Britton M Schiavi J Vaughan T
Full Access

Type-2 Diabetic (T2D) patients experience up to a 3-fold increase in bone fracture risk[1]. Paradoxically, T2D-patients have a normal or increased bone mineral density when compared to non-diabetic patients. This implies that T2D has a deleterious effect on bone quality, whereby the intrinsic material properties of the bone matrix are altered. Creating clinical challenges as current diagnostic techniques are unable to accurately predict the fracture probability in T2D-patients. To date, the relationship between cyclic fatigue loading, mechanical properties and microdamage accumulation of T2D-bone tissue has not yet been examined and thus our objective is to investigate this relationship.

Ethically approved femoral heads were obtained from patients, with (n=8) and without (n=8) T2D. To obtain the mechanical properties of the sample, one core underwent a monotonic compression test to 10% strain, the other core underwent a cyclic compression test at a normalized stress ratio between 0.0035mm/mm and 0.016mm/mm to a maximum strain of 3%. Microdamage was evaluated by staining the tissue with barium sulfate precipitate [2] and conducting microcomputed tomography scanning with a voxel size of 10μm.

The monotonically tested T2D-group showed no statistical difference in mechanical properties to the non-T2D-group, even when normalised against BV/TV. There was also no difference in BV/TV. For the cyclic test, the T2D-group had a significantly higher initial modulus (p<0.01) and final modulus (p<0.05). There was no difference in microdamage accumulation.

Previous population-level studies have found that T2D-patients have been shown to have an increased fracture risk when compared to non-T2D-patients. This research indicates that T2D does not impair the mechanical properties of trabecular bone from the femoral heads of T2D-patients, suggesting that other mechanisms may be responsible for the increased fracture risk seen in T2D-patients.


Orthopaedic Proceedings
Vol. 105-B, Issue SUPP_7 | Pages 135 - 135
4 Apr 2023
Monahan G Schiavi-Tritz J Vaughan T
Full Access

This study aims to assess the fracture mechanics of type-2 diabetic (T2D) femoral bone using innovative site-specific tests, whilst also examining the cortical and trabecular bone microarchitecture from various regions using micro-computed tomography (CT) of the femur as the disease progresses.

Male [Zucker Diabetic Fatty (ZDF: fa/fa) (T2D) and Zucker Lean (ZL: fa/+) (Control)] rats were euthanized at 12-weeks of age, thereafter, right and left femora were dissected (Right femora: n = 6, per age, per condition; Left femora: n=8-9, per age, per condition). Right femurs were notched in the posterior of the midshaft. Micro-CT was used to scan the proximal femur, notched and unnotched femoral midshaft (cortical) of the right femur and the distal metaphysis (trabecular) of the left femur to investigate microarchitecture and composition. Right femurs were fracture toughness tested to measure the stress intensity factor (Kic) followed by a sideways fall test using a custom-made rig to investigate femoral neck mechanical properties.

There was no difference in trabecular and cortical tissue material density (TMD) between T2D and control rats. Cortical thickness was unchanged, but trabeculae were thinner (p<0.01) in T2D rats versus controls. However, T2D rats had a greater number of trabeculae (p<0.05) although trabecular spacing was not different to controls. T2D rats had a higher connectivity distribution (p<0.05) and degree of anisotropy (p<0.05) in comparison to controls. There was no difference in the mechanical properties between strains.

At 12-weeks of age, rats are experiencing early-stage T2Ds and the disease impact is currently not very clear. Structural and material properties are unchanged between strains, but the trabecular morphology shows that T2D rats have more trabecular struts present in order to account for the thinner trabeculae.


Orthopaedic Proceedings
Vol. 103-B, Issue SUPP_13 | Pages 93 - 93
1 Nov 2021
Schiavi J Remo A McNamara L Vaughan T
Full Access

Introduction and Objective

Bone remodelling is a continuous process whereby osteocytes regulate the activity of osteoblasts and osteoclasts to repair loading-induced microdamage. While many in vitro studies have established the role of paracrine factors (e.g., RANKL/OPG) and cellular pathways involved in bone homeostasis, these techniques are generally limited to two-dimensional cell culture, which neglects the role of the native extracellular matrix in maintaining the phenotype of osteocyte. Recently, ex vivo models have been used to understand cell physiology and mechanobiology in the presence of the native matrix. Such approaches could be applicable to study the mechanisms of bone repair, whilst also enabling exploration of biomechanical cues. However, to date an ex vivo model of bone remodelling in cortical bone has not been developed. In this study, the objective was to develop an ex vivo model where cortical bone was subjected to cyclic strains to study the remodelling of bone.

Materials and Methods

Ex vivo model of bone remodelling induced by cyclic loading: At the day of culling, beam-shape bovine bone samples were cut and preserved in PBS + 5% Pen/Strep + 2 mM L-Glut overnight at 37°C. Cyclic strains were applied with a three-point bend system to induce damage with a regime at 16.66 mm/min for 5,000 cycles in sterile PBS in Evolve® bags (maximum strain 6%). A control group was cultured under static conditions.

Metabolic activity: Alamar Blue assays were performed after 1 and 7 days of ex vivo culture for each group (Static, Loaded) and normalized to weight.

Bone remodelling: ALP activity was assessed in the media at day 1 and 7. After 24 hours cell culture conditioned media (CM) was collected from each group and stored at −80°C. RAW264.7 cells were cultured with CM for 6 days, after which the samples were stained for TRAP, to determine osteoclastogenesis, and imaged.

Histomorphometry: Samples were cultured with calcein for 3 days to label bone formation between day 4 and 7. Fluorescent images were captured at day 7. μCT scanning was performed at 3 μm resolution after labelling samples with BaSO4 precipitate to quantify bone damage.


Orthopaedic Proceedings
Vol. 103-B, Issue SUPP_13 | Pages 68 - 68
1 Nov 2021
Monahan G Schiavi J Vaughan T
Full Access

Introduction and Objective

Individuals with type 2 diabetes (T2D) have a 3-fold increased risk of bone fracture compared to non-diabetics, with the majority of fractures occurring in the hip, vertebrae and wrists. However, unlike osteoporosis, in T2D, increased bone fragility is generally not accompanied by a reduction in bone mineral density (BMD). This implies that T2D is explained by poorer bone quality, whereby the intrinsic properties of the bone tissue itself are impaired, rather than bone mass. Yet, the mechanics remain unclear. The objective of this study is to (1) assess the fracture mechanics of bone at the structural and tissue level; and (2) investigate for changes in the composition of bone tissue along with measuring total fluorescent advanced glycation end products (fAGEs) from the skin, as T2D progresses with age in Zucker diabetic fatty (ZDF (fa/fa)) and lean Zucker (ZL (fa/+)) rats.

Materials and Methods

Right ulnae and skin sections were harvested from ZDF (fa/fa) (T2D) and ZL (fa/+) (Control) rats at 12 and 46 weeks (wks) of age (n = 8, per strain and age) and frozen. Right ulnae were thawed for 12 hrs before micro-CT (μCT) scanning to assess the microstructure and measure BMD. After scanning, ulnae were loaded until failure via three-point bending. Fourier transform-infrared microspectroscopy (FTIR) was used to measure various bone mineral- and collagen-related parameters such as, mineral-to-matrix ratio and nonenzymatic cross-link ratio. Finally, fAGEs were measured from skin sections using fluorescence spectrometry and an absorbance assay, reported in units of ng quinine/ mg collagen.


Orthopaedic Proceedings
Vol. 100-B, Issue SUPP_15 | Pages 122 - 122
1 Nov 2018
Parle E Tio S Behre A Carey J Murphy C O'Brien T Curtin W Kearns S McCabe J Coleman C Vaughan T McNamara L
Full Access

Recent studies have shown that bone mineral distribution is more heterogeneous in bone tissue from an animal model of osteoporosis and osteoporotic human vertebral trabeculae. These tissue alterations may play a role in bone fragility seen in osteoporosis, albeit that they are not detectable by current diagnostic techniques (dual-energy X-ray absorptiometry, DXA). Type II Diabetes Mellitus (T2DM) also increases a patient's fracture risk beyond what can be explained or diagnosed by DXA, and is associated with impaired bone cell function, compromised collagen structure and reduced mechanical properties. However, it is not currently known whether osteoporosis or T2DM leads to an increased mineral heterogeneity in the femoral head of humans, a common osteoporotic fracture site. In this study, we examine bone microarchitecture, mineralisation and mechanical properties of trabecular bone from osteoarthritic, diabetic and osteoporotic patients. We report that while osteoporotic trabecular bone has significantly deteriorated mechanical properties and microarchitecture compared to the other groups, there is also a significant increase in mean mineral content. Moreover, the heterogeneity of the mineral content in osteoporotic bone is significantly higher than osteoarthritic (+35%) and diabetic (+13%) groups. We propose that the compromised architecture following bone loss at the onset of osteoporosis alters the mechanical environment, which initiates compensatory changes in mineral content. We show for the first time that trabecular bone mineralisation is significantly more heterogeneous (+20%) in T2DM compared to osteoarthritic controls. Interestingly, bone microarchitecture and mechanical properties are not significantly different between diabetic and osteoarthritic groups despite this increase in mineral heterogeneity.


Orthopaedic Proceedings
Vol. 100-B, Issue SUPP_14 | Pages 36 - 36
1 Nov 2018
Vaughan T
Full Access

The complex structural arrangement of bone gives rise to anisotropic, rate-dependent failure behaviour, which varies significantly depending on tissue composition and architecture. This presents significant challenges in the development of orthopaedic surgical cutting instruments, which are required to generate sufficient forces to penetrate bone tissue, while minimizing the risk of thermal and mechanical damage to the surrounding environment. Currently, instrument designers rely heavily on empirical-based strategies to understand tool-bone interactions, with significant amounts of prototyping and validation experiments required throughout the design process. The aim of this study is to develop an experimentally-validated predictive computational model of orthopaedic cutting processes in three dimensions to understand the role of various cutting parameters on cutting forces and chip formation. An experimental model of orthogonal cutting was developed, whereby an adaptable cutting tool fixture driven by a servo-hydraulic uniaxial test machine was used to carry out high-rate cutting tests on Sawbone® trabecular bone analogues. A three-dimensional computational model was also developed using Abaqus/Explicit. The constitutive model describing material behaviour considers strain-rate and pressure-dependant yield behaviour using a Drucker-Prager elastic-plastic damage model, with Strain-hardening and rate-dependent model constants determined through dynamic uniaxial high-strain rate compression tests of material cubes. An excellent correlation between experimental and computational models was found, with the computational model accurately predicting tool cutting forces and chip development ahead of the tool during the cutting process. It was identifying that lower tool rake-angles resulted in the formation of larger discontinuous chips and higher cutting forces, while higher rake angles tended to lead to more continuous chip formation and lower cutting forces.