and compared our findings with previous clinical and in vitro studies of the same material. Patients and Methods. The proximal penetration of the femoral head five years post-operatively was measured for 15 patients using radiostereometric analysis (RSA). Results. The median proximal bedding-in within the first post-operative year was 0.022 mm (interquartile range (IQR) -0.050 to 0.091). The median proximal rate of wear between one and five years was -0.004 mm/year (IQR -0.021 to 0.022). The rates of proximal, medial, 2D or 3D wear between one and five years post-operatively of the X3 HXLPE liner did not increase with larger articulations compared with our previous study of 32 mm articulations. Conclusion. Although reassuring, the use of larger articulations requires continued monitoring to determine whether the low wear observed in the short-term continues to the mid- to long-term. Cite this article: Bone Joint J 2016;98-B:1604–10

We investigated the rate of polyethylene wear of a cementless acetabular component at different periods of follow-up in order to test the hypothesis than an irrecoverable deformation process (creep) was followed by an initially low, but gradually increasing wear rate. We studied prospectively 93 uncemented total hip arthroplasties in 83 patients (mean age 50 years (22 to 63)) with a mean follow-up of 8.2 years (3 to 12). We measured the penetration of the femoral head from radiographs taken immediately after surgery at three, six and nine years, or at the latest follow-up. The median wear rate was 0.17 mm per year in the first three years, a finding which we considered to be caused by creep. Thereafter, the rate of wear declined to 0.07 mm per year (four- to six-year period) and then increased to 0.17 mm per year (seven to nine years) and 0.27 mm per year (more than nine years), which we considered to be a reflection of genuine polyethylene wear. After the nine-year follow-up the wear rates were higher in patients with marked osteolysis. We found no relationship between the inclination angle of the acetabular component or femoral head orientation and the rate of wear. No acetabular component required revision

Objectives. The accuracy and precision of two new methods of model-based radiostereometric analysis (RSA) were hypothesised to be superior to a plain radiograph method in the assessment of polyethylene (PE) wear. Methods. A phantom device was constructed to simulate three-dimensional (3D) PE wear. Images were obtained consecutively for each simulated wear position for each modality. Three commercially available packages were evaluated: model-based RSA using laser-scanned cup models (MB-RSA), model-based RSA using computer-generated elementary geometrical shape models (EGS-RSA), and PolyWare. Precision (95% repeatability limits) and accuracy (Root Mean Square Errors) for two-dimensional (2D) and 3D wear measurements were assessed. Results. The precision for 2D wear measures was 0.078 mm, 0.102 mm, and 0.076 mm for EGS-RSA, MB-RSA, and PolyWare, respectively. For the 3D wear measures the precision was 0.185 mm, 0.189 mm, and 0.244 mm for EGS-RSA, MB-RSA, and PolyWare respectively. Repeatability was similar for all methods within the same dimension, when compared between 2D and 3D (all p > 0.28). For the 2D RSA methods, accuracy was below 0.055 mm and at least 0.335 mm for PolyWare. For 3D measurements, accuracy was 0.1 mm, 0.2 mm, and 0.3 mm for EGS-RSA, MB-RSA and PolyWare respectively. PolyWare was less accurate compared with RSA methods (p = 0.036). No difference was observed between the RSA methods (p = 0.10). Conclusions. For all methods, precision and accuracy were better in 2D, with RSA methods being superior in accuracy. Although less accurate and precise, 3D RSA defines the clinically relevant wear pattern (multidirectional). PolyWare is a good and low-cost alternative to RSA, despite being less accurate and requiring a larger sample size

We report the five-year outcome of a randomised controlled trial which used radiostereometric analysis (RSA) to assess the influence of surface oxidised zirconium (OxZr, Oxinium) on polyethylene wear in vivo. A total of 120 patients, 85 women and 35 men with a mean age of 70 years (59 to 80) who were scheduled for primary cemented total hip arthroplasty were randomly allocated to four study groups. Patients were blinded to their group assignment and received either a conventional polyethylene (CPE) or a highly cross-linked (HXL) acetabular component of identical design. On the femoral side patients received a 28 mm head made of either cobalt-chromium (CoCr) or OxZr. . The proximal head penetration (wear) was measured with repeated RSA examinations over five years. Clinical outcome was measured using the Harris hip score. . There was no difference in polyethylene wear between the two head materials when used with either of the two types of acetabular component (p = 0.3 to 0.6). When comparing the two types of polyethylene there was a significant difference in favour of HXLPE, regardless of the head material used (p < 0.001). . In conclusion, we found no advantage of OxZr over CoCr in terms of polyethylene wear after five years of follow-up. Our findings do not support laboratory results which have shown a reduced rate of wear with OxZr. They do however add to the evidence on the better resistance to wear of HXLPE over CPE. Cite this article: Bone Joint J 2015;97-B:1463–9

The presence of pseudotumours, which are soft-tissue masses relating to the hip, after metal-on-metal hip resurfacing arthroplasty has been associated with elevated levels of metal ions in serum, suggesting that pseudotumours occur when there is increased wear. We aimed to quantify the wear in vivo of implants revised for pseudotumours (eight) and of a control group of implants (22) revised for other reasons of failure. We found that the implant group with pseudotumours had a significantly higher rate of median linear wear of the femoral component at 8.1 μm/year (2.75 to 25.4) than the 1.79 μm/year (0.82 to 4.15; p = 0.002) of the non-pseudotumour group. For the acetabular component a significantly higher rate of median linear wear of 7.36 μm/year (1.61 to 24.9) was observed in the pseudotumour group compared with 1.28 μm/year (0.81 to 3.33, p = 0.001) in the other group. Wear of the acetabular component in the pseudotumour group always involved the edge of the implant, indicating that edge-loading had occurred. Our findings are the first direct evidence that pseudotumour is associated with increased wear at the metal-on-metal articulation. Furthermore, edge-loading with the loss of fluid-film lubrication may be an important mechanism of generation of wear in patients with a pseudotumour

Oxidised zirconium (OxZi) has been developed as an alternative bearing surface for femoral heads in total hip arthroplasty (THA). This study has investigated polyethylene wear, functional outcomes and complications, comparing OxZi and cobalt–chrome (CoCr) as part of a three-arm, multicentre randomised controlled trial. Patients undergoing THA from four institutions were prospectively randomised into three groups. Group A received a CoCr femoral head and highly cross-linked polyethylene (XLPE) liner; Group B received an OxZi femoral head and XLPE liner; Group C received an OxZi femoral head and ultra-high molecular weight polyethylene (UHMWPE) liner. At five years, 368 patients had no statistically significant differences in short-form-36 (p = 0.176 mental, p = 0.756 physical), Western Ontario and McMaster Universities Osteoarthritis Index (p = 0.847), pain scores (p = 0.458) or complications. The mean rate of linear wear was 0.028 mm/year (standard deviation (. sd) 0.010). for Group A, 0.023 mm/year (. sd. 0.010) for Group B, and 0.09 mm/year (. sd. 0.045) for Group C. Penetration was significantly higher in the UHMWPE liner group compared with both XLPE liner groups (p < 0.001) but no significant difference was noted between CoCr and OxZi when articulating with XLPE (p = 0.153). In this, the largest randomised study of this bearing surface, it appears that using a XLPE acetabular liner is more important in reducing THA component wear than the choice of femoral head bearing, at mid-term follow-up. There is a non-significant trend towards lower wear, coupling OxZi rather than CoCr with XLPE but long-term analysis is required to see if this observation changes with time and becomes significant. Cite this article: Bone Joint J 2015;97-B:883–9

We measured the orientation of the acetabular and femoral components in 45 patients (33 men, 12 women) with a mean age of 53.4 years (30 to 74) who had undergone revision of metal-on-metal hip resurfacings. Three-dimensional CT was used to measure the inclination and version of the acetabular component, femoral version and the horizontal femoral offset, and the linear wear of the removed acetabular components was measured using a roundness machine. We found that acetabular version and combined version of the acetabular and femoral components were weakly positively correlated with the rate of wear. The acetabular inclination angle was strongly positively correlated with the rate of wear. Femoral version was weakly negatively correlated with the rate of wear. Application of a threshold of > 5 μm/year for the rate of wear in order to separate the revisions into low or high wearing groups showed that more high wearing components were implanted outside Lewinnek’s safe zone, but that this was mainly due to the inclination of the acetabular component, which was the only parameter that significantly differed between the groups. We were unable to show that excess version of the acetabular component alone or combined with femoral version was associated with an increase in the rate of wear based on our assessment of version using CT