Periprosthetic infection remains a clinical challenge that may lead to revision surgeries, increased spending, disability, and mortality. The cost for treating hip and knee total joint infections is anticipated to be $1.62 billion by 2020. There is a need for implant surface modifications that simultaneously resist bacterial biofilm formation and adhesion, while promoting periprosthetic bone formation and osseointegration.

In vitro research has shown that nanotextured titanium promotes osteoblast differentiation, and upregulates metabolic markers of osteoblast activity and osteoblast proliferation. In vivo rat studies confirmed increased bone-implant contact area, enhanced de novo bone formation on and adjacent to the implant, and higher pull-out forces compared to non-textured titanium. The authors have advanced a benign electrochemical anodization process based on ammonium fluoride that creates a nanotube surface in as little as 10 minutes (Fig. 1), which can also integrate antibacterial nanosilver (Fig. 2).

The work reported here summarizes in vitro post-inoculation and in vivo post-implantation studies, showing inherent inhibition of methicillin-resistant Staphylococcus aureus (MRSA) by titanium surfaces with nanotubes (TiNT), nanotubes with nanosilver (TiNT+Ag), plain (Ti), and thermal plasma sprayed (TPS) titanium. Ti6Al4V was the base material for all surfaces. In vitro studies evaluated Ti, TPS, four TiNT groups with varying nanotube diameters (60nm, 80nm, 110nm, 150nm), and TiNT+Ag. After seeding with MRSA (10⁵, 10⁶, and 10⁸ CFU/mL), the 110nm diameter nanotubes showed MRSA inhibition up to three-orders of magnitude lower than the Ti and TPS surfaces at 2, 6, and 48 hours.

Following on the in vitro results, New Zealand White rabbits underwent a bilateral implantation of intramedullary tibial implants of the four material groups (4 mm outside diameter; 110nm NT diameter on TiNT and TiNT+Ag implants). One intramedullary canal was inoculated with clinically-derived MRSA (10⁵ CFU in broth) at the time of implantation; one canal had only culture media introduced (control). At a 2-week endpoint, limbs were harvested for analysis, including implant sonication with sonicant bacterial cultured, histology, and microcomputed chromatography. In the sonicant analysis cohort, TPS showed the lowest average MRSA count, while TiNT and TiNT+Ag were the highest. There was one sample each of TPS, TiNT and TiNT+Ag that showed no MRSA. After an additional 24-hour implant incubation, the TiNT and TiNT+Ag samples had no bacteria, but the TPS grew bacteria; therefore, the authors hypothesize that MRSA more readily releases from the TiNT and TiNT+Ag implants during sonication, indicating weaker biofilm adhesion and development. Histologic analysis is currently underway. In a therapeutic experiment, rabbits underwent bilateral implantation, followed by 1 week of infection development, and then 1 week of vancomycin treatment. At the endpoint, implants were sonicated and bacteria was quantified from the sonicant. TiNT showed viable MRSA at only 30% that of TPS-coated levels, while TiNT+Ag implants showed viable MRSA at only 5% that of TPS-coated levels (Fig. 3). These early results indicate that the TiNT and TiNT+Ag surfaces have some inherent antibacterial activity against MRSA, which may increase the efficacy of systemic antibiotic treatments in the setting of periprosthetic joint infections.

Titanium knee, shoulder and hip implants are typically grit-blasted, thermal plasma spray coated, or sintered to provide ingrowth surface features having texture with pore sizes on the order of hundreds of micrometers. This provides macro and micro-mechanical locking upon bone remodeling. However, at the nanoscale and cellular level, these surfaces appear smooth. In vitro and in vivo research shows surfaces with nanoscale features result in enhanced osseointegration, greater bone-implant contact area and pullout force, and the potential to be bactericidal via a simple hybrid anodization surface modification process. Prior processes for creating nanotube nano-textured surfaces via electrochemical anodization relied on hydrofluoric acid electrolyte and platinum cathodes. This novel process uses ammonium fluoride electrolytes and graphite cathodes which are more cost effective and easier to handle during processing. Hybrid electrolytes with differing concentrations of ethylene glycol, water, and ammonium fluoride provide a variety of nanotube morphologies and sizes. Nano-tubular surfaces on knee tibial and femoral implants, hip stems and acetabular cups, bone screws and other 3D printed parts have been enhanced by this method of nano-texturing in as little as 30 minutes.

In vivo work in a Sprague Dawley rat model showed bone-implant contact area up to 2.9-times greater, and uniaxial pullout forces up to 6.9-times greater, than implanted smooth titanium controls at 4 and 12-week time points. In these tests, 1.25mm Kirschner wires were implanted in the rat femora to simulate an intramedullary nail. Histomorphometry in the mid-shaft and distal regions showed greater trabecular thickness and bone tissue mineral density than controls. Axial pullout tests often resulted in bone failure before the bone-implant interface.

In vitro evidence suggests that nanoscale surfaces may have an antibacterial effect due to surface energy changes that reduce the ability of bacteria to adhere. However, it is recognized that silver is highly antibacterial in appropriate concentrations. It is also recognized that nanosilver, approximately 10–20nm, is especially effective. Ammonium fluoride anodization is modified using a hybrid electrolyte that includes silver fluoride. By substituting some of the ammonium fluoride with silver fluoride, to maintain a constant total fluorine mass, nanosilver is integrated within and among the nanotubes in the same single process that forms the nanotubes.

This hybrid process in nano-texturing titanium implants can be integrated into current manufacturing production at low cost.