Orthopaedic Proceedings
Vol. 95-B, Issue SUPP_13 | Pages 16 - 16
1 Mar 2013
Tawonsawatruk T Spadaccino A Wallace R Simpson A
Full Access

Introduction. Bending tests are commonly used to evaluate the mechanical behaviour of small animal bones. To test whole bones, it is normal that soft tissue should be removed before testing. However, cleaning the specimens might disturb the callus, interfering with the mechanical properties. This study compares mechanical properties of rat tibia between specimen with and without muscle cleaning. Materials and methods. 12 male Wistar rats aged 3–4 months were used. Soft tissues including skin and muscle were removed from right tibias (Group A), whereas muscles on the left tibia were left intact (Group B). 4-point bending was used to find the ultimate load, stress and Young's modulus. Results. All specimens displayed a basic failure pattern from load-displacement graph. Mean ultimate load of 105.2N (S.E.M.=7.60, n=12) for group A and 101.6N (S.E.M.=7.32, n=12) group B. Mean stress at failure of 281.50MPa (S.E.M.=34.98, n=12) was found for group A 288.70MPa (S.E.M.=20.83, n=12) for group B. Mean Young's modulus was 8.97GPa (S.E.M.=1.44, n=12) for group A and 10.05GPa (S.E.M=0.69, n=12) for group B. No statistical differences for any mechanical properties were found between groups for either t-test(p>0.05) or Bland-Altman plot. Discussion. No differences in mechanical properties were found with or without soft tissue. Therefore, biomechanical testing of small specimen bending without removing muscle can be used. The advantages of this technique are reduced specimen preparation time and decreasing risk of creating a stress raiser at the callus


Orthopaedic Proceedings
Vol. 103-B, Issue SUPP_16 | Pages 69 - 69
1 Dec 2021
MacLeod A Taylor R Casonato A Gill H
Full Access

Abstract

Objectives

Additive manufacturing has led to numerous innovations in orthopaedic surgery: surgical guides; surface coatings/textures; and custom implants. Most contemporary implants are made from titanium alloy (Ti-6Al-4V). Despite being widely available industrially and clinically, there is little published information on the performance of this 3D printed material for orthopaedic devices with respect to regulatory approval. The aim of this study was to document the mechanical, chemical and biological properties of selective laser sintering (SLS) manufactured specimens following medical device (TOKA®, 3D Metal Printing LTD, UK) submission and review by the UK Medicines and Healthcare Products Regulatory Agency (MHRA).

Methods

All specimens were additively manufactured in Ti-6Al-4V ELI (Renishaw plc, UK). Mechanical tests were performed according to ISO6892-1, ISO9585 and ISO12107 for tensile (n=10), bending (n=3) and fatigue (n=16) respectively (University of Bath, UK). Appropriate chemical characterisation and biological tests were selected according to recommendations in ISO10993 and conducted by external laboratories (Wickham Labs, UK; Lucideon, UK; Edwards Analytical, UK) in adherence with Good Lab Practise guidelines. A toxicological review was conducted on the findings (Bibra, UK).


Orthopaedic Proceedings
Vol. 100-B, Issue SUPP_16 | Pages 51 - 51
1 Nov 2018
Ishibashi T Tomita T Yamazaki T Fujito T Kono K Konda S Tamaki M Yoshikawa H Sugamoto K
Full Access

Bi-cruciate stabilized (BCS) TKA is the prosthesis that aims to substitute bi-cruciate ligament with post-cam engagement. We estimated to describe the in vivo kinematics during deep knee bending in BCS and Cruciate retaining (CR) TKA with the same articular geometry. We analyzed 26 knees who agreed to the current investigation under institutional review board approval. 17 knees were implanted with BCS (Journey ∥BCS, Smith & Nephew. Memphis, US) and 9 knees with CR (Journey∥CR). Each patient was asked to perform deep knee bending under weight-bearing condition. To estimate the spatial position and orientation of the TKA, 2D/3D registration technique with single fluoroscopy was used. We evaluated anteroposterior (AP) translation of the nearest point from femoral component to tibial axial plane for medial and lateral sides, femoral external rotation relative to tibial component and post-cam engagement in BCS. Measurement results were analyzed using Wilcoxon test. Values of P<0.05 were considered statistically significant. Medial AP translation indicated 11.7±5.1% posterior movement in BCS and 4.0±6.6% anterior movement in CR from minimum flexion to 130°. Lateral AP translation indicated 28.9±11.4% posterior movement in BCS and 18.3±6.2% posterior movement in CR from minimum flexion to 130°. Femoral external rotation were observed in both group and the amount of rotation were 5.2°±4.5° in BCS and 8.2°±4.0° in CR. Anterior post-cam engagement was not observed in all cases (76.5%). But medial AP translation in BCS was anteriorly in shallow flexion angles compared to CR. It suggested that anterior post-cam engagement couldn't work in valid.


Orthopaedic Proceedings
Vol. 100-B, Issue SUPP_4 | Pages 23 - 23
1 Apr 2018
Krticka M Michlovska L Nekuda V Chamradova I Sojka K Kaiser J Zboncak M Vojtova L
Full Access

Introduction

In recent years, there has been a growing interest, in many fields of medicine, in the use of bone adhesives that are biodegraded to non-toxic products and resorbed after fulfilling their function in contact with living tissue. Biomechanical properties of newly developed bone glue, such as adhesion to bone and elastic modulus were tested in our study.

Material and methods

Newly developed injectable biodegradable “self-setting” bone adhesive prepared from inorganic tricalcium phosphate powder and aqueous solution of organic thermogelling polymers was used for ex-vivo fixing fractured pig femur. Ex-vivo biomechanical tests were performed on 45 fresh pig femurs. Control group consist of 10 healthy bones, tested group was created by 35 bones with artificial fractures in diaphysis – oblique (O) and bending wedge (BW) type of fracture. Tested group were divided to following 4 subgroups (sg); sg1 – O fracture (n=15) glued together with 3 different type of bone adhesives, sg2 BW fracture (n=5) glued together with bone adhesive (n=5); sg3 – BW fracture fixed with locking compression plate (LCP), n=5; sg4 – BW fracture fixed with LCP in combination with bone adhesive. Three-point bending force and shear compression tests were performed on linear electrodynamic test instrument (ElectroPuls E10000, Instron). Femurs from sg1, sg2 and sg4 were tested on Micro-CT before and after biomechanical testing.


Orthopaedic Proceedings
Vol. 94-B, Issue SUPP_XVIII | Pages 38 - 38
1 May 2012
Savaridas T Wallace R Dawson S Simpson A
Full Access

The effect of bisphosphonates on the mechanical properties of the uninjured contra-lateral cortical bone during fracture healing is poorly reported. There remains conflicting evidence with regards the effect of bisphosphonate therapy on cortical bone strength. We assessed the effect of nine weeks of Ibandronate therapy, in a dose known to preserve cancellous bone BMD and strength, on the mechanical properties of the uninjured rat tibial diaphyses using a standardised model of tibial osteotomy and plate fixation. Skeletally mature ex-breeder rats were used. Stress at failure of the tibial diaphyses was measured by a four-point bending test using a custom made jig for rat tibiae. The mechanical strength was compared with radiographic measurements of bone density. Animals received daily subcutaneous injections. 11 rats received 1μg/kg Ibandronate (IBAN) daily and 17 rats received 1ml 0.9% Sodium Chloride (CONTROL) daily.

The IBAN group had a statistically significant, p=0.024, higher stress at failure 212.7 (±42.04) MPa compared to the CONTROL group 171.7 (±46.13)MPa. There was a positive correlation between the mechanical strength of bone and the radiological measure of bone density.

Osteopenia is known to occur following a fracture even in the contra-lateral limb. This study demonstrates that ibandronate therapy has no detrimental effect and may even increase the strength of uninjured cortical bone during the fracture healing process. The longer term effect of ibandronate on cortical bone especially in relation to the accumulation of mico-damage requires further study. Bisphosphonate effect on the uninjured limb needs to be considered when reporting proportional strength of fracture repair compared to the uninjured limb.


Orthopaedic Proceedings
Vol. 103-B, Issue SUPP_13 | Pages 79 - 79
1 Nov 2021
Skeats M Hill D Barbour M
Full Access

Introduction and Objective. The continued effectiveness of antibiotic loaded bone cements is threatened by antibiotic resistance. The common antiseptic, chlorhexidine (CHX), is a potential alternative to antibiotics in bone cements, but conventional salts are highly soluble, causing burst release and rapid decline to subinhibitory local CHX concentrations. Here, chlorhexidine triphosphate (CHX-TP), a low solubility CHX salt, is investigated as an alternative antimicrobial in PMMA bone cements. The aim was to assess duration of antimicrobial release and antimicrobial efficacy, along with handling, setting and mechanical properties of CHX-TP loaded cements, compared with an existing cement formulation containing gentamicin. Materials and Methods. Palacos R (Heraeus Medical, Newbury, UK) with 0, 1, 4, 7 and 12% CHX-TP (w/w) cements were prepared by combining solid CHX-TP with Palacos R components, and compared with Palacos R+G. All cements were prepared without vacuum and under ISO 5833:2002 conditions. Cements were tested under ISO 5833:2002 for compressive and bending properties, setting time, maximum temperature and doughing time. Antimicrobial release from the cements into deionised water was studied and antimicrobial efficacy of unaged and aged cements against Staphylococcus aureus (ATCC 29213) was assessed using a disc diffusion assay. Results. Compressive strength of CHX-TP loaded cements was not significantly different to Palacos R or Palacos R+G (p > 0.05, all exceeding ISO 5833:2002 minimum of 70 MPa). Mean bending strength was significantly lower with CHX-TP loading (p < 0.05) than bending strength of Palacos R and Palacos R+G, though all bending moduli exceeded the ISO 5833:2002 minimum (1800 MPa). All cements studied were within the ISO 5833:2002 limits for setting time (3 to 15 min), doughing time (≤ 5 min) and maximum temperature (90 . o. C). Mean doughing time for Palacos R, Palacos R+G and Palacos R + 12 % CHX-TP respectively: 52.5 s, 45 s and 45 s. Mean setting time and mean maximum temperature for Palacos R, Palacos R+G and Palacos R + 1, 4, 7 and 12% CHX-TP respectively: 11.00 min (73 . o. C), 11.25 min (72 . o. C), 12.25 min (66 . o. C), 10.50 min (70 . o. C), 10.00 min (70 . o. C), 10.75 min (62 . o. C). Sustained CHX release into deionised water was observed from all Palacos R + CHX-TP cements. Duration varied according to CHX-TP dosing and diminished over time, although to an extent that itself varied with dosing. 1 % CHX-TP ceased releasing CHX at 6.9 weeks; 4 % CHX-TP ceased at 67.7 weeks; 7 % and 12 % CHX-TP were ongoing at 75.5 weeks. Palacos R+G cements ceased releasing detectable levels of gentamicin after 14.4 weeks. Palacos R+G and Palacos R + CHX-TP cement discs showed efficacy against S. aureus (ATCC 29213) when applied as prepared (unaged) to S. aureus bacterial lawns in disc diffusion assays, with CHX-TP cements showing dose dependency. Zone of inhibition (ZOI) size was significantly reduced for Palacos R+G cements and Palacos R + 1% CHX-TP cements after 1 week and 6 weeks aging, compared to ZOI from unaged cements (p < 0.05). ZOI size produced by Palacos R + 4, 7, and 12 % CHX-TP cements did not decline significantly after 6 weeks aging (p > 0.05). Conclusions. CHX-TP can be incorporated into the Palacos R cement matrix up to 12% w/w without deterioration of compressive strength, bending modulus, doughing time, setting time or maximum temperature. Bending strength was significantly reduced at all CHX-TP loadings studied. Palacos R + 4, 7 and 12% CHX-TP cements provided sustained CHX release, exceeding the duration of gentamicin release from Palacos R+G, and showed sustained efficacy against S. Aureus after 6 weeks aging, which was not achieved by Palacos R+G cements


The Journal of Bone & Joint Surgery British Volume
Vol. 92-B, Issue 3 | Pages 454 - 460
1 Mar 2010
Baleani M Bialoblocka-Juszczyk E Engels GE Viceconti M

We investigated the effect of pre-heating a femoral component on the porosity and strength of bone cement, with or without vacuum mixing used for total hip replacement.

Cement mantles were moulded in a manner simulating clinical practice for cemented hip replacement. During polymerisation, the temperature was monitored. Specimens of cement extracted from the mantles underwent bending or fatigue tests, and were examined for porosity.

Pre-heating the stem alone significantly increased the mean temperature values measured within the mantle (+14.2°C) (p < 0.001) and reduced the mean curing time (−1.5 min) (p < 0.001). The addition of vacuum mixing modulated the mean rise in the temperature of polymerisation to 11°C and reduced the mean duration of the process by one minute and 50 seconds (p = 0.01 and p < 0.001, respectively). In all cases, the maximum temperature values measured in the mould simulating the femur were < 50°C. The mixing technique and pre-heating the stem slightly increased the static mechanical strength of bone cement. However, the fatigue life of the cement was improved by both vacuum mixing and pre-heating the stem, but was most marked (+ 280°C) when these methods were combined.

Pre-heating the stem appears to be an effective way of improving the quality of the cement mantle, which might enhance the long-term performance of bone cement, especially when combined with vacuum mixing.


The Journal of Bone & Joint Surgery British Volume
Vol. 87-B, Issue 12 | Pages 1694 - 1699
1 Dec 2005
Floerkemeier T Hurschler C Witte F Wellmann M Thorey F Vogt U Windhagen H

The ability to predict load-bearing capacity during the consolidation phase in distraction osteogenesis by non-invasive means would represent a significant advance in the management of patients undergoing such treatment. Measurements of stiffness have been suggested as a promising tool for this purpose. Although the multidimensional characteristics of bone loading in compression, bending and torsion are apparent, most previous experiments have analysed only the relationship between maximum load-bearing capacity and a single type of stiffness. We have studied how compressive, bending and torsional stiffness are related to the torsional load-bearing capacity of healing callus using a common set of samples of bone regenerate from 26 sheep treated by tibial distraction osteogenesis.

Our findings showed that measurements of torsional, bending and compressive stiffness were all suitable as predictors of the load-bearing capacity of healing callus. Measurements of torsional stiffness performed slightly better than those of compressive and bending stiffness.