Ceramic-on-ceramic hip replacements have generated great interest in recent years due to substantial improvements in manufacturing techniques and material properties1. Microseparation conditions that could occur due to several clinical factors such as head offset deficiency, medialised cup combined with laxity of soft tissue resulting in a translation malalignment, have been shown to cause edge loading, replicate clinically relevant wear mechanisms2,3 and increase the wear of ceramic-on-ceramic bearings3,4. The aim of this study was to investigate the influence of increasing the femoral head size on the wear of ceramic-on-ceramic bearings under several clinically relevant simulator conditions. The wear of size 28mm and 36mm ceramic-on-ceramic bearings (BIOLOX® INTRODUCTION
MATERIALS AND METHODS
Retrieval and clinical studies of metal-on-metal (MoM) bearings have associated increased wear1 and elevated patient ion levels2 with steep cup inclination angles and edge loading conditions. The University of Leeds have previously developed a hip simulator method that has been validated against retrievals and shown to replicate clinically relevant wear rates and wear mechanisms3,4. This method involves introducing lateral microseparation to represent adverse joint laxity and offset deficiency. This study aimed to investigate the effect of microseparation representing translational malpostion, and increased cup inclination angle, representing rotational malposition, in isolation and combined on the wear of different sizes (28 and 36mm) MoM bearing in total hip replacement (THRs). The wear of size 28mm and 36mm MoM THRs bearings was determined under different INTRODUCTION
MATERIALS AND METHODS
High cup abduction angles generate increased contact stresses, higher wear rates and increased revision rates. However, there is no reported study about the influence of cup abduction on stresses under head lateralisation conditions for ceramic-on-Ceramic THA. A finite elements model of a ceramic-on-ceramic THA was developed in order to predict the contact area and the contact pressure, first under an ideal regime and then under lateralised conditions. A 32 mm head diameter with a 30 microns radial clearance was used. The cup was positioned with a 0°anteversion angle and the abduction angle was varied from 45° to 90°. The medial-lateral lateralisation was varied from 0 to 500 microns. A load of 2500 N was applied through the head center.Background
Material and method
Squeaking after total hip replacement has been reported in up to 10% of patients. Some authors proposed that sound emissions from squeaking hips result from resonance of one or other or both of the metal parts and not the bearing surfaces. There is no reported in vitro study about the squeaking frequencies under lubricated regime. The goal of the study was to reproduce the squeaking in vitro under lubricated conditions, and to compare the in vitro frequencies to in vivo frequencies determined in a group of squeaking patients. The frequencies may help determining the responsible part of the noise. Four patients, who underwent THR with a Ceramic-on-Ceramic THR (Trident(r), Stryker(r)) presented a squeaking noise. The noise was recorded and analysed with acoustic software (FMaster(r)). In-vitro 3 alumina ceramic (Biolox Forte Ceramtec(r)) 32 mm diameter (Ceramconcept(r)) components were tested using a PROSIM(r) hip friction simulator. The cup was positioned with a 75° abduction angle in order to achieve edge loading conditions. The backing and the cup liner were cut with a diamond saw, in order to avoid neck-head impingement and dislocation in case of high cup abduction angles (Figure1). The head was articulated ± 10° at 1 Hz with a load of 2.5kN for a duration of 300 cycles. The motion was along the edge. Tests were conducted under lubricated conditions with 25% bovine serum without and with the addition of a 3rd body alumina ceramic particle (200 μm thickness and 2 mm length). Before hand, engineering blue was used in order to analyze the contact area and to determine whether edge loading was achieved.INTRODUCTION
METHODS
The search for the ideal bearing surface in Total Hip Replacements continues. The current ‘best’ materials are felt to be combinations of metal, ceramics and cross-linked polyethylene. Laboratory studies suggest that ceramic-on-metal articulations may provide distinct advantages. This study aims to identify the best bearing surface combination with the lowest adverse side effect profile. Between February 2004 and September 2007, 164 hips were replaced in 142 patients. 39% were male and 69% were female. The average age at surgery was 53 years (17-72 years). Follow-up assessment included radiographs, the Harris Hip Score and whole blood samples for metal ion levels. Complications to date included 3 hips which needed femoral revision because of surgery related factors, and 3 cases of sepsis of which 1 settled and 2 needed revision. One hip needed revision of head and liner to a larger bearing size for recurrent dislocations, and is no longer being followed up for blood metal ions. Post-operative whole blood metal ion levels were compared to pre-operative levels to determine the increase or decrease in metal ion levels. There were no changes in those patients with ceramic-on-ceramic and ceramic-on-polyethylene articulations. Moderately raised whole blood metal ion levels were noted at 3 months in the ceramic-on-metal group, while the metal-on-metal group show the greatest increase. This study agrees with laboratory bearing surface wear studies demonstrating lower wear rates in the ceramic-on-metal group compared to the metal-on-metal group. With concerns related to high blood metal ion levels in metal-on-metal articulations, ceramic-on-metal bearing surfaces may well become a bearing surface of choice in the future, but progress needs to be monitored in the longer term.