Objectives. Few studies have assessed outcomes following non-metal-on-metal hip arthroplasty (non-MoMHA) revision surgery performed for
Aims. We investigated whether blood metal ion levels could effectively
identify patients with bilateral Birmingham Hip Resurfacing (BHR)
implants who have
We sought to establish the incidence of joint failure secondary to
To determine the outcomes following revision surgery of metal-on-metal
hip arthroplasties (MoMHA) performed for adverse reactions to metal
debris (ARMD), and to identify factors predictive of re-revision. We performed a retrospective observational study using National
Joint Registry (NJR) data on 2535 MoMHAs undergoing revision surgery
for ARMD between 2008 and 2014. The outcomes studied following revision were
intra-operative complications, mortality and re-revision surgery.
Predictors of re-revision were identified using competing-risk regression
modelling.Aims
Patients and Methods
Objectives. Alarm over the reported high failure rates for metal-on-metal (MoM) hip implants as well as their potential for locally aggressive Adverse Reactions to Metal Debris (ARMDs) has prompted government agencies, internationally, to recommend the monitoring of patients with MoM hip implants. Some have advised that a blood ion level >7 µg/L indicates potential for ARMDs. We report a systematic review and meta-analysis of the performance of metal ion testing for ARMDs. Methods. We searched MEDLINE and EMBASE to identify articles from which it was possible to reconstruct a 2 × 2 table. Two readers independently reviewed all articles and extracted data using explicit criteria. We computed a summary receiver operating curve using a Bayesian random-effects hierarchical model. Results. Our literature search returned 575 unique articles; only six met inclusion criteria defined a priori. The discriminative capacity of ion tests was homogeneous across studies but that there was substantial cut-point heterogeneity. Our best estimate of the “true” area under curve (AUC) for metal ion testing is 0.615, with a 95% credible interval of 0.480 to 0.735, thus we can state that the probability that metal ion testing is actually clinically useful with an AUC ≥ 0.75 is 1.7%. Conclusion. Metal ion levels are not useful as a screening test for identifying high risk patients because ion testing will either lead to a large burden of false positive patients, or otherwise marginally modify the pre-test probability. With the availability of more accurate non-invasive tests, we did not find any evidence for using blood ion levels to diagnose symptomatic patients. Cite this article: M. Pahuta, J. M. Smolders, J. L. van Susante, J. Peck, P. R. Kim, P. E. Beaule. Blood metal ion levels are not a useful test for
Introduction.
Recent case reports have described V40 taper failure with clinically relevant
Objectives. Modular dual-mobility (MDM) constructs are used to reduce dislocation rates after total hip replacement (THR). They combine the advantages of dual mobility with the option of supplementary acetabular screw fixation in complex revision surgery. However, there are concerns about
A-70-year old woman underwent uncomplicated total hip arthroplasty using a titanium modular stem with a 46mm CoCr femoral head, a titanium shell, and a metal linear (Wright Medical Technology). Eight years after implantation, she presented with a painful left hip. A pelvic radiograph revealed adequate positioning of both hip implants without any signs of wear of loosening. CT scanning confirmed the presence of a 5 × 5 cm soft tissue mass in the ilium above the cup component accompanied by the iliac fracture. The patient was diagnosed as having an
Abstract. Objectives. Modular dual-mobility (MDM) constructs are used to reduce dislocation rates after total hip replacement (THR). They combine the advantages of dual mobility with the option of supplementary acetabular screw fixation in complex revision surgery. However, there are concerns about
We conducted a retrospective study to assess
the prevalence of
Trunnionosis, due to mechanical wear and/or corrosion at the head stem taper junction, can occur in metal on polyethylene (MOP) hip implants. In some patients this results in severe soft tissue destruction or
Early failure associated with
Aims. The Birmingham Hip Resurfacing (BHR) was introduced in 1997 to address the needs of young active patients using a historically proven large-diameter metal-on-metal (MoM) bearing. A single designer surgeon’s consecutive series of 130 patients (144 hips) was previously reported at five and ten years, reporting three and ten failures, respectively. The aim of this study was to extend the follow-up of this original cohort at 25 years. Methods. The study extends the reporting on the first consecutive 144 resurfacing procedures in 130 patients for all indications. All operations were undertaken between August 1997 and May 1998. The mean age at operation was 52.1 years (SD 9.93; 17 to 76), and included 37 female patients (28.5%). Failure was defined as revision of either component for any reason. Kaplan-Meier survival analysis was performed. Routine follow-up with serum metal ion levels, radiographs, and Oxford Hip Scores (OHSs) was undertaken. Results. Overall implant survival was 83.50% (95% confidence interval (CI) 0.79 to 0.90) at 25 years, and the number at risk was 79. Survival in male patients at 25 years was 89.5% (95% CI 0.83 to 0.96) compared to 66.9% for female patients (95% CI 0.51 to 0.83). Ten additional failures occurred in the period of ten to 25 years. These involved an
To determine ten-year failure rates following 36 mm metal-on-metal
(MoM) Pinnacle total hip arthroplasty (THA), and identify predictors
of failure. We retrospectively assessed a single-centre cohort of 569 primary
36 mm MoM Pinnacle THAs (all Corail stems) followed up since 2012
according to Medicines and Healthcare Products Regulation Agency
recommendations. All-cause failure rates (all-cause revision, and
non-revised cross-sectional imaging failures) were calculated, with predictors
for failure identified using multivariable Cox regression.Aims
Patients and Methods
We investigated the changes seen on serial metal
artefact reduction magnetic resonance imaging scans (MARS-MRI) of
metal-on-metal total hip arthroplasties (MoM THAs). In total 155
THAs, in 35 male and 100 female patients (mean age 70.4 years, 42
to 91), underwent at least two MRI scans at a mean interval of 14.6
months (2.6 to 57.1), at a mean of 48.2 months (3.5 to 93.3) after
primary hip surgery. Scans were graded using a modification of the
Oxford classification. Progression of disease was defined as an
increase in grade or a minimum 10% increase in fluid lesion volume
at second scan. A total of 16 hips (30%) initially classified as
‘normal’ developed an abnormality on the second scan. Of those with
‘isolated trochanteric fluid’ 9 (47%) underwent disease progression,
as did 7 (58%) of ‘effusions’. A total of 54 (77%) of hips initially
classified as showing
In 1997 the Birmingham Hip Resurfacing was introduced to address the needs of young active patients. Alternative designs were introduced to try and improve wear performance. The aim of this study was a comparative cohort study of two types of metal-on-metal bearing to determine the mechanism of failure at 15 years. The study reviewed 91 Brimingham Hip Resurfacings (BHR) (Smith and Nephew) and 715 DUROM hip resurfacing (Zimmer) procedures in prior to 2009. Failure was defined as revision of either component for any reason. Kaplan-Meyer survivorship analysis performed. Routine follow-up with serum metal ion levels and radiographs. Mean follow-up was 17.9 years (range 15.2 – 25.1). The mean age at operation was 51.6 years (SD 8.6, range 20.7 to 70.2), including 299 women (37.1%). The Birmingham resurfacing demonstrated 92.3% survivorship at 15 years (SE 2.8, 95% CI 3.9 – 7.8) and 90.0% at latest follow-up (SE 3.5, 95% CI 4.9 to 9.4). By comparison, the DUROM survivorship at 15 years was 89.1% at 15 years (SE 1.2, 95% CI 2.0 to 2.5) and 87.4% (SE 1.3, 95% CI 2.5 to 2.3) at latest follow-up. There was no statistically significant difference in survivorship between groups (p= 0.32). Survival in male patients was 92.7% compared to 80.0% in females. The reported failures occurred from
Introduction. Large head total hip arthroplasty (THA) reduces dislocation rates and provides a theooretically larger range of motion. We hypothesised that this would translate into greater improvement in functional scores when compared to 28mm metal-on-polyethylene THA at 5 years. We believe ours to be the first in vivo comparison study. Methods. A multi-surgeon case-control study in a District General Hospital. The study group consisted of 427 patients with 452 hips, the 38mm uncemented metal-on-metal articulation THA (M2A/Bi-metric, Biomet UK). The control group consisted of 438 age and sex-matched patients with 460 28mm metal-on-polyethylene articulation THA (Exeter/Exeter or Exeter/Duraloc - Stryker UK. All patients were assessed in a physiotherapist led Joint Review Service as part of their standard follow up, with functional scoring using Oxford Hip (scored 0–48) and WOMAC scores (0–100). Results. The demographics for the 38mm and 28mm groups gave mean ages of 65.8 years and 66.4 years, 40.4% and 39.3% male respectively. Pre-operative functional scores were comparable, with Oxford Hip scores of 23.3 and 26.8 respectively, WOMAC 49 compared to 53. At each review point there was no statistical difference in either Oxford or WOMAC scores and this was sustained at 5 yrs. Dislocation rates in the 38mm group were lower (2.9% vs. 5%) though not statistically significant (p = 0.111). Revision rate was significantly higher in the larger head group, primarily due to
BACKGROUND. The most common salvage of a failed metal-on-metal hip resurfacing is to remove both the femoral and acetabular resurfacing components and perform a total hip replacement. The other choices are to perform an acetabular or femoral only revision. A one or two piece acetabular component or a polyethylene bipolar femoral component that matches the retained metal resurfacing acetabular component is used. The considerations in favor of performing a one component resurfacing revision are maintaining the natural femoral head size, limiting the surgical effort for the patient and surgeon, and bone conservation. There are often favorable cost considerations with single component revision surgery. The reasons for femoral component revision are femoral neck fracture, femoral component loosening and an