Abstract
Abstract
Introduction
Several studies have reported significant cobalt(Co) and chromium(Cr) elevations in the blood of patients with total-knee-replacements (TKRs), and histological signs of metal sensitivity have been reported in up to 44% of patients undergoing revision of their TKRs. We carried out this investigation to determine the source and quantity of metal release in TKRs.
Methodology
We identified all TKRs with polished CoCr trays (N=59) [Vanguard=29, Attune=4 and PFC=26]. These were analysed using peer-reviewed [coordinate-measuring-machine (CMM)] methodology to measure the volumetric wear of the polyethylene (PE) bearing surfaces and trays. The trays were analysed using 2D-profilometry (surface roughness-Ra) and 4D-microscopy. Histological and blood metal ion concentration analyses were performed.
Results
The median(IQR) PE wear rate was 10(6to20) mm3/year. Microscopic analysis identified pitting on superior surface of 36(49%) trays. Ra [median (IQR)] of superior surface of pitted trays [0.076 (0.060–0.084) µm] showed a statistically significant increase (p<0.001) compared with unpitted trays [0.057(0.049–0.066) µm]. 4D-microscopy and CMM analysis estimated wear volumes of up to 2mm3 secondary to pitting. The median (range) Co and Cr concentrations were 2.5µg/l (0.2–69.4) and 1.7µg/l (0.5–12.5) respectively in 40 patients. Of the tissue samples examined in 30 patients,6 had at-least “mild”-ALVAL infiltrate. All corresponding “ALVAL” explants were found to be pitted and/or show evidence of loosening of the tray.
Conclusion
This study provides further evidence that CoCr release in TKR appears to be an under-recognised cause of adverse clinical outcomes. Gross metal ion elevations occurred in association with micromotion/loosening of the tray.