INTRODUCTION. The advantages of large diameter metal on metal total hip arthroplasty (MoM THA) and hip resurfacing arthroplasty are decreased wear rate, preservation of bone stock, anatomical restoration and enhanced stability. Large amounts of metal wear particles and metal ions are released which may induce adverse reactions including local soft tissue toxicity, hypersensitivity reactions, bone loss and risk of carcinogenesis. Aseptic loosening can be the result of a peri-prosthetic osteolysis generated as a result of a biological response to particulate wear debris. No reports in the literature exist as to whether circulating levels of Chromium (Cr) and Cobalt (Co) decrease upon removal of a symptomatic large diameter MoM implant or whether levels remain high due to the effect of metal ions debris left behind in the soft tissues after revision surgery. PATIENTS AND METHODS. Between June 2006 and June 2009 we undertook 44 revision surgeries of both large head MoM THAs (femoral head diameter 38mm) and metal-on-metal hip resurfacings for suspected metallosis. Mean time from original implant to revision was 4 years, 8 months (1yr 4mo–7yr 9mo). The mean follow up evaluation was 2 years and 2 months (1yr 2mo–4 years). Blood samples were taken for whole blood Cr and serum Co according to a recognised protocol and compared with reference levels indicated by the Medicines and Healthcare Regulatory Agency recommendation of less than 7ppb for Cr (130nM/L) and Co (119nM/L). RESULTS. 42 patients were found to have histological evidence of either metal allergy, metal toxicity or foreign body reaction. 2 patients had evidence of infection with no features of metal reaction. 3 patients suffered early dislocation requiring closed reduction. 1 patient had infective complications necessitating Girdlestones. 11 patients were lost to follow up, 8 patients were diagnosed pre operatively on Co and Cr levels in urine or synovial fluid aspirate alone. 23 patients had pre revision blood or serum
Introduction. Metal on metal articulations produce chromium (Cr) and cobalt (Co) debris, particularly when the articulations are worn in. High levels in the peripheral blood are indicative of excess wear and may cause adverse effects. The present RCT investigates
Introduction. Metal-on-metal (MoM) articulations in total hip replacement (THR) have become an attractive option for young, active patients. Short-term reports have demonstrated elevated systemic
Introduction. The advantages of metal on metal (MOM) hip replacement are decreased wear rate, preservation of bone stock, anatomical restoration and enhanced stability. Large amounts of metal wear particles and metal ions are released which may induce adverse reactions including local soft tissue toxicity, hypersensitivity reactions, bone loss and risk of carcinogenesis. Aseptic loosening can be the result of a peri prosthetic osteolysis generated as a result of a biological response to particulate wear debris. Our aim in this study was to determine whether a steeply inclined acetabular component would give rise to a higher concentration of metal ions. Patients and methods. Between April 2003 and June 2006, 22 patients had MOM hip replacement for osteoarthritis by a single Surgeon. There were 12 male and 10 female patients. The average age at the time of surgery was 56 years (Range: 44–69 years). We divided the 22 patients into 2 groups, one group (A) of 11 patients with the acetabular inclination angle more than 50 degrees and the other group (B) of 11 patients with the angle less than 50 degrees. The inclination of the acetabular cup was measured using a standard AP radiograph of the pelvis. The patients had
INTRODUCTION. Femoral neck narrowing (NN) following Metal-on-Metal Hip Resurfacing Arthroplasty (MoMHRA) is a well-recognised clinical phenomenon. The incidence of resurfaced hips with NN > 10% is reported to be up to 27%. Its pathogenesis is thought to be multi-factorial secondary to stress shielding, impingement, osteolysis secondary to wear/ion particles and as a result of reduced vascularity and pressure effect on cancellous bone secondary to the presence of a soft-tissue mass around the resurfaced hip. Recognised risk factors for its development include: female gender and the presence of a pseudotumour. Serum Chromium (Cr) and Cobalt (Co) are recognised surrogate markers of in-vivo wear of MoMHRA. The aims of this study were to establish whether NN is associated with increased wear. METHODS. A cohort of 214 patients with unilateral MoMHRA (139M: 75F) was included in this study. Primary osteoarthritis was the diagnosis leading to surgery for the majority of patients (208). The average age at surgery was 54.1 years old (13–73). Six different implants were used; BHR (116), Conserve plus (92), Recap (2), ASR (2), Adept (1) and Cormet (1). The average femoral component size was 49.2mm (range: 38–59). The average follow up was 4.3 years (range: 2–10). Patients were subdivided into 3 groups as per implant size. Small size component group had implants <45mm, average size group had components 45–51mm and large component size group had components >51mm. All patients had Prosthesis-Junction-Ratio (PJR) measured from postoperative (PJRpost) and at latest follow up (PJRfollow) radiographs. Measurements were made using the method described by Lilikakis1.