Large femoral heads have been used with increasing frequency over the last decade. The prime reason is likely the effect of large heads on stability. The larger head neck ratio, combined with the increased jump distance of larger heads result in a greater arc of impingement free motion, and greater resistance to dislocation in a provocative position. Multiple studies have demonstrated clear clinical efficacy in diminishing dislocation rates with the use of large femoral heads. With crosslinked polyethylene, wear has been shown to be equivalent between larger and smaller heads. However, the stability advantages of increasing diameter beyond 38 mm have not been clearly demonstrated. More importantly, recent data implicates large heads in the increasing prevalence of groin pain and psoas impingement. There are clear benefits with larger femoral head diameters, but the advantages of diameters beyond 38 mm have not yet been demonstrated clinically.

Implantation of a large-diameter femoral head prosthesis with a metal-on-metal bearing surface reduces the risk of dislocation, increases the range of movement, minimises the risk of impingement and, in theory, results in little wear.

Between February 2004 and March 2007 we implanted 100 consecutive total hip replacements with a metal-on-metal bearing and a large femoral head into 92 patients. There were 51 men and 41 women with a mean age of 50 years (18 to 70) at the time of surgery.

Outcome was assessed using the Western Ontario McMaster University osteoarthritis index and the Harris hip score as well as the Devane activity score. These all improved significantly (p < 0.0001). At the last follow-up there were no cases of dislocation, no impingement, a good range of movement and no osteolysis, but seven revisions, two for infection and five for aseptic loosening. The probability of groin pain increased if the other acetabular component inclination exceeded 50° (p = 0.0007). At 4.8 years of follow-up, the projected survival of the Durom acetabular component, with revision for any reason, was 92.4% (sd 2.8) (95% confidence interval 89.6 to 95.2).

The design of the component made it difficult both to orientate and seat, which when combined with a poor porous coating, produced unpredictable fixation and a low survival at five years.

Aims. This study reports the mid-term results of total hip arthroplasty (THA) performed using a monoblock acetabular component with a large-diameter head (LDH) ceramic-on-ceramic (CoC) bearing. Patients and Methods. Of the 276 hips (246 patients) included in this study, 264 (96%) were reviewed at a mean of 67 months (48 to 79) postoperatively. Procedures were performed with a mini posterior approach. Clinical and radiological outcomes were recorded at regular intervals. A noise assessment questionnaire was completed at last follow-up. Results. There were four re-operations (1%) including one early revision for insufficient primary fixation (0.4%). No hip dislocation was reported. The mean University of California, Los Angeles (UCLA) activity score, 12-Item Short-Form Health Survey (SF-12) Mental Component Summary (MCS) score, SF-12 Physical Component Summary (PCS) score, Western Ontario and McMaster Universities Osteoarthritis Index (WOMAC) score, and Forgotten Joint Score (FJS) were 6.6 (2 to 10), 52.8 (25.5 to 65.7), 53.0 (27.2 to 66.5), 7.7 (0 to 63), and 88.5 (23 to 100), respectively. No signs of loosening or osteolysis were observed on radiological review. The incidence of squeaking was 23% (n = 51/225). Squeaking was significantly associated with larger head diameter (p < 0.001), younger age (p < 0.001), higher SF-12 PCS (p < 0.001), and UCLA scores (p < 0.001). Squeaking did not affect patient satisfaction, with 100% of the squeaking hips satisfied with the surgery. Conclusion. LDH CoC THAs have demonstrated excellent functional outcomes at medium-term follow-up, with very low revision rate and no dislocations. The high incidence of squeaking did not affect patient satisfaction or function. LDH CoC with a monoblock acetabular component has the potential to provide long term implant survivorship with unrestricted activity, while avoiding implant impingement, liner fracture at insertion, and hip instability. Cite this article: Bone Joint J 2018;100-B:1434–41

Aims. The purpose of this study is to examine six types of bearing surfaces implanted at a single institution over three decades to determine whether the reasons for revision vary among the groups and how long it takes to identify differences in survival. Methods. We considered six cohorts that included a total of 1,707 primary hips done between 1982 and 2010. These included 223 conventional polyethylene sterilized with γ irradiation in air (CPE-GA), 114 conventional polyethylene sterilized with gas plasma (CPE-GP), 116 crosslinked polyethylene (XLPE), 1,083 metal-on-metal (MOM), 90 ceramic-on-ceramic (COC), and 81 surface arthroplasties (SAs). With the exception of the COC, all other groups used cobalt-chromium (CoCr) femoral heads. The mean follow-up was 10 (0.008 to 35) years. Descriptive statistics with revisions per 100 component years (re/100 yr) and survival analysis with revision for any reason as the endpoint were used to compare bearing surfaces. Results. XLPE liners demonstrated a lower cumulative incidence of revision at 15 years compared to the CPE-GA and CPE-GP groups owing to the absence of wear-related revisions (4% for XLPE vs 18%, p = 0.02, and 15%, p = 0.003, respectively). Revisions for adverse local tissue reactions occurred exclusively among the MOM (0.8 re/100 year) and SA groups (0.1 re/100 year). The revision rate for instability was lower among hips with 36 mm and larger head sizes compared to smaller head sizes (0.2% vs 2%, p < 0.001). Conclusion. The introduction of XLPE has eliminated wear-related revisions through 15-year follow-up compared to CPE-GP and CPE-GA. Dislocation incidence has been reduced with the introduction of larger diameter heads but remains a persistent concern. The potential for adverse local tissue reactions with MOM requires continued follow-up. Cite this article: Bone Joint J 2020;102-B(7 Supple B):105–111

Dislocation remains among the most common complications of, and reasons for, revision of both primary and revision total hip replacements (THR). Hence, there is great interest in maximising stability to prevent this complication. Head size has been recognised to have a strong influence on the risk of dislocation post-operatively. As femoral head size increases, stability is augmented, secondary to an increase in impingement-free range of movement. Larger head sizes also greatly increase the ‘jump distance’ required for the head to dislocate in an appropriately positioned cup. Level-one studies support the use of larger diameter heads as they decrease the risk of dislocation following primary and revision THR. Highly cross-linked polyethylene has allowed us to increase femoral head size, without a marked increase in wear. However, the thin polyethylene liners necessary to accommodate larger heads may increase the risk of liner fracture and larger heads have also been implicated in causing soft-tissue impingement resulting in groin pain. Larger diameter heads also impart larger forces on the femoral trunnion, which may contribute to corrosion, metal release, and adverse local tissue reactions. Alternative large bearings including large ceramic heads and dual mobility bearings may mitigate some of these risks, and several of these devices have been used with clinical success. Cite this article: Bone Joint J 2014;96-B(11 Suppl A):23–6

Aims

Several short- and mid-term studies have shown minimal liner wear of highly cross-linked polyethylene (HXLPE) in total hip arthroplasty (THA), but the safety of using thinner HXLPE liners to maximize femoral head size remains uncertain. The objective of this study was to analyze clinical survival and radiological wear rates of patients with HXLPE liners, a 36 mm femoral head, and a small acetabular component with a minimum of ten years’ follow-up.

Aims

This study aims to assess the relationship between history of pseudotumour formation secondary to metal-on-metal (MoM) implants and periprosthetic joint infection (PJI) rate, as well as establish ESR and CRP thresholds that are suggestive of infection in these patients. We hypothesized that patients with a pseudotumour were at increased risk of infection.

Aims

The present study investigated the five-year interval changes in pseudotumours and measured serum metal ions at long-term follow-up of a previous report of 28 mm diameter metal-on-metal (MoM) total hip arthroplasty (THA).

Aims

There are limited published data detailing the volumetric material loss from tapers of conventional metal-on-polyethylene (MoP) total hip arthroplasties (THAs). Our aim was to address this by comparing the taper wear rates measured in an explanted cohort of the widely used Exeter THA with those measured in a group of metal-on-metal (MoM) THAs.

When fracture of an extensively porous-coated femoral component occurs, its removal at revision total hip arthroplasty (THA) may require a femoral osteotomy and the use of a trephine. The remaining cortical bone after using the trephine may develop thermally induced necrosis. A retrospective review identified 11 fractured, well-fixed, uncemented, extensively porous-coated femoral components requiring removal using a trephine with a minimum of two years of follow-up.

The mean time to failure was 4.6 years (1.7 to 9.1, standard deviation (sd) 2.3). These were revised using a larger extensively porous coated component, fluted tapered modular component, a proximally coated modular component, or a proximal femoral replacement. The mean clinical follow-up after revision THA was 4.9 years (2 to 22, sd 3.1). The mean diameter of the femoral component increased from 12.7 mm (sd 1.9) to 16.2 mm (sd 3.4; p >  0.001). Two revision components had radiographic evidence of subsidence that remained radiographically stable at final follow-up. The most common post-operative complication was instability affecting six patients (54.5%) on at least one occasion.

A total of four patients (36.4%) required further revision: three for instability and one for fracture of the revision component. There was no statistically significant difference in the mean Harris hip score before implant fracture (82.4; sd 18.3) and after trephine removal and revision THA (81.2; sd 14.8, p = 0.918).

These findings suggest that removal of a fractured, well-fixed, uncemented, extensively porous-coated femoral component using a trephine does not compromise subsequent fixation at revision THA and the patient’s pre-operative level of function can be restored. However, the loss of proximal bone stock before revision may be associated with a high rate of dislocation post-operatively.

Cite this article: Bone Joint J 2015;97-B:1192–6.

We investigated the incidence of soft-tissue lesions after small head metal-on-metal total hip replacement (MoM THR). Between December 1993 and May 1999, 149 patients (195 hips) underwent primary cementless MoM THR.

During the follow-up period, three patients (five THRs) died and eight patients (14 THRs) were lost to follow-up. We requested that all patients undergo CT evaluation. After exclusion of five patients (six THRs) who had undergone a revision procedure, and 22 (28 THRs) who were unwilling to take part in this study, 111 patients (142 THRs) were evaluated. There were 63 men (88 THRs) and 48 women (54 THRs) with a mean age of 45.7 years (37 to 56) at the time of surgery. The mean follow-up was 15.4 years (13 to 19). A soft-tissue lesion was defined as an abnormal peri-prosthetic collection of fluid, solid lesion or asymmetrical soft-tissue mass.

At final follow-up, soft-tissue lesions were found in relation to 28 THRs (19.7%), including 25 solid and three cystic lesions. They were found in 20 men and eight women; 26 lesions were asymptomatic and two were symptomatic. The mean maximal diameter of the soft-tissue lesion was 42.3 mm (17 to 135). The relatively high rate of soft-tissue lesions observed with small head MoM THR remains a concern.

Cite this article: Bone Joint J 2014;96-B:1594–9.

Surgical interventions consisting of internal fixation (IF) or total hip replacement (THR) are required to restore patient mobility after hip fractures. Conventionally, this decision was based solely upon the degree of fracture displacement. However, in the last ten years, there has been a move to incorporate patient characteristics into the decision making process. Research demonstrating that joint replacement renders superior functional results when compared with IF, in the treatment of displaced femoral neck fractures, has swayed the pendulum in favour of THR. However, a high risk of dislocation has always been the concern. Fortunately, there are newer technologies and alternative surgical approaches that can help reduce the risk of dislocation. The authors propose an algorithm for the treatment of femoral neck fractures: if minimally displaced, in the absence of hip joint arthritis, IF should be performed; if arthritis is present, or the fracture is displaced, then THR is preferred.

Cite this article: Bone Joint J 2014;96-B(11 Suppl A):43–7.

We conducted a retrospective study to assess the prevalence of adverse reactions to metal debris (ARMD) in patients operated on at our institution with metal-on-metal (MoM) total hip replacements with 36 mm heads using a Pinnacle acetabular shell. A total of 326 patients (150 males, 175 hips; 176 females, 203 hips) with a mean age of 62.7 years (28 to 85) and mean follow-up of 7.5 years (0.1 to 10.8) participating in our in-depth modern MoM follow-up programme were included in the study, which involved recording whole blood cobalt and chromium ion measurements, Oxford hip scores (OHS) and plain radiographs of the hip and targeted cross-sectional imaging. Elevated blood metal ion levels (> 5 parts per billion) were seen in 32 (16.1%) of the 199 patients who underwent unilateral replacement. At 23 months after the start of our modern MoM follow-up programme, 29 new cases of ARMD had been revealed. Hence, the nine-year survival of this cohort declined from 96% (95% CI 95 to 98) with the old surveillance routine to 86% (95% CI 82 to 90) following the new protocol. Although ARMD may not be as common in 36 mm MoM THRs as in those with larger heads, these results support the Medicines and Healthcare Products Regulatory Agency guidelines on regular reviews and further investigations, and emphasise the need for specific a follow-up programme for patients with MoM THRs.

Cite this article: Bone Joint J 2014; 96-B:1610–17.

Dislocation is one of the most common causes of patient and surgeon dissatisfaction following hip replacement and to treat it, the causes must first be understood. Patient factors include age greater than 70 years, medical comorbidities, female gender, ligamentous laxity, revision surgery, issues with the abductors, and patient education. Surgeon factors include the annual quantity of procedures and experience, the surgical approach, adequate restoration of femoral offset and leg length, component position, and soft-tissue or bony impingement. Implant factors include the design of the head and neck region, and so-called skirts on longer neck lengths. There should be offset choices available in order to restore soft-tissue tension. Lipped liners aid in gaining stability, yet if improperly placed may result in impingement and dislocation. Late dislocation may result from polyethylene wear, soft-tissue destruction, trochanteric or abductor disruption and weakness, or infection. Understanding the causes of hip dislocation facilitates prevention in a majority of instances. Proper pre-operative planning includes the identification of patients with a high offset in whom inadequate restoration of offset will reduce soft-tissue tension and abductor efficiency. Component position must be accurate to achieve stability without impingement. Finally, patient education cannot be over-emphasised, as most dislocations occur early, and are preventable with proper instructions.

Cite this article: Bone Joint J 2013;95-B, Supple A:67–9.

This study reports the mid-term results of a large-bearing hybrid metal-on-metal total hip replacement in 199 hips (185 patients) with a mean follow-up of 62 months (32 to 83).

Two patients died of unrelated causes and 13 were lost to follow-up. In all, 17 hips (8.5%) have undergone revision, and a further 14 are awaiting surgery. All revisions were symptomatic. Of the revision cases, 14 hips showed evidence of adverse reactions to metal debris. The patients revised or awaiting revision had significantly higher whole blood cobalt ion levels (p = 0.001), but no significant difference in acetabular component size or position compared with the unrevised patients. Wear analysis (n = 5) showed increased wear at the trunnion-head interface, normal levels of wear at the articulating surfaces and evidence of corrosion on the surface of the stem.

The cumulative survival rate, with revision for any reason, was 92.4% (95% confidence interval 87.4 to 95.4) at five years. Including those awaiting surgery, the revision rate would be 15.1% with a cumulative survival at five years of 89.6% (95% confidence interval 83.9 to 93.4).

This hybrid metal-on-metal total hip replacement series has shown an unacceptably high rate of failure, with evidence of high wear at the trunnion-head interface and passive corrosion of the stem surface. This raises concerns about the use of large heads on conventional 12/14 tapers.

We reviewed the results of 84 total hip replacements performed with a short metaphyseal-fitting anatomical cementless femoral component in 84 unselected consecutive patients with a mean age of 78.9 years (70 to 88). The mean follow-up was 4.6 years (4 to 5). The mean pre-operative Harris hip score was 26 points (0 to 56), which improved to 89 (61 to 100) at the final follow-up. No patient had thigh pain. The mean pre-operative Western Ontario and McMaster Universities osteoarthritis index score was 61 points (48 to 75), which improved to 21 (6 to 46). The mean University of California, Los Angeles activity score was 5.5 points (3 to 7) at the final follow-up. Osseointegration was seen in all femoral and acetabular components. All hips had grade 1 stress shielding of the proximal femur. No acetabular or femoral osteolysis was identified.

These results demonstrate that a short metaphyseal-fitting femoral component achieves optimal fixation without diaphyseal anchorage in elderly patients.

We retrospectively analysed concentrations of chromium and cobalt ions in samples of synovial fluid and whole blood taken from a group of 92 patients with failed current-generation metal-on-metal hip replacements. We applied acid oxidative digestion to our trace metal analysis protocol, which found significantly higher levels of metal ion concentrations in blood and synovial fluid than a non-digestive method. Patients were subcategorised by mode of failure as either ‘unexplained pain’ or ‘defined causes’. Using this classification, chromium and cobalt ion levels were present over a wider range in synovial fluid and not as strongly correlated with blood ion levels as previously reported. There was no significant difference between metal ion concentrations and manufacturer of the implant, nor femoral head size below or above 50 mm. There was a moderately positive correlation between metal ion levels and acetabular component inclination angle as measured on three-dimensional CT imaging.

Our results suggest that acid digestion of samples of synovial fluid samples is necessary to determine metal ion concentrations accurately so that meaningful comparisons can be made between studies.

We reviewed 1039 revision total hip replacements where an angle-bore acetabular component was used. After a mean follow-up of nine years (0 to 20.6), the incidence of revision for dislocation was 2.1% (22 revisions), a success rate of 97.9%. In 974 revisions, where the indication was other than dislocation, the success rate was 98.5%. Of the 65 revisions for dislocation, 58 (89.2%) were successful after the first revision and a further five after the second revision, an overall success of 96.9%. Two patients elected to have their implants removed. Dislocation after revision of failed total hip replacement is a complex issue. There is often no single cause and no simple solution. The angle-bore acetabular component, in combination with a 22.225-mm diameter femoral head, offers a high level of success.