Abstract
Aim:
The aim of this study was test the amount of corrosion occurring at the (Ti) /cobalt chrome (CoCr) interface comparing this with Ti and Ti interfaces. This was compared with retrieved metal work visualised under a scanning electron microscope (SEM).
Methods:
The interface of interest is the interface between rod and the screw. We investigated corrosion seen at that interface with a CoCr rod coupled to a Ti screw versus a Ti rod coupled to a Ti screw (6 screws were used) Implants were loaded according to the ASTM F2193 – 02 Standard Specifications and Test Methods for Components Used in the Surgical Fixation of the Spinal Skeletal System. Pitting potentials were monitored using cyclic potentiodynamic polarization tests (ASTM F2129 – 08 Standard Test Method for Conducting Cyclic Potentiodynamic Polarisation Measurements) to determine corrosion susceptibility. Retrieved implants were visualised under (SEM) to confirm corrosion.
Results:
Mean fretting current for titanium and cobalt chrome was 7.94 (μA) and for titanium on titanium 5.89 (μA). The results of SEM showed evidence of fretting and galvanic corrosion.
Discussion:
Cobalt chrome ions in hip implants have raised concern amongst the orthopaedic community. This study showed that metal ion production occurs due to fretting and galvanic corrosion. This corrosion is increased in cobalt chrome and titanium constructs but statistically more tests are required to confirm this. Further research is required to understand this interface as cobalt chrome ions pose a potential hazard to patients with their reproductive years ahead.
Conflict Of Interest Statement: No conflict of interest.