Elastic stable intramedullary nailing (ESIN) is generally acknowledged to be the treatment of choice for displaced diaphyseal femoral fractures in children over the age of three years, although complication rates of up to 50% are described. Pre-bending the nails is recommended, but there are no published data to support this. Using synthetic bones and a standardised simulated fracture, we performed biomechanical testing to determine the influence on the stability of the fracture of pre-bending the nails before implantation. Standard ESIN was performed on 24 synthetic femoral models with a spiral fracture. In eight cases the nails were inserted without any pre-bending, in a further eight cases they were pre-bent to 30° and in the last group of eight cases they were pre-bent to 60°. Mechanical testing revealed that pre-bending to 60° produced a significant increase in the stiffness or stability of the fracture. Pre-bending to 60° showed a significant positive influence on the stiffness compared with unbent nails. Pre-bending to 30° improved stiffness only slightly.

These findings validate the recommendations for pre-bending, but the degree of pre-bend should exceed 30°. Adopting higher degrees of pre-bending should improve stability in spiral fractures and reduce the complications of varus deformity and shortening.

Aims

To investigate metallosis in patients with magnetically controlled growing rods (MCGRs) and characterize the metal particle profile of the tissues surrounding the rod.

Aims

We conducted a prospective study of a delta ceramic total hip arthroplasty (THA) to determine the rate of ceramic fracture, to characterise post-operative noise, and to evaluate the mid-term results and survivorship.

Aims

In order to prevent dislocation of the hip after total hip arthroplasty (THA), patients have to adhere to precautions in the early post-operative period. The hypothesis of this study was that a protocol with minimal precautions after primary THA using the posterolateral approach would not increase the short-term (less than three months) risk of dislocation.

Adolescent idiopathic scoliosis (AIS) is a complex 3D deformity of the spine. Its prevalence is between 2% and 3% in the general population, with almost 10% of patients requiring some form of treatment and up to 0.1% undergoing surgery. The cosmetic aspect of the deformity is the biggest concern to the patient and is often accompanied by psychosocial distress. In addition, severe curves can cause cardiopulmonary distress. With proven benefits from surgery, the aims of treatment are to improve the cosmetic and functional outcomes. Obtaining correction in the coronal plane is not the only important endpoint anymore. With better understanding of spinal biomechanics and the long-term effects of multiplanar imbalance, we now know that sagittal balance is equally, if not more, important. Better correction of deformities has also been facilitated by an improvement in the design of implants and a better understanding of metallurgy. Understanding the unique character of each deformity is important. In addition, using the most appropriate implant and applying all the principles of correction in a bespoke manner is important to achieve optimum correction.

In this article, we review the current concepts in AIS surgery.

Cite this article: Bone Joint J 2018;100-B:415–24.

Aims

In a multicentre, randomised study of adolescents undergoing posterior spinal fusion for idiopathic scoliosis, we investigated the effect of adding gelatine matrix with human thrombin to the standard surgical methods of controlling blood loss.

Methods

In this study of patients who underwent internal fixation without fusion for a burst thoracolumbar or lumbar fracture, we compared the serial changes in the injured disc height (DH), and the fractured vertebral body height (VBH) and kyphotic angle between patients in whom the implants were removed and those in whom they were not. Radiological parameters such as injured DH, fractured VBH and kyphotic angle were measured. Functional outcomes were evaluated using the Greenough low back outcome scale and a VAS scale for pain.

The aim of this study was to assess the effect of frictional torque and bending moment on fretting corrosion at the taper interface of a modular femoral component and to investigate whether different combinations of material also had an effect. The combinations we examined were 1) cobalt–chromium (CoCr) heads on CoCr stems 2) CoCr heads on titanium alloy (Ti) stems and 3) ceramic heads on CoCr stems.

In test 1 increasing torque was imposed by offsetting the stem in the anteroposterior plane in increments of 0 mm, 4 mm, 6 mm and 8 mm when the torque generated was equivalent to 0 Nm, 9 Nm, 14 Nm and 18 Nm.

In test 2 we investigated the effect of increasing the bending moment by offsetting the application of axial load from the midline in the mediolateral plane. Increments of offset equivalent to head + 0 mm, head + 7 mm and head + 14 mm were used.

Significantly higher currents and amplitudes were seen with increasing torque for all combinations of material. However, Ti stems showed the highest corrosion currents. Increased bending moments associated with using larger offset heads produced more corrosion: Ti stems generally performed worse than CoCr stems. Using ceramic heads did not prevent corrosion, but reduced it significantly in all loading configurations.

Cite this article: Bone Joint J 2015;97-B:463–72.

We investigated the effect of pre-heating a femoral component on the porosity and strength of bone cement, with or without vacuum mixing used for total hip replacement.

Cement mantles were moulded in a manner simulating clinical practice for cemented hip replacement. During polymerisation, the temperature was monitored. Specimens of cement extracted from the mantles underwent bending or fatigue tests, and were examined for porosity.

Pre-heating the stem alone significantly increased the mean temperature values measured within the mantle (+14.2°C) (p < 0.001) and reduced the mean curing time (−1.5 min) (p < 0.001). The addition of vacuum mixing modulated the mean rise in the temperature of polymerisation to 11°C and reduced the mean duration of the process by one minute and 50 seconds (p = 0.01 and p < 0.001, respectively). In all cases, the maximum temperature values measured in the mould simulating the femur were < 50°C. The mixing technique and pre-heating the stem slightly increased the static mechanical strength of bone cement. However, the fatigue life of the cement was improved by both vacuum mixing and pre-heating the stem, but was most marked (+ 280°C) when these methods were combined.

Pre-heating the stem appears to be an effective way of improving the quality of the cement mantle, which might enhance the long-term performance of bone cement, especially when combined with vacuum mixing.

The ability to predict load-bearing capacity during the consolidation phase in distraction osteogenesis by non-invasive means would represent a significant advance in the management of patients undergoing such treatment. Measurements of stiffness have been suggested as a promising tool for this purpose. Although the multidimensional characteristics of bone loading in compression, bending and torsion are apparent, most previous experiments have analysed only the relationship between maximum load-bearing capacity and a single type of stiffness. We have studied how compressive, bending and torsional stiffness are related to the torsional load-bearing capacity of healing callus using a common set of samples of bone regenerate from 26 sheep treated by tibial distraction osteogenesis.

Our findings showed that measurements of torsional, bending and compressive stiffness were all suitable as predictors of the load-bearing capacity of healing callus. Measurements of torsional stiffness performed slightly better than those of compressive and bending stiffness.

This study validates the short-form WOMAC function scale for assessment of conservative treatment of osteoarthritis of the knee. Data were collected before treatment and six and nine months later, from 100 patients with osteoarthritis of the knee to determine the validity, internal consistency, test-retest reliability, floor and ceiling effects, and responsiveness of the short-form WOMAC function scale. The scale showed high correlation with the traditional WOMAC and other measures. The internal consistency was good (Cronbach α: 0.88 to 0.95) and an excellent test-retest reliability was found (Lin’s concordance correlation coefficient (ρ_c): 0.85 to 0.94). The responsiveness was adequate and comparable to that of the traditional WOMAC (standardised response mean 0.56 to 0.44 and effect size 0.64 to 0.57) and appeared not to be significantly affected by floor or ceiling effects (0% and 7%, respectively).

The short-form WOMAC function scale is a valid, reliable and responsive alternative to the traditional WOMAC in the evaluation of patients with osteoarthritis of the knee managed conservatively. It is simple to use in daily practice and is therefore less of a burden for patients in clinical trials.

We used immediate post-operative in vivo three-dimensional computed tomography to compare graft bending angles and femoral tunnel lengths in 155 patients who had undergone single-bundle reconstruction of the anterior cruciate ligament using the transtibial (n = 37), anteromedial portal (n = 72) and outside-in (n = 46) techniques.

The bending angles in the sagittal and axial planes were significantly greater but the coronal-bending angle was significantly less in the transtibial group than in the anteromedial portal and outside-in groups (p < 0.001 each). The mean length of the femoral tunnel in all three planes was significantly greater in the transtibial group than the anteromedial portal and outside-in groups (p < 0.001 each), but all mean tunnel lengths in the three groups exceeded 30 mm. The only significant difference was the coronal graft- bending angle in the anteromedial portal and outside-in groups (23.5° vs 29.8°, p = 0.012).

Compared with the transtibial technique, the anteromedial portal and outside-in techniques may reduce the graft-bending stress at the opening of the femoral tunnel. Despite the femoral tunnel length being shorter in the anteromedial portal and outside-in techniques than in the transtibial technique, a femoral tunnel length of more than 30 mm in the anteromedial portal and outside-in techniques may be sufficient for the graft to heal.

Cite this article: Bone Joint J 2014;96-B:743–51.

A total of 12 epileptic patients (14 shoulders) with recurrent seizures and anterior dislocations of the shoulder underwent a Latarjet procedure and were reviewed at a mean of 8.3 years (1 to 20) post-operatively. Mean forward flexion decreased from 165° (100° to 180°) to 160° (90° to 180°) (p = 0.5) and mean external rotation from 54° (10° to 90°) to 43° (5° to 75°) (p = 0.058). The mean Rowe score was 76 (35 to 100) at the final follow-up. Radiologically, all shoulders showed a glenoid-rim defect and Hill-Sachs lesions pre-operatively. Osteo-arthritic changes of the glenohumeral joint were observed in five shoulders (36%) pre-operatively and in eight shoulders (57%) post-operatively. Re-dislocation during a seizure occurred in six shoulders (43%). Five of these patients underwent revision surgery using a bone buttress from the iliac crest and two of these patients re-dislocated due to a new seizure.

Due to the unacceptably high rate of re-dislocation after surgery in these patients, the most important means of reducing the incidence of further dislocation is the medical management of the seizures. The Latarjet procedure should be reserved for the well-controlled patient with epilepsy who has recurrent anterior dislocation of the shoulder during activities of daily living.

Although the Western Ontario and McMaster Universities (WOMAC) osteoarthritis index was originally developed for the assessment of non-operative treatment, it is commonly used to evaluate patients undergoing either total hip (THR) or total knee replacement (TKR). We assessed the importance of the 17 WOMAC function items from the perspective of 1198 patients who underwent either THR (n = 704) or TKR (n = 494) in order to develop joint-specific short forms. After these patients were administered the WOMAC pre-operatively and at three, six, 12 and 24 months’ follow-up, they were asked to nominate an item of the function scale that was most important to them. The items chosen were significantly different between patients undergoing THR and those undergoing TKR (p < 0.001), and there was a shift in the priorities after surgery in both groups. Setting a threshold for prioritised items of ≥ 5% across all follow-up, eight items were selected for THR and seven for TKR, of which six items were common to both. The items comprising specific WOMAC-THR and TKR function short forms were found to be equally responsive compared with the original WOMAC function form.

Cite this article: Bone Joint J 2013;95-B:239–43.

We evaluated the biomechanical properties of two different methods of fixation for unstable fractures of the proximal humerus. Biomechanical testing of the two groups, locking plate alone (LP), and locking plate with a fibular strut graft (LPSG), was performed using seven pairs of human cadaveric humeri. Cyclical loads between 10 N and 80 N at 5 Hz were applied for 1 000 000 cycles. Immediately after cycling, an increasing axial load was applied at a rate of displacement of 5 mm/min. The displacement of the construct, maximum failure load, stiffness and mode of failure were compared.

The displacement was significantly less in the LPSG group than in the LP group (p = 0.031). All maximum failure loads and measures of stiffness in the LPSG group were significantly higher than those in the LP group (p = 0.024 and p = 0.035, respectively). In the LP group, varus collapse and plate bending were seen. In the LPSG group, the humeral head cut out and the fibular strut grafts fractured. No broken plates or screws were seen in either group.

We conclude that strut graft augmentation significantly increases both the maximum failure load and the initial stiffness of this construct compared with a locking plate alone.

Coloured bone cements have been introduced to make the removal of cement debris easier at the time of primary and revision joint replacement. We evaluated the physical, mechanical and pharmacological effects of adding methylene blue to bone cement with or without antibiotics (gentamicin, vancomycin or both). The addition of methylene blue to plain cement significantly decreased its mean setting time (570 seconds (sd 4) vs 775 seconds (sd 11), p = 0.01), mean compression strength (95.4 MPa (sd 3) vs 100.1 MPa (sd 6), p = 0.03), and mean bending strength (65.2 MPa (sd 5) vs 76.6 MPa (sd 4), p < 0.001) as well as its mean elastic modulus (2744 MPa (sd 97) vs 3281 MPa (sd 110), p < 0.001). The supplementation of the coloured cement with vancomycin and gentamicin decreased its mean bending resistance (55.7 MPa (sd 4) vs 65.2 MPa (sd 5), p < 0.001).The methylene blue significantly decreased the mean release of gentamicin alone (228.2 µg (sd 24) vs 385.5 µg (sd 26), p < 0.001) or in combination with vancomycin (498.5 µg (sd 70) vs 613 µg (sd 25), p = 0.018) from the bone cement. This study demonstrates several theoretical disadvantages of the antibiotic-loaded bone cement coloured with methylene blue.

This systematic review of the literature summarises the clinical experience with ceramic-on-ceramic hip bearings over the past 40 years and discusses the concerns that exist in relation to the bearing combination. Loosening, fracture, liner chipping on insertion, liner canting and dissociation, edge-loading and squeaking have all been reported, and the relationship between these issues and implant design and surgical technique is investigated. New design concepts are introduced and analysed with respect to previous clinical experience.

Polymethylmethacrylate remains one of the most enduring materials in orthopaedic surgery. It has a central role in the success of total joint replacement and is also used in newer techniques such as percutaneous vertebroplasty and kyphoplasty.

This article describes the current uses and limitations of polymethylmethacrylate in orthopaedic surgery. It focuses on its mechanical and chemical properties and links these to its clinical performance. The behaviour of antibiotic-loaded bone cement are discussed, together with areas of research that are now shedding light upon the behaviour of this unique biomaterial.