Abstract
Introduction
Total hip replacement failure due to fretting-corrosion remains a clinical concern. We recently described that damage within CoCrMo femoral heads can occur either by mechanically-dominated fretting processes leading to imprinting (via rough trunnions) and surface fretting (via smooth trunnions), or by a chemically-dominated etching process along preferential corrosion sites, termed “column damage”. These corrosion sites occur due to banding of the alloy microstructure. Banding is likely caused during thermo-mechanical processing of the alloy and is characterized by local molybdenum depletion. It was the objective of this study to quantify material loss from femoral heads with severe corrosion, identify the underlying damage modes, and to correlate the damage to the alloy's microstructure.
Methods
105 femoral heads with a Goldberg score 4 were evaluated. Coordinate measuring machine data was used to compute material loss and visualize damage features. Time in situ and stem alloy were identified. Metallographic samples were produced for each case. Grain size and banding were identified using light-microscopy. Mann-Whitney tests were conducted to compare material loss between groups.
Results
Heads exhibited imprinting and column damage in 72 and 51 cases, respectively, with an overlap of 36 cases. 18 heads exhibited surface fretting only. All heads with column damage exhibited a banded microstructure. Heads with column damage had higher material loss (p=0.05) than those without. Also, heads with a banded microstructure had higher material loss (p=0.035) than those with a homogenous microstructure. Grain size, carbide content, and time did not correlate with material loss.
Conclusion
Column damage is a detrimental damage mode within CoCrMo femoral heads that is directly linked to banding within its microstructure. It appears that banding even affects material loss before column damage is identifiable. These results indicate that implant alloy microstructure must be optimized to minimize the release of fretting-corrosion products and related implant failure.