Aims. The risk of mechanical failure of modular revision hip stems is frequently mentioned in the literature, but little is currently known about the actual clinical failure rates of this type of prosthesis. The current retrospective long-term analysis examines the distal and modular failure patterns of the Prevision hip stem from 18 years of clinical use. A design improvement of the modular taper was introduced in 2008, and the data could also be used to compare the original and the current design of the modular connection. Methods. We performed an analysis of the Prevision modular hip stem using the manufacturer’s vigilance database and investigated different mechanical failure patterns of the hip stem from January 2004 to December 2022. Results. Two mechanical failure patterns were identified: fractures in the area of the distal fluted profile (distal stem fracture) and failure of the modular taper (modular fracture). A failure rate of 0.07% was observed for distal stem fracture, and modular fracture rates of 1.74% for the original and 0.013% for the current taper design. Conclusion. A low risk of mechanical failure for both fracture types was observed compared to other known complications in revision hip arthroplasty. In addition, the data show that a design change did significantly reduce the risk of a modular fracture. Cite this article: Bone Joint J 2024;106-B(2):151–157

Aims. Head-taper corrosion is a cause of failure in total hip arthroplasty (THA). Recent reports have described an increasing number of V40 taper failures with adverse local tissue reaction (ALTR). However, the real incidence of V40 taper damage and its cause remain unknown. The aim of this study was to evaluate the long-term incidence of ALTR in a consecutive series of THAs using a V40 taper and identify potentially related factors. Methods. Between January 2006 and June 2007, a total of 121 patients underwent THA using either an uncemented (Accolade I, made of Ti. 12. Mo. 6. Zr. 2. Fe; Stryker, USA) or a cemented (ABG II, made of cobalt-chrome-molybdenum (CoCrMo); Stryker) femoral component, both with a V40 taper (Stryker). Uncemented acetabular components (Trident; Stryker) with crosslinked polyethylene liners and CoCr femoral heads of 36 mm diameter were used in all patients. At a mean folllow-up of 10.8 years (SD 1.1), 94 patients (79%) were eligible for follow-up (six patients had already undergone a revision, 15 had died, and six were lost to follow-up). A total of 85 THAs in 80 patients (mean age 61 years (24 to 75); 47 (56%) were female) underwent clinical and radiological evaluation, including the measurement of whole blood levels of cobalt and chrome. Metal artifact reduction sequence MRI scans of the hip were performed in 71 patients. Results. A total of 20 ALTRs were identified on MRI, with an incidence of 26%. Patients with ALTR had significantly higher median Co levels compared with those without ALTR (2.96 μg/l (interquartile range (IQR) 1.35 to 4.98) vs 1.44 μg/l (IQR 0.79 to 2.5); p = 0.019). Radiological evidence of osteolysis was also significantly associated with ALTR (p = 0.014). Median Cr levels were not significantly higher in those with ALTR compared with those without one (0.97 μg/l (IQR 0.72 to 1.9) v 0.67 μg/l (IQR 0.5 to 1.19; p = 0.080). BMI, sex, age, type of femoral component, head length, the inclination of the acetabular component, and heterotopic ossification formation showed no significant relationship with ALTR. Conclusion. Due to the high incidence of local ALTR in our cohort after more than ten years postoperatively, we recommend regular follow-up investigation even in asymptomatic patients with V40 taper and metal heads. As cobalt levels correlate with ALTR occurrence, routine metal ion screening and consecutive MRI investigation upon elevation could be discussed. Cite this article: Bone Joint J 2022;104-B(7):852–858

Aims. We sought to determine whether cobalt-chromium alloy (CoCr) femoral stem tapers (trunnions) wear more than titanium (Ti) alloy stem tapers (trunnions) when used in a large diameter (LD) metal-on-metal (MoM) hip arthroplasty system. Patients and Methods. We performed explant analysis using validated methodology to determine the volumetric material loss at the taper surfaces of explanted LD CoCr MoM hip arthroplasties used with either a Ti alloy (n = 28) or CoCr femoral stem (n = 21). Only 12/14 taper constructs with a rough male taper surface and a nominal included angle close to 5.666° were included. Multiple regression modelling was undertaken using taper angle, taper roughness, bearing diameter (horizontal lever arm) as independent variables. Material loss was mapped using a coordinate measuring machine, profilometry and scanning electron microscopy. Results. After adjustment for other factors, CoCr stem tapers were found to have significantly greater volumetric material loss than the equivalent Ti stem tapers. Conclusion. When taper junction damage is identified during revision of a LD MoM hip, it should be suspected that a male taper composed of a standard CoCr alloy has sustained significant changes to the taper cone geometry which are likely to be more extensive than those affecting a Ti alloy stem. Cite this article: Bone Joint J 2017;99-B:1304–12

Aims. The aim of this study was to evaluate the suitability of the tapered cone stem in total hip arthroplasty (THA) in patients with excessive femoral anteversion and after femoral osteotomy. Methods. We included patients who underwent THA using Wagner Cone due to proximal femur anatomical abnormalities between August 2014 and January 2019 at a single institution. We investigated implant survival time using the endpoint of dislocation and revision, and compared the prevalence of prosthetic impingements between the Wagner Cone, a tapered cone stem, and the Taperloc, a tapered wedge stem, through simulation. We also collected Oxford Hip Score (OHS), visual analogue scale (VAS) satisfaction, and VAS pain by postal survey in August 2023 and explored variables associated with those scores. Results. Of the 58 patients (62 hips), two (two hips) presented with dislocation or reoperation, and Kaplan-Meier analysis indicated a five-year survival rate of 96.7% (95% CI 92.4 to 100). Mean stem anteversion was 35.2° (SD 18.2°) for the Taperloc stem and 29.8° (SD 7.9°) for the Wagner Cone stem; mean reduction from Taperloc to Wagner Cone was 5.4° (SD 18.8°). Overall, 55 hips (52 patients) were simulated, and the prevalence of prosthetic impingement was lower for the Wagner Cone (5.5%, 3/55) compared with the Taperloc (20.0%, 11/55) stem, with an odds ratio of 0.20 (p = 0.038). Among the 33 respondents to the postal survey (36 hips), the mean scores were VAS pain 10.9, VAS satisfaction 86.9, and OHS 44.7. A multivariable analysis revealed that reduction of stem anteversion from Taperloc to Wagner Cone was more favourable for VAS pain (p = 0.029) and VAS satisfaction (p = 0.002). Conclusion. The mid-term survival rate for THA using the Wagner Cone stem was high, which may be supported by a reduction in prosthetic impingement. The reduction in excessive stem anteversion by using a tapered cone stem was associated with reduced pain and increased patient satisfaction. Cite this article: Bone Jt Open 2024;5(10):858–867

Aims. United Classification System (UCS) B2 and B3 periprosthetic fractures in total hip arthroplasties (THAs) have been commonly managed with modular tapered stems. No study has evaluated the use of monoblock fluted tapered titanium stems for this indication. This study aimed to evaluate the effects of a monoblock stems on implant survivorship, postoperative outcomes, radiological outcomes, and osseointegration following treatment of THA UCS B2 and B3 periprosthetic fractures. Methods. A retrospective review was conducted of all patients who underwent revision THA (rTHA) for periprosthetic UCS B2 and B3 periprosthetic fracture who received a single design monoblock fluted tapered titanium stem at two large, tertiary care, academic hospitals. A total of 72 patients met inclusion and exclusion criteria (68 UCS B2, and four UCS B3 fractures). Primary outcomes of interest were radiological stem subsidence (> 5 mm), radiological osseointegration, and fracture union. Sub-analysis was also done for 46 patients with minimum one-year follow-up. Results. For the total cohort, stem osseointegration, fracture union, and stem subsidence were 98.6%, 98.6%, and 6.9%, respectively, at latest follow-up (mean follow-up 27.0 months (SD 22.4)). For patients with minimum one-year of follow-up, stem osseointegration, fracture union, and stem subsidence were 97.8%, 97.8%, and 6.5%, respectively. Conclusion. Monoblock fluted stems can be an acceptable modality for the management of UCS B2 periprosthetic fractures in rTHAs due to high rates of stem osseointegration and survival, and the low rates of stem subsidence, and revision. Further research on the use of this stem for UCS B3 periprosthetic fractures is warranted to determine if the same conclusion can be made for this fracture pattern. Cite this article: Bone Jt Open 2023;4(8):551–558

Aims. This study investigates head-neck taper corrosion with varying head size in a novel hip simulator instrumented to measure corrosion related electrical activity under torsional loads. Methods. In all, six 28 mm and six 36 mm titanium stem-cobalt chrome head pairs with polyethylene sockets were tested in a novel instrumented hip simulator. Samples were tested using simulated gait data with incremental increasing loads to determine corrosion onset load and electrochemical activity. Half of each head size group were then cycled with simulated gait and the other half with gait compression only. Damage was measured by area and maximum linear wear depth. Results. Overall, 36 mm heads had lower corrosion onset load (p = 0.009) and change in open circuit potential (OCP) during simulated gait with (p = 0.006) and without joint movement (p = 0.004). Discontinuing gait’s joint movement decreased corrosion currents (p = 0.042); however, wear testing showed no significant effect of joint movement on taper damage. In addition, 36 mm heads had greater corrosion area (p = 0.050), but no significant difference was found for maximum linear wear depth (p = 0.155). Conclusion. Larger heads are more susceptible to taper corrosion; however, not due to frictional torque as hypothesized. An alternative hypothesis of taper flexural rigidity differential is proposed. Further studies are necessary to investigate the clinical significance and underlying mechanism of this finding. Cite this article: Bone Jt Open 2021;2(11):1004–1016

Aims. When performing revision total hip arthroplasty using diaphyseal-engaging titanium tapered stems (TTS), the recommended 3 to 4 cm of stem-cortical diaphyseal contact may not be available. In challenging cases such as these with only 2 cm of contact, can sufficient axial stability be achieved and what is the benefit of a prophylactic cable? This study sought to determine, first, whether a prophylactic cable allows for sufficient axial stability when the contact length is 2 cm, and second, if differing TTS taper angles (2° vs 3.5°) impact these results. Methods. A biomechanical matched-pair cadaveric study was designed using six matched pairs of human fresh cadaveric femora prepared so that 2 cm of diaphyseal bone engaged with 2° (right femora) or 3.5° (left femora) TTS. Before impaction, three matched pairs received a single 100 lb-tensioned prophylactic beaded cable; the remaining three matched pairs received no cable adjuncts. Specimens underwent stepwise axial loading to 2600 N or until failure, defined as stem subsidence > 5 mm. Results. All specimens without cable adjuncts (6/6 femora) failed during axial testing, while all specimens with a prophylactic cable (6/6) successfully resisted axial load, regardless of taper angle. In total, four of the failed specimens experienced proximal longitudinal fractures, three of which occurred with the higher 3.5° TTS. One fracture occurred in a 3.5° TTS with a prophylactic cable yet passed axial testing, subsiding < 5 mm. Among specimens with a prophylactic cable, the 3.5° TTS resulted in lower mean subsidence (0.5 mm (SD 0.8)) compared with the 2° TTS (2.4 mm (SD 1.8)). Conclusion. A single prophylactic beaded cable dramatically improved initial axial stability when stem-cortex contact length was 2 cm. All implants failed secondary to fracture or subsidence > 5 mm when a prophylactic cable was not used. A higher taper angle appears to decrease the magnitude of subsidence but increased the fracture risk. The fracture risk was mitigated by the use of a prophylactic cable. Cite this article: Bone Jt Open 2023;4(7):472–477

Aims. There are limited published data detailing the volumetric material loss from tapers of conventional metal-on-polyethylene (MoP) total hip arthroplasties (THAs). Our aim was to address this by comparing the taper wear rates measured in an explanted cohort of the widely used Exeter THA with those measured in a group of metal-on-metal (MoM) THAs. Patients and Methods. We examined an existing retrieval database to identify all Exeter V40 and Universal MoP THAs. Volumetric wear analysis of the taper surfaces was conducted using previously validated methodology. These values were compared with those obtained from a series of MoM THAs using non-parametric statistical methodology. A number of patient and device variables were accounted for using multiple regression modelling. Results. A total of 95 Exeter MoP and 249 MoM THAs were examined. The median volumetric loss from the MoM cohort was over four times larger than that from the MoP cohort (1.01 mm. 3. vs 0.23 mm. 3. , p < 0.001), despite a significantly shorter median period in vivo for the MoM group (48 months vs 90 months, p < 0.001). Multiple regression modelling indicated that the dominant variables leading to greater female taper material loss were bearing diameter (p < 0.001), larger female taper angles (p < 0.001), and male titanium stem tapers (p < 0.001). Conclusion. Consistent with the long-term clinical success of the device, the volumetric material loss from Exeter femoral head tapers was, in general, small compared with that from larger-diameter MoM head tapers. Cite this article: Bone Joint J 2018;100-B:1310–9

Aims. The aim of this study was to develop a novel computational model for estimating head/stem taper mechanics during different simulated assembly conditions. Methods. Finite element models of generic cobalt-chromium (CoCr) heads on a titanium stem taper were developed and driven using dynamic assembly loads collected from clinicians. To verify contact mechanics at the taper interface, comparisons of deformed microgroove characteristics (height and width of microgrooves) were made between model estimates with those measured from five retrieved implants. Additionally, these models were used to assess the role of assembly technique—one-hit versus three-hits—on the taper interlock mechanical behaviour. Results. The model compared well to deformed microgrooves from the retrieved implants, predicting changes in microgroove height (mean 1.1 μm (0.2 to 1.3)) and width (mean 7.5 μm (1.0 to 18.5)) within the range of measured changes in height (mean 1.4 μm (0.4 to 2.3); p = 0.109) and width (mean 12.0 μm (1.5 to 25.4); p = 0.470). Consistent with benchtop studies, our model found that increasing assembly load magnitude led to increased taper engagement, contact pressure, and permanent deformation of the stem taper microgrooves. Interestingly, our model found assemblies using three hits at low loads (4 kN) led to decreased taper engagement, contact pressures and microgroove deformations throughout the stem taper compared with tapers assembled with one hit at the same magnitude. Conclusion. These findings suggest additional assembly hits at low loads lead to inferior taper interlock strength compared with one firm hit, which may be influenced by loading rate or material strain hardening. These unique models can estimate microgroove deformations representative of real contact mechanics seen on retrievals, which will enable us to better understand how both surgeon assembly techniques and implant design affect taper interlock strength. Cite this article: Bone Joint J 2020;102-B(7 Supple B):33–40

Aims. Revision total hip arthroplasty in patients with Vancouver type B3 fractures with Paprosky type IIIA, IIIB, and IV femoral defects are difficult to treat. One option for Paprovsky type IIIB and IV defects involves modular cementless, tapered, revision femoral components in conjunction with distal interlocking screws. The aim of this study was to analyze the rate of reoperations and complications and union of the fracture, subsidence of the stem, mortality, and the clinical outcomes in these patients. Methods. A total of 46 femoral components in patients with Vancouver B3 fractures (23 with Paprosky type IIIA, 19 with type IIIB, and four with type IV defects) in 46 patients were revised with a transfemoral approach using a modular, tapered, cementless revision Revitan curved femoral component with distal cone-in-cone fixation and prospectively followed for a mean of 48.8 months (SD 23.9; 24 to 112). The mean age of the patients was 80.4 years (66 to 100). Additional distal interlocking was also used in 23 fractures in which distal cone-in-cone fixation in the isthmus was < 3 cm. Results. One patient (2.2%) died during the first postoperative year. After six months, 43 patients (93.5%) had osseous, and three had fibrous consolidation of the fracture and the bony flap, 42 (91.3%) had bony ingrowth and four had stable fibrous fixation of the stem. No patient had radiolucency around the interlocking screws and no screw broke. One patient had non-progressive subsidence and two had a dislocation. The mean Harris Hip Score increased from of 57.8 points (SD 7.9) three months postoperatively to 76.1 points (SD 10.7) 24 months postoperatively. Conclusion. The 2° tapered, fluted revision femoral component with distal cone-in-cone-fixation, combined with additional distal interlocking in patients with bony deficiency at the isthmus, led to reproducibly good results in patients with a Vancouver B3 fracture and Paprosky type IIIA, IIIB, and IV defects with regard to union of the fracture, subsidence or loosening of the stem, and clinical outcomes. Cite this article: Bone Joint J 2024;106-B(4):344–351

If a surgeon is faced with altered lesser trochanter anatomy when revising the femoral component in revision total hip replacement, a peri-prosthetic fracture, or Paprosky type IIIb or type IV femoral bone loss, a modular tapered stem offers the advantages of accurately controlling femoral version and length. The splines of the taper allow rotational control, and improve the fit in femoral canals with diaphyseal bone loss. In general, two centimetres of diaphyseal contact is all that is needed to gain stability with modular tapered stems. By allowing the proximal body trial to rotate on a well-fixed distal segment during trial reduction, appropriate anteversion can be obtained in order to improve intra-operative stability, and decrease the dislocation risk. However, modular stems should not be used for all femoral revisions, as implant fracture and corrosion at modular junctions can still occur. Cite this article: Bone Joint J 2013;95-B, Supple A:95–7

Aims. The purpose of this study is to report our updated results at a minimum follow-up of 30 years using a first generation uncemented tapered femoral component in primary total hip arthroplasty (THA). Methods. The original cohort consisted of 145 consecutive THAs performed by a single surgeon in 138 patients. A total of 37 patients (40 hips) survived a minimum of 30 years, and are the focus of this review. The femoral component used in all cases was a first-generation Taperloc with a non-modular 28 mm femoral head. Clinical follow-up at a minimum of 30 years was obtained on every living patient. Radiological follow-up at 30 years was obtained on all but four. Results. Seven femoral components (18%) required revision, and none for septic loosening. Four well fixed stems were removed during acetabular revision and three were revised for late infection. One femoral component (3%) was loose by radiological criteria. The mean Harris Hip Score improved from 47 points (SD 4.62) preoperatively to 83 points (SD 9.27) at final follow-up. With revision for any reason as the endpoint, survival of the femoral component was 80% (95% confidence interval (CI) 61% to 90%) at 32 years. With revision for aseptic loosing femoral component, survival was 99% (95% CI 93% to 99%). Conclusion. With regards to aseptic loosening, the Taperloc femoral component provides excellent fixation at a mean follow-up of 32 years. Cite this article: Bone Jt Open 2023;4(2):79–86

Aims. The aim of this study was to radiologically evaluate the quality of cement mantle and alignment achieved with a polished tapered cemented femoral stem inserted through the anterior approach and compared with the posterior approach. Methods. A comparative retrospective study of 115 consecutive hybrid total hip arthroplasties or cemented hemiarthroplasties in 110 patients, performed through anterior (n = 58) or posterior approach (n = 57) using a collarless polished taper-slip femoral stem, was conducted. Cement mantle quality and thickness were assessed in both planes. Radiological outcomes were compared between groups. Results. No significant differences were identified between groups in Barrack grade on the anteroposterior (AP) (p = 0.640) or lateral views (p = 0.306), or for alignment on the AP (p = 0.603) or lateral views (p = 0.254). An adequate cement mantle (Barrack A or B) was achieved in 77.6% (anterior group, n = 45) and in 86% (posterior group, n = 49), respectively. Multivariate analysis revealed factors associated with unsatisfactory cement mantle (Barrack C or D) included higher BMI, left side, and Dorr Type C morphology. A mean cement mantle thickness of ≥ 2 mm was achieved in all Gruen zones for both approaches. The mean cement mantle was thicker in zone 7 (p < 0.001) and thinner in zone 9 for the anterior approach (p = 0.032). Incidence of cement mantle defects between groups was similar (6.9% (n = 4) vs 8.8% (n = 5), respectively; p = 0.489). Conclusion. An adequate cement mantle and good alignment can be achieved using a collarless polished tapered femoral component inserted through the anterior approach. Cite this article: Bone Joint J 2021;103-B(7 Supple B):46–52

Objectives. An ongoing prospective study to investigate failing metal-on-metal hip prostheses was commenced at our centre in 2008. We report on the results of the analysis of the first consecutive 126 failed mated total hip prostheses from a single manufacturer. Methods. Analysis was carried out using highly accurate coordinate measuring to calculate volumetric and linear rates of the articular bearing surfaces and also the surfaces of the taper junctions. The relationship between taper wear rates and a number of variables, including bearing diameter and orientation of the acetabular component, was investigated. Results. The measured rates of wear and distribution of material loss from the taper surfaces appeared to show that the primary factor leading to taper failure is the increased lever arm acting on this junction in contemporary large-diameter metal-on-metal hip replacements. Conclusions. Our analysis suggests that varus stems, laterally engaging taper systems and larger head diameters all contribute to taper failure

Aims. The aim of this prospective cohort study was to evaluate the early migration of the TriFit cementless proximally coated tapered femoral stem using radiostereometric analysis (RSA). Methods. A total of 21 patients (eight men and 13 women) undergoing primary total hip arthroplasty (THA) for osteoarthritis of the hip were recruited in this study and followed up for two years. Two patients were lost to follow-up. All patients received a TriFit stem and Trinity Cup with a vitamin E-infused highly cross-linked ultra-high molecular weight polyethylene liner. Radiographs for RSA were taken postoperatively and then at three, 12, and 24 months. Oxford Hip Score (OHS), EuroQol five-dimension questionnaire (EQ-5D), and adverse events were reported. Results. At two years, the mean subsidence of the head and tip for the TriFit stem was 0.38 mm (SD 0.32) and 0.52 mm (SD 0.36), respectively. The total migration of the head and tip was 0.55 mm (SD 0.32) and 0.71 mm (SD 0.38), respectively. There were no statistically significant differences between the three to 12 months' migration (p = 0.105) and 12 to 24 months' migration (p = 0.694). The OHS and EQ-5D showed significant improvements at two years. Conclusion. The results of this study suggest that the TriFit femoral stem achieves initial stability and is likely to be stable in the mid and long term. A long-term outcome study is required to assess late mechanisms of failure and the effects of bone mineral density (BMD) related changes. Cite this article: Bone Joint J 2021;103-B(4):644–649

Objectives. This study aimed to characterise and qualitatively grade the severity of the corrosion particles released into the hip joint following taper corrosion. Methods. The 26 cases examined were CoC/ABG Modular (n = 13) and ASR/SROM (n = 13). Blood serum metal ion levels were collected before and after revision surgery. The haematoxylin and eosin tissue sections were graded on the presence of fibrin exudates, necrosis, inflammatory cells and corrosion products. The corrosion products were identified based on visible observation and graded on abundance. Two independent observers blinded to the clinical patient findings scored all cases. Elemental analysis was performed on corrosion products within tissue sections. X-Ray diffraction was used to identify crystalline structures present in taper debris. Results. The CoC/ABG Modular patients had a mean age of 64.6 years (49.4 to 76.5) and ASR/SROM patients had a mean age of 58.2 years (33.3 to 85.6). The mean time in situ for CoC/ABG was 4.9 years (2 to 6.4) and ASR/SROM was 6.1 years (2.5 to 8.1). The blood serum metal ion concentrations reduced following revision surgery with the exception of Cr levels within CoC/ABG. The grading of tissue sections showed that the macrophage response and metal debris were significantly higher for the ASR/SROM patients (p < 0.001). The brown/red particles were significantly higher for ASR/SROM (p < 0.001). The taper debris contained traces of titanium oxide, chromium oxide and aluminium nitride. Conclusion. This study characterised and qualitatively graded the severity of the corrosion particles released into the hip joint from tapers that had corrosion damage. Cite this article: S. Munir, R. A. Oliver, B. Zicat, W. L. Walter, W. K. Walter, W. R. Walsh. The histological and elemental characterisation of corrosion particles from taper junctions. Bone Joint Res 2016;5:370–378. DOI: 10.1302/2046-3758.59.2000507

Objectives. Favourable results for collarless polished tapered stems have been reported, and cement creep due to taper slip may be a contributing factor. However, the ideal cement thickness around polished stems remains unknown. We investigated the influence of cement thickness on stem subsidence and cement creep. Methods. We cemented six collarless polished tapered (CPT) stems (two stems each of small, medium and large sizes) into composite femurs that had been reamed with a large CPT rasp to achieve various thicknesses of the cement mantle. Two or three tantalum balls were implanted in the proximal cement in each femur. A cyclic loading test was then performed for each stem. The migration of the balls was measured three-dimensionally, using a micro-computed tomography (CT) scanner, before and after loading. A digital displacement gauge was positioned at the stem shoulder, and stem subsidence was measured continuously by the gauge. Final stem subsidence was measured at the balls at the end of each stem. Results. A strong positive correlation was observed between mean cement thickness and stem subsidence in the CT slices on the balls. In the small stems, the balls moved downward to almost the same extent as the stem. There was a significant negative correlation between cement thickness and the horizontal:downward ratio of ball movement. Conclusion. Collarless polished tapered stems with thicker cement mantles resulted in greater subsidence of both stem and cement. This suggests that excessive thickness of the cement mantle may interfere with effective radial cement creep. Cite this article: E. Takahashi, A. Kaneuji, R. Tsuda, Y. Numata, T. Ichiseki, K. Fukui, N. Kawahara. The influence of cement thickness on stem subsidence and cement creep in a collarless polished tapered stem: When are thick cement mantles detrimental? Bone Joint Res 2017;6:–357. DOI: 10.1302/2046-3758.65.BJR-2017-0028.R1

Aims. We wished to investigate the influence of metal debris exposure on the subsequent immune response and resulting soft-tissue injury following metal-on-metal (MoM) hip arthroplasty. Some reports have suggested that debris generated from the head-neck taper junction is more destructive than equivalent doses from metal bearing surfaces. . Patients and Methods. We investigated the influence of the source and volume of metal debris on chromium (Cr) and cobalt (Co) concentrations in corresponding blood and hip synovial fluid samples and the observed agglomerated particle sizes in excised tissues using multiple regression analysis of prospectively collected data. A total of 199 explanted MoM hips (177 patients; 132 hips female) were analysed to determine rates of volumetric wear at the bearing surfaces and taper junctions. . Results. The statistical modelling suggested that a greater source contribution of metal debris from the taper junction was associated with smaller aggregated particle sizes in the local tissues and a relative reduction of Cr ion concentrations in the corresponding synovial fluid and blood samples. Metal debris generated from taper junctions appears to be of a different morphology, composition and therefore, potentially, immunogenicity to that generated from bearing surfaces. Conclusion. The differences in debris arising from the taper and the articulating surfaces may provide some understanding of the increased incidence of soft-tissue reactions reported in patients implanted with MoM total hip arthroplasties compared with patients with hip resurfacings. Cite this article: Bone Joint J 2016;98-B:925–33

Aims. The aims of this study were to evaluate the incidence of reoperation (all cause and specifically for periprosthetic femoral fracture (PFF)) and mortality, and associated risk factors, following a hemiarthroplasty incorporating a cemented collarless polished taper slip stem (PTS) for management of an intracapsular hip fracture. Methods. This retrospective study included hip fracture patients aged 50 years and older treated with Exeter (PTS) bipolar hemiarthroplasty between 2019 and 2022. Patient demographics, place of domicile, fracture type, delirium status, American Society of Anesthesiologists (ASA) grade, length of stay, and mortality were collected. Reoperation and mortality were recorded up to a median follow-up of 29.5 months (interquartile range 12 to 51.4). Cox regression was performed to evaluate independent risk factors associated with reoperation and mortality. Results. The cohort consisted of 1,619 patients with a mean age of 82.2 years (50 to 104), of whom 1,100 (67.9%) were female. In total, 29 patients (1.8%) underwent a reoperation; 12 patients (0.7%) sustained a PFF during the observation period (United Classification System (UCS)-A n = 2; UCS-B n = 5; UCS-C n = 5), of whom ten underwent surgical management. Perioperative delirium was independently associated with the occurrence of PFF (hazard ratio (HR) 5.92; p = 0.013) and surgery for UCS-B PFF (HR 21.7; p = 0.022). Neither all-cause reoperation nor PFF-related surgery was independently associated with mortality (HR 0.66; p = 0.217 and HR 0.38; p = 0.170, respectively). Perioperative delirium, male sex, older age, higher ASA grade, and pre-fracture residential status were independently associated with increased mortality risk following hemiarthroplasty (p < 0.001). Conclusion. The cumulative incidence of PFF at four years was 1.1% in elderly patients following cemented PTS hemiarthroplasty for a hip fracture. Perioperative delirium was independently associated with a PFF. However, reoperation for PPF was not independently associated with patient mortality after adjusting for patient-specific factors. Cite this article: Bone Jt Open 2024;5(4):269–276

Revision total hip arthroplasty (THA) is challenging when there is severe loss of bone in the proximal femur. The purpose of this study was to evaluate the clinical and radiographic outcomes of revision THA in patients with severe proximal femoral bone loss treated with a fluted, tapered, modular femoral component. Between January 1998 and December 2004, 92 revision THAs were performed in 92 patients using a single fluted, tapered, modular femoral stem design. Pre-operative diagnoses included aseptic loosening, infection and peri-prosthetic fracture. Bone loss was categorised pre-operatively as Paprosky types III-IV, or Vancouver B3 in patients with a peri-prosthetic fracture. The mean clinical follow-up was 6.4 years (2 to 12). A total of 47 patients had peri-operative complications, 27 of whom required further surgery. However, most of these further operations involved retention of a well-fixed femoral stem, and 88/92 femoral components (97%) remained in situ. Of the four components requiring revision, three were revised for infection and were well fixed at the time of revision; only one (1%) was revised for aseptic loosening. The most common complications were post-operative instability (17 hips, 19%) and intra-operative femoral fracture during insertion of the stem (11 hips, 12%). Diaphyseal stress shielding was noted in 20 hips (22%). There were no fractures of the femoral component. At the final follow-up 78% of patients had minimal or no pain. . Revision THA in patients with extensive proximal femoral bone loss using the Link MP fluted, tapered, modular stem led to a high rate of osseointegration of the stem at mid-term follow-up. Cite this article: Bone Joint J 2015; 97-B:312–17