We conducted a retrospective study to assess the prevalence of adverse reactions to metal debris (ARMD) in patients operated on at our institution with metal-on-metal (MoM) total hip replacements with 36 mm heads using a Pinnacle acetabular shell. A total of 326 patients (150 males, 175 hips; 176 females, 203 hips) with a mean age of 62.7 years (28 to 85) and mean follow-up of 7.5 years (0.1 to 10.8) participating in our in-depth modern MoM follow-up programme were included in the study, which involved recording whole blood cobalt and chromium ion measurements, Oxford hip scores (OHS) and plain radiographs of the hip and targeted cross-sectional imaging. Elevated blood metal ion levels (> 5 parts per billion) were seen in 32 (16.1%) of the 199 patients who underwent unilateral replacement. At 23 months after the start of our modern MoM follow-up programme, 29 new cases of ARMD had been revealed. Hence, the nine-year survival of this cohort declined from 96% (95% CI 95 to 98) with the old surveillance routine to 86% (95% CI 82 to 90) following the new protocol. Although ARMD may not be as common in 36 mm MoM THRs as in those with larger heads, these results support the Medicines and Healthcare Products Regulatory Agency guidelines on regular reviews and further investigations, and emphasise the need for specific a follow-up programme for patients with MoM THRs. Cite this article: Bone Joint J 2014; 96-B:1610–17

We sought to establish the incidence of joint failure secondary to adverse reaction to metal debris (ARMD) following metal-on-metal hip resurfacing in a large, three surgeon, multicentre study involving 4226 hips with a follow-up of 10 to 142 months. Three implants were studied: the Articular Surface Replacement; the Birmingham Hip Resurfacing; and the Conserve Plus. Retrieved implants underwent analysis using a co-ordinate measuring machine to determine volumetric wear. There were 58 failures associated with ARMD. The median chromium and cobalt concentrations in the failed group were significantly higher than in the control group (p < 0.001). Survival analysis showed a failure rate in the patients with Articular Surface Replacement of 9.8% at five years, compared with < 1% at five years for the Conserve Plus and 1.5% at ten years for the Birmingham Hip Resurfacing. Two ARMD patients had relatively low wear of the retrieved components. Increased wear from the metal-on-metal bearing surface was associated with an increased rate of failure secondary to ARMD. However, the extent of tissue destruction at revision surgery did not appear to be dose-related to the volumetric wear

Objectives. Few studies have assessed outcomes following non-metal-on-metal hip arthroplasty (non-MoMHA) revision surgery performed for adverse reactions to metal debris (ARMD). We assessed outcomes following non-MoMHA revision surgery performed for ARMD, and identified predictors of re-revision. Methods. We performed a retrospective observational study using data from the National Joint Registry for England and Wales. All non-MoMHAs undergoing revision surgery for ARMD between 2008 and 2014 were included (185 hips in 185 patients). Outcome measures following ARMD revision were intra-operative complications, mortality and re-revision surgery. Predictors of re-revision were identified using Cox regression. Results. Intra-operative complications occurred in 6.0% (n = 11) of the 185 cases. The cumulative four-year patient survival rate was 98.2% (95% CI 92.9 to 99.5). Re-revision surgery was performed in 13.5% (n = 25) of hips at a mean time of 1.2 years (0.1 to 3.1 years) following ARMD revision. Infection (32%; n = 8), dislocation/subluxation (24%; n = 6), and aseptic loosening (24%; n = 6) were the most common re-revision indications. The cumulative four-year implant survival rate was 83.8% (95% CI 76.7 to 88.9). Multivariable analysis identified three predictors of re-revision: multiple revision indications (hazard ratio (HR) = 2.78; 95% CI 1.03 to 7.49; p = 0.043); selective component revisions (HR = 5.76; 95% CI 1.28 to 25.9; p = 0.022); and ceramic-on-polyethylene revision bearings (HR = 3.08; 95% CI 1.01 to 9.36; p = 0.047). Conclusions. Non-MoMHAs revised for ARMD have a high short-term risk of re-revision, with important predictors of future re-revision including selective component revision, multiple revision indications, and ceramic-on-polyethylene revision bearings. Our findings may help counsel patients about the risks of ARMD revision, and guide reconstructive decisions. Future studies attempting to validate the predictors identified should also assess the effects of implant design (metallurgy and modularity), given that this was an important study limitation potentially influencing the reported prognostic factors. Cite this article: G. S. Matharu, A. Judge, D. W. Murray, H. G. Pandit. Outcomes following revision surgery performed for adverse reactions to metal debris in non-metal-on-metal hip arthroplasty patients: Analysis of 185 revisions from the National Joint Registry for England and Wales. Bone Joint Res 2017;6:405–413. DOI: 10.1302/2046-3758.67.BJR-2017-0017.R2

Objectives. Alarm over the reported high failure rates for metal-on-metal (MoM) hip implants as well as their potential for locally aggressive Adverse Reactions to Metal Debris (ARMDs) has prompted government agencies, internationally, to recommend the monitoring of patients with MoM hip implants. Some have advised that a blood ion level >7 µg/L indicates potential for ARMDs. We report a systematic review and meta-analysis of the performance of metal ion testing for ARMDs. Methods. We searched MEDLINE and EMBASE to identify articles from which it was possible to reconstruct a 2 × 2 table. Two readers independently reviewed all articles and extracted data using explicit criteria. We computed a summary receiver operating curve using a Bayesian random-effects hierarchical model. Results. Our literature search returned 575 unique articles; only six met inclusion criteria defined a priori. The discriminative capacity of ion tests was homogeneous across studies but that there was substantial cut-point heterogeneity. Our best estimate of the “true” area under curve (AUC) for metal ion testing is 0.615, with a 95% credible interval of 0.480 to 0.735, thus we can state that the probability that metal ion testing is actually clinically useful with an AUC ≥ 0.75 is 1.7%. Conclusion. Metal ion levels are not useful as a screening test for identifying high risk patients because ion testing will either lead to a large burden of false positive patients, or otherwise marginally modify the pre-test probability. With the availability of more accurate non-invasive tests, we did not find any evidence for using blood ion levels to diagnose symptomatic patients. Cite this article: M. Pahuta, J. M. Smolders, J. L. van Susante, J. Peck, P. R. Kim, P. E. Beaule. Blood metal ion levels are not a useful test for adverse reactions to metal debris: a systematic review and meta-analysis. Bone Joint Res 2016;5:379–386. DOI: 10.1302/2046-3758.59.BJR-2016-0027.R1

Introduction. Adverse reaction to metal debris (ARMD) is an increasingly recognised complication of metal-on-metal hip arthroplasty. A previous study described poor results following revision and recommended early intervention. 1. We determined the outcome of revision for ARMD and present the largest case series to date. Methods. Between 2005 and 2010, 98 patients (101 hips) underwent revision for ARMD. The diagnosis of ARMD was based on clinical history, examination, appearance at revision and histology. Patients were reviewed at 3, 6 and 12 months and annually thereafter. Patient satisfaction, Harris hip scores (HHS) and metal ions were analysed. Results. 54 patients (55 hips) with an average age of 58 years (29 to 81 years) completed minimum one year follow-up (range 1 to 5 years). The mean HHS improved from 49.7 (10 to 79) to 86.3 (40 to 100). Forty-five (81%) patients were satisfied and nine (16%) patients were not satisfied with the outcome. The mean serum cobalt 24.5 (1.65 to 96.6) improved to 1.17 (0.31 to 6.99). Two patients died from unrelated diseases. There were 8 (14%) dislocations and one (1.8%) sciatic nerve palsy that has not recovered. Eight (14%) patients needed re-revision (dislocation: 5 and pain: 3). 26 % had severe soft tissue damage. Six patients have persistent pain and four had recurrent effusions. There were no dislocations in the most recent 50 cases. Discussion. Treatment of ARMD is technically demanding because extensive soft tissue damage can compromise stability. Early results in the current study were promising. Early intervention reduced the dislocation rate and appeared to have a positive impact on outcome. A small group of patients may have persistent pain and recurrent effusions that may require re-revision

Recent case reports have described V40 taper failure with clinically relevant adverse reaction to metal debris (ARMD). The real incidence of V40 taper damage and potential consequences are currently unclear, however. Aim of this study is therefore, to evaluate the long-term incidence of pseudotumors in a consecutive series of THA with V40 taper and identify potential influencing factors. From 2006 to 2007 a total number of 120 patients (127 hips) received either an uncemented (Accolade©) or cemented hip stem (ABGII©), both with V40 taper (Stryker© Mahwah, New Jersey, USA). They all were combined with 36 mm Vitallium (CoCrMo) heads and uncemented cups (Trident©) with XLPE inlays. 11,2 +/− 0,5 years post-op 82 patients with 87 hips (mean age 74 years, 58 % female) underwent clinical (PROMs) and radiographic evaluation. In 71 patients (75 hips) MARS- MRI of the hip was performed. 38 patients were lost to follow-up. In 81 patients (86 hips) chrome and cobalt levels were determined. MRI-investigation revealed 20 pseudotumors (26%) and 18 of them had a diameter of >2cm. Patients with pseudotumors had significant higher median cobalt ion levels compared to those without (2,85 μg/l vs. 1,32 μg/l; p=0,022) and a significant correlation between pseudotumors and cobalt levels was found. Radiographic osteolysis was associated with pseudotumors as well (p= 0,014). Neither approach, BMI, gender, age, type of stem, head length, inclination nor heterotope ossification showed a significant correlation to pseudotumor occurrence. Due to the high incidence of local ARMD in in asymptomatic patients with V40 taper and metal heads we recommend regular post-operative follow-up investigations including routine metal ion screening and consecutive MRI investigation upon elevation

Objectives. Modular dual-mobility (MDM) constructs are used to reduce dislocation rates after total hip replacement (THR). They combine the advantages of dual mobility with the option of supplementary acetabular screw fixation in complex revision surgery. However, there are concerns about adverse reaction to metal debris (ARMD) as a result of fretting corrosion between the metal liner and shell. Methods: The aim of this systematic review was to find and review all relevant studies to establish the outcomes and risks associated with MDM hip replacement. All articles on MDM THRs in the Medline, EMBASE, CINAHL, Cochrane Library, and Prospero databases were searched. A total of 14 articles were included. A random intercept logistic regression model was used for meta-analysis, giving estimated average values. Results: There were 6 cases of ARMD out of 1312 total. Estimated median incidence of ARMD from meta-analysis was 0.3% (95% CI 0.1 – 1.4%). Mean postoperative serum Cobalt was 0.81 μg/L (95% CI 0.33 – 1.29 μg/L), and Chromium was 0.77 μg/L (95% 0.35 – 1.19 μg/L), from 279 cases in 7 studies. Estimated median incidence of a serum cobalt or chromium ion measurement ≥1 μg/L was 7.9% (95% CI 3.5 – 16.8%), and ≥7 μg/L was 1.8% (95% CI 0.7 – 4.2%). Conclusions: ARMD is a rare but significant complication following total hip replacement using a MDM construct. Its incidence appears higher than that reported in non-metal-on-metal (MoM) hip replacements but lower than that of MoM hip replacements. MDM hip replacements are associated with raised serum metal ion levels postoperatively, but there was no correlation with worse clinical hip function within studies. Studies were poor quality and at high risk of confounding. Pending further work, MDM constructs should be used with caution, reserved for select cases at particularly high risk of dislocation

A-70-year old woman underwent uncomplicated total hip arthroplasty using a titanium modular stem with a 46mm CoCr femoral head, a titanium shell, and a metal linear (Wright Medical Technology). Eight years after implantation, she presented with a painful left hip. A pelvic radiograph revealed adequate positioning of both hip implants without any signs of wear of loosening. CT scanning confirmed the presence of a 5 × 5 cm soft tissue mass in the ilium above the cup component accompanied by the iliac fracture. The patient was diagnosed as having an adverse reaction to metal debris (ARMD) after a metal-on-metal THA and revision was performed. Perioperatively?tissue necrosis and partial destruction of the abductor mechanism were found in the absence of any macroscopic infection. Both the neck trunnion and bore of the head showed slight signs of corrosion. The modular neck was revised with a ceramic 28mm head and a new dual-mobility liner(Zimmer Biomet). The iliac fracture was fixed with a porous trabecular metal augment(Zimmer Biomet). The histopathology of tissue sample revealed extensively necrotic material with focal cellular areas of inflammatory cells containing macrophages and neutrophilas. Metalic debris was also scattered in the necrotic materials. After the revision, the patient was recovered without pain or dislocation, and iliac fracture was well fixed. Instability is a substantial problem in the revision of ARMD. Extensive necrosis with gross deficiency of the abductor mechanism is associated with postoperative dislocation. Revision of failed MoM THA a dual-mobility device an effective strategy

Aims. We investigated whether blood metal ion levels could effectively identify patients with bilateral Birmingham Hip Resurfacing (BHR) implants who have adverse reactions to metal debris (ARMD). Patients and Methods. Metal ion levels in whole blood were measured in 185 patients with bilateral BHRs. Patients were divided into those with ARMD who either had undergone a revision for ARMD or had ARMD on imaging (n = 30), and those without ARMD (n = 155). Receiver operating characteristic analysis was used to determine the optimal thresholds of blood metal ion levels for identifying patients with ARMD. Results. The maximum level of cobalt or chromium ions in the blood was the parameter which produced the highest area under the curve (91.0%). The optimal threshold for distinguishing between patients with and without ARMD was 5.5 µg/l (83.3% sensitivity, 88.4% specificity, 58.1% positive and 96.5% negative predictive values). Similar results were obtained in a subgroup of 111 patients who all underwent cross-sectional imaging. Between 3.2% and 4.3% of patients with ARMD were missed if United Kingdom (7 µg/l) and United States (10 µg/l) authority thresholds were used respectively, compared with 2.7% if our implant specific threshold was used, though these differences did not reach statistical significance (p ≥ 0.248). Conclusion. Patients with bilateral BHRs who have blood metal ion levels below our implant specific threshold were at low-risk of having ARMD. Cite this article: Bone Joint J 2016;98-B:1455–62

Abstract. Objectives. Modular dual-mobility (MDM) constructs are used to reduce dislocation rates after total hip replacement (THR). They combine the advantages of dual mobility with the option of supplementary acetabular screw fixation in complex revision surgery. However, there are concerns about adverse reaction to metal debris (ARMD) as a result of fretting corrosion between the metal liner and shell. Methods. The aim of this systematic review was to find and review all relevant studies to establish the outcomes and risks associated with MDM hip replacement. All articles on MDM THRs in the Medline, EMBASE, CINAHL, Cochrane Library, and Prospero databases were searched. A total of 14 articles were included. A random intercept logistic regression model was used for meta-analysis, giving estimated mean values. Results. There were 6 cases of ARMD out of 1312 total. Estimated median incidence of ARMD from meta-analysis was 0.3% (95% CI 0.1 – 1.4%). Mean postoperative serum Cobalt was 0.81 μg/L (95% CI 0.33 – 1.29 μg/L), and Chromium was 0.77 μg/L (95% 0.35 – 1.19 μg/L), from 279 cases in 7 studies. Estimated median incidence of a serum cobalt or chromium ion measurement ≥1 μg/L was 7.9% (95% CI 3.5 – 16.8%), and ≥7 μg/L was 1.8% (95% CI 0.7 – 4.2%). Conclusions. ARMD is a rare but significant complication following total hip replacement using a MDM construct. Its incidence appears higher than that reported in non-metal-on-metal (MoM) hip replacements but lower than that of MoM hip replacements. MDM hip replacements are associated with raised serum metal ion levels postoperatively, but there was no correlation with worse clinical hip function within studies. Studies were poor quality and at high risk of confounding. Pending further work, MDM constructs should be used with caution, reserved for select cases at particularly high risk of dislocation. Declaration of Interest. (b) declare that there is no conflict of interest that could be perceived as prejudicing the impartiality of the research reported:I declare that there is no conflict of interest that could be perceived as prejudicing the impartiality of the research project

Adverse reaction to metal debris (ARMD) is well recognised as a complication of large head metal on metal total hip replacement (THR) leading to pain, bone and tissue loss and the need for revision surgery. An emerging problem of trunnionosis in metal on polyethylene total hip replacements leading to ARMD has been reported in a few cases. Increased metal ion levels have been reported in THR's with a titanium stem and a cobalt chrome head such as the Accolade-Trident THR (Stryker). We present 3 cases of ARMD with Accloade-Trident THR's with 36mm cobalt chrome head and a polyethylene liner. Metal ion levels were elevated in all three patients (cobalt 10.3 – 161nmol/l). Intraoperative tissue samples were negative for infection and inflammatory markers were normal. Abnormal fluid collections were seen in all three cases and bone loss was severe in one patient leading to a proximal femoral replacement. Histology demonstrated either a non-specific inflammatory reaction in a case which presented early or a granulomatous reaction in a more advanced case suggesting a local foreign body reaction. All patients had improved symptoms post-operatively. 1 patient who had staged bilateral Accolade-Trident THR's required revision of both THR's. ARMD in metal on polyethylene THR's with a titanium stem represents a potential emerging problem. Further studies are required to assess whether these occurrences are rare or represent the tip of an iceberg

Trunnionosis, due to mechanical wear and/or corrosion at the head stem taper junction, can occur in metal on polyethylene (MOP) hip implants. In some patients this results in severe soft tissue destruction or Adverse Reaction to Metal Debris (ARMD). The amount of material required to cause ARMD is unknown but analyses of retrieved hips may provide the answer to this clinically important question. We collected implants from 20 patients with failed hips with MOP bearings, revised due to ARMD. We collected clinical, imaging and blood test data. We graded the severity of taper corrosion (1 to 4), and quantified the volume of material loss from this junction. We compared our results with previous data collected for metal-on-metal (MOM) hips. The median time to revision of the MOP hips was 51.3 (23.1–56.4) months. All head tapers were moderately to severely corroded with a median corrosion score of 4. The median (range) of total material loss at the taper of the MOP hips was 3.9 mm. 3. (2.96 – 7.85 mm. 3. ) and the material loss rate was 1.4 mm. 3. / year (0.56 – 1.82). Comparison with MOM hips revealed no significant difference in taper material loss (p=0.7344) with a median rate of 0.81 mm. 3. / year (0.01–3.45). We are the first to quantify the volume of material loss at the head taper of hip implants with MOP bearings that were revised due to trunnionosis. This data indicates that a clinically significant dose of cobalt and chromium to induce ARMD is approximately 1.4 mm. 3. / year. We have identified a clinically significant volume of taper material loss in MOP hips

Aims

To determine the outcomes following revision surgery of metal-on-metal hip arthroplasties (MoMHA) performed for adverse reactions to metal debris (ARMD), and to identify factors predictive of re-revision.

Aims

In metal-on-polyethylene (MoP) total hip arthroplasty (THA), large metal femoral heads have been used to increase stability and reduce the risk of dislocation. The increased size of the femoral head can, however, lead to increased taper corrosion, with the release of metal ions and adverse reactions. The aim of this study was to investigate the relationship between the size of the femoral head and the levels of metal ions in the blood in these patients.

Early failure associated with adverse reactions to metal debris is an emerging problem after hip resurfacing but the exact mechanism is unclear. We analysed our entire series of 660 metal-on-metal resurfacings (Articular Surface Replacement (ASR) and Birmingham Hip Resurfacing (BHR)) and large-bearing ASR total hip replacements, to establish associations with metal debris-related failures. Clinical and radiological outcomes, metal ion levels, explant studies and lymphocyte transformation tests were performed. A total of 17 patients (3.4%) were identified (all ASR bearings) with adverse reactions to metal debris, for which revision was required. This group had significantly smaller components, significantly higher acetabular component anteversion, and significantly higher whole concentrations of blood and joint chromium and cobalt ions than asymptomatic patients did (all p < 0.001). Post-revision lymphocyte transformation tests on this group showed no reactivity to chromium or cobalt ions. Explants from these revisions had greater surface wear than retrievals for uncomplicated fractures. The absence of adverse reactions to metal debris in patients with well-positioned implants usually implies high component wear. Surgeons must consider implant design, expected component size and acetabular component positioning in order to reduce early failures when performing large-bearing metal-on-metal hip resurfacing and replacement

Aims. The Birmingham Hip Resurfacing (BHR) was introduced in 1997 to address the needs of young active patients using a historically proven large-diameter metal-on-metal (MoM) bearing. A single designer surgeon’s consecutive series of 130 patients (144 hips) was previously reported at five and ten years, reporting three and ten failures, respectively. The aim of this study was to extend the follow-up of this original cohort at 25 years. Methods. The study extends the reporting on the first consecutive 144 resurfacing procedures in 130 patients for all indications. All operations were undertaken between August 1997 and May 1998. The mean age at operation was 52.1 years (SD 9.93; 17 to 76), and included 37 female patients (28.5%). Failure was defined as revision of either component for any reason. Kaplan-Meier survival analysis was performed. Routine follow-up with serum metal ion levels, radiographs, and Oxford Hip Scores (OHSs) was undertaken. Results. Overall implant survival was 83.50% (95% confidence interval (CI) 0.79 to 0.90) at 25 years, and the number at risk was 79. Survival in male patients at 25 years was 89.5% (95% CI 0.83 to 0.96) compared to 66.9% for female patients (95% CI 0.51 to 0.83). Ten additional failures occurred in the period of ten to 25 years. These involved an adverse reaction to metal debris in four patients, a periprosthetic femoral neck fracture affecting five patients, and aseptic loosening in one patient. The median chromium levels were 49.50 nmol/l (interquartile range (IQR) 34 to 70), and the median cobalt serum levels were 42 nmol/l (IQR 24.50 to 71.25). The median OHS at last follow-up was 35 (IQR 10 to 48). During the 25-year study period, 29 patients died. Patient survival at 25 years was 75.10% (95% CI 0.67 to 0.83). Conclusion. This study demonstrates that MoM hip resurfacing using the BHR provides a durable alternative to total hip arthroplasty (THA), particularly in younger male patients with osteoarthritis wishing to maintain a high level of function. These results compare favourably to the best results for THAs. Cite this article: Bone Joint J 2024;106-B(6):540–547

Objectives

We have encountered patients who developed large joint fluid collections with massive elevations in chromium (Cr) and cobalt (Co) concentrations following metal-on-metal (MoM) hip arthroplasties. In some cases, retrieval analysis determined that these ion concentrations could not be explained simply by the wear rates of the components. We hypothesized that these effects may be associated with aseptic lymphocyte-dominated vasculitis-associated lesion (ALVAL).

Objectives

An ongoing prospective study to investigate failing metal-on-metal hip prostheses was commenced at our centre in 2008. We report on the results of the analysis of the first consecutive 126 failed mated total hip prostheses from a single manufacturer.

We investigated the changes seen on serial metal artefact reduction magnetic resonance imaging scans (MARS-MRI) of metal-on-metal total hip arthroplasties (MoM THAs). In total 155 THAs, in 35 male and 100 female patients (mean age 70.4 years, 42 to 91), underwent at least two MRI scans at a mean interval of 14.6 months (2.6 to 57.1), at a mean of 48.2 months (3.5 to 93.3) after primary hip surgery. Scans were graded using a modification of the Oxford classification. Progression of disease was defined as an increase in grade or a minimum 10% increase in fluid lesion volume at second scan. A total of 16 hips (30%) initially classified as ‘normal’ developed an abnormality on the second scan. Of those with ‘isolated trochanteric fluid’ 9 (47%) underwent disease progression, as did 7 (58%) of ‘effusions’. A total of 54 (77%) of hips initially classified as showing adverse reactions to metal debris (ARMD) progressed, with higher rates of progression in higher grades. Disease progression was associated with high blood cobalt levels or an irregular pseudocapsule lining at the initial scan. There was no association with changes in functional scores. Adverse reactions to metal debris in MoM THAs may not be as benign as previous reports have suggested. Close radiological follow-up is recommended, particularly in high-risk groups. Cite this article: Bone Joint J 2015;97-B:1328–37

In 1997 the Birmingham Hip Resurfacing was introduced to address the needs of young active patients. Alternative designs were introduced to try and improve wear performance. The aim of this study was a comparative cohort study of two types of metal-on-metal bearing to determine the mechanism of failure at 15 years. The study reviewed 91 Brimingham Hip Resurfacings (BHR) (Smith and Nephew) and 715 DUROM hip resurfacing (Zimmer) procedures in prior to 2009. Failure was defined as revision of either component for any reason. Kaplan-Meyer survivorship analysis performed. Routine follow-up with serum metal ion levels and radiographs. Mean follow-up was 17.9 years (range 15.2 – 25.1). The mean age at operation was 51.6 years (SD 8.6, range 20.7 to 70.2), including 299 women (37.1%). The Birmingham resurfacing demonstrated 92.3% survivorship at 15 years (SE 2.8, 95% CI 3.9 – 7.8) and 90.0% at latest follow-up (SE 3.5, 95% CI 4.9 to 9.4). By comparison, the DUROM survivorship at 15 years was 89.1% at 15 years (SE 1.2, 95% CI 2.0 to 2.5) and 87.4% (SE 1.3, 95% CI 2.5 to 2.3) at latest follow-up. There was no statistically significant difference in survivorship between groups (p= 0.32). Survival in male patients was 92.7% compared to 80.0% in females. The reported failures occurred from Adverse Reaction to Metal Debris (32 patients), periprosthetic femoral neck fracture (6) and aseptic loosening (41), PJI (12) and undiagnosed pain (6). The mean cobalt and chromium levels at last follow-up were 33.4 nmol/L and 36.5 nmol/L respectively. This study demonstrates two differently designed metal-on-metal hip resurfacing provided a durable alternative to total hip replacement, particularly in younger male patients with osteoarthritis. Differences in design did determine the reason for revision with acetabular fixation being one of the principal failure mechanisms for the DUROM compared to elevated ion levels