Objectives

To determine the pattern of mutations of the WISP3 gene in clinically identified progressive pseudorheumatoid dysplasia (PPD) in an Indian population.

Although much has been published on the causes of slipped upper femoral epiphysis and the results of treatment, little attention has been given to the mechanism of the slip. This study presents the results of the analysis of 13 adolescent femora, and the attempts to reproduce the radiological appearances of a typical slip. The mean age of the skeletons was 13 years (11 to 15). It was found that the internal bony architecture in the zone of the growth plate was such that a slip of the epiphysis on the metaphysis (in the normal meaning of the word slip) could not take place, largely relating to the presence of a tubercle of bone projecting down from the epiphysis. The only way that the appearance of a typical slipped upper femoral epiphysis could be reproduced was by rotating the epiphysis posteromedially on the metaphysis. The presence and size of this peg-like tubercle was shown radiologically by CT scanning in one pair of intact adolescent femurs.

We examined the mechanical properties of Vicryl (polyglactin 910) mesh in vitro and assessed its use in vivo as a novel biomaterial to attach tendon to a hydroxyapatite-coated metal implant, the interface of which was augmented with autogenous bone and marrow graft. This was compared with tendon re-attachment using a compressive clamp device in an identical animal model. Two- and four-ply sleeves of Vicryl mesh tested to failure under tension reached 5.13% and 28.35% of the normal ovine patellar tendon, respectively. Four-ply sleeves supported gait in an ovine model with 67.05% weight-bearing through the operated limb at 12 weeks, without evidence of mechanical failure.

Mesh fibres were visible at six weeks but had been completely resorbed by 12 weeks, with no evidence of chronic inflammation. The tendon-implant neoenthesis was predominantly an indirect type, with tendon attached to the bone-hydroxyapatite surface by perforating collagen fibres.

Our aim was to investigate the relationship between urinary excretion of deoxypyridinoline (DPD) as a marker of bone resorption, and Perthes’ disease. There were 39 children with Perthes’ disease in the florid stage who collected first-morning urine samples at regular intervals of at least three months. The level of urinary DPD was analysed by chemiluminescence immunoassay and was correlated with the radiological stage of the disease as classified by Waldenström, and the severity of epiphyseal involvement according to the classification systems of Catterall and Herring. The urinary DPD levels of a group of 44 healthy children were used as a control.

The median urinary DPD/creatinine (CREA) ratio was significantly reduced (p < 0.0001) in the condensation stage and increased to slightly elevated values at the final stage (p = 0.05) when compared with that of the control group. Herring-C patients showed significantly lower median DPD/CREA ratios than Herring-B patients (p = 0.03). The significantly decreased median DPD/CREA ratio in early Perthes’ disease indicated a reduced bone turnover and supports the theory of a systemic aetiology. Urinary levels of DPD may therefore be used to monitor the course of Perthes’ disease.

The Capital Hip implant was a Charnley-based system which included a flanged and a roundback stem, both of which were available in stainless steel and titanium. The system was withdrawn from the market because of its inferior performance. However, all four of the designs did not produce poor rates of survival. Using a simulated-based, finite-element analysis, we have analysed the Capital Hip system. Our aim was to investigate whether our simulation was able to detect differences which could account for the varying survival between the Capital Hip designs, thereby further validating the simulation. We created finite-element models of reconstructions with the flanged and roundback Capital Hips. A loading history was applied representing normal walking and stair-climbing, while we monitored the formation of fatigue cracks in the cement. Corresponding to the clinical findings, our simulation was able to detect the negative effects of the titanium material and the flanged design in the Capital Hip system. Although improvements could be made by including the effect of the roughness of the surface of the stem, our study increased the value of the model as a predictive tool for determining failure of an implant

Recently, femoroacetabular impingement has been recognised as a cause of early osteoarthritis. There are two mechanisms of impingement: 1) cam impingement caused by a non-spherical head and 2) pincer impingement caused by excessive acetabular cover. We hypothesised that both mechanisms result in different patterns of articular damage. Of 302 analysed hips only 26 had an isolated cam and 16 an isolated pincer impingement. Cam impingement caused damage to the anterosuperior acetabular cartilage with separation between the labrum and cartilage. During flexion, the cartilage was sheared off the bone by the non-spherical femoral head while the labrum remained untouched. In pincer impingement, the cartilage damage was located circumferentially and included only a narrow strip. During movement the labrum is crushed between the acetabular rim and the femoral neck causing degeneration and ossification.

Both cam and pincer impingement lead to osteoarthritis of the hip. Labral damage indicates ongoing impingement and rarely occurs alone.

We have examined 26 retrieved, failed titanium-alloy femoral stems. The clinical details, radiological appearances and the histology of the surrounding soft tissues in each patient were also investigated.

The stems were predominantly of the flanged design and had a characteristic pattern of wear. A review of the radiographs showed a series of changes, progressive with time. The first was lateral debonding with subsidence of the stem. This was followed by calcar resorption and fragmentation or fracture of the cement. Finally, osteolysis was seen, starting with a radiolucency at the cement-bone interface and progressing to endosteal cavitation.

Three histological appearances were noted: granulomatous, necrobiotic and necrotic. We suggest that an unknown factor, possibly related to the design of the stem, caused it to move early. After this, micromovement at the cement-stem interface led to the generation of particulate debris and fracture of the cement. A soft-tissue reaction to the debris resulted in osteolysis and failure of fixation of the prostheses.