Aim:. The aim of this study was test the amount of corrosion occurring at the (Ti) /cobalt chrome (CoCr) interface comparing this with Ti and Ti interfaces. This was compared with retrieved metal work visualised under a scanning electron microscope (SEM). Methods:. The interface of interest is the interface between rod and the screw. We investigated corrosion seen at that interface with a CoCr rod coupled to a Ti screw versus a Ti rod coupled to a Ti screw (6 screws were used) Implants were loaded according to the ASTM F2193 – 02 Standard Specifications and Test Methods for Components Used in the Surgical Fixation of the Spinal Skeletal System. Pitting potentials were monitored using cyclic potentiodynamic polarization tests (ASTM F2129 – 08 Standard Test Method for Conducting Cyclic Potentiodynamic Polarisation Measurements) to determine corrosion susceptibility. Retrieved implants were visualised under (SEM) to confirm corrosion. Results:. Mean fretting current for titanium and cobalt chrome was 7.94 (μA) and for titanium on titanium 5.89 (μA). The results of SEM showed evidence of fretting and galvanic corrosion. Discussion:. Cobalt chrome ions in hip implants have raised concern amongst the orthopaedic community. This study showed that metal ion production occurs due to fretting and galvanic corrosion. This corrosion is increased in cobalt chrome and titanium constructs but statistically more tests are required to confirm this. Further research is required to understand this interface as cobalt chrome ions pose a potential hazard to patients with their reproductive years ahead. Conflict Of Interest Statement: No conflict of interest

Anterior debridement, grafting of the defect and posterior instrumentation as a single-stage procedure is a controversial method of managing pyogenic vertebral osteomyelitis. Between 1994 and 2005, 37 patients underwent this procedure at our hospital, of which two died and three had inadequate follow-up. The remaining 32 were reviewed for a mean of 36 months (12 to 66). Their mean age was 48 years (17 to 68). A significant pre-operative neurological deficit was present in 13 patients (41%). The mean duration of surgery was 285 minutes (240 to 360) and the mean blood loss was 900 ml (300 to 1600). Pyogenic organisms were isolated in 21 patients (66%). All patients began to mobilise on the second post-operative day. The mean hospital stay was 13.6 days (10 to 20). Appropriate antibiotics were administered for 10 to 12 weeks. Early wound infection occurred in four patients (12.5%), and late infection in two (6.3%).

At final follow-up, the infection had resolved in all patients, neurological recovery was seen in ten of 13 (76.9%) and interbody fusion had occurred in 30 (94%). The clinical outcome was excellent or good in 30 patients according to Macnab’s criteria.

This surgical protocol can be used to good effect in patients with pyogenic vertebral osteomyelitis when combined with appropriate antibiotic therapy.