Abstract
Ceramic head and metal liner hip replacements (COM) have shown reduced wear in comparison to metal-on-metal (MOM) bearings. The aim of this study was to further assess the performance by a wear simulator study under standard and adverse conditions, including the wear of a metal head against a ceramic liner.
Components were Biolox Delta and CoCrMo alloy. Hip simulator testing applied a simplified walking cycle to anatomically mounted prostheses. The lubricant was 25% calf-serum and wear was measured gravimetrically. In hip simulator testing with edge loading a standard cycle was adapted so the head sub-luxed in the swing phase forcing the head onto the edge of the cup at heel strike, this was applied to ceramic on metal and metal on ceramic material combinations.
Under standard conditions the total overall mean wear rate of the MOM THR (1.01±0.38mm3/Mc) was significantly higher in comparison to the COM and COC (< 0.015mm3/Mc). The overall mean wear rate for the MOC bearings (0.71±0.30mm3/Mc) was significantly higher than the wear rate for the COM bearings (0.09±0.025mm3/Mc). The contact of the head against the rim of the cup caused deep stripe wear on the metallic heads of the MOC bearings. This region on the head is exposed to high stress conditions and susceptible to damage in edge contact, the effect of this is increased when the cup is a harder material than the head. The wear of a metal-on-metal (MOM) couple under similar conditions was almost two-fold greater than the MOC couple (1.58mm3/Mc, Williams et al., 2006) providing further evidence of the reduced wear with COM in comparison to MOM.
Reduced wear from COM bearings will address some concerns associated with MOM THRs regarding reports of elevated ion levels clinically. These studies have provided valuable data demonstrating reduced wear with COM bearings. COM bearings are undergoing clinical trials, early data suggests reduced metal ion release in patients compared to metal-on-metal
The abstracts were prepared by David AF Morgan. Correspondence should be addressed to him at davidafmorgan@aoa.org.au
Declaration of interest: c: In relation to the conduct of this study, one or more the authors have received, or are likely to receive direct material benefits.