Abstract
Background
Second-generation high-carbon CoCrMo-alloy metal-on-metal total hip arthroplasty (THA) was introduced in the late 1980s following reports of early loosening, impingement, pronounced wear, and hypersensitivity in the first-generation metal-on-metal articulations. There has been inconsistent data that specifically addresses the clinical performance and longevity of second-generation metal-on-metal THA. The purpose of this study was to evaluate the survival of second-generation metal-on-metal primary THA and to assess the influence of demographic factors on implant survival in a large patient cohort.
Methods
One thousand two hundred and seventy second-generation 28 mm metal-on-metal primary THA in 1121 patients were performed at one institution from 1994 to 2004. According to the International Documentation and Evaluation System patients were followed routinely at one year, two years and every five years thereafter. Clinical and radiographic outcome data was prospectively recorded using a hospital joint registry. At a mean follow-up of 6.8 years postoperatively, the probability of survival of THA was estimated using the method of Kaplan and Meier. Relative risk factors for implant failure that included age, gender, BMI, type of implant fixation and size of implant components were calculated using the Cox proportional-hazards model.
Results
Sixty three (5%) hips were revised because of aseptic loosening (28 hips), infection (8 hips), periprosthetic fracture (8 hips), recurrent dislocation (8 hips), pain without implant loosening (7 hips) and breakage of the cup (4 hips). The probability of survival at ten years, with revision for any reason as the endpoint, for the THA as a whole was 0.90 (95% confidence interval, 0.87 to 0.94). The probability of survival for the cup was 0.90 (95% confidence interval, 0.86 to 0.93) and for the stem 0.94 (95% confidence interval, 0.91 to 0.97). No demographic factors or covariates were found to significantly affect survivorship.
Conclusion
Second-generation metal-on-metal primary THA did not demonstrate a superior probability of survival at ten years compared with previous reports on other weight-bearing surfaces. Based on these findings and with consideration of concerns that relate to putative local and systemic toxicity of metal debris, the use of second-generation metal-on-metal articulations for primary THA remains moot.