Abstract
Introduction:
The risk for late periprosthetic fractures is higher in patients treated for a neck of femur fracture compared to those treated for osteoarthritis. It has been hypothesised that osteopenia and consequent decreased stiffness of the proximal femur are responsible for this. We investigated if a femoral component with a bigger body would increase the torque to failure in a biaxially loaded composite sawbone model.
Method:
A biomechanical composite sawbone model was used. Two different body sizes (Exeter 44-1 vs 44-4) of a polished tapered cemented stem were implanted by an experienced surgeon, in 7 sawbones each and loaded at 40 deg/s internal rotation until failure. Torque to fracture and fracture energy were measured using a biaxial materials testing device (Instron 8874). Data are non-parametric and tested with Mann-Whitney U-test.
Results:
The mean torque load to fracture was 154.1 NM (SD 4.4) for the 44-1 stem and 229 NM (SD10.9) for the 44-4 stem (p = 0.01). The mean fracture energy was 9.6 J (SD1.2) for the 44-1 stem and 17.2 J (SD2.0) for the 44-4 stem (p = 0.14).
Conclusion:
the use of a large body polished tapered cemented stem for neck of femur fractures increases the torque to failure in a biomechanical model and therefore is likely to reduce late periprosthetic fracture risk in this vulnerable cohort.