Abstract
Background: Joint replacements are being performed on ever younger patients at a time when average expectancy of life is continuing to rise. Any reduction in the strength and mass of periprosthetic bone could threaten the longevity of implant by predisposing to loosening and migration of prosthesis, periprosthetic fracture and problems in revision arthroplasty.
Aims and Objectives: This study aims to analyse and compare prospectively the femoral periprosthetic stress-shielding around 4/5th and 1/3rd porous coated cementless femoral stems in patients undergoing unilateral cementless total hip replacement done using DEXA scan by quantifying the changes in bone mineral density around femoral component.
Material and Method: Femoral periprosthetic bone mineral density was measured in the seven Gruen Zones with DEXA scan at 2 weeks, 1 years and 2 years after surgery in 60 patients who had undergone unilateral cementless total hip replacement, of which 30 patients had been implanted with 4/5th porous coated stems and other 30 patients with 1/3rd porous coated stems.
Results: At both one and two years postoperatively, bone loss due to stress-shielding was seen in both stems with maximum loss in zone VII and minimum in zone III, IV, V. The maximum mean percentage bone mineral density loss in 4/5th porous coated stems in zone VII was 16.03% at one year and 22.42% at 2 years as compared to loss of 10.07% and 16.01% in 1/3rd porous coated stems. Increased bone loss was seen in patients who had larger diameter stem (> 13.0 mm) and in patients with low bone mineral density in the unoperated hip.
Conclusion: Bone loss as a result of stress-shielding is more pronounced in 4/5th porous coated stems as compared to 1/3rd porous coated stems.