The Bone & Joint Journal
Vol. 103-B, Issue 6 Supple A | Pages 94 - 101
1 Jun 2021
Roy ME Whiteside LA Ly KK Gauvain MJ

Aims. The aims of this study were to evaluate wear on the surface of cobalt-chromium (CoCr) femoral components used in total knee arthroplasty (TKA) and compare the wear of these components with that of ceramic femoral components. Methods. Optical profilometry was used to evaluate surface roughness and to examine the features created by the wear process in a knee wear simulator. We developed a method of measuring surface changes on five CoCr femoral components and quantifying the loss of material from the articular surface during the wear process. We also examined the articular surface of three ceramic femoral components from a previous test for evidence of surface damage, and compared it with that of CoCr components. Results. We found that the surface roughness of CoCr components rapidly increased during the first 1,000 wear cycles, then reached a steady state, but material loss from the surface continued at a rate of 1,778,000 μm. 3. per million cycles as carbides were removed from its matrix. These carbides formed third-body wear particles, leading to the formation of new scratches even as older scratches were worn away. In contrast, no scratching, loss of material, or other surface damage, when evaluated with one nanometer resolution, was found on the surface of the ceramic components after a 15 M wear cycle test. Conclusion. This study showed wear and loss of CoCr material from scratching and microabrasive wear in TKA. The material loss from the surface continued in a linear relationship with increasing cycles. We also found the absence of scratching and roughening of ceramic femoral components in simulated wear, suggesting an advantage in wear rate and avoiding metal sensitivity. This may have implications in the management of persistent pain after TKA. Cite this article: Bone Joint J 2021;103-B(6 Supple A):94–101


The Bone & Joint Journal
Vol. 103-B, Issue 1 | Pages 98 - 104
1 Jan 2021
van Ooij B Sierevelt IN van der Vis HM Hoornenborg D Haverkamp D

Aims

For many designs of total knee arthroplasty (TKA) it remains unclear whether cemented or uncemented fixation provides optimal long-term survival. The main limitation in most studies is a retrospective or non-comparative study design. The same is true for comparative trials looking only at the survival rate as extensive sample sizes are needed to detect true differences in fixation and durability. Studies using radiostereometric analysis (RSA) techniques have shown to be highly predictive in detecting late occurring aseptic loosening at an early stage. To investigate the difference in predicted long-term survival between cemented, uncemented, and hybrid fixation of TKA, we performed a randomized controlled trial using RSA.

Methods

A total of 105 patients were randomized into three groups (cemented, uncemented, and hybrid fixation of the ACS Mobile Bearing (ACS MB) knee system, implantcast). RSA examinations were performed on the first day after surgery and at scheduled follow-up visits at three months, six months, one year, and two years postoperatively. Patient-reported outcome measures (PROMs) were obtained preoperatively and after two years follow-up. Patients and follow-up investigators were blinded for the result of randomization.


The Bone & Joint Journal
Vol. 102-B, Issue 6 Supple A | Pages 138 - 144
1 Jun 2020
Heckmann ND Nahhas CR Yang J Della Valle CJ Yi PH Culvern CN Gerlinger TL Nam D

Aims

In patients with a “dry” aspiration during the investigation of prosthetic joint infection (PJI), saline lavage is commonly used to obtain a sample for analysis. The aim of this study was to investigate prospectively the impact of saline lavage on synovial fluid analysis in revision arthroplasty.

Methods

Patients undergoing revision hip (THA) or knee arthroplasty (TKA) for any septic or aseptic indication were enrolled. Intraoperatively, prior to arthrotomy, the maximum amount of fluid possible was aspirated to simulate a dry tap (pre-lavage) followed by the injection with 20 ml of normal saline and re-aspiration (post-lavage). Pre- and post-lavage synovial white blood cell (WBC) count, percent polymorphonuclear cells (%PMN), and cultures were compared.


The Bone & Joint Journal
Vol. 101-B, Issue 2 | Pages 227 - 232
1 Feb 2019
Walker T Rutkowski L Innmann M Panzram B Herre J Gotterbarm T Aldinger PR Merle C

Aims

The treatment of patients with allergies to metal in total joint arthroplasty is an ongoing debate. Possibilities include the use of hypoallergenic prostheses, as well as the use of standard cobalt-chromium (CoCr) alloy. This non-designer study was performed to evaluate the clinical outcome and survival rates of unicondylar knee arthroplasty (UKA) using a standard CoCr alloy in patients reporting signs of a hypersensitivity to metal.

Patients and Methods

A consecutive series of patients suitable for UKA were screened for symptoms of metal hypersensitivity by use of a questionnaire. A total of 82 patients out of 1737 patients suitable for medial UKA reporting cutaneous metal hypersensitivity to cobalt, chromium, or nickel were included into this study and prospectively evaluated to determine the functional outcome, possible signs of hypersensitivity, and short-term survivorship at a minimum follow-up of 1.5 years.


The Bone & Joint Journal
Vol. 96-B, Issue 2 | Pages 217 - 223
1 Feb 2014
Namba RS Inacio MCS Cafri G

The outcome of total knee replacement (TKR) using components designed to increase the range of flexion is not fully understood. The short- to mid-term risk of aseptic revision in high flexion TKR was evaluated. The endpoint of the study was aseptic revision and the following variables were investigated: implant design (high flexion vs non-high flexion), the thickness of the tibial insert (≤ 14 mm vs > 14 mm), cruciate ligament (posterior stabilised (PS) vs cruciate retaining), mobility (fixed vs rotating), and the manufacturer (Zimmer, Smith & Nephew and DePuy). Covariates included patient, implant, surgeon and hospital factors. Marginal Cox proportional hazard models were used.

In a cohort of 64 000 TKRs, high flexion components were used in 8035 (12.5%). The high flexion knees with tibial liners of thickness > 14 mm had a density of revision of 1.45/100 years of observation, compared with 0.37/100 in non-high flexion TKR with liners ≤ 14 mm thick. Relative to a standard fixed PS TKR, the NexGen (Zimmer, Warsaw, Indiana) Gender Specific Female high flexion fixed PS TKR had an increased risk of revision (hazard ratio (HR) 2.27 (95% confidence interval (CI) 1.48 to 3.50)), an effect that was magnified when a thicker tibial insert was used (HR 8.10 (95% CI 4.41 to 14.89)).

Surgeons should be cautious when choosing high flexion TKRs, particularly when thicker tibial liners might be required.

Cite this article: Bone Joint J 2014;96-B:217–23.


The Bone & Joint Journal
Vol. 95-B, Issue 3 | Pages 301 - 304
1 Mar 2013
Brennan SA Devitt BM O’Neill CJ Nicholson P

Focal femoral inlay resurfacing has been developed for the treatment of full-thickness chondral defects of the knee. This technique involves implanting a defect-sized metallic or ceramic cap that is anchored to the subchondral bone through a screw or pin. The use of these experimental caps has been advocated in middle-aged patients who have failed non-operative methods or biological repair techniques and are deemed unsuitable for conventional arthroplasty because of their age. This paper outlines the implant design, surgical technique and biomechanical principles underlying their use. Outcomes following implantation in both animal and human studies are also reviewed.

Cite this article: Bone Joint J 2013;95-B:301–4.


Bone & Joint Research
Vol. 1, Issue 11 | Pages 281 - 288
1 Nov 2012
Conlisk N Gray H Pankaj P Howie CR

Objectives

Orthopaedic surgeons use stems in revision knee surgery to obtain stability when metaphyseal bone is missing. No consensus exists regarding stem size or method of fixation. This in vitro study investigated the influence of stem length and method of fixation on the pattern and level of relative motion at the bone–implant interface at a range of functional flexion angles.

Methods

A custom test rig using differential variable reluctance transducers (DVRTs) was developed to record all translational and rotational motions at the bone–implant interface. Composite femurs were used. These were secured to permit variation in flexion angle from 0° to 90°. Cyclic loads were applied through a tibial component based on three peaks corresponding to 0°, 10° and 20° flexion from a normal walking cycle. Three different femoral components were investigated in this study for cementless and cemented interface conditions.


The Journal of Bone & Joint Surgery British Volume
Vol. 94-B, Issue 9 | Pages 1221 - 1227
1 Sep 2012
Kim Y Park J Kim J

Despite many claims of good wear properties following total knee replacement (TKR) with an oxidised zirconium (OxZr) femoral component, there are conflicting clinical results. We hypothesised that there would be no difference in either the mid-term clinical and radiological outcomes or the characteristics of the polyethylene wear particles (weight, size and shape) in patients using an OxZr or cobalt-chrome (CoCr) femoral component. In all 331 patients underwent bilateral TKR, receiving an OxZr femoral component in one knee and a CoCr femoral component in the other. The mean follow-up was 7.5 years (6 to 8). Following aspiration, polyethylene wear particles were analysed using thermogravimetric methods and scanning electron microscopy. At the most recent follow-up, the mean Knee Society score, Western Ontario and McMaster Universities Osteoarthritis Index score, range of movement and satisfaction score were not significantly different in the two groups. The mean weight, size, aspect ratio and roundness of the aspirated wear particles were similar for each femoral component. Survivorship of the femoral, tibial and patellar components was 100% in both groups.

In the absence of evidence of an advantage in the medium term we cannot justify the additional expense of an OxZr femoral component.


The Journal of Bone & Joint Surgery British Volume
Vol. 93-B, Issue 2 | Pages 205 - 209
1 Feb 2011
Willis-Owen CA Keene GC Oakeshott RD

Metallosis is a rare cause of failure after total knee replacement and has only previously been reported when there has been abnormal metal-on-metal contact. We describe 14 patients (15 knees) whose total knee replacement required revision for a new type of early failure caused by extensive metallosis. A modification of a cementless rotating platform implant, which had previously had excellent long-term survival, had been used in each case. The change was in the form of a new porous-beaded surface on the femoral component to induce cementless fixation, which had been used successfully in the fixation of acetabular and tibial components. This modification appeared to have resulted in metallosis due to abrasive two-body wear. The component has subsequently been recalled and is no longer in use. The presentation, investigation, and findings at revision are described and a possible aetiology and its implications are discussed.