We studied the effect of the surface finish of the stem on the transfer of load in the proximal femur in a sheep model of cemented hip arthroplasty. Strain-gauge analysis and corresponding finite-element (FE) analysis were performed to assess the effect of friction and creep at the cement-stem interface. No difference was seen between the matt and polished stems. FE analysis showed that the effects of cement creep and friction at the stem-cement interface on femoral strain were small compared with the effect of inserting a cemented stem

It has been suggested that the endurance of cemented femoral reconstructions in total hip arthroplasty is affected by the creep of acrylic cement, but it is not known to what extent cement creeps under loading conditions in vivo, or how this affects load transfer. We have simulated the long-term creep properties of acrylic cement in finite-element models of femoral stem constructs and analysed their effects. We investigated whether subsidence rates measured in vivo could be explained by creep of acrylic cement, and if polished, unbonded, stems accommodated creep better than bonded stems. Our findings showed that polished prostheses subsided only about 50 μm as a result of cement creep. The long-term prosthetic subsidence rates caused by creep of acrylic cement are therefore very small and do not explain the excessive migration rates which have sometimes been reported. Cement creep did, however, relax cement stresses and create a more favourable stress distribution at the interfaces. These trends were found around both the bonded and unbonded stems. Our results did not confirm that polished, unbonded, stems accommodated creep better than bonded stems in terms of cement and interface stress patterns

We have tested the axial and torsional stability of femoral components after revision arthroplasty in a cadaver model, using impacted morsellised cancellous graft and cement. Each one of six matched pairs of fresh frozen human femora had either a primary or a revision prosthesis cemented in place. For the ‘revision’ experiments, all cancellous bone was removed from the proximal femur which was then over-reamed to create a smooth-walled cortical shell. An MTS servohydraulic test frame was used to apply axial and torsional loads to each specimen through the prosthetic femoral heads with the femur submerged in isotonic saline solution at 37°C. The mean subsidence was 0.27 ± 0.17 mm for the primary and 0.52 ± 0.30 mm for the revision groups. The difference was statistically significant (p < 0.025), but the mean subsidence was < 1 mm in both groups. The mean maximum torque before failure was 42.9 ± 26.9 N-m for the primary and 34.8± 20.7 N-m for the revision groups. This difference was not statistically significant (p > 0.015). Based on our results we suggest that revision of the femoral component using morsellised cancellous graft followed by cementing with a collarless prosthesis with a polished tapered stem restores the integrity of the proximal femur and provides immediate stability of the implant

We have investigated the role of the penetration of saline on the shear strength of the cement-stem interface for stems inserted at room temperature and those preheated to 37°C using a variety of commercial bone cements. Immersion in saline for two weeks at 37°C reduced interfacial strength by 56% to 88% after insertion at room temperature and by 28% to 49% after preheating of the stem. The reduction in porosity as a result of preheating ranged from 71% to 100%. Increased porosity correlated with a reduction in shear strength after immersion in saline (r = 0.839, p < 0.01) indicating that interfacial porosity may act as a fluid conduit.

We investigated the effect of pre-heating a femoral component on the porosity and strength of bone cement, with or without vacuum mixing used for total hip replacement.

Cement mantles were moulded in a manner simulating clinical practice for cemented hip replacement. During polymerisation, the temperature was monitored. Specimens of cement extracted from the mantles underwent bending or fatigue tests, and were examined for porosity.

Pre-heating the stem alone significantly increased the mean temperature values measured within the mantle (+14.2°C) (p < 0.001) and reduced the mean curing time (−1.5 min) (p < 0.001). The addition of vacuum mixing modulated the mean rise in the temperature of polymerisation to 11°C and reduced the mean duration of the process by one minute and 50 seconds (p = 0.01 and p < 0.001, respectively). In all cases, the maximum temperature values measured in the mould simulating the femur were < 50°C. The mixing technique and pre-heating the stem slightly increased the static mechanical strength of bone cement. However, the fatigue life of the cement was improved by both vacuum mixing and pre-heating the stem, but was most marked (+ 280°C) when these methods were combined.

Pre-heating the stem appears to be an effective way of improving the quality of the cement mantle, which might enhance the long-term performance of bone cement, especially when combined with vacuum mixing.