Aims

Radiostereometric analysis (RSA) is the most accurate radiological method to measure in vivo wear of highly cross-linked polyethylene (XLPE) acetabular components. We have previously reported very low wear rates for a sequentially irradiated and annealed X3 XLPE liner (Stryker Orthopaedics, USA) when used in conjunction with a 32 mm femoral heads at ten-year follow-up. Only two studies have reported the long-term wear rate of X3 liners used in conjunction with larger heads using plain radiographs which have poor sensitivity. The aim of this study was to measure the ten-year wear of thin X3 XLPE liners against larger 36 or 40 mm articulations with RSA.

First-time revision acetabular components have a 36% re-revision rate at 10 years in Australia, with subsequent revisions known to have even worse results. Acetabular component migration >1mm at two years following revision THA is a surrogate for long term loosening. This study aimed to measure the migration of porous tantalum components used at revision surgery and investigate the effect of achieving press-fit and/or three-point fixation within acetabular bone.

Between May 2011 and March 2018, 55 patients (56 hips; 30 female, 25 male) underwent acetabular revision THR with a porous tantalum component, with a post-operative CT scan to assess implant to host bone contact achieved and Radiostereometric Analysis (RSA) examinations on day 2, 3 months, 1 and 2 years. A porous tantalum component was used because the defects treated (Paprosky IIa:IIb:IIc:IIIa:IIIb; 2:6:8:22:18; 13 with pelvic discontinuity) were either deemed too large or in a position preventing screw fixation of an implant with low coefficient of friction. Press-fit and three-point fixation of the implant was assessed intra-operatively and on postoperative imaging.

Three-point acetabular fixation was achieved in 51 hips (92%), 34 (62%) of which were press-fit. The mean implant to host bone contact achieved was 36% (range 9–71%). The majority (52/56, 93%) of components demonstrated acceptable early stability. Four components migrated >1mm proximally at two years (1.1, 3.2, 3.6 and 16.4mm). Three of these were in hips with Paprosky IIIB defects, including 2 with pelvic discontinuity. Neither press-fit nor three-point fixation was achieved for these three components and the cup to host bone contact achieved was low (30, 32 and 59%).

The majority of porous tantalum components had acceptable stability at two years following revision surgery despite treating large acetabular defects and poor bone quality. Components without press-fit or three-point fixation were associated with unacceptable amounts of early migration.

Aims

A typical pattern of blood loss associated with total hip arthroplasty (THA) is 200 ml intraoperatively and 1.3 l in the first 48 postoperative hours. Tranexamic acid (TXA) is most commonly given as a single preoperative dose only and is often withheld from patients with a history of thromboembolic disease as they are perceived to be “high-risk” with respect to postoperative venous thromboembolism (VTE). The TRanexamic ACid for 24 hours trial (TRAC-24) aimed to identify if an additional 24-hour postoperative TXA regime could further reduce blood loss beyond a once-only dose at the time of surgery, without excluding these high-risk patients.

Background

91% of blood loss in Total Hip Replacement (THR) occurs in the period after skin closure and the first 24 post-operative hours. TRAC-24 was established to identify if an additional 24-hour post-operative oral regime of Tranexamic acid (TXA) is superior to a once-only intravenous dose at surgery.

Introduction

In 2010, a widely used metal-on-metal hip implant was voluntarily recalled from the market by the manufacturer. Our lab performed detailed retrieval analysis of 548 of the explanted devices and 165 periprosthetic tissue specimens. We reported a high degree of variability in the multiple measurements that we performed on the components, including volumetric wear.

Other studies using semi-quantitative tissue grading methods to describe the histology of the periprosthetic tissues from metal-on-metal hips have looked for relationships between component wear and histological features. Grammatopoulos et al found higher ALVAL scores in 45 hip resurfacing patients with pseudotumors compared to 11 without pseudotumors and a moderately positive correlation between wear and the histological rankings for tissue necrosis and lymphocytic response.

We examined correlations between the component wear measurements from retrieval analysis and the tissue features in this large group of one metal-on-metal hip design.

Since the introduction of national guidelines in 2009 encouraging the use of total hip arthroplasty (THA) to treat intracapsular neck of femur fractures there has been no population-based studies into the surgical outcomes for this indication. This study aims to calculate the complication rates for THA when performed for a fractured neck of femur and compare them to THA performed for primary osteoarthritis in the same population.

The Scottish Arthroplasty Project was used to identify all THAs performed in Scotland for neck of femur fracture and osteoarthritis between 1st of January 2009 and 31st December 2014. Dislocation, infection and revision rates at 1 year were calculated.

The rate of dislocation, infection and revision at 1 year were all significantly increased among the fracture neck of femur cohort. In total 44046 THAs were performed, 38316 for OA and 2715 for a neck of femur fracture. 2.1% of patients (n=57) who underwent a THA for a neck of femur fracture suffered a dislocation in the 1st year postoperatively, compared to 0.9% (n=337) when the THA was performed for osteoarthritis. Relative Risk of dislocation: 2.3870 (95% C.I. 1.8077–3.1252, p value <0.0001). Relative Risk of infection: 1.4561 (95% C.I. 1.0496–2.0200, p value 0.0245) Relative Risk of revision: 1.4807 (95% C.I. 1.0308–2.1268, p value 0.0336).

This is the first time a dislocation rate for THA performed for a neck of femur fracture has been calculated for an entire population. As the number of THAs for neck of femur fracture increases this dislocation rate will have clinical implications.

Aims

The increased in vivo resistance to wear of highly crosslinked polyethylene (HXLPE) in total hip arthroplasty (THA) has led to an increased use of larger articulations which have been shown to reduce the incidence of early dislocation. To date, there are few reports of the wear of larger articulations using second generation HXLPE liners. Our prospective cohort study measured the bedding-in and early wear of large (36 mm and 40 mm diameter) articulations involving a second generation X3 HXLPE liner and compared our findings with previous clinical and in vitro studies of the same material.

Objectives

To investigate psychosocial and biomedical outcomes following total hip replacement (THR) and to identify predictors of recovery from THR.

Objectives

We aimed to determine the effect of surgical approach on the histology of the femoral head following resurfacing of the hip.

We report a case of a male patient presenting with bilateral painful but apparently well-positioned and -fixed large-diameter metal-on-metal hip replacements four years post-operatively. Multiple imaging modes revealed a thick-walled, cystic expansile mass in communication with the hip joint (a pseudotumour). Implant retrieval analysis and tissue culture eliminated high bearing wear or infection as causes for the soft-tissue reaction, but noted marked corrosion of the modular neck taper adaptor and corrosion products in the tissues. Therefore, we believe corrosion products from the taper caused by mismatch of the implant components led to pseudotumour formation requiring revision.

We examined the relationships between the serum levels of chromium and cobalt ions and the inclination angle of the acetabular component and the level of activity in 214 patients implanted with a metal-on-metal resurfacing hip replacement. Each patient had a single resurfacing and no other metal in their body. All serum measurements were performed at a minimum of one year after operation. The inclination of the acetabular component was considered to be steep if the abduction angle was greater than 55°.

There were significantly higher levels of metal ions in patients with steeply-inclined components (p = 0.002 for chromium, p = 0.003 for cobalt), but no correlation was found between the level of activity and the concentration of metal ions. A highly significant (p < 0.001) correlation with the arc of cover was found. Arcs of cover of less than 10 mm were correlated with a greater risk of high concentrations of serum metal ions. The arc of coverage was also related to the design of the component and to size as well as to the abduction angle of the acetabular component. Steeply-inclined acetabular components, with abduction angles greater than 55°, combined with a small size of component are likely to give rise to higher serum levels of cobalt and chromium ions. This is probably due to a greater risk of edge-loading.

We have reviewed 42 patients who had revision of metal-on-metal resurfacing procedures, mostly because of problems with the acetabular component. The revisions were carried out a mean of 26.2 months (1 to 76) after the initial operation and most of the patients (30) were female.

Malpositioning of the acetabular component resulted in 27 revisions, mostly because of excessive abduction (mean 69.9°; 56° to 98°) or insufficient or excessive anteversion. Seven patients had more than one reason for revision. The mean increase in the diameter of the component was 1.8 mm (0 to 4) when exchange was needed.

Malpositioning of the components was associated with metallosis and a high level of serum ions. The results of revision of the femoral component to a component with a modular head were excellent, but four patients had dislocation after revision and four required a further revision.

Resurfacing arthroplasty of the hip is being used increasingly as an alternative to total hip replacement, especially for young active patients. There is concern about necrosis of the femoral head after resurfacing which can result in fracture and loosening. Most systems use a cemented femoral component, with the potential for thermal necrosis of the cancellous bone of the reamed femoral head. We used thermal probes to record temperatures close to the cement-bone interface during resurfacing arthroplasty.

The maximum temperature recorded at the cement-bone interface in four cases was approximately 68°C which was higher than that reported to kill osteocytes. A modified surgical technique using insertion of a suction cannula into the lesser trochanter, generous pulsed lavage and early reduction of the joint significantly reduced the maximum recorded cancellous bone temperature to approximately 36°C in five cases (p = 0.014).

We recommend the modified technique since it significantly reduces temperatures at the cement-bone interface.

During hip resurfacing arthroplasty, excessive valgus positioning or surgical technique can result in notching of the femoral neck. Although mechanical weakening and subsequent fracture of the femoral neck are well described, the potential damage to the retinacular vessels leading to an ischaemic event is relatively unknown. Using laser Doppler flowmetry, we measured the blood flow in 14 osteoarthritic femoral heads during routine total hip replacement surgery, before and after notching of the femoral neck. In ten hips there was a reduction in blood flow of more than 50% from the baseline value after simulated notching of the femoral neck. Our results suggest that femoral head vascularity in the osteoarthritic state is similar to the non-arthritic state, where damage to the extraosseous vessels can predispose to avascular necrosis. Surgeons who perform resurfacing arthroplasty of the hip should pay careful attention to these vessels by avoiding excessive dissection around the femoral neck and/or notching.

We describe three prostheses with cemented titanium-alloy stems and Al₂O₃ ceramic femoral heads which had to be revised after a mean period of implantation of 78 months. In each case, the neck of the prosthesis had been so severely worn that the profile was elliptical rather than circular. There was severe metallosis of the periprosthetic tissues. Metal particles isolated from the tissues were approximately one nanometre in size and the ratios of titanium, aluminium and vanadium in the particles were the same as in the original alloy. Histologically, the high concentration of metal particles masked the presence of high-density polyethylene (HDP) debris, but again particles about one nanometre in size were isolated from the tissues. The severe necrobiosis and necrosis noted were consistent with other reports of the presence of extensive wear particles in periprosthetic tissues. Wear is presumed to have occurred as a result of mismatch between the shape or size of the taper cone and the femoral head, or to changes in the geometry of loading due to migration of the cup. To facilitate early intervention, patients with this design of prosthesis should be monitored radiologically.