Aims. To find out if there is an inverse association between estimated glomerular filtration rate (eGFR) and whole blood cobalt (Co) and chromium (Cr) levels in patients with metal-on-metal (MoM) hip arthroplasties and renal insufficiency, suggesting that renal insufficiency could cause accumulation of Co and Cr in blood. Methods. Out of 2,520 patients with 3,013
Aims. In metal-on-metal (MoM) hip arthroplasties and resurfacings, mechanically induced corrosion can lead to elevated serum metal ions, a local inflammatory response, and formation of pseudotumours, ultimately requiring revision. The size and diametral clearance of anatomical (ADM) and modular (MDM) dual-mobility polyethylene bearings match those of Birmingham hip MoM components. If the acetabular component is satisfactorily positioned, well integrated into the bone, and has no surface damage, this presents the opportunity for revision with exchange of the metal head for ADM/MDM polyethylene bearings without removal of the acetabular component. Methods. Between 2012 and 2020, across two centres, 94 patients underwent revision of Birmingham
Aims. Acetabular edge-loading was a cause of increased wear rates in
In metal-on-metal (MoM) hip replacements or resurfacings, mechanical induced corrosion can lead to a local inflammatory response, pseudo tumours and elevated serum metal ions, requiring revision surgery. The size and diametral clearance of Anatomic (ADM) and Modular (MDM) Dual Mobility bearings matches that of certain MOM components. Presenting the opportunity for revision with exchange of the metal head for ADM/MDM bearings without removal of the acetabular component if it is well-fixed and appropriately positioned. Between 2012 and 2020, across two centres, 94 patients underwent revision of a MoM hip replacement or resurfacing. The mean age was 65.5 (33–87) years. In 53 patients (56.4%), the acetabular component was retained, and dual mobility bearings were used (DM); in 41 (43.6%) the acetabulum was revised (AR). DM was only considered where the acetabular component was satisfactorily positioned and well-integrated into bone, with no surface damage. Patients underwent clinical and radiographic follow-up to at least one-year (mean 42.4 (12–96) months). One (1.1%) patient died before one-year, for reasons unrelated to the surgery. In the DM group, two (3.8%) patients underwent further surgery; one (1.9%) for dislocation and one (1.9%) for infection. In the AR group, four (12.2%) underwent further procedures; two (4.9%) for loosening of the acetabular component and two (4.9%) following dislocations. There were no other dislocations in either group. In the DM group, operative time (68.4 v 101.5 mins, p<0.001), postoperative drop in haemoglobin (16.6 v 27.8 g/L, p<0.001), and length of stay (1.8 v 2.4 days, p<0.001) were significantly lower. There was a significant reduction in serum metal ions postoperatively in both groups (p<0.001 both Cobalt and Chromium) although there was no difference between groups for this reduction (p=0.674 Cobalt; p=0.186 Chromium). In selected patients with
Objectives. We investigated the reliability of the cobalt-chromium (CoCr) synovial joint fluid ratio (JFR) in identifying the presence of a severe aseptic lymphocyte-dominated vasculitis-associated lesion (ALVAL) response and/or suboptimal taper performance (SOTP) following metal-on-metal (MoM) hip arthroplasty. We then examined the possibility that the CoCr JFR may influence the serum partitioning of Co and Cr. Methods. For part A, we included all revision surgeries carried out at our unit with the relevant data, including volumetric wear analysis, joint fluid (JF) Co and Cr concentrations, and ALVAL grade (n = 315). Receiver operating characteristic curves were constructed to assess the reliability of the CoCr JFR in identifying severe ALVAL and/or SOTP. For part B, we included only patients with unilateral prostheses who had given matched serum and whole blood samples for Co and Cr analysis (n = 155). Multiple regression was used to examine the influence of JF concentrations on the serum partitioning of Co and Cr in the blood. Results. A CoCr JFR > 1 showed a specificity of 83% (77% to 88%) and sensitivity of 63% (55% to 70%) for the detection of severe ALVAL and/or SOTP. In patients with CoCr JFRs > 1, the median blood Cr to serum Cr ratio was 0.99, compared with 0.71 in patients with CoCr JFRs < 1 (p < 0.001). Regression analysis demonstrated that the blood Cr to serum Cr value was positively associated with the JF Co concentration (p = 0.011) and inversely related to the JF Cr concentration (p < 0.001). Conclusion. Elevations in CoCr JFRs are associated with adverse biological (severe ALVAL) or tribocorrosive processes (SOTP). Comparison of serum Cr with blood Cr concentrations may be a useful additional clinical tool to help to identify these conditions. Cite this article: D. J. Langton, S. Natu, C. F. Harrington, J. G. Bowsher, A. V. F. Nargol. Is the synovial fluid cobalt-to-chromium ratio related to the serum partitioning of metal debris following
Background:. Higher than expected revision rates have been observed in large bearing metal-on-metal total hip replacements. We have introduced a metal on metal hip screening clinic at our unit and report the results. Methods:. All patients who had a metal-on-metal total hip replacement implanted at our unit were recalled to clinic. Screening consisted of clinical examination, Oxford hip score, radiographs, MARS MRI and serum cobalt/chromium ion levels. MRI scans were graded (Norwich Classification) by a single consultant radiologist who was blinded to the history, examination, and metal levels. Patients were sub-classified into 6 groups, which determined further follow up and were either entered into a regular screening programme or referred to a revision arthroplasty surgeon for a decision on whether revision was required. Results:. A total of 278 patients were identified. Four patients had moved away, 2 refused follow-up and 1 patient had died. This left 271 patients in our cohort, having 299
Aims. To determine whether there is any association between glomerular
filtration rate (GFR) and blood cobalt (Co) and chromium (Cr) levels
in patients with metal-on-metal (MoM) hip arthroplasty. Patients and Methods. We identified 179 patients with a unilateral 36 mm diameter head
as part of a stemmed Summit-Pinnacle
Introduction. Many worldwide regulatory authorities recommend regular surveillance of
Objectives. We have encountered patients who developed large joint fluid collections with massive elevations in chromium (Cr) and cobalt (Co) concentrations following metal-on-metal (MoM) hip arthroplasties. In some cases, retrieval analysis determined that these ion concentrations could not be explained simply by the wear rates of the components. We hypothesized that these effects may be associated with aseptic lymphocyte-dominated vasculitis-associated lesion (ALVAL). Patients and Methods. We examined the influence of the ALVAL grade on synovial fluid Co and Cr concentrations following adjustment for patient and device variables, including volumetric wear rates. Initially restricting the analysis to include only patients with one MoM hip resurfacing device, we performed multiple regression analyses of prospectively collected data. We then repeated the same statistical approach using results from a larger cohort with different MoM designs, including total hip arthroplasties. Results. In the resurfacing cohort (n = 76), the statistical modelling indicated that the presence of severe ALVAL and a large fluid collection were associated with greater joint fluid Co concentrations after adjustment for volumetric wear rates (p = 0.005). These findings were replicated in the mixed implant group (n = 178), where the presence of severe ALVAL and a large fluid collection were significantly associated with greater fluid Co concentrations (p < 0.001). Conclusion. The development of severe ALVAL is associated with elevations in metal ion concentrations far beyond those expected from the volumetric loss from the prosthetic surfaces. This finding may aid the understanding of the sequence of events leading to soft-tissue reactions following
Introduction. It has been speculated that impact deformation of thin 1-piece cups used for modern
Background:. Potential systemic toxicity of metal ions from
Introduction. The MHRA guidelines for metal on metal (MOM) suggest cobalt and chromium levels of more than 7ppb as potential for soft tissue reaction. However, in some patients soft tissue reaction is seen even in the presence of normal serum metal ions levels. Methods. A prospective review of all patients who had
Purpose. There is a postulated association between increased serum metal ions and pseudotumour formation in patients with
We retrospectively analysed concentrations of chromium and cobalt ions in samples of synovial fluid and whole blood taken from a group of 92 patients with failed current-generation
Introduction. We investigated predictors of poor outcomes following
Aims. Surgeons have commonly used modular femoral heads and stems from
different manufacturers, although this is not recommended by orthopaedic
companies due to the different manufacturing processes. We compared the rate of corrosion and rate of wear at the trunnion/head
taper junction in two groups of retrieved hips; those with mixed
manufacturers (MM) and those from the same manufacturer (SM). . Materials and Methods. We identified 151 retrieved hips with large-diameter cobalt-chromium
heads; 51 of two designs that had been paired with stems from different
manufacturers (MM) and 100 of seven designs paired with stems from
the same manufacturer (SM). We determined the severity of corrosion
with the Goldberg corrosion score and the volume of material loss
at the head/stem junction. We used multivariable statistical analysis
to determine if there was a significant difference between the two
groups. . Results. We found no significant difference in the corrosion scores of
the two groups. The median rate of material loss at the head/stem
junction for the MM and SM groups were 0.39 mm. 3. /year
(0.00 to 4.73) and 0.46 mm. 3. /year (0.00 to 6.71) respectively;
this difference was not significant after controlling for confounding
factors (p = 0.06). . Conclusion. The use of stems with heads of another manufacturer does not
appear to affect the amount of metal lost from the surfaces between
these two components at total hip arthroplasty. Other surgical,
implant and patient factors should be considered when determining
the mechanisms of failure of large diameter
In this paper, we will consider the current role
of metal-on-metal bearings by looking at three subtypes of MoM hip
arthroplasty separately: Hip resurfacing, large head (>
36 mm) MoM
THA and MoM THA with traditional femoral head sizes.
Outcomes following
Metal-on-metal bearings are being increasingly used in young patients. The potential adverse effects of systemic metal ion elevation are the subject of ongoing investigation. The purpose of this study was to investigate whether cobalt and chromium ions cross the placenta of pregnant women with a metal-on-metal hip resurfacing and reach the developing fetus. Whole blood levels were estimated using high-resolution inductively-coupled plasma mass spectrometry. Our findings showed that cobalt and chromium are able to cross the placenta in the study patients with metal-on-metal hip resurfacings and in control subjects without any metal implants. In the study group the mean concentrations of cobalt and chromium in the maternal blood were 1.39 μg/l (0.55 to 2.55) and 1.28 μg/l (0.52 to 2.39), respectively. The mean umbilical cord blood concentrations of cobalt and chromium were comparatively lower, at 0.839 μg/l (0.42 to 1.75) and 0.378 μg/l (0.14 to 1.03), respectively, and this difference was significant with respect to chromium (p <
0.05). In the control group, the mean concentrations of cobalt and chromium in the maternal blood were 0.341 μg/l (0.18 to 0.54) and 0.199 μg/l (0.12 to 0.33), and in the umbilical cord blood they were 0.336 μg/l (0.17 to 0.5) and 0.194 μg/l (0.11 to 0.56), respectively. The differences between the maternal and umbilical cord blood levels in the controls were marginal, and not statistically significant (p >
0.05). The mean cord blood level of cobalt in the study patients was significantly greater than that in the control group (p <
0.01). Although the mean umbilical cord blood chromium level was nearly twice as high in the study patients (0.378 μg/l) as in the controls (0.1934 μg/l), this difference was not statistically significant. (p >
0.05) The transplacental transfer rate was in excess of 95% in the controls for both metals, but only 29% for chromium and 60% for cobalt in study patients, suggesting that the placenta exerts a modulatory effect on the rate of metal ion transfer.