Aims

Periprosthetic hip fractures (PPFs) after total hip arthroplasty are difficult to treat. Therefore, it is important to identify modifiable risk factors such as stem selection to reduce the occurrence of PPFs. This study aimed to clarify differences in fracture torque, surface strain, and fracture type analysis between three different types of cemented stems.

Aims. While cementless fixation offers potential advantages over cemented fixation, such as a shorter operating time, concerns linger over its higher cost and increased risk of periprosthetic fractures. If the risk of fracture can be forecasted, it would aid the shared decision-making process related to cementless stems. Our study aimed to develop and validate predictive models of periprosthetic femoral fracture (PPFF) necessitating revision and reoperation after elective total hip arthroplasty (THA). Methods. We included 154,519 primary elective THAs from the Swedish Arthroplasty Register (SAR), encompassing 21 patient-, surgical-, and implant-specific features, for model derivation and validation in predicting 30-day, 60-day, 90-day, and one-year revision and reoperation due to PPFF. Model performance was tested using the area under the curve (AUC), and feature importance was identified in the best-performing algorithm. Results. The Lasso regression excelled in predicting 30-day revisions (area under the receiver operating characteristic curve (AUC) = 0.85), while the Gradient Boosting Machine (GBM) model outperformed other models by a slight margin for all remaining endpoints (AUC range: 0.79 to 0.86). Predictive factors for revision and reoperation were identified, with patient features such as increasing age, higher American Society of Anesthesiologists grade (> III), and World Health Organization obesity classes II to III associated with elevated risks. A preoperative diagnosis of idiopathic necrosis increased revision risk. Concerning implant design, factors such as cementless femoral fixation, reverse-hybrid fixation, hip resurfacing, and small (< 35 mm) or large (> 52 mm) femoral heads increased both revision and reoperation risks. Conclusion. This is the first study to develop machine-learning models to forecast the risk of PPFF necessitating secondary surgery. Future studies are required to externally validate our algorithm and assess its applicability in clinical practice. Cite this article: Bone Joint Res 2025;14(1):46–57

Objectives

This study tests the biomechanical properties of adjacent locked plate constructs in a femur model using Sawbones. Previous studies have described biomechanical behaviour related to inter-device distances. We hypothesise that a smaller lateral inter-plate distance will result in a biomechanically stronger construct, and that addition of an anterior plate will increase the overall strength of the construct.

Aims. This study aimed to investigate the optimal sagittal positioning of the uncemented femoral component in total knee arthroplasty to minimize the risk of aseptic loosening and periprosthetic fracture. Methods. Ten different sagittal placements of the femoral component, ranging from -5 mm (causing anterior notch) to +4 mm (causing anterior gap), were analyzed using finite element analysis. Both gait and squat loading conditions were simulated, and Von Mises stress and interface micromotion were evaluated to assess fracture and loosening risk. Results. During gait, varied sagittal positioning did not lead to excessive Von Mises stress or micromotion. However, under squat conditions, posterior positioning (-4 and -5 mm) resulted in stress exceeding 150 MPa at the femoral notch, indicating potential fracture risk. Conversely, +1 mm and 0 mm sagittal positions demonstrated minimal interface micromotion. Conclusion. Slightly anterior sagittal positioning (+1 mm) or neutral positioning (0 mm) effectively reduced stress concentration at the femoral notch and minimized interface micromotion. Thus, these positions are deemed suitable to decrease the risk of aseptic loosening and periprosthetic femoral fracture

Objectives. Periprosthetic femoral fractures (PFFs) have a higher incidence with cementless stems. The highest incidence among various cementless stem types was observed with double-wedged stems. Short stems have been introduced as a bone-preserving alternative with a higher incidence of PFF in some studies. The purpose of this study was a direct load-to-failure comparison of a double-wedged cementless stem and a short cementless stem in a cadaveric fracture model. Methods. Eight hips from four human cadaveric specimens (age mean 76 years (60 to 89)) and eight fourth-generation composite femurs were used. None of the cadaveric specimens had compromised quality (mean T value 0.4 (-1.0 to 5.7)). Each specimen from a pair randomly received either a double-wedged stem or a short stem. A materials testing machine was used for lateral load-to-failure test of up to a maximal load of 5000 N. Results. Mean load at failure of the double-wedged stem was 2540 N (1845 to 2995) and 1867 N (1135 to 2345) for the short stem (p < 0.001). All specimens showed the same fracture pattern, consistent with a Vancouver B2 fracture. The double-wedged stem was able to sustain a higher load than its short-stemmed counterpart in all cases. Failure force was not correlated to the bone mineral density (p = 0.718). Conclusion. Short stems have a significantly lower primary load at failure compared with double-wedged stems in both cadaveric and composite specimens. Surgeons should consider this biomechanical property when deciding on the use of short femoral stem. Cite this article: A. Klasan, M. Bäumlein, P. Dworschak, C. Bliemel, T. Neri, M. D. Schofer, T. J. Heyse. Short stems have lower load at failure than double-wedged stems in a cadaveric cementless fracture model. Bone Joint Res 2019;8:489–494. DOI: 10.1302/2046-3758.810.BJR-2019-0051.R1

Aims

There are concerns regarding initial stability and early periprosthetic fractures in cementless hip arthroplasty using short stems. This study aimed to investigate stress on the cortical bone around the stem and micromotions between the stem and cortical bone according to femoral stem length and positioning.