To compare complications, survivorship and results in 2 groups of Furlong-HAP Active, one with ceramic-ceramic and the other with metal-XLPE friction pair

Prospective, non-randomized, comparison of 2 series of JRI uncemented prosthesis, implanted with identical protocol by 1 surgeon in 1 hospital from 2006 to 2014. Friction pair was ceramic (Biolox Forte or Delta) in 35 patients of 53.7+/−10.6 years (25–69) (21 males, 60%), and CrCo-XLPE in 65 cases of 69.0+/−8.9 years (42–81) (36 males, 55%); there were significant differences in age (p<0.00001) but not in sex (p=0.6565).

Head diameter: Ce-Ce with 19 of 28mm, 9 of 32 and 7 of 36mm; Me-PE with 63 of 28mm, 1 of 32 and 1 of 36. Follow-up averaged 10.5+/−3.1 years (1–15) in ceramic and 9.8+/−3.8 years (2–15) in XLPE group. Pearson, Fisher, Kolmogorov-Smirnov, Student, Mann-Whitney, calculated with the informatic tools Microsoft Excel 2007 and https://www.socscistatistics.com/tests/.

Complications in ceramic joints: 2 late infections (Fisher exact test=0.6101) (1 DAIR, 1 one-stage exchange); 1 dislocation (Fisher exact test=0.2549) (closed reduction); 1 Vancouver C fracture (ORIF) (Fisher exact test=0.6548). Complications in Me-XLPE joints: 2 late infections (Fisher=0.6101) (1 DAIR, 1 two-stage exchange); 7 dislocations (Fisher=0.2549) (2 early, open reduction) (5 late: 3 closed reduction, 1 cup revision, 1 constrained cup); 4 Vancouver B fractures (Fisher=0.6548) (2 intraoperative, cerclages; 2 late, exchange).

Final follow-up: Harris Hip Score averaged 93.2+/−13.7 (23–100) in ceramic and 94.3+/−8.7 (65–100) in XLPE joints (p=0.64552).

Wear: 0.06+/−0.38mm (0–1.5) in ceramic and 0.16+/−0.5mm (0–2) in Me-PE THAs (p=0.30302).

Osteolysis in Charnley-De Lee zones: 8 zones (6 patients) (17%) in ceramic cups, 25 zones (15 patients) (23%) in XLPE cups (p=0.980127).

Survivorship without any surgery or closed reduction after 15 years: 91.0% in ceramic joints, 83.8% in Me-XLPE joints.

Survivorship without component exchange after 15 years: 93.9% in ceramic joints, 93.6% in Me-XLPE joints.

At least after 10 years follow-up of Furlong-HAP Active, metal-XLPE and ceramic-ceramic joints present no significant differences in complications, clinical score, wear, acetabular osteolysis, or survivorship without component exchange. On the contrary, survivorship without any surgery or closed reduction is different because of the high rate of dislocation in 28mm metal-poly joints.

The purpose of this study was to compare the effect of femoral head material (delta ceramic versus metal) on polyethylene wear in a consecutive prospective randomized series of low friction total hip arthroplasty. A total of 110 patients with a mean age of 60.6 ± 9.3 (34–75) years were randomized (power of 90%, alpha of 5%) to receive either a metal (55 hips) or a delta ceramic (55 hips) femoral head. The polyethylene socket was moderately cross-linked (3 Mrads of gamma radiation in nitrogen) and annealed at 130°C in all hips. All other parameters were identical in both groups. The primary criterion for evaluation was linear head penetration measurement using the Martell system, performed by an investigator blinded to the material of the femoral head. Creep and steady state wear values were calculated. At the minimum of 3-year follow-up, complete data were available for analysis in 38 hips at a median follow-up of 4.4 years (3.0 to 5.7), and in 42 hips at a median follow-up of 4.0 years (3.0 to 5.4) in the metal and delta ceramic groups, respectively. The mean creep, measured as the linear head penetration at one year follow-up, was 0.42 ± 1.0 mm in the metal group versus 0.30 ± 0.81 mm in the delta ceramic group (Mann and Whitney test, p = 0.56). The mean steady state penetration rate from one year onwards measured 0.17 ± 0.44 mm/year (median 0.072) in the metal group versus 0.074 ± 0.44 mm/year (median 0.072) in the delta ceramic group (Mann and Whitney test, p = 0.48). No case of delta ceramic femoral head fracture was recorded, and no hip had signs of periprosthetic osteolysis. This study demonstrated that up to 5-year follow-up, delta ceramic femoral head did not significantly influence creep neither wear of a contemporary annealed polyethylene. Longer follow-up is necessary to further evaluate the potential clinical benefits of delta ceramic

Aims

In 2015, we published the results of our ceramic-on-metal (CoM) total hip arthroplasties (THAs) performed between October 2007 and July 2009 with a mean follow-up of 34 months (23 to 45) and a revision rate of 3.1%. The aim of this paper is to present the longer-term outcomes.

The purpose of this randomized controlled trial was to evaluate serum metal levels in patients undergoing total hip arthroplasty (THA) with a conventional compared to a modular dual-mobility bearing. Patients undergoing primary THA for osteoarthritis were randomized to receive either a modular dual-mobility or conventional polyethylene bearing. All patients received the same titanium acetabular and femoral component and a ceramic femoral head. Serum metal levels were drawn pre-operatively then annually for a minimum of two years postoperatively. An a priori power analysis determined that 40 patients (20 per cohort) were needed to identify a clinically relevant difference in serum cobalt of 0.35 ng/ml (ppb) at 90% power. Forty-six patients were randomized to a modular dual-mobility (n=25) or conventional bearing (n=21) with 40 at a minimum follow-up of two years. No differences in serum cobalt (mean 0.14 ppb [range, 0.075–0.29] vs. 0.20 ppb [range, 0.075–0.57], p=0.39) or chromium levels (mean 0.14 ppb [range, 0.05–0.50] vs. 0.12 ppb [range, 0.05–0.35], p=0.65) were identified between the modular dual-mobility and conventional cohorts, respectively. There was no statistically significant difference in serum Co or Cr at two years postoperatively in subjects implanted with a ceramic head and this particular dual mobility bearing in comparison to a ceramic head and a conventional acetabular component. While modest expected elevations in serum Co and Cr were observed in the dual mobility group, in no case did the Co level exceed the laboratory reference range nor the threshold of one part per billion that has been associated with adverse local tissue reactions to mechanically-assisted crevice corrosion

Objectives. The use of ceramic femoral heads in total hip arthroplasty (THA) has increased due to their proven low bearing wear characteristics. Ceramic femoral heads are also thought to reduce wear and corrosion at the head-stem junction with titanium (Ti) stems when compared with metal heads. We sought to evaluate taper damage of ceramic compared with metal heads when paired with cobalt chromium (CoCr) alloy stems in a single stem design. Methods. This retrieval study involved 48 total hip arthroplasties (THAs) with CoCr V40 trunnions paired with either CoCr (n = 21) or ceramic (n = 27) heads. The taper junction of all hips was evaluated for fretting/corrosion damage and volumetric material loss using a roundness-measuring machine. We used linear regression analysis to investigate taper damage differences after adjusting for potential confounding variables. Results. We measured median taper material loss rates of 0.210 mm. 3. /year (0.030 to 0.448) for the metal head group and 0.084 mm. 3. /year (0.059 to 0.108) for the ceramic group. The difference was not significant (p = 0.58). Moreover, no significant correlation between material loss and implant or patient factors (p > 0.05) was found. Conclusions. Metal heads did not increase taper damage on CoCr trunnions compared with ceramic heads from the same hip design. The amount of material released at the taper junctions was very low when compared with available data regarding CoCr/Ti coupling in metal-on-metal bearings. Cite this article: A. Di Laura, H. Hothi, J. Henckel, I. Swiatkowska, M. H. L. Liow, Y-M. Kwon, J. A. Skinner, A. J. Hart. Retrieval analysis of metal and ceramic femoral heads on a single CoCr stem design. Bone Joint Res 2017;6:–350. DOI: 10.1302/2046-3758.65.BJR-2016-0325.R1

Aims

The aim of this study was to evaluate the incidence of liner malseating in two commonly used dual-mobility (DM) designs. Secondary aims included determining the risk of dislocation, survival, and clinical outcomes.

Aims

The aim of our study was to investigate the effect of asymmetric crosslinked polyethylene liner use on the risk of revision of cementless and hybrid total hip arthroplasties (THAs).

Total Hip Arthroplasty (THA) is a successful operation for the management of end stage hip osteoarthritis (OA) but long term success is limited by wear of the polyethylene bearing surface. The aim of this study was to compare the rate of revision at 15 years in patients <55 who had a THA for OA, and received either cross-linked (XLPE) or conventional non cross-linked polyethylene (non-XLPE). The study population was all patients with primary THAs undertaken for OA from 1999 to 31 December 2016. Outcomes were determined for all procedures, comparing THA performed with non-XLPE and XLPE and including the effect of age, sex, and reason for revision. The principal outcome measure was time to first revision using Kaplan-Meier estimates of survivorship. There were 17,869 procedures recorded for younger patients <55 years of age undergoing THA for OA and using either non XLPE or XLPE. There was a fivefold increase in the rate of revision for procedures using non-XLPE after seven years. The 15 year cumulative percent revision of primary THA performed for OA in patients <55 with non XLPE was 17.4% (95% CI 15.5,19.5) and for XLPE was 6.6% (95%CI 5.5,7.8) HR >7 years =5.3, p<0.001. Non-XLPE and XLPE were combined with three different femoral head bearing surfaces: ceramic, metal and ceramicised metal. Within each bearing surface, XLPE had a lower rate of revision than non-XLPE. For the most common head size of 28mm XLPE had a lower rate of revision. The use of XLPE has resulted in a significant reduction in the rate of revision for younger patients undergoing THA for OA at 15 years. This evidence suggests that longevity of THA is likely to be improved and may enable younger patients to undergo surgery, confident of a reduced need for revision in the long term

Aims

To investigate the effect of polyethylene manufacturing characteristics and irradiation dose on the survival of cemented and reverse hybrid total hip arthroplasties (THAs).

The bearing surface is the critical element in determining the longevity of a total hip arthroplasty. Over the past decade problems associated with bearing surfaces and modular femoral tapers have had an impact on surgeon selection of both acetabular liners and modular femoral heads. The purpose of this study was to analyse THA bearing surface trends from 2007 through 2014 using a large national database. A retrospective review of the Nationwide Inpatient Sample (NIS) database was conducted from 2007 to 2014. All patients who underwent a primary THA were identified using International Classification of Diseases, 9th edition (ICD-9) procedure codes. Bearing surface data was extracted by identifying patients with ICD-9 procedure modifier codes. Patient and hospital characteristics were recorded for each patient. Descriptive statistics were employed to characterise bearing surface trends for the following bearing surfaces: metal on polyethylene (MoP); ceramic on polyethylene (CoP); ceramic on ceramic (CoC) and metal on metal (MoM). Univariate analysis was performed to identify differences between the bearing surface groups. During the study period, 2,460,640 primary THA discharges were identified, of which 1,059,825 (43.1%) had bearing surface data available for further analysis. The breakdown of the bearing surfaces used for these THAs were as follows: MoP − 49.1% (496,713); CoP − 29.1% (307,907); CoC − 4.2% (44,823); and MoM − 19.9% (210,381). MoM utilization peaked in 2008 with 51,033 cases representing 40.1% of THAs implanted that year. The usage steadily declined and by 2014 there were only 6,600 MoM cases representing only 4.0% of the THAs. From 2007 to 2014, the use of CoP bearing surfaces increased from 11,482 discharges (11.1% of cases) in 2007, to 83,300 discharges (50.8% of cases) in 2014. CoP utilization surpassed MoP in 2014. MoP accounted for 54.7% of discharges in 2011 and just 42.1% in 2014. During the study period, MoM bearing surface usage declined precipitously, while CoP surpassed MoP as the most prevalent bearing surface used in total hip arthroplasty patients. These changes in bearing surface usage over time were clearly influenced by concerns regarding high failure rates associated with MoM articulations and reports of taper corrosion associated with modular metal femoral heads

Aims

The main advantage of 3D-printed, off-the-shelf acetabular implants is the potential to promote enhanced bony fixation due to their controllable porous structure. In this study we investigated the extent of osseointegration in retrieved 3D-printed acetabular implants.

Aims

The aim of this study was to identify the effect of the manufacturing characteristics of polyethylene acetabular liners on the survival of cementless and hybrid total hip arthroplasty (THA).

It has been suggested that the wear of ultra-high molecular weight polyethylene (UHMWPE) in total hip replacement is substantially reduced when the femoral head is ceramic rather than metal. However, studies of alumina and zirconia ceramic femoral heads on the penetration of an UHMWPE liner in vivo have given conflicting results. The purpose of this study was to examine the surface characteristics of 30 alumina and 24 zirconia ceramic femoral heads and to identify any phase transformation in the zirconia heads. We also studied the penetration rate of alumina and zirconia heads into contemporary UHMWPE liners. The alumina heads had been implanted for a mean of 11.3 years (8.1 to 16.2) and zirconia heads for a mean of 9.8 years (7.5 to 15). The mean surface roughness values of the explanted alumina heads (Ra 40.12 nm and Rpm 578.34 nm) were similar to those for the explanted zirconia heads (Ra 36.21 nm and Rpm 607.34 nm). The mean value of the monoclinic phase of two control zirconia heads was 1% (0.8% to 1.5%) and 1.2% (0.9% to 1.3%), respectively. The mean value of the monoclinic phase of 24 explanted zirconia heads was 7.3% (1% to 26%). In the alumina group, the mean linear penetration rate of the UMWPE liner was 0.10 mm/yr (0.09 to 0.12) in hips with low Ra and Rpm values (13.22 nm and 85.91 nm, respectively). The mean linear penetration rate of the UHMWPE liner was 0.13 mm/yr (0.07 to 0.23) in hips with high Ra and Rpm values (198.72 nm and 1329 nm, respectively). This difference was significant (p = 0.041). In the zirconia head group, the mean linear penetration rate of the UHMWPE liner was 0.09 mm/yr (0.07 to 0.14) in hips with low Ra and Rpm values (12.78 nm and 92.99 nm, respectively). The mean linear penetration rate of the UHMWPE liner was 0.12 mm/yr (0.08 to 0.22) in hips with high Ra and Rpm values (199.21 nm and 1381 nm, respectively). This difference was significant (p = 0.039). The explanted zirconia heads which had a minimal phase transformation had similar surface roughness and a similar penetration rate of UHMWPE liner as the explanted alumina head

Objectives

Modern metal-on-metal (MoM) hip resurfacing arthroplasty (HRA), while achieving good results with well-orientated, well-designed components in ideal patients, is contraindicated in women, men with head size under 50 mm, or metal hypersensitivity. These patients currently have no access to the benefits of HRA. Highly crosslinked polyethylene (XLPE) has demonstrated clinical success in total hip arthroplasty (THA) and, when used in HRA, potentially reduces metal ion-related sequelae. We report the early performance of HRA using a direct-to-bone cementless mono-bloc XLPE component coupled with a cobalt-chrome femoral head, in the patient group for whom HRA is currently contraindicated.

Aims

Instability continues to be a troublesome complication after total hip arthroplasty (THA). Patient-related risk factors associated with a higher dislocation risk include the preoperative diagnosis, an age of 75 years or older, high body mass index (BMI), a history of alcohol abuse, and neurodegenerative diseases. The goal of this study was to assess the dislocation rate, radiographic outcomes, and complications of patients stratified as high-risk for dislocation who received a dual mobility (DM) bearing in a primary THA at a minimum follow-up of two years.

Aims

Our aim was to report survivorship data and lessons learned with the Corail/Pinnacle cementless total hip arthroplasty (THA) system.

Aims

To report our experience with trunnion corrosion following metal-on-polyethylene total hip arthroplasty, in particular to report the spectrum of presentation and determine the mean time to presentation.

Aims

To present a surgically relevant update of trunnionosis.

Large ceramic femoral heads offer several advantages that are potentially advantageous to patients undergoing both primary and revision total hip replacement. Many high-quality studies have demonstrated the benefit of large femoral heads in reducing post-operative instability. Ceramic femoral heads may also offer an advantage in reducing polyethylene wear that has been reported in vitro and is starting to become clinically apparent in mid-term clinical outcome studies. Additionally, the risk of taper corrosion at a ceramic femoral head–neck junction is clearly lower than when using a metal femoral head. With improvements in the material properties of both modern ceramic femoral heads and polyethylene acetabular liners that have reduced the risk of mechanical complications, large ceramic heads have gained popularity in recent years.

Cite this article: Bone Joint J 2013;95-B, Supple A:63–6.

Objectives

This study aimed to characterise and qualitatively grade the severity of the corrosion particles released into the hip joint following taper corrosion.