Abstract
We report on an innovative surface grafting to highly crosslinked (HXLPE) bearing for THA using a biocompatible-phospholipid-polymer poly (2-methacryloyloxyethyl phosphorylcholine) (PMPC). Such hydrophilic surfaces mimic articular cartilage and are hypothesized to improve lubrication and thereby reduce friction and wear.
We performed in vitro testing of wear and friction of ceramic-on-polyethylene THRs with the PMPC treatment, and compared them with untreated controls. Highly cross-linked UHMWPE bearings, gamma-ray-irradiated at different levels with and without vitamin E (HXL Vit. E: 125 kGy, HXL: 75 kGy, respectively) were divided so half were PMPC treated (n=3 for all four groups). All were paired with identical 40 mm diameter zirconia-toughened-alumina ceramic heads. Testing was carried-out on an AMTI hip simulator for 10 million simulated walking cycles with standard lubricant and conditions (ISO-14242-1). Wear was measured gravimetrically at 21 intervals, and so was frictional torque with a previously described and tested methodology.
PMPC treatment produced a statistically significant 71% in wear reduction of HXL poly (1.70±1.36 mg/Mc for PMPC vs. 5.86±0.402 mg/Mc for controls, p=0.013). A similar significant wear reduction was found for PMPC treated HXL with Vit. E liners (0.736±0.750 mg/Mc, vs. 2.14±0.269 mg/Mc, p=0.035). The improvements were associated with 12% and 5% reductions in friction of the HXL and Vit. E HXL respectively (statistically significant p=0.003, and marginal p=0.116, one tailed).
These results were an important step in the quest for lower wearing, thin and strong UHMWPE liners for larger diameter femoral heads with the potential benefit of longevity and less risk of dislocation after surgery.