Abstract
Aims: Metal-on-Metal (MOM) bearings for Total Hip Arthroplasty (THA) are known to elevate the serum concentrations of metal ions, raising concern about possible long-term side-effects. One potential modifier of ion release is the bearing diameter used. Resurfacing MOM bearings have a large surface area available for corrosion, but may benefit from improved lubrication and reduced production of corrodible wear debris. The net effect of these two variables on metal ion release is unknown.
Methods: In this study, we measured the serum cobalt and chromium levels from 22 large diameter MOM resurfacing arthroplasties (Cormet2000 & Birmingham Hip Resurfacing) and compared them to 22 THA (Ultima) with a bearing diameter of 28 mm. Patients were prospectively matched for activity level, weight and date after surgery. All were at least 6 months after surgery.
Results: At a median of 16 months (range 7 to 56) after resurfacing arthroplasty, we found the median serum cobalt and chromium levels to be 38 nmol/l (14 to 44) and 53 nmol/l (23 to 165) respectively. Both these figures were significantly greater than the levels after 28 mm MOM THA, which were 22 nmol/l (15 to 87, p=0.021) and 19 nmol/l (2 to 58, p< 0.001) for cobalt and chromium respectively.
Conclusions: As the upper limit of normal in patients without implants is typically 5 nmol/l, both groups had significantly raised metal ion levels, albeit at a relatively short median follow-up period. Large diameter MOM bearings resulted in a greater systemic release of cobalt and chromium ions than did small diameter bearings. This may be of relevance for potential long-term side-effects. It is not known to what extent this difference is due to corrosion of the component surfaces or of the wear particles produced.
Theses abstracts were prepared by Mr Peter Kay. Correspondence should be address to him at The Hip Centre, Wrightington Hospital, Appley Bridge, Wigan, Lancashire WN6 9EP.