Majority of ultra-high molecular weight polyethylene (UHMWPE) medical devices used in total joint arthroplasty are crosslinked using gamma radiation to improve wear resistance. Alternative methods of crosslinking are urgently needed to replace gamma radiation due to rapid decline in its supply. Peroxide crosslinking is a candidate method with widespread industrial applications. Oxidative stability and biocompatibility, which are critical requirements for medical device applications, can be achieved using vitamin-E as an additive and by removing peroxide by-products through high temperature melting, respectively. We investigated compression molded UHMWPE/vitamin-E/di-cumyl peroxide blends followed by high-temperature melting in inert gas as a material candidate for tibial knee inserts. Wear resistance increased and mechanical properties remained largely unchanged. Oxidation induction time was higher than most of the other clinically available formulations. The material passed the local-end point biocompatibility tests per ISO 10993. Compounds found in exhaustive extraction were of no concern with margin-of-safety values well above the accepted level, indicating a desirable toxicological risk profile. Peroxide crosslinked, vitamin-E stabilized, and high temperature melted UHMWPE has recently been cleared for clinical use in tibial knee inserts. With all the salient characteristics needed in a material that can provide superior long-term performance in total joint patients, peroxide crosslinking can replace gamma radiation crosslinking of UHMWPE for use in all total joint replacement implant including acetabular liners

Introduction. Ultra-high molecular weight polyethylene (UHMWPE) can provide local sustained delivery of therapeutics. 1,2. For example, it can deliver analgesics to address post-arthroplasty pain. 2. Given that several analgesics, such as bupivacaine (anesthetic) and tolfenamic acid (NSAID), were shown to possess antibacterial activity against Staphylococci, we hypothesize that analgesic-loaded UHMWPE can also yield antimicrobial effects, preventing the development of periprosthetic joint infections. Methods. Bupivacaine and tolfenamic acid were incorporated into UHMWPE via phase-separated compression molding. Drug release from the prepared samples was measured using high-performance liquid chromatography. Antibacterial studies of the obtained materials were conducted against methicillin-sensitive, and methicillin-resistant S. aureus, as well as S. epidermidis. Time-kill curves were obtained to characterize antimicrobial activity against planktonic bacteria. The dynamics of bacterial adhesion were assessed to characterize antibiofilm activity. Scanning electron microscopy (SEM) was used to visualize adherent bacteria. Anticolonizing activity of the tested materials was characterized using the “daughter cell” method as outlined elsewhere. 3. Cytotoxicity profile of drug-loaded UHMWPEs was evaluated using MG-63 osteoblast cell line. Results. The bupivacaine release rate generally increased with increasing drug loading (e.g. a model knee implant loaded with bupivacaine would release ca. 15–500 mg over 24 hours). While also proportional, drug release from UHMWPE loaded with tolfenamic acid was much lower. The bacterial viability curves showed that bupivacaine-loaded UHMWPE possessed moderate antibacterial activity against planktonic MSSA, MRSA, and S. epidermidis, slowing bacteria proliferation by up to 70%. Bupivacaine-loaded UHMWPE also mitigated biofilm formation and development during the initial culture period. SEM images confirmed the observed antibiofilm effect (Fig. 1). Tolfenamic acid-loaded UHMWPE allowed proliferation of planktonic bacteria. At the same time, these materials showed pronounced dose-dependent anticolonizing activity against tested strains, providing 3-log reduction of “daughter” cells. Bupivacaine- and tolfenamic acid-loaded UHMWPEs showed little-to-no cytotoxicity against osteoblasts. Discussion & Conclusions. We demonstrated for the first time that bupivacaine-loaded UHMWPE possesses dose-dependent antibacterial properties against planktonic and adherent MSSA, MRSA, and S. epidermidis – pathogens commonly associated with periprosthetic joint infections. Pronounced anticolonizing activity was evident for tolfenamic acid-loaded UHMWPE. Due to the low solubility of tolfenamic acid, the material's antibacterial effect against planktonic bacteria was lower. These results demonstrate that analgesic-loaded UHMWPE, used as a tool in multimodal pain management, can also yield antibacterial effects, opening an entirely new avenue for providing post-arthroplasty antibacterial prophylaxis. This pioneering approach has a potential to reduce patients' morbidity and mortality after arthroplasty. For any tables or figures, please contact the authors directly

Aims. This study reports the ten-year wear rates, incidence of osteolysis, clinical outcomes, and complications of a multicentre randomized controlled trial comparing oxidized zirconium (OxZr) versus cobalt-chrome (CoCr) femoral heads with ultra-high molecular weight polyethylene (UHMWPE) and highly cross-linked polyethylene (XLPE) liners in total hip arthroplasty (THA). Methods. Patients undergoing primary THA were recruited from four institutions and prospectively allocated to the following treatment groups: Group A, CoCr femoral head with XLPE liner; Group B, OxZr femoral head with XLPE liner; and Group C, OxZr femoral head with UHMWPE liner. All study patients and assessors recording outcomes were blinded to the treatment groups. The outcomes of 262 study patients were analyzed at ten years’ follow-up. Results. Patients in Group C were associated with increased mean liner wear rates compared to patients in Group A (0.133 mm/yr (SD 0.21) vs 0.031 mm/yr (SD 0.07), respectively; p < 0.001) and Group B (0.133 mm/yr (SD 0.21) vs 0.022 mm/yr (SD 0.05), respectively; p < 0.001) at ten years’ follow-up. Patients in Group C were also associated with increased risk of osteolysis and aseptic loosening requiring revision surgery, compared with patients in Group A (7/133 vs 0/133, respectively; p = 0.007) and Group B (7/133 vs 0/135, respectively; p = 0.007). There was a non-statistically significant trend towards increased mean liner wear rates in Group A compared with Group B (0.031 mm/yr (SD 0.07) vs 0.022 mm/yr (SD 0.05), respectively; p = 0.128). All three groups were statistically comparable preoperatively and at ten years’ follow-up when measuring normalized Western Ontario and McMaster Universities Osteoarthritis Index (p = 0.410), 36-Item Short Form Health Survey (p = 0.465 mental, p = 0.713 physical), and pain scale scores (p = 0.451). Conclusion. The use of UHMWPE was associated with progressively increased annual liner wear rates after THA compared to XLPE. At ten years’ follow-up, the group receiving UHMWPE demonstrated an increased incidence of osteolysis and aseptic loosening requiring revision surgery compared to XLPE. Femoral heads composed of OxZr were associated with trend towards reduced wear rates compared to CoCr, but this did not reach statistical significance and did not translate to any differences in osteolysis, functional outcomes, or revision surgery between the two femoral head components. Cite this article: Bone Joint J 2022;104-B(7):833–843

Aims. We present the ten-year data of a cohort of patients, aged between 18 and 65 years (mean age 52.7 years; 19 to 64), who underwent total hip arthroplasty. Patients were randomised to be treated with a cobalt-chrome (CoCr) femoral head with an ultra-high molecular weight polyethylene (UHMWPE), highly cross-linked polyethylene (XLPE) or ceramic-on-ceramic (CoC) bearing surface. Patients and Methods. A total of 102 hips (91 patients) were randomised into the three groups. At ten years, 97 hips were available for radiological and functional follow-up. Two hips (two patients) had been revised (one with deep infection and one for periprosthetic fracture) and three were lost to follow-up. Radiological analysis was performed using a validated digital assessment programme to give linear, directional and volumetric wear of the two polyethylene groups. Results. There was a significantly reduced rate of steady-state linear wear with XLPE (0.07 mm/yr) compared with UHMWPE (0.37 mm/yr) (p = 0.001). Volumetric wear was also significantly reduced in the XLPE group (29.29 mm. 3. /yr) compared with the UHMWPE group (100.75mm. 3. /yr) (p = 0.0001). There were six patients with UHMWPE who had non-progressive osteolysis and none in the XLPE group. All three bearing groups had significant improvements in 12-item short form health survey scores, Western Ontario and McMaster Universities Osteoarthritis Index score and Harris Hip Score. However, the improvement in HSS was significantly less in the UHMWPE group (p = 0.0188) than in the other two groups. At ten years, the rates of volumetric and linear wear in the XLPE group remain low and predominantly below the estimated threshold for osteolysis (1 mm/yr). The rate of linear wear in the XLPE group was three times less than in the UHMWPE group at five-year follow-up and five times less at ten years. The rate of volumetric wear was also three times less in the XLPE group at ten years. Conclusion. While CoC also performs well, XLPE at ten years remains a safe and excellent bearing option in young patients, with low rates of wear and no evidence of osteolysis. Cite this article: Bone Joint J 2017;99-B:1590–5

This study reports the ten-year polyethylene liner wear rates, incidence of osteolysis, clinical outcomes and complications of a three-arm, multicentre randomised controlled trial comparing Cobalt-Chrome (CoCr) and Oxidised Zirconium (OxZr) femoral heads with ultra-high molecular weight polyethylene (UHMWPE) versus highly cross-linked polyethylene (XLPE) liners in total hip arthroplasty (THA). Patients undergoing THA from four institutions were prospectively randomised into three groups. Group A received a CoCr femoral head and XLPE liner; Group B received an OxZr femoral head and XLPE liner; and Group C received an OxZr femoral head and UHMWPE liner. Blinded observers recorded predefined outcomes in 262 study patients at regular intervals for ten years following THA. At ten years follow-up, increased linear wear rates were recorded in group C compared to group A (0.133 ± 0.21 mm/yr vs 0.031 ± 0.07 mm/yr respectively, p<0.001) and group B (0.133 ± 0.21 mm/yr vs 0.022 ± 0.05 mm/yr respectively, p<0.001). Patients in group C were associated with increased risk of osteolysis and aseptic loosening requiring revision surgery compared with group A (7/133 vs 0/133 respectively, p=0.007) and group B (7/133 vs 0/135 respectively, p=0.007). There was a non-significant trend towards increased liner wear rates in group A compared to group B (0.031 ± 0.07 mm/yr vs 0.022 ± 0.05 mm/yr respectively, p=0.128). All three groups were statistically comparable preoperatively and at ten years follow-up when measuring normalised Western Ontario and McMaster Universities Osteoarthritis Index(p=0.410), short-form-36 (p = 0.465 mental, p = 0.713 physical), and pain scale scores (p=0.451). The use of UHMWPE was associated with progressively increased annual liner wear rates after THA. At ten years follow-up, this translated to UHMWPE leading to an increased incidence of osteolysis and aseptic loosening requiring revision THA, compared with XLPE. Femoral heads composed of OxZr were associated with a non-significant trend towards reduced wear rates compared to CoCr, but this did not translate to any differences in osteolysis, functional outcomes, or revision surgery between the two treatments groups

It has been suggested that the wear of ultra-high molecular weight polyethylene (UHMWPE) in total hip replacement is substantially reduced when the femoral head is ceramic rather than metal. However, studies of alumina and zirconia ceramic femoral heads on the penetration of an UHMWPE liner in vivo have given conflicting results. The purpose of this study was to examine the surface characteristics of 30 alumina and 24 zirconia ceramic femoral heads and to identify any phase transformation in the zirconia heads. We also studied the penetration rate of alumina and zirconia heads into contemporary UHMWPE liners. The alumina heads had been implanted for a mean of 11.3 years (8.1 to 16.2) and zirconia heads for a mean of 9.8 years (7.5 to 15). The mean surface roughness values of the explanted alumina heads (Ra 40.12 nm and Rpm 578.34 nm) were similar to those for the explanted zirconia heads (Ra 36.21 nm and Rpm 607.34 nm). The mean value of the monoclinic phase of two control zirconia heads was 1% (0.8% to 1.5%) and 1.2% (0.9% to 1.3%), respectively. The mean value of the monoclinic phase of 24 explanted zirconia heads was 7.3% (1% to 26%). In the alumina group, the mean linear penetration rate of the UMWPE liner was 0.10 mm/yr (0.09 to 0.12) in hips with low Ra and Rpm values (13.22 nm and 85.91 nm, respectively). The mean linear penetration rate of the UHMWPE liner was 0.13 mm/yr (0.07 to 0.23) in hips with high Ra and Rpm values (198.72 nm and 1329 nm, respectively). This difference was significant (p = 0.041). In the zirconia head group, the mean linear penetration rate of the UHMWPE liner was 0.09 mm/yr (0.07 to 0.14) in hips with low Ra and Rpm values (12.78 nm and 92.99 nm, respectively). The mean linear penetration rate of the UHMWPE liner was 0.12 mm/yr (0.08 to 0.22) in hips with high Ra and Rpm values (199.21 nm and 1381 nm, respectively). This difference was significant (p = 0.039). The explanted zirconia heads which had a minimal phase transformation had similar surface roughness and a similar penetration rate of UHMWPE liner as the explanted alumina head

This study reports the ten-year outcomes of a three-arm, multicentre randomised controlled trial comparing Cobalt-Chrome (CoCr) and Oxidised Zirconium (OxZr) femoral heads with ultra-high molecular weight polyethylene (UHMWPE) versus highly cross-linked polyethylene (XLPE) liners in total hip arthroplasty (THA). Patients undergoing THA from four institutions were prospectively randomised into three groups. Group A received a CoCr femoral head and XLPE liner; Group B received an OxZr femoral head and XLPE liner; and Group C received an OxZr femoral head and UHMWPE liner. The outcomes of 262 study patients were analysed at ten years follow-up. At ten years, increased linear wear rates were recorded in group C compared to group A (0.133 ± 0.21 mm/yr vs 0.031 ± 0.07 mm/yr respectively, p<0.001) and group B (0.133 ± 0.21 mm/yr vs 0.022 ± 0.05 mm/yr respectively, p<0.001). Patients in group C had increased risk of osteolysis and aseptic loosening requiring revision surgery compared with group A (7/133 vs 0/133 respectively, p=0.007) and group B (7/133 vs 0/135 respectively, p=0.007). There was a non- significant trend towards increased liner wear rates in group A compared to group B (0.031 ± 0.07 mm/yr vs 0.022 ± 0.05 mm/yr respectively, p=0.128). All three groups were statistically comparable preoperatively and at ten years follow-up from a clinical score perspective. The use of UHMWPE was associated with progressively increased annual liner wear rates. At ten years follow-up, this translated to an increased incidence of osteolysis and aseptic loosening requiring revision, compared with XLPE. Femoral heads composed of OxZr were associated with a non-significant trend towards reduced wear rates compared to CoCr, but this did not translate to any differences in osteolysis, functional outcomes, or revision surgery between the two treatments groups

The gold standard for PJI treatment comprises the use of antibiotic-loaded bone cement spacers, which are limited in their load bearing capacity[1]. Thus, developing an antibiotic-eluting UHMWPE bearing surface can improve the mechanical properties of spacers and improve the quality of life of PJI patients. In this study, we incorporated vancomycin into UHMWPE to investigate its elution characteristics, mechanical properties and its efficacy against an acute PJI in an animal model. Vancomycin hydrochloride was incorporated into UHMWPE (2 to 14%) by blending and consolidation. We studied drug elution with blocks in PBS and UV-Vis spectroscopy at 280 nm. We determined the tensile mechanical properties and impact strength [3]. We implanted osteochondral plugs in rabbits using either control UHMWPE, bone cement (40g) containing vancomycin (1g) and tobramycin (3.6g) or vancomycin-eluting UHMWPE (n=5) plugs in the patellofemoral groove of rabbits. All rabbits received a beaded titanium rod in the tibial canal. All groups received two doses of 5×10. 7. cfu of bioluminescent S. aureus in the distal tibial canal prior to insertion of the rod and the articular space after closure of the joint capsule. No intravenous antibiotics were used. Bioluminescence signal was measured when the rabbits expired, or at 21-day post-op. Hardware, polyethylene implants, and joint tissues were sonicated to further quantify live bacteria via plate seeding. Vancomycin elution increased with increasing drug loading. Vancomycin elution above MIC for 3 weeks and optimized mechanical properties were obtained at 6–7 wt% vancomycin loading in UHMWPE. In our lapine acute infection model using bioluminescent S. aureus, knees treated with UHMWPE without antibiotics and bone cement containing vancomycin and tobramycin had significantly higher bioluminescence compared to those treated with vancomycin-eluting UHMWPE. These results suggest that an antibiotic-eluting UHMWPE spacer with acceptable properties as a bearing surface could be used to treat periprosthetic joint infection in lieu of bone cement spacers and this could allow safer load bearing and a higher quality of life for the patients during treatment. In addition, this presents a safer alternative in cases where the second stage surgery for the implantation of new components is hindered

We report on an innovative surface grafting to highly crosslinked (HXLPE) bearing for THA using a biocompatible-phospholipid-polymer poly (2-methacryloyloxyethyl phosphorylcholine) (PMPC). Such hydrophilic surfaces mimic articular cartilage and are hypothesized to improve lubrication and thereby reduce friction and wear. We performed in vitro testing of wear and friction of ceramic-on-polyethylene THRs with the PMPC treatment, and compared them with untreated controls. Highly cross-linked UHMWPE bearings, gamma-ray-irradiated at different levels with and without vitamin E (HXL Vit. E: 125 kGy, HXL: 75 kGy, respectively) were divided so half were PMPC treated (n=3 for all four groups). All were paired with identical 40 mm diameter zirconia-toughened-alumina ceramic heads. Testing was carried-out on an AMTI hip simulator for 10 million simulated walking cycles with standard lubricant and conditions (ISO-14242-1). Wear was measured gravimetrically at 21 intervals, and so was frictional torque with a previously described and tested methodology. PMPC treatment produced a statistically significant 71% in wear reduction of HXL poly (1.70±1.36 mg/Mc for PMPC vs. 5.86±0.402 mg/Mc for controls, p=0.013). A similar significant wear reduction was found for PMPC treated HXL with Vit. E liners (0.736±0.750 mg/Mc, vs. 2.14±0.269 mg/Mc, p=0.035). The improvements were associated with 12% and 5% reductions in friction of the HXL and Vit. E HXL respectively (statistically significant p=0.003, and marginal p=0.116, one tailed). These results were an important step in the quest for lower wearing, thin and strong UHMWPE liners for larger diameter femoral heads with the potential benefit of longevity and less risk of dislocation after surgery

Aims

Limited implant survival due to aseptic cup loosening is most commonly responsible for revision total hip arthroplasty (THA). Advances in implant designs and materials have been crucial in addressing those challenges. Vitamin E-infused highly cross-linked polyethylene (VEPE) promises strong wear resistance, high oxidative stability, and superior mechanical strength. Although VEPE monoblock cups have shown good mid-term performance and excellent wear patterns, long-term results remain unclear. This study evaluated migration and wear patterns and clinical and radiological outcomes at a minimum of ten years’ follow-up.

Aims

This study reports the results of 38 total hip arthroplasties (THAs) in 33 patients aged less than 50 years, using the JRI Furlong hydroxyapatite ceramic (HAC)-coated femoral component.

Aims

The primary outcome was investigating differences in wear, as measured by femoral head penetration, between cross-linked vitamin E-diffused polyethylene (vE-PE) and cross-linked polyethylene (XLPE) acetabular component liners and between 32 and 36 mm head sizes at the ten-year follow-up. Secondary outcomes included acetabular component migration and patient-reported outcome measures (PROMs) such as the EuroQol five-dimension questionnaire, 36-Item Short-Form Health Survey, Harris Hip Score, and University of California, Los Angeles Activity Scale (UCLA).

Osteolysis secondary to ultra-high molecular weight polyethylene (UHMWPE) wear is a leading cause of late-term implant failure via aseptic loosening in patients treated with total hip arthroplasty (THA). Radiation crosslinking of UHMWPE has been shown to decrease wear. However, the resulting polymer (crosslinked-PE) has a high free radical content. Two different methods that have been used to reduce the remaining free radicals are mechanical annealing and chemical stabilization using Vitamin E, a free radical scavenger. The primary purpose of the current study was to evaluate and compare the wear properties of vitamin E-doped crosslinked-PE (VEPE) and one formulation of mechanically annealed crosslinked-PE using radiostereometric analysis (RSA) in patients five years after primary THA. We also sought to understand the association between polyethylene wear and patient-reported outcome measures (PROMs). Three-hundred and five patients from six international centers were enrolled. Seventy-six percent were treated with highly-crosslinked (95 kGy) VEPE liners, and the rest received moderately-crosslinked (50 kGy) (ModXL), mechanically annealed liners. Data was collected prospectively at one-, two-, and five-year intervals. At the 5-year follow-up, proximal femoral head penetration into the VEPE liners (median = 0.05mm (range, −0.03–1.20)) was significantly lower than the penetration into the ModXL liners (median = 0.15mm (range, −0.22–1.04)) (p<0.001). In the VEPE cohort the median proximal penetration did not increase from one- to five-year follow-up (p=0.209). In contrast, there was a significant increase in femoral head penetration for the ModXL group (p<0.001) during that same time. Multivariable regression showed that the only variable predictive of increased wear was ModXL liner type (B=0.12, p<0.001). There were no differences in PROMs between the liner groups, and there was no correlation between polyethylene wear and PROMs for the cohort as a whole. The current study is the largest analysis of polyethylene wear at five-year follow-up using the RSA technique. We observed similar bedding in through the two-year interval between the two liner types, however, there was significantly more wear in the ModXL cohort at five-years. Currently, the wear rates for both liner groups are below the osteolysis threshold and have not led to any implant failures via aseptic loosening. Continued follow-up will provide a better understanding of the association between wear rate and clinical outcomes

Aims

Femoral bone preparation using compaction technique has been shown to preserve bone and improve implant fixation in animal models. No long-term clinical outcomes are available. There are no significant long-term differences between compaction and broaching techniques for primary total hip arthroplasty (THA) in terms of migration, clinical, and radiological outcomes.

Aims

This study investigates head-neck taper corrosion with varying head size in a novel hip simulator instrumented to measure corrosion related electrical activity under torsional loads.

Aims

Uncemented metal acetabular components show good osseointegration, but material stiffness causes stress shielding and retroacetabular bone loss. Cemented monoblock polyethylene components load more physiologically; however, the cement bone interface can suffer fibrous encapsulation and loosening. It was hypothesized that an uncemented titanium-sintered monoblock polyethylene component may offer the optimum combination of osseointegration and anatomical loading.

Introduction. Cross linked polyethylene (XLPE) has gained popularity as a bearing surface of choice for younger patients despite only medium term results being available for wear rates. Concern remains regarding the long-term stability and durability of these materials. In order to address these issues we present the longest radiological and clinical follow-up of XLPE. Patients/Materials & Methods. Since 1986, we have prospectively studied a group of 17 patients (19 hips) that underwent a cemented Charnley low friction arthroplasty using a combination of 22.225mm alumina ceramic femoral head, a modified Charnley flanged stem and a chemically cross-linked polyethylene cup. We now report the 28 year clinical and radiological results. Results. At the latest review nine patients (11 hips) were still attending for clinical and radiographic follow-up at a mean of 27.5 years (26 – 28). The mean age at surgery in this group was 47 years (26 – 58). Seven patients died whilst still under follow-up, and one was revised at 17 years for late deep infection following urological surgery. There have been no mechanical failures of the components and no aseptic loosening. The mean initial penetration rate at 1 year was 0.13mm/year; between one and four years was 0.034mm/year; and between 4 years and latest follow-up (mean 27.5 years) was 0.007mm/year. One patient in this group subsequently had a contralateral Charnley metal on UHMWPE hip replacement and had a total cup penetration of 6.1mm at 27 years, compared to 0.41mm at 28 years in the XLPE and alumina ceramic combination. Conclusion. The clinical and radiological results in this group of patients remain excellent with no aseptic loosening. There was an initial bedding in period, after which there was an extremely low wear rate. The results highlight the long term stability and durability of cross-linked polyethylene when used in combination with a small diameter alumina ceramic head

We reviewed 261 patients with 320 Charnley low-friction arthroplasties who had a mean follow-up of 22 years 10 months (20 to 30). Of these, 93.9% considered the operation to be a success; 82.3% were free from pain and 11.6% had occasional discomfort. Satisfactory function was achieved in 59.6% and 62% had an excellent range of movement. The clinical results did not correlate well with the radiological appearance; radiologically loose components did not affect the clinical outcome. The main long-term problem was wear and loosening of the UHMWPE cup. Our findings suggest that the radiological appearance of the arthroplasty is a more reliable indication of the state of the arthroplasty than the clinical results

Aims

We present the results, in terms of survival, clinical outcome, and radiological appearance at 20 years, in a cohort of 225 cemented Exeter Universal femoral components (Stryker, Newbury, UK) implanted in 207 patients, at a district general hospital.

Aims

Vitamin E-infused highly crosslinked polyethylene (VEPE) has been introduced into total hip arthroplasty (THA) with the aim of further improving the wear characteristics of moderately and highly crosslinked polyethylenes (ModXLPE and HXLPE). There are few studies analyzing the outcomes of vitamin E-infused components in cemented arthroplasty, though early acetabular component migration has been reported. The aim of this study was to measure five-year polyethylene wear and acetabular component stability of a cemented VEPE acetabular component compared with a ModXLPE cemented acetabular component.